Abstract: Research on the utilization of fly ash will no longer refer the fly ash as a waste material of thermal power plants. Use of fly ash in concrete making, makes the concrete economical as well as durable. The fly ash is being added to the concrete in three ways namely, as partial replacement to cement, as partial replacement to fine aggregates and as admixture. Addition of fly ash to the concrete in any one of the form mentioned above, makes the concrete more workable and durable than the conventional concrete. Studies on fly ash as partial replacement to cement gained momentum as such replacement makes the concrete economical. In the present study, an attempt has been made to understand the effects of fly ash on the workability characteristics and strength aspects of fly ash concretes. In India major number of thermal power plants is producing low calcium fly ash. Hence in the present investigation low calcium fly ash has been used. Fly ash in concrete was considered for the partial replacement of cement. The percentage replacement of cement by fly ash varied from 0% to 40% at regular intervals of 10%. More over the fine aggregate to coarse aggregate ratio also has been varied as 1:1, 1:2 and 1:3. The workability tests revealed that up to 30% replacement of cement by fly ash in concrete mixes water demand for reduces, beyond 30% replacement of cement by fly ash demanded more water content for constant workability.
Abstract: The research investigates the effects of super plasticizer and molarity of sodium hydroxide alkaline solution on the workability, microstructure and compressive strength of self compacting geopolymer concrete (SCGC). SCGC is an improved way of concreting execution that does not require compaction and is made by complete elimination of ordinary Portland cement content. The parameters studied were superplasticizer (SP) dosage and molarity of NaOH solution. SCGC were synthesized from low calcium fly ash, activated by combinations of sodium hydroxide and sodium silicate solutions, and by incorporation of superplasticizer for self compactability. The workability properties such as filling ability, passing ability and resistance to segregation were assessed using slump flow, T-50, V-funnel, L-Box and J-ring test methods. It was found that the essential workability requirements for self compactability according to EFNARC were satisfied. Results showed that the workability and compressive strength improved with the increase in superplasticizer dosage. An increase in strength and a decrease in workability of these concrete samples were observed with the increase in molarity of NaOH solution from 8M to 14M. Improvement of interfacial transition zone (ITZ) and micro structure with the increase of SP and increase of concentration from 8M to 12M were also identified.
Abstract: The present paper reports results of an experimental
program conducted to study performance of fly ash based
geopolymer pastes at elevated temperature. Three series of
geopolymer pastes differing in Na2O content (8.5%, 10% and 11.5%)
were manufactured by activating low calcium fly ash with a mixture
of sodium hydroxide and sodium silicate solution. The paste
specimens were subjected to temperatures as high as 900oC and the
behaviour at elevated temperatures were investigated on the basis of
physical appearance, weight losses, residual strength, shrinkage
measurements and sorptivity tests at different temperatures. Scanning
electron microscopy along with EDX and XRD tests were also
conducted to examine microstructure and mineralogical changes
during the thermal exposure. Specimens which were initially grey
turned reddish accompanied by appearance of small cracks as the
temperature increased to 900oC. Loss of weight was more in
specimens manufactured with highest Na2O content. Geopolymer
paste specimen containing minimum Na2O performed better than
those with higher Na2O content in terms of residual compressive
strength.
Abstract: Use of fly ash as a supplementary cementing material
in large volumes can bring both technological and economic benefits
for concrete industry. In this investigation mix proportions for high
volume fly ash concrete were determined at cement replacement
levels of 50%, 55%, 60% and 65% with low calcium fly ash. Flexural
and compressive strengths of different mixes were measured at ages
of 7, 28 and 90 days. Flexural strength of composite section prepared
from pavement quality and lean high volume fly ash concrete was
determined at the age of 28 days. High volume fly ash concrete mixes
exhibited higher rate of strength gain and age factors than
corresponding reference concrete mixes. The optimum cement
replacement level for pavement quality concrete was found to be
60%. The consideration of bond between pavement quality and lean
of high volume fly ash concrete will be beneficial in design of rigid
pavements.