Abstract: There have been many reports of the destructive effects of cement on the environment in recent years. In the present research, it has been attempted to reduce the destructive effects of cement by replacing silica fume as adhesive materials instead of cement. The present study has attempted to improve the mechanical properties of cement slurry by using waste material from a glass production factory, located in Qazvin city of Iran, in which accumulation volume has become an environmental threat. The chemical analysis of the waste material indicates that this material contains about 94% of SiO2 and AL2O3 and has a close structure to silica fume. Also, the particle grain size test was performed on the mentioned waste. Then, the unconfined compressive strength test of the slurry was performed by preparing a mixture of water and adhesives with different percentages of cement and silica fume. The water to an adhesive ratio of this mixture is 1:3, and the curing process last 28 days. It was found that the sample had an unconfined compressive strength of about 300 kg/cm2 in a mixture with equal proportions of cement and silica fume. Besides, the sample had a brittle fracture in the slurry sample made of pure cement, however, the fracture in cement-silica fume slurry mixture is flexible and the structure of the specimen remains coherent after fracture. Therefore, considering the flexibility that is achieved by replacing this waste, it can be used to stabilize soils with cracking potential.
Abstract: Due to the difficult placement and vibration between reinforcements of reinforced concrete and the defects that it may cause, the use of self-compacting concrete (SCC) is becoming more widespread. Ordinary Portland Cement (OPC) is the most widely used binder in the construction industry. However, the manufacture of this cement results in a significant amount of CO2 being released, which is detrimental to the environment. Thus, an alternative to reduce the cost of SCC is the use of more economical and environmental mineral additives in partial or total substitution of Portland cement. Our study is in this context and aims to develop SCCs both economic and ecological. Two natural pozzolans such as pumice and zeolite are chosen in this research. This research tries to answer questions including the microstructure of the two types of natural pozzolan and their influence on the mechanical properties as well as on the transport property of SCC. Based on the findings of this study, the studied zeolite is a clinoptilolite that presents higher pozzolan activity compared to pumice. However, the use of zeolite decreases the compressive strength of SCC composites. On the contrary, the compressive strength in SCC containing of pumice increases at both early and long term ages with a remarkable increase at long term. A correlation is obtained between the compressive strength with permeable pore and capillary absorption. Also, the results concerning compressive strength and transport property are well justified by evaporable and non-evaporable water content measurement. This paper shows that the substitution of Portland cement by 15% of pumice or 10% of zeolite in HSSCC is suitable in all aspects.
Abstract: Rice Husk (RH) is the major byproduct in the
processing of paddy rice. The management of this waste has become
a big challenge to some of the rice producers, some of these wastes
are left in open dumps while some are burn in the open space, and
these two actions have been contributing to environmental pollution.
This study evaluates an alternative waste management of this
agricultural product for use as a civil engineering material. The RH
was burn in a controlled environment to form Rice Husk Ash (RHA).
The RHA was mix with lateritic clay at 0, 2, 4, 6, 8, and 10%
proportion by weight. Chemical test was conducted on the open burn
and controlled burn RHA with the lateritic clay. Physical test such as
particle size distribution, Atterberg limits test, and density test were
carried out on the mix material. The chemical composition obtained
for the RHA showed that the total percentage compositions of Fe2O3,
SiO2 and Al2O3 were found to be above 70% (class “F” pozzolan)
which qualifies it as a very good pozzolan. The coefficient of
uniformity (Cu) was 8 and coefficient of curvature (Cc) was 2 for the
soil sample. The Plasticity Index (PI) for the 0, 2, 4, 6, 8. 10% was
21.0, 18.8, 16.7, 14.4, 12.4 and 10.7 respectively. The work
concluded that RHA can be effectively used in hydraulic barriers and
as a stabilizing agent in soil stabilization.
Abstract: High strength concrete has been used in situations
where it may be exposed to elevated temperatures. Numerous authors
have shown the significant contribution of polypropylene fiber to the
spalling resistance of high strength concrete.
When cement-based composite that reinforced by polypropylene
fibers heated up to 170 °C, polypropylene fibers readily melt and
volatilize, creating additional porosity and small channels in to the
matrix that cause the poor structure and low strength.
This investigation develops on the mechanical properties of mortar
incorporating polypropylene fibers exposed to high temperature.
Also effects of different pozzolans on strength behaviour of samples
at elevated temperature have been studied.
To reach this purpose, the specimens were produced by partial
replacement of cement with finely ground glass, silica fume and rice
husk ash as high reactive pozzolans. The amount of this replacement
was 10% by weight of cement to find the effects of pozzolans as a
partial replacement of cement on the mechanical properties of
mortars. In this way, lots of mixtures with 0%, 0.5%, 1% and 1.5% of
polypropylene fibers were cast and tested for compressive and
flexural strength, accordance to ASTM standard. After that
specimens being heated to temperatures of 300, 600 °C, respectively,
the mechanical properties of heated samples were tested.
Mechanical tests showed significant reduction in compressive
strength which could be due to polypropylene fiber melting. Also
pozzolans improve the mechanical properties of sampels.