Abstract: Psyllium gum alone and in combination with
sunflower oil was investigated as a possible alternative edible coating
for improvement of quality and shelf life of fresh-cut papaya.
Different concentrations including 0.5, 1 and 1.5 percent of psyllium
gum were used for coating of fresh-cut papaya. In some samples,
refined sunflower oil was used as a lipid component to increase the
effectiveness of coating in terms of water barrier properties. Soya
lecithin was used as an emulsifier in coatings containing oil.
Pretreatment with 1% calcium chloride was given to maintain the
firmness of fresh-cut papaya cubes. 1% psyllium gum coating was
found to yield better results. Further, addition of oil helped to
maintain the quality and acted as a barrier to water vapour, therefore,
minimizing the weight loss.
Abstract: The future and the development of science is therefore
seen in interdisciplinary areas such as biomedical engineering. Selfassembled
structures, similar to stem cell niches would inhibit fast
division process and subsequently capture the stem cells from the
blood flow. By means of surface topography and the stiffness as well
as microstructure progenitor cells should be differentiated towards
the formation of endothelial cells monolayer which effectively will
inhibit activation of the coagulation cascade. The idea of the material
surface development met the interest of the clinical institutions,
which support the development of science in this area and are waiting
for scientific solutions that could contribute to the development of
heart assist systems. This would improve the efficiency of the
treatment of patients with myocardial failure, supported with artificial
heart assist systems. Innovative materials would enable the redesign,
in the post project activity, construction of ventricular heart assist.
Abstract: In the past decade, the use of digital image correlation
(DIC) techniques has increased significantly in the area of
experimental mechanics, especially for materials behavior
characterization. This non-contact tool enables full field displacement
and strain measurements over a complete region of interest. The DIC
algorithm requires a random contrast pattern on the surface of the
specimen in order to perform properly. To create this pattern, the
specimen is usually first coated using a white matt paint. Next, a
black random speckle pattern is applied using any suitable method. If
the applied paint coating is too thick, its top surface may not be able
to exactly follow the deformation of the specimen, and consequently,
the strain measurement might be underestimated. In the present
article, a study of the influence of the paint thickness on the strain
underestimation is performed for different strain levels. The results
are then compared to typical paint coating thicknesses applied by
experienced DIC users. A slight strain underestimation was observed
for paint coatings thicker than about 30μm. On the other hand, this
value was found to be uncommonly high compared to coating
thicknesses applied by DIC users.
Abstract: Development of new generation bio-tribological,
multilayer coatings opens an avenue for fabrication of future hightech
functional surfaces. In the presented work, nano-composite,
Cr/CrN+[Cr/ a-C:H implanted by metallic nanocrystals] multilayer
coatings have been developed for surface protection of medical tools.
Thin films were fabricated by a hybrid Pulsed Laser Deposition
technique. Complex microstructure analysis of nanomultilayer
coatings, subjected to mechanical and biological tests, were
performed by means of transmission electron microscopy (TEM).
Microstructure characterization revealed the layered arrangement of
Cr23C6 nanoparticles in multilayer structure. Influence of deposition
conditions on bio-tribological properties of the coatings was studied.
The bio-tests were used as a screening tool for the analyzed
nanomultilayer coatings before they could be deposited on medical
tools. Bio-medical tests were done using fibroblasts. The mechanical
properties of the coatings were investigated by means of a ball-ondisc
mechanical test. The micro hardness was done using Berkovich
indenter. The scratch adhesion test was done using Rockwell
indenter. From the bio-tribological point of view, the optimal
properties had the C106_1 material.
Abstract: Electrodeposition is a simple and economic technique
for precision coating of different shaped substrates with pure metal,
alloy or composite films. Dc electrodeposition was used to produce
Cr, Co-Cr and Co-Cr/TiO2 nano-composite coatings from Cr(III)
based electrolytes onto 316L SS substrates. The effects of TiO2 nanoparticles
concentration on co-deposition of these particles along with
Cr content and microhardness of the coatings were investigated.
Morphology of the Cr, Co-Cr and Co-Cr/TiO2 coatings besides their
tribological behavior were studied. The results showed that increment
of TiO2 nanoparticles concentration from 0 to 30 g L-1 in the bath
increased their co-deposition and Cr content of the coatings from 0 to
3.5 wt.% and from 23.7 to 31.2 wt.%, respectively. Microhardness of
Cr coating was about 920 Hv which was higher than Co-Cr and even
Co-Cr/TiO2 films. Microhardness of Co-Cr and Co-Cr/TiO2 coatings
were improved by increasing their Cr and TiO2 content. All the
coatings had nodular morphology and contained microcracks.
Nodules sizes and the number of microcracks in the alloy and
composite coatings were lower than the Cr film. Wear results
revealed that the Co-Cr/TiO2 coating had the lowest wear loss
between all the samples, while the Cr film had the worst wear
resistance.
Abstract: Sol-enhanced Zn-Ni-Al2O3 nanocomposite coatings
were electroplated on mild steel by our newly developed solenhanced
electroplating method. In this method, transparent Al2O3 sol
was added into the acidic Zn-Ni bath to produced Zn-Ni-Al2O3nanocomposite
coatings. The chemical composition, microstructure and
mechanical properties of the composite and alloy coatings deposited
at two different agitation speed were investigated. The structure of all
coatings was single γ-Ni5Zn21 phase. The composite coatings possess
refined crystals with higher microhardness compared to Zn-Ni alloy
coatings. The wear resistance of Zn-Ni coatings was improved
significantly by incorporation of alumina nano particles into the
coatings. Higher agitation speed provided more uniform coatings
with smaller grain sized and slightly higher microhardness.
Considering composite coatings, high agitation speeds may facilitate
co-deposition of alumina in the coatings.
Abstract: Non contact evaluation of the thickness of paint
coatings can be attempted by different destructive and nondestructive
methods such as cross-section microscopy, gravimetric mass
measurement, magnetic gauges, Eddy current, ultrasound or
terahertz. Infrared thermography is a nondestructive and non-invasive
method that can be envisaged as a useful tool to measure the surface
thickness variations by analyzing the temperature response. In this
paper, the thermal quadrupole method for two layered samples heated
up with a pulsed excitation is firstly used. By analyzing the thermal
responses as a function of thermal properties and thicknesses of both
layers, optimal parameters for the excitation source can be identified.
Simulations show that a pulsed excitation with duration of ten
milliseconds allows obtaining a substrate-independent thermal
response. Based on this result, an experimental setup consisting of a
near-infrared laser diode and an Infrared camera was next used to
evaluate the variation of paint coating thickness between 60 μm and
130 μm on two samples. Results show that the parameters extracted
for thermal images are correlated with the estimated thicknesses by
the Eddy current methods. The laser pulsed thermography is thus an
interesting alternative nondestructive method that can be moreover
used for nonconductive substrates.
Abstract: Considering palm oil as non-drying oil owing to its
low iodine value, an attempt was taken to increase the unsaturation in
the fatty acid chains of palm oil for the preparation of alkyds. To
increase the unsaturation in the palm oil, sulphuric acid (SA) and
para-toluene sulphonic acid (PTSA) was used prior to alcoholysis for
the dehydration process. The iodine number of the oil samples was
checked for the unsaturation measurement by Wijs method. Alkyd
resin was prepared using the dehydrated palm oil by following
alcoholysis and esterification reaction. To improve the film properties
0.5wt.% multi-wall carbon nano tubes (MWCNTs) were used to
manufacture polymeric film. The properties of the resins were
characterized by various physico-chemical properties such as density,
viscosity, iodine value, saponification value, etc. Structural
elucidation was confirmed by Fourier transform of infrared
spectroscopy and proton nuclear magnetic resonance; surfaces of the
films were examined by field-emission scanning electron microscope.
In addition, pencil hardness and chemical resistivity was also
measured by using standard methods. The effect of enhancement of
the unsaturation in the fatty acid chain found significant and
motivational. The resin prepared with dehydrated palm oil showed
improved properties regarding hardness and chemical resistivity
testing. The incorporation of MWCNTs enhanced the thermal
stability and hardness of the films as well.
Abstract: Surface modification and functionalization has been
an important tool for scientists in order to open new frontiers in
nanoscience and nanotechnology. Desired surface characteristics for
the intended applications can be achieved with surface
functionalization.
In this work, the effect of water soluble ligands on the adsorption
capabilities of silver nanoparticles onto AC which was synthesized
from German beech wood was investigated. Sodium borohydride
(NaBH4) and polyvinyl alcohol (PVA) were used as the ligands.
Silver nanoparticles with different surface coatings have average
sizes range from 10 to 13 nm. They were synthesized in aqueous
media by reducing Ag (I) ion in the presence of ligands. These
particles displayed adsorption tendencies towards AC when they
were mixed together and shaken in distilled water.
Silver nanoparticles (NaBH4-AgNPs) reduced and stabilized by
NaBH4 adsorbed onto AC with a homogenous dispersion of
aggregates with sizes in the range of 100-400 nm. Beside, silver
nanoparticles, which were prepared in the presence of both NaBH4
and PVA (NaBH4/PVA-Ag NPs), demonstrated that NaBH4/PVA-Ag
NPs adsorbed and dispersed homogenously but, they aggregated with
larger sizes on the AC surface (range from 300 to 600 nm). In
addition, desorption resistance of Ag nanoparticles were investigated
in distilled water. According to the results AgNPs were not desorbed
on the AC surface in distilled water.
Abstract: In this study, an experiment was executed related to
the strength of wooden materials which have been commonly used
both in the past and present against pressure and whether fire
retardant materials used against fire have any effects or not. Totally
81 samples which included 3 different wood species, 3 different
sizes, 2 different fire retardants and 2 unprocessed samples were
prepared. Compressive pressure tests were applied to the prepared
samples, their variance analyses were executed in accordance with
the obtained results and it was aimed to determine the most
convenient wooden materials and fire-retardant coating material. It
was also determined that the species of wood and the species of
coating caused the decrease and/or increase in the resistance against
pressure.
Abstract: To develop AZ91D magnesium alloys with improved
properties, we have applied TiN and VN/TiN multilayer coatings
using DC magnetron sputter technique. Coating structure, surface
morphology, chemical bonding and corrosion resistance of coatings
were analyzed by x-ray diffraction (XRD), scanning electron
microscope (SEM), x-ray photoelectron spectroscopy (XPS), and
tafel extrapolation method, respectively. XPS analysis reveal that VN
overlayer reacts with oxygen at the VN/TiN interface and forms more
stable TiN layer. Morphological investigations and the corrosion
results show that VN/TiN multilayer thin film coatings are quite
effective to optimize the corrosion resistance of Mg alloys.
Abstract: In this paper, the effect of WC-12Co particle
temperature in HVOF thermal spraying process on the coating
thickness has been studied. The statistical results show that the spray
distance and oxygen-to-fuel ratio are effective factors on particle
characterization and thickness of HVOF thermal spraying coatings.
Spray Watch diagnostic system, scanning electron microscopy
(SEM), X-ray diffraction and thickness measuring system were used
for this purpose.
Abstract: Concerns on corrosion and effective coating
protection of double hull tankers and bulk carriers in service have
been raised especially in water ballast tanks (WBTs). Test
protocols/methodologies specifically that which is incorporated in the
International Maritime Organisation (IMO), Performance Standard
for Protective Coatings for Dedicated Sea Water ballast tanks (PSPC)
are being used to assess and evaluate the performance of the coatings
for type approval prior to their application in WBTs. However, some
of the type approved coatings may be applied as very thick films to
less than ideally prepared steel substrates in the WBT. As such films
experience hygrothermal cycling from operating and environmental
conditions, they become embrittled which may ultimately result in
cracking. This embrittlement of the coatings is identified as an
undesirable feature in the PSPC but is not mentioned in the test
protocols within it. There is therefore renewed industrial research
aimed at understanding this issue in order to eliminate cracking and
achieve the intended coating lifespan of 15 years in good condition.
This paper will critically review test protocols currently used for
assessing and evaluating coating performance, particularly the IMO
PSPC.
Abstract: Microfibrous palygorskite and tubular halloysite clay mineral combined with nanocrystalline TiO2 are incorporating in the preparation of nanocomposite films on glass substrates via sol-gel route at 450oC. The synthesis is employing nonionic surfactant molecule as pore directing agent along with acetic acid-based sol-gel route without addition of water molecules. Drying and thermal treatment of composite films ensure elimination of organic material lead to the formation of TiO2 nanoparticles homogeneously distributed on the palygorskite or halloysite surfaces. Nanocomposite films without cracks of active anatase crystal phase on palygorskite and halloysite surfaces are characterized by microscopy techniques, UV-Vis spectroscopy, and porosimetry methods in order to examine their structural properties.
The composite palygorskite-TiO2 and halloysite-TiO2 films with variable quantities of palygorskite and halloysite were tested as photocatalysts in the photo-oxidation of Basic Blue 41 azo dye in water. These nanocomposite films proved to be most promising photocatalysts and highly effective to dye’s decoloration in spite of small amount of palygorskite-TiO2 or halloysite-TiO2 catalyst immobilized onto glass substrates mainly due to the high surface area and uniform distribution of TiO2 on clay minerals avoiding aggregation.
Abstract: In this paper, the effect of WC-12Co particle velocity in HVOF thermal spraying process on the coating thickness has been studied. The statistical results show that the spray distance and oxygen-to-fuel ratio are more effective factors on particle characterization and thickness of HVOF thermal spraying coatings. Spray Watch diagnostic system, scanning electron microscopy (SEM), X-ray diffraction and thickness measuring system were used for this purpose.
Abstract: High velocity oxygen fuel (HVOF) spray technique is one of the leading technologies that have been proposed as an alternative to the replacement of electrolytic hard chromium plating in a number of engineering applications. In this study, WC-Co powder was coated on AISI1045 steel using high velocity oxy fuel (HVOF) method. The sin2ψ method was used to evaluate the through thickness residual stress by means of XRD after mechanical layer removal process (only grinding). The average of through thickness residual stress using X-Ray diffraction was -400 MPa.
Abstract: Polymer nanocomposites represent a new class of materials in which nanomaterials act as the reinforcing material in composites, wherein small additions of nanomaterials lead to large enhancements in thermal, optical and mechanical properties. A boost in these properties is due to the large interfacial area per unit volume or weight of the nanoparticles and the interactions between the particle and the polymer. Micro sized particles used as reinforcing agents scatter light, thus reducing light transmittance and optical clarity. Efficient nanoparticle dispersion combined with good polymer–particle interfacial adhesion eliminates scattering and allows the exciting possibility of developing strong yet transparent films, coatings and membranes. This paper aims at synthesising zinc oxide nanoparticles which are reinforced in poly vinyl alcohol (PVA) polymer. The mechanical properties showed that the tensile strength of the PVA nanocomposites increases with the increase in the amount of nanoparticles.
Abstract: Silicon substrates coated with multiwalled carbon nanotubes (MWCNTs) were experimentally investigated to determine spark breakdown voltages relative to uncoated surfaces, the degree of surface degradation associated with the spark discharge, and techniques to minimize the surface degradation. The results may be applicable to instruments or processes that use MWCNT as a means of increasing local electric field strength and where spark breakdown is a possibility that might affect the devices’ performance or longevity. MWCNTs were shown to reduce the breakdown voltage of a 1mm gap in air by 30-50%. The relative decrease in breakdown voltage was maintained over gap distances of 0.5 to 2mm and gauge pressures of 0 to 4 bar. Degradation of the MWCNT coated surfaces was observed. Several techniques to improve durability were investigated. These included: chromium and gold-palladium coatings, tube annealing, and embedding clusters of MWCNT in a ceramic matrix.
Abstract: The paper presents a new drugs delivery system, based on the thin film technology. As a model antitumor drug, highly toxic doxorubicin is chosen. The system is based on the technology of obtaining zinc oxide composite of doxorubicin by deposition of nanosize ZnO films on the surface of doxorubicin coating on glass substrate using DC magnetron sputtering of zinc targets in Ar:O2 medium at room temperature. For doxorubicin zinc oxide compositions in the form of coatings and gels with 180-200nm thick ZnO films, higher (by a factor 2) in vivo (ascitic Ehrlich's carcinoma) antitumor activity is observed at low doses of doxorubicin in comparison with that of the initial preparation at therapeutic doses. The vector character of the doxorubicin zinc oxide composite transport to tumor tissues ensures the increase in antitumor activity as well as decrease of toxicity in comparison with the initial drug.
Abstract: A study on the physicochemical properties of Jatropha curcas seed oil for industrial applications were carried out. Physicochemical properties of J. curcas seed oil (59.32% lipids) showed high content of LA (36.70%), iodine value (104.90 mg/g) and saponification value (203.36 mg/g). The present study shows that, J. curcas seed oil is rich in oleic and linoleic acids. The J. curcas seed oil with the highest amount of polyunsaturated fatty acids (linoleic acid) can find an application in surface coating industries and biolubricant base oil applications, whereas the high amount of monounsaturated fatty acid can find an application as a biodiesel feed stock. J. curcas seed oil contains major TAG of monounsaturated OLL, POL, SLL, PLL, OOL, OOO and POP followed by LLL. J. curcas seed oil can be classified as unsaturated oil with an unsaturated fat level of 80.42%. Hence the J. curcas seed oil has great potential for industrial applications such as in paint and surface coatings, production of biodiesel and biolubricant. Therefore, it is crucial to have more research on J. curcas seed oil in the future to explore its potential as a future industrial oilseed crop.