Abstract: This paper presents the experimental results of silicone rubber housing material for 24kV lightning arrester under artificial accelerated ageing test based on IEC 61109 specifications. Specimens having inclined and alternated shed made of HTV silicone rubber with ATH content and having leakage distance 625 mm were tested continuously 1000 hrs in artificial salt fog chamber. After 1000 hrs of salt fog ageing test, obviously surface erosion was observed on trunk between the upper large shed and the lower small shed near the energized end. Decreasing in hydrophobicity and increasing in hardness were measured on tested specimen comparing with new specimen. Chemical analysis by ATR-FTIR confirmed the observation results.
Abstract: This paper presents the experimental results on
artificial ageing test of 22 kV XLPE cable for distribution system
application in Thailand. XLPE insulating material of 22 kV cable
was sliced to 60-70 μm in thick and was subjected to ac high voltage
at 23
Ôùª
C, 60
Ôùª
C and 75
Ôùª
C. Testing voltage was constantly applied to
the specimen until breakdown. Breakdown voltage and time to
breakdown were used to evaluate life time of insulating material.
Furthermore, the physical model by J. P. Crine for predicts life time
of XLPE insulating material was adopted as life time model and was
calculated in order to compare the experimental results. Acceptable
life time results were obtained from Crine-s model comparing with
the experimental result. In addition, fourier transform infrared
spectroscopy (FTIR) for chemical analysis and scanning electron
microscope (SEM) for physical analysis were conducted on tested
specimens.