Abstract: This study investigates the effect of using carbon-free fly ash (CfFA) and ground granulated blast-furnace slag (GGBFS) on the compressive strength of mortar. The CfFA used in this investigation is high-quality fly ash and the carbon content is 1.0% or less. In this study, three types of blends with a 30% water-binder ratio (w/b) were prepared: control, binary and ternary blends. The Control blend contained only Ordinary Portland Cement (OPC), in binary and ternary blends OPC was partially replaced with CfFA and GGBFS at different substitution rates. Mortar specimens were cured for 1 day, 7 days and 28 days under two curing conditions: steam curing and water curing. The steam cured specimens were exposed to two different pre-curing times (1.5 h and 2.5 h) and one steam curing duration (6 h) at 45 °C. The test results showed that water cured specimens revealed higher compressive strength than steam cured specimens at later ages. An increase in CfFA and GGBFS contents caused a decrease in the compressive strength of mortar. Ternary mixes exhibited better compressive strength than binary mixes containing CfFA with the same replacement ratio of mineral admixtures.
Abstract: This paper is focused on the mechanical characterization of foamed concrete specimens with protein-based foaming agent. Unlike classic foamed concrete, a peculiar property of the analyzed foamed concrete is the extrudability, which is achieved via a specific additive in the concrete mix that significantly improves the cohesion and viscosity of the fresh cementitious paste. A broad experimental campaign was conducted to evaluate the compressive strength and the indirect tensile strength of the specimens. The study has comprised three different cement types, two water/cement ratios, three curing conditions and three target dry densities. The variability of the strength values upon the above mentioned factors is discussed.
Abstract: Geopolymer mortar is produced by alkaline activation of pozzolanic materials such as fly ground granulated blast-furnace slag (GGBFS) and fly ash (FA). Its unique reaction pathway facilitates rapid strength development in comparison with hydration of ordinary Portland cement (OPC). Geopolymer can be fabricated using various types and dosages of alkali-activator, which effectively gives a wider control over the performance of the final product. The present study investigates the effect of types of precursors and curing conditions on the fresh state and strength development characteristics of geopolymers, thereby comparatively exploring the effect of precursors from various sources of origin. The obtained result showed that the setting time and strength development of the specimens with the identical mix proportion but different precursors displayed significant variations.
Abstract: Concrete is the predominant construction material in Bangladesh. In large projects, stringent quality control procedures are usually followed under the supervision of experienced engineers and skilled labors. However, in the case of small projects and particularly at distant locations from major cities, proper quality control is often an issue. It has been found from experience that such quality related issues mainly arise from inappropriate proportioning of concrete mixes and improper curing conditions. In most cases external curing method is followed which requires supply of adequate quantity of water along with proper protection against evaporation. Often these conditions are found missing in the general construction sites and eventually lead to production of weaker concrete both in terms of strength and durability. In this study, an attempt has been made to investigate the performance of general concreting works of the country when subjected to several adverse curing conditions that are quite common in various small to medium construction sites. A total of six different types of adverse curing conditions were simulated in the laboratory and samples were kept under those conditions for several days. A set of samples was also submerged in normal curing condition having proper supply of curing water. Performance of concrete was evaluated in terms of compressive strength, tensile strength, chloride permeability and drying shrinkage. About 37% and 25% reduction in 28-day compressive and tensile strength were observed respectively, for samples subjected to most adverse curing condition as compared to the samples under normal curing conditions. Normal curing concrete exhibited moderate permeability (close to low permeability) whereas concrete under adverse curing conditions showed very high permeability values. Similar results were also obtained for shrinkage tests. This study, thus, will assist concerned engineers and supervisors to understand the importance of quality assurance during the curing period of concrete.
Abstract: Lightweight concrete is being used in the construction industry as a building material in its own right. Ultra-lightweight concrete can be applied as a filler and support material for the manufacturing of composite building materials. This paper is about the development of a stable and reproducible ultra-lightweight concrete with the inclusion of poly-lactic acid (PLA) beads and assessing the feasibility of PLA as a lightweight aggregate that will deliver advantages such as a more eco-friendly concrete and a non-petroleum polymer aggregate. In total, sixty-three samples were prepared and the effectiveness of mineral admixture, curing conditions, water-cement ratio, PLA ratio, EPS ratio and perlite ratio on compressive strength of perlite concrete are studied. The results show that PLA particles are sensitive to alkali environment of cement paste and considerably shrank and lost their strength. A higher compressive strength and a lower density was observed when expanded polystyrene (EPS) particles replaced PLA beads. In addition, a set of equations is proposed to estimate the water-cement ratio, cement content and compressive strength of perlite concrete.
Abstract: The purpose of this study is to compare Self
Compacting Concrete (SCC) and Conventional Concrete (CC) in
terms of their capillary water absorption. During the comparison of
SCC and CC, the effects of two different factors were also
investigated: concrete strength class and curing condition. In the
study, both SCC and CC were produced in three different concrete
classes (C25, C50 and C70) and the other parameter (i.e. curing
condition) was determined as two levels: moisture and air curing. It
was observed that, for both curing environments and all strength
classes of concrete, SCCs had lower capillary water absorption values
than that of CCs. It was also detected that, for both SCC and CC,
capillary water absorption values of samples kept in moisture curing
were significantly lower than that of samples stored in air curing.
Additionally, it was determined that capillary water absorption values
for both SCC and CC decrease with increasing strength class of
concrete for both curing environments.
Abstract: The main objective of the study is focused in
producing slag based geopolymer concrete obtained with the addition
of alkali activator. Test results indicated that the reaction of silicates
in slag is based on the reaction potential of sodium hydroxide and the
formation of alumino-silicates. The study also comprises on the
evaluation of the efficiency of polymer reaction in terms of the
strength gain properties for different geopolymer mixtures.
Geopolymer mixture proportions were designed for different binder
to total aggregate ratio (0.3 & 0.45) and fine to coarse aggregate ratio
(0.4 & 0.8). Geopolymer concrete specimens casted with normal
curing conditions reported a maximum 28 days compressive strength
of 54.75 MPa. The addition of glued steel fibres at 1.0% Vf in
geopolymer concrete showed reasonable improvements on the
compressive strength, split tensile strength and flexural properties of
different geopolymer mixtures. Further, comparative assessment was
made for different geopolymer mixtures and the reinforcing effects of
steel fibres were investigated in different concrete matrix.
Abstract: Service life of existing reinforced concrete (RC)
structures in coastal towns of Sabah has been affected very much.
Concrete crack, spalling of concrete cover and reinforcement rusting
of RC buildings are seen even within 5 years of construction in
Sabah. Hence, in this study a new mix design of concrete grout was
developed using locally available materials and investigated under
two curing conditions and workability, compressive strength,
Accelerated Mortar Bar Test (AMBT), water absorption, volume of
permeable voids (VPV), Sorptivity and 90-days salt ponding test
were conducted. The compressive strength of concrete grout at the
age 90 days was found to be 44.49 N/mm2 under water curing. It was
observed that the percentage of mortar bar length change was below
1% for developed concrete grout. The water absorption of the
concrete grout was in between the range of 0.88 % to 3.60 % under
two different curing up to the age 90 days. It was also observed that
the VPV of concrete was in the range of 0 % to 9.75 and 2.44% to
13.05% under water curing and site curing respectively. It was found
that the Sorptivity of the concrete grout under water curing at the age
of 28 days is 0.211mm/√min and at the age 90 day are 0.067
mm/√min. The chloride content decreased greatly, 90% after a depth
of 15 mm. It was noticed that the site cured samples showed higher
chloride contents near surface compared to water cured samples.
This investigation suggested that the developed mix design of
concrete grout using locally available construction materials can be
used for crack repairing of existing RC structures in Sabah.
Abstract: The compressive strength development through
polymerization process of alkaline solution and fly ash blended with Microwave Incinerated Rice Husk Ash (MIRHA) is described in this
paper. Three curing conditions, which are hot gunny curing, ambient
curing, and external humidity curing are investigated to obtain the suitable curing condition for cast in situ provision. Fly ash was
blended with MIRHA at 3%, 5%, and 7% to identify the effect of blended mixes to the compressive strength and microstructure
properties of geopolymer concrete. Compressive strength results
indicated an improvement in the strength development with external humidity curing concrete samples compared to hot gunny curing and
ambient curing. Blended mixes also presented better performance
than control mixes. Improvement of interfacial transition zone (ITZ)
and micro structure in external humidity concrete samples were also
identified compared to hot gunny and ambient curing.
Abstract: This paper reports the results of an experimental work
conducted to investigate the effect of curing conditions on the
compressive strength of self-compacting geopolymer concrete
prepared by using fly ash as base material and combination of sodium
hydroxide and sodium silicate as alkaline activator. The experiments
were conducted by varying the curing time and curing temperature in
the range of 24-96 hours and 60-90°C respectively. The essential
workability properties of freshly prepared Self-compacting
Geopolymer concrete such as filling ability, passing ability and
segregation resistance were evaluated by using Slump flow,
V-funnel, L-box and J-ring test methods. The fundamental
requirements of high flowability and resistance to segregation as
specified by guidelines on Self-compacting Concrete by EFNARC
were satisfied. Test results indicate that longer curing time and curing
the concrete specimens at higher temperatures result in higher
compressive strength. There was increase in compressive strength
with the increase in curing time; however increase in compressive
strength after 48 hours was not significant. Concrete specimens cured
at 70°C produced the highest compressive strength as compared to
specimens cured at 60°C, 80°C and 90°C.
Abstract: An advanced composite flywheel rotor consisting of
intra and inter hybrid rims was designed to optimally increase the energy capacity, and was manufactured using filament winding with
in-situ curing. The flywheel has recently attracted considerable attention from many investigators since it possesses great potential in
many energy storage applications, including electric utilities, hybrid or
electric automobiles, and space vehicles. In this investigation, a comprehensive study was conducted with the intent to implement
composites in high performance flywheel applications.The inner two
intra-hybrid rims (rims 1 and 2) were manufactured as a whole part
through continuous filament winding under in-situ curing conditions,
and so were the outer two rims (rims 3 and 4). The outer surface of rim
2 and the inner surface of rim 3 were CNC-tapered for press-fitting. Machined rims were finally press-fitted using a hydraulic press with a
maximum compressive force of approximately 1000 ton.
Abstract: Refractive index control of benzocyclobutene (BCB 4024-40) is achieved by facilitating different conditions during the thermal curing of BCB film. Refractive index (RI) change of 1.49% is obtained with curing of BCB film using an oven, while the RI change is 0.1% when the BCB is cured using a hotplate. The two different curing methods exhibit a temperature dependent refractive index change of the BCB photosensitive polymer. By carefully controlling the curing conditions, multiple layers of BCB with different RI can be fabricated, which can then be applied in the fabrication of optical waveguides.