Abstract: Rice Husk (RH) is the major byproduct in the
processing of paddy rice. The management of this waste has become
a big challenge to some of the rice producers, some of these wastes
are left in open dumps while some are burn in the open space, and
these two actions have been contributing to environmental pollution.
This study evaluates an alternative waste management of this
agricultural product for use as a civil engineering material. The RH
was burn in a controlled environment to form Rice Husk Ash (RHA).
The RHA was mix with lateritic clay at 0, 2, 4, 6, 8, and 10%
proportion by weight. Chemical test was conducted on the open burn
and controlled burn RHA with the lateritic clay. Physical test such as
particle size distribution, Atterberg limits test, and density test were
carried out on the mix material. The chemical composition obtained
for the RHA showed that the total percentage compositions of Fe2O3,
SiO2 and Al2O3 were found to be above 70% (class “F” pozzolan)
which qualifies it as a very good pozzolan. The coefficient of
uniformity (Cu) was 8 and coefficient of curvature (Cc) was 2 for the
soil sample. The Plasticity Index (PI) for the 0, 2, 4, 6, 8. 10% was
21.0, 18.8, 16.7, 14.4, 12.4 and 10.7 respectively. The work
concluded that RHA can be effectively used in hydraulic barriers and
as a stabilizing agent in soil stabilization.
Abstract: Construction and Demolition (C&D) wastes contribute the highest percentage of wastes worldwide (75%). Furthermore, ceramic materials contribute the highest percentage of wastes within the C&D wastes (54%). The current option for disposal of ceramic wastes is landfill. This is due to unavailability of standards, avoidance of risk, lack of knowledge and experience in using ceramic wastes in construction. The ability of ceramic wastes to act as a pozzolanic material in the production of cement has been effectively explored. The results proved that temperatures used in the manufacturing of these tiles (about 900⁰C) are sufficient to activate pozzolanic properties of clay. They also showed that, after optimization (11-14% substitution); the cement blend performs better, with no morphological difference between the cement blended with ceramic waste, and that blended with other pozzolanic materials. Sanitary ware and electrical insulator porcelain wastes are some wastes investigated for usage as aggregates in concrete production. When optimized, both produced good results, better than when natural aggregates are used. However, the research on ceramic wastes as partial substitute for fine aggregates or cement has not been overly exploited as the other areas. This review has been concluded with focus on investigating whether ceramic wall tile wastes used as partial substitute for cement and fine aggregates could prove to be beneficial since the two materials are the most high-priced during concrete production.