Abstract: The self-consolidating concrete (SCC) performance over ordinary concrete is generally related to the ingredients used. The metakaolin can modify various properties of concrete, due to high pozzolanic reactions and also makes a denser microstructure. The objective of this paper is to examine the influence of three types of Portland cement and metakaolin on compressive strength and transport properties of SCC at early ages and up to 90 days. Six concrete mixtures were prepared with three types of different cements and substitution of 15% metakaolin. The results show that the highest value of compressive strength was achieved for Portland Slag Cement (PSC) and without any metakaolin at age of 90 days. Conversely, the lowest level of compressive strength at all ages of conservation was obtained for Pozzolanic Portland Cement (PPC) and containing 15% metakaolin. As can be seen in the results, compressive strength in SCC containing Portland cement type II with metakaolin is higher compared to that relative to SCC without metakaolin from 28 days of age. On the other hand, the samples containing PSC and PPC with metakaolin had a lower compressive strength than the plain samples. Therefore, it can be concluded that metakaolin has a negative effect on the compressive strength of SCC containing PSC and PPC. In addition, results show that metakaolin has enhanced chloride durability of SCCs and reduced capillary water absorption at 28, 90 days.
Abstract: This paper presents results of compressive strength,
capillary water absorption, and density tests conducted on concrete
containing recycled aggregate (RCA) which is obtained from
structural waste generated by the construction industry in Turkey. In
the experiments, 0%, 15%, 30%, 45% and 60% of the normal
(natural) coarse aggregate was replaced by the recycled aggregate.
Maximum aggregate particle sizes were selected as 16 mm, 22,4 mm
and 31,5 mm; and 0,06%, 0,13% and 0,20% of air-entraining agent
(AEA) were used in mixtures. Fly ash and superplasticizer were used
as a mineral and chemical admixture, respectively. The same type
(CEM I 42.5) and constant dosage of cement were used in the study.
Water/cement ratio was kept constant as 0.53 for all mixture. It was
concluded that capillary water absorption, compressive strength, and
density of concrete decreased with increasing RCA ratio. Increasing
in maximum aggregate particle size and amount of AEA also affect
the properties of concrete significantly.
Abstract: The purpose of this study is to compare Self
Compacting Concrete (SCC) and Conventional Concrete (CC) in
terms of their capillary water absorption. During the comparison of
SCC and CC, the effects of two different factors were also
investigated: concrete strength class and curing condition. In the
study, both SCC and CC were produced in three different concrete
classes (C25, C50 and C70) and the other parameter (i.e. curing
condition) was determined as two levels: moisture and air curing. It
was observed that, for both curing environments and all strength
classes of concrete, SCCs had lower capillary water absorption values
than that of CCs. It was also detected that, for both SCC and CC,
capillary water absorption values of samples kept in moisture curing
were significantly lower than that of samples stored in air curing.
Additionally, it was determined that capillary water absorption values
for both SCC and CC decrease with increasing strength class of
concrete for both curing environments.