Abstract: The current study has investigated the ageing
phenomena of silica optical fibres in relation to water activity which might be accelerated when exposed to a supplementary energy, such as microwaves. A controlled stress by winding fibres onto accurate
diameter mandrel was applied. Taking into account that normally a
decrease in fibre strength is induced in time by chemical action of water, the effects of cumulative reagents such as: water, applied stress and supplementary energy (microwave) in some cases acted in
the opposite manner. The microwave effect as a structural relaxation
catalyst appears unexpected, even if the overall gain in fibre strength is not high, but the stress corrosion factor revealed significant
increase in certain simulation conditions.
Abstract: This is the first report from India on a beverage resulting from alcoholic fermentation of the juice of sea buckthorn (Hippophae rhamnoides L) using lab isolated yeast strain. The health promoting potential of the product was evaluated based on its total phenolic content. The most important finding was that under the present fermentation condition, the total phenolic content of the wine product was 689 mg GAE/L. Investigation of influence of bottle ageing on the sea buckthorn wine showed a slight decrease in the phenolic content (534 m mg GAE/L). This study also includes the comparative analysis of the phenolic content of wines from other selected fruit juices like grape, apple and black currant. KeywordsAlcoholic fermentation, Hippophae, Total phenolic content, Wine
Abstract: Telemedicine is brought to life by contemporary changes of our world and summarizes the entire range of services that are at the crossroad of traditional healthcare and information technology. It is believed that eHealth can help in solving critical issues of rising costs, care for ageing and housebound population, staff shortage. It is a feasible tool to provide routine as well as specialized health service as it has the potential to improve both the access to and the standard of care. eHealth is no more an optional choice. It has already made quite a way but it still remains a fantastic challenge for the future requiring cooperation and coordination at all possible levels. The strategic objectives of this paper are: 1. To start with an attempt to clarify the mass of terms used nowadays; 2. To answer the question “Who needs eHealth"; 3. To focus on the necessity of bridging telemedicine and medical (health) informatics as well as on the dual relationship between them; as well as 4. To underline the need of networking in understanding, developing and implementing eHealth.
Abstract: Non-uniform current distribution in polymer
electrolyte membrane fuel cells results in local over-heating,
accelerated ageing, and lower power output than expected. This
issue is very critical when fuel cell experiences water flooding. In
this work, the performance of a PEM fuel cell is investigated under
cathode flooding conditions. Two-dimensional partially flooded
GDL models based on the conservation laws and electrochemical
relations are proposed to study local current density distributions
along flow fields over a wide range of cell operating conditions.
The model results show a direct association between cathode inlet
humidity increases and that of average current density but the
system becomes more sensitive to flooding. The anode inlet
relative humidity shows a similar effect. Operating the cell at
higher temperatures would lead to higher average current densities
and the chance of system being flooded is reduced. In addition,
higher cathode stoichiometries prevent system flooding but the
average current density remains almost constant. The higher anode
stoichiometry leads to higher average current density and higher
sensitivity to cathode flooding.
Abstract: This paper presents the experimental results of salt fog ageing test of silicone rubber housing material for outdoor polymer insulator based on IEC 61109. Four types of HTV silicone rubber sheet with different amount of ATH were tested continuously 1000
Abstract: As the resources for naturally occurring aggregates
diminished at an ever increasing rate, researchers are keen to utilize
recycled materials in road construction in harmony with sustainable
development. Steel slag, a waste product from the steel making
industry, is one of the recycled materials reported to exhibit great
potential to replace naturally occurring aggregates in asphalt
mixtures. This paper presents the resilient modulus properties of
steel slag asphalt mixtures subjected to short term oven ageing
(STOA). The resilient modulus test was carried out to evaluate the
stiffness of asphalt mixtures at 10ºC, 25ºC and 40ºC. Previous
studies showed that stiffness changes in asphalt mixture played an
important role in inflicting pavement distress particularly cracking
and rutting that are common at low and high temperatures
respectively. Temperature was found to significantly influence the
resilient modulus of asphalt mixes. The resilient modulus of the
asphalt specimens tested decreased by more than 90% when the test
temperature increased from 10°C to 40°C.
Abstract: This paper presents the experimental results of silicone rubber housing material for 24kV lightning arrester under artificial accelerated ageing test based on IEC 61109 specifications. Specimens having inclined and alternated shed made of HTV silicone rubber with ATH content and having leakage distance 625 mm were tested continuously 1000 hrs in artificial salt fog chamber. After 1000 hrs of salt fog ageing test, obviously surface erosion was observed on trunk between the upper large shed and the lower small shed near the energized end. Decreasing in hydrophobicity and increasing in hardness were measured on tested specimen comparing with new specimen. Chemical analysis by ATR-FTIR confirmed the observation results.
Abstract: This paper presents the experimental results of silicone rubber outdoor polymer insulators in salt fog ageing test based on IEC 61109. Specimens made ofHTV silicone rubber with ATH content having three different configurations, straight shedsalternated sheds, and incline and alternate sheds, were tested continuously 1000 hrs.in artificial salt fog chamber. Contamination level, reduction of hydrophobicity and hardness measurement were used as physical damaged inspection techniques to evaluate degree of surface deterioration. In addition, chemical changing of tested specimen surface was evaluated by ATR-FTIRto confirm physical damaged inspection. After 1000 hrs.of salt fog test, differences in degree of surface deterioration were observed on all tested specimens. Physical damaged inspection and chemical analysis results confirmed the experimental results as well.
Abstract: The accomplished study is based on the appointment
and identification of ageing effects and according to this absorption
of moisture of aircraft cabin components over the life-cycle. In the
first step of the study ceiling panels from same age and from the
same aircraft cabin have been examined according to weight changes
depending on the position in the aircraft cabin. In the second step of
the study different aged ceiling panels have been examined
concerning deflection, weight changes and the acoustic sound
transmission loss. To prove the assumption of water absorption
within the study and with the theoretical background from literature
and scientific papers, an older test panel was exposed extreme
thermal conditions (humidity and temperature) within a climate
chamber to show that there is a general ingress of water to cabin
components and that this ingress of water leads to the change of
different mechanical properties.
Abstract: The present study aims at determining the effect of ageing on the impact toughness and microstructure of 2024 Al-Cu - Mg alloy. Following the 2 h solutionizing treatment at 450°C and water quench, the specimens were aged at 200°C for various periods (1 to 18 h). The precipitation stages during ageing were monitored by hardness measurements. For each specimen group, Charpy impact and hardness tests were carried out. During ageing the impact toughness of the alloy first increased, and then, following a maxima decreased due to the precipitation of intermediate phases, finally it reached its minimum at the peak hardness. Correlations between hardness and impact toughness were investigated.
Abstract: Degradation of polymeric insulation systems of
electrical equipments increases the space charge density and the
concentration of electrical dipoles. By consequence, the maximum
values and the slopes of absorption/resorption (A/R) currents can
change with insulation systems ageing. In this paper, an analysis of
the nature of the A/R currents and the importance of their
components, especially the polarization current and the current given
by the space charge, is presented. The experimental study concerns
the A/R currents measurements of plane samples (made from
CALMICAGLAS tapes), virgin and thermally accelerated aged. The
obtained results show that the ageing process produces an increase of
the values and a decrease of shapes of the A/R currents. Finally, the
possibility of estimating insulations ageing state and lifetime from
A/R currents measurements is discussed.
Abstract: This paper presents the experimental results of silicone rubber polymer insulators for 22 kV systems under salt water dip wheel test based on IEC 62217. Straight shed silicone rubber polymer insulators having leakage distance 685 mm were tested continuously 30,000 cycles. One test cycle includes 4 positions, energized, de-energized, salt water dip and deenergized, respectively. For one test cycle, each test specimen remains stationary for about 40 second in each position and takes 8 second for rotate to next position. By visual observation, sever surface erosion was observed on the trunk near the energized end of tested specimen. Puncture was observed on the upper shed near the energized end. In addition, decreasing in hydrophobicity and increasing in hardness were measured on tested specimen comparing with new specimen. Furthermore, chemical analysis by ATR-FTIR was conducted in order to elucidate the chemical change of tested specimens comparing with new specimen.
Abstract: A model is presented to find the optimal design of the
mixed renewable warranty policy for non-repairable Weibull life
products. The optimal design considers the conflict of interests
between the customer and the manufacturer: the customer interests
are longer full rebate coverage period and longer total warranty
coverage period, the manufacturer interests are lower warranty cost
and lower risk. The design factors are full rebate and total warranty
coverage periods. Results showed that mixed policy is better than full
rebate policy in terms of risk and total warranty coverage period in all
of the three bathtub regions. In addition, results showed that linear
policy is better than mixed policy in infant mortality and constant
failure regions while the mixed policy is better than linear policy in
ageing region of the model. Furthermore, the results showed that
using burn-in period for infant mortality products reduces warranty
cost and risk.
Abstract: This paper presents ageing experiments controlled by the evolution of junction parameters. The deterioration of the device is related to high injection effects which modified the transport mechanisms in the space charge region of the junction. Physical phenomena linked to the degradation of junction parameters that affect the devices reliability are reported and discussed. We have used the method based on numerical analysis of experimental current-voltage characteristic of the junction, in order to extract the electrical parameters. The simultaneous follow-up of the evolutions of the series resistance and of the transition voltage allow us to introduce a new parameter for reliability evaluation.
Abstract: The power transformer is the most expensive, indispensable and arguably the most important equipment item in a power system Insulation failure in transformers can cause long term interruption to supply and loss of revenue and the condition assessment of the insulation is thus an important maintenance procedure. Oil-impregnated transformer insulation consists of mainly organic materials including mineral oil and cellulose-base paper and pressboard. The operating life of cellulose-based insulation, as with most organic insulation, depends heavily on its operating temperature rise above ambient. This paper reports results of a laboratory-based experimental investigation of partial discharge (PD) activity at high temperature in oil-impregnated insulation. The experiments reported here are part an on-going programme aimed at investigating the way in which insulation deterioration can be monitored and quantified by use of partial discharge diagnostics. Partial discharge patterns were recorded and analysed during increasing and decreasing phases of the temperature. The effect of ageing of the insulation on the PD patterns in oil and oil-impregnated insulation are also considered.
Abstract: This paper presents the comparison ageing deterioration of silicone rubber housing material for outdoor polymer insulators by using salt fog ageing test based on IEC 61109 and outdoor exposure test.Four types of high temperature silicone vulcanized silicone rubber sheet with different amount of ATH were used as testing specimen. For salt fog ageing test, the specimens were tested continuously 1000 hours with energized in test chamber. For outdoor exposure test, the specimens were hung continuously 18 months without energized. Physical and chemical analyses were conducted to evaluate degree of ageing deterioration of tested specimens. Slightly surface erosion was observed on specimen surface after salt fog ageing test and no erosion was observed on surface of outdoor exposure specimen. However, comparable degree of ageing deterioration can be seen from surface analysis results.
Abstract: This paper presents the experimental results on
artificial ageing test of 22 kV XLPE cable for distribution system
application in Thailand. XLPE insulating material of 22 kV cable
was sliced to 60-70 μm in thick and was subjected to ac high voltage
at 23
Ôùª
C, 60
Ôùª
C and 75
Ôùª
C. Testing voltage was constantly applied to
the specimen until breakdown. Breakdown voltage and time to
breakdown were used to evaluate life time of insulating material.
Furthermore, the physical model by J. P. Crine for predicts life time
of XLPE insulating material was adopted as life time model and was
calculated in order to compare the experimental results. Acceptable
life time results were obtained from Crine-s model comparing with
the experimental result. In addition, fourier transform infrared
spectroscopy (FTIR) for chemical analysis and scanning electron
microscope (SEM) for physical analysis were conducted on tested
specimens.