Abstract: The main objective of this paper is to evaluate the use of plastic waste as a low cost asphalt binder modifier. For this purpose Marshall mix design procedure was used. Marshall mix design procedure seeks to select the Optimum Binder Content (OBC) to be added to a specific aggregate blend resulting in a mixture that satisfies the desired properties of strength and durability. In order to evaluate the plastic waste modified (PWM) asphalt mixtures, the OBC for the conventional asphalt mix was first identified, and then different percentages of crushed plastic waste by weight of the identified OBC were tested. Marshall test results for the modified asphalt mixtures were analyzed to find the optimum PWM content. Finally, the static indirect tensile strength (IDT) was determined for all mixtures using the splitting tensile test. It was found that PWM content of 7.43% by weight of OBC is recommended as the optimum PWM content needed for enhancing the performance of asphalt mixtures. It enhanced stability by 42.56%, flow by 89.91% and strength by 13.54%. This would lead to a more durable pavement by improving the pavement resistance to fatigue cracking and rutting.
Abstract: This paper is focused on the mechanical characterization of foamed concrete specimens with protein-based foaming agent. Unlike classic foamed concrete, a peculiar property of the analyzed foamed concrete is the extrudability, which is achieved via a specific additive in the concrete mix that significantly improves the cohesion and viscosity of the fresh cementitious paste. A broad experimental campaign was conducted to evaluate the compressive strength and the indirect tensile strength of the specimens. The study has comprised three different cement types, two water/cement ratios, three curing conditions and three target dry densities. The variability of the strength values upon the above mentioned factors is discussed.
Abstract: The recent hike in raw materials costs and the quest for preservation of the environment has prompted asphalt industries to adopt greener road construction technology. This paper presents a study on such technology by means of asphalt recycling and use of warm mix asphalt (WMA) additive. It evaluates the effects of a WMA named RH-WMA on binder rheological properties and asphalt mixture performance. The recycled asphalt, obtained from local roads, was processed, fractionated, and incorporated with virgin aggregate and binder. For binder testing, the recycled asphalt was extracted and blended with virgin binder. The binder and mixtures specimen containing 30 % and 50 % recycled asphalt contents were mixed with 3 % RH-WMA. The rheological properties of the binder were evaluated based on fundamental, viscosity, and frequency sweep tests. Indirect tensile strength and resilient modulus tests were carried out to assess the mixture’s performances. The rheological properties and strength performance results showed that the addition of RH-WMA slightly reduced the binder and mixtures stiffness. The percentage of recycled asphalt increased the stiffness of binder and mixture, and thus improves the resistance to rutting. Therefore, the integration of recycled asphalt and RH-WMA can be an alternative material for road sustainable construction for countries in the tropics.
Abstract: This paper discusses the effect of using blast furnace iron slag as a part of fine aggregate on the mechanical performance of hot mix asphalt (HMA). The mechanical performance was evaluated based on various mechanical properties that include; Marshall/stiffness, indirect tensile strength and unconfined compressive strength. The effect of iron slag content on the mechanical properties of the mixtures was also investigated. Four HMA with various iron slag contents, namely; 0%, 5%, 10% and 15% by weight of total mixture were studied. Laboratory testing has revealed an enhancement in the compressive strength of HMA when iron slag was used. Within the tested range of iron slag content, a considerable increase in the compressive strength of the mixtures was observed with the increase of slag content. No significant improvement on Marshall/stiffness and indirect tensile strength of the mixtures was observed when slag was used. Even so, blast furnace iron slag can still be used in asphalt paving for environmental advantages.
Abstract: With the strengthened regulation on the mandatory use
of recycled aggregate, development of construction materials using
recycled aggregate has recently increased. This study aimed to secure
the performance of asphalt concrete mixture by developing
recycled-modified asphalt using recycled basalt aggregate from the
Jeju area. The strength of the basalt aggregate from the Jeju area used
in this study was similar to that of general aggregate, while the specific
surface area was larger due to the development of pores. Modified
asphalt was developed using a general aggregate-recycled aggregate
ratio of 7:3, and the results indicated that the Marshall stability
increased by 27% compared to that of asphalt concrete mixture using
only general aggregate, and the flow values showed similar levels.
Also, the indirect tensile strength increased by 79%, and the toughness
increased by more than 100%. In addition, the TSR for examining
moisture resistance was 0.95 indicating that the reduction in the
indirect tensile strength due to moisture was very low (5% level), and
the developed recycled-modified asphalt could satisfy all the quality
standards of asphalt concrete mixture.
Abstract: This study investigates the effect of moisture
conditioning on the Indirect Tensile Strength (ITS) of asphalt
concrete. As a first step, cylindrical samples of 100 mm diameter and
50 mm thick were prepared using a Superpave gyratory compactor.
Next, the samples were conditioned using Moisture Induced
Susceptibility Test (MIST) device at different numbers of moisture
conditioning cycles. In the MIST device, samples are subjected water
pressure through the sample pores cyclically. The MIST conditioned
samples were tested for ITS. Results show that the ITS does not
change significantly with MIST conditioning at the specific pressure
and cycles adopted in this study.