Abstract: In this study, the experiments were carried out to
determine the best coolant for the quenching process among waterbased
silica, alumina, titania and copper oxide nanofluids (0.1 vol%).
A sphere made up off brass material was used in the experiments.
When the spherical test specimen was heated at high temperatures, it
was suddenly immersed into the nanofluids. All experiments were
carried out at saturated conditions and under atmospheric pressure.
After the experiments, the cooling curves were obtained by using the
temperature-time data of the specimen. The experimental results
showed that the cooling performance of test specimen depended on
the type of nanofluids. The silica nanoparticles enhanced the
performance of boiling heat transfer and it is the best coolant for the
quenching among other nanoparticles.
Abstract: The effect of N2 pretreatment on the catalytic activity
of tungsten-based catalysts was investigated in the metathesis of
ethylene and trans-2-butene at 450oC and atmospheric pressure. The
presence of tungsten active species was confirmed by UV-Vis and
Raman spectroscopy. Compared to the WO3-based catalysts treated
in air, higher amount of WO4 2-tetrahedral species and lower amount
of WO3 crystalline species were observed on the N2-treated ones.
These contribute to the higher conversion of 2-butene and propylene
selectivity during 10 h time-on-stream. Moreover, N2 treatment led to
lower amount of coke formation as revealed by TPO of the spent
catalysts.
Abstract: Propylene self-metathesis to ethylene and butene was
studied over WOx/SiO2 catalysts at 450oC and atmospheric pressure.
The WOx/SiO2 catalysts were prepared by incipient wetness
impregnation of ammonium metatungstate aqueous solution. It was
found that, adding nano-sized extra supports (SiO2 and TiO2) by
physical mixing with the WOx/SiO2 enhanced propylene conversion.
The UV-Vis and FT-Raman results revealed that WOx could migrate
from the original silica support to the extra support, leading to a
better dispersion of WOx. The ICP-OES results also indicate that
WOx existed on the extra support. Coke formation was investigated
on the catalysts after 10 h time-on-stream by TPO. However, adding
nano-sized extra supports led to higher coke formation which may be
related to acidity as characterized by NH3-TPD.
Abstract: Activated carbons (M4P0, M4P2, and M5P2) used in
this research were produced from palm shell and polyetherether
ketone (PEEK) via carbonization, impregnation and microwave
activation. The adsorption/desorption process was carried out using
static volumetric adsorption. Regeneration is important in the overall
economy of the process and waste minimization. This work focuses
on the thermal regeneration of the CO2 exhausted microwave
activated carbons. The regeneration strategy adopted was thermal
with nitrogen purge desorption with N2 feed flow rate of 20 ml/min
for 1 h at atmospheric pressure followed by drying at 150oC.Seven
successive adsorption/regeneration processes were carried out on the
material. It was found that after seven adsorption regeneration cycles;
the regeneration efficiency (RE) for CO2 activated carbon from palm
shell only (M4P0) was more than 90% while that of hybrid palm
shell-PEEK (M4P2, M5P2) was above 95%. The cyclic adsorption
and regeneration shows the stability of the adsorbent materials.
Abstract: Co metal supported on SiO2 and Al2O3 catalysts with
a metal loading varied from 30 of 70 wt.% were evaluated for
decomposition of methane to COx free hydrogen and carbon
nanomaterials. The catalytic runs were carried out from 550-800oC
under atmospheric pressure using fixed bed vertical flow reactor. The
fresh and spent catalysts were characterized by BET surface area
analyzer, XRD, SEM, TEM and TG analysis. The data showed that
50% Co/Al2O3 catalyst exhibited remarkable higher activity at 800oC
with respect to H2 production compared to rest of the catalysts.
However, the catalytic activity and durability was greatly declined at
higher temperature. The main reason for the catalytic inhibition of Co
containing SiO2 catalysts is the higher reduction temperature of
Co2SiO4. TEM images illustrate that the carbon materials with
various morphologies, carbon nanofibers (CNFs), helical-shaped
CNFs and branched CNFs depending on the catalyst composition and
reaction temperature were obtained.
Abstract: The present work aims to throw light on the effects of
arcing in air on the surface state of contact pastilles made of silvernickel
Ag-Ni (60/40). Also, the photoelectric emission from these
electrical contacts has been investigated in the spectral range of 196-
256 nm. In order to study the effects of arcing on the EWF, the
metallic samples were subjected to electrical arcs in air, at
atmospheric pressure and room temperature, after that, they have
been introduced into the vacuum chamber of an experimental UHV
set-up for EWF measurements. Both Fowler method of isothermal
curves and linearized Fowler plots were used for the measurement of
the EWF by the photoelectric effect.
It has been found that the EWF varies with the number of applied
arcs. Thus, after 500 arcs in air, the observed EWF increasing is
probably due to progressive inclusion of oxide on alloy surface.
Microscopic examination is necessary to get better understandings on
EWF of silver alloys, for both virgin and arced electrical contacts.
Abstract: The study is devoted to define the optimal conditions
for the nitriding of pure iron at atmospheric pressure by using NH3-
Ar-C3H8 gas mixtures. After studying the mechanisms of phase
formation and mass transfer at the gas-solid interface, a mathematical
model is developed in order to predict the nitrogen transfer rate in the
solid, the ε-carbonitride layer growth rate and the nitrogen and
carbon concentration profiles. In order to validate the model and to
show its possibilities, it is compared with thermogravimetric
experiments, analyses and metallurgical observations (X-ray
diffraction, optical microscopy and electron microprobe analysis).
Results obtained allow us to demonstrate the sound correlation
between the experimental results and the theoretical predictions.
Abstract: Ozone is well known as a powerful, fast reacting oxidant. Ozone based processes produce no by-product residual as non-reacted ozone decomposes to molecular oxygen. Therefore an application of ozone is widely accepted as one of the main approaches for a Sustainable and Clean Technologies development.
There are number of technologies which require ozone to be delivered to specific points of a production network or reactors construction. Due to space constraints, high reactivity and short life time of ozone the use of ozone generators even of a bench top scale is practically limited. This requires development of mini/micro scale ozone generator which can be directly incorporated into production units.
Our report presents a feasibility study of a new micro scale rector for ozone generation (MROG). Data on MROG calibration and indigo decomposition at different operation conditions are presented.
At selected operation conditions with residence time of 0.25 s the process of ozone generation is not limited by reaction rate and the amount of ozone produced is a function of power applied. It was shown that the MROG is capable to produce ozone at voltage level starting from 3.5kV with ozone concentration of 5.28*10-6 (mol/L) at 5kV. This is in line with data presented on numerical investigation for a MROG. It was shown that in compare to a conventional ozone generator, MROG has lower power consumption at low voltages and atmospheric pressure.
The MROG construction makes it applicable for both submerged and dry systems. With a robust compact design MROG can be used as an integrated module for production lines of high complexity.
Abstract: The development of alternative energy is interesting in the present especially, hydrogen production because it is an important energy resource in the future. This paper studied the hydrogen production from catalytic dehydrogenation of ethanol through via low temperature (
Abstract: This research work examines the effect of variations of metrological parameters on the tropospheric radio refractivity during dry and raining seasons for Akure in 2013. The daily averages of radio refractivity during dry (January) and raining (August) seasons were calculated from the data obtained from the Nigeria Metrological Agency (NIMET). The data that was used for the computation of radio refractivity is a daily interval of the variations of metrological parameters for each day in the troposphere for Akure. Consequently, the daily averages of radio refractivity during raining season (August) were greater than the results in dry season (January) as a result of the variations in meteorological parameters such as temperature, humidity and atmospheric pressure in the lower troposphere.
Abstract: Numerical simulation performed to investigate the behavior of the high pressure hydrogen jetting of air. High pressure hydrogen (30–40 MPa) was injected to air at atmospheric pressure through 2mm orifice. Numerical simulations were performed with Kiva3V code with 2D axisymmetric geometry. Numerical simulations showed that auto ignition of high pressure hydrogen to air are possible due to molecular diffusion. Auto ignition was predicted at hydrogen-air contact surface due to mass and energy exchange between high temperature hydrogen and air heated by shock wave.
Abstract: In aircraft applications, according to the nature of
electrical equipment its location may be in unpressurized area or very
close to the engine; thus, the environmental conditions may change
from atmospheric pressure to less than 100 mbar, and the temperature
may be higher than the ambient one as in most real working
conditions of electrical equipment. Then, the classical Paschen curve
has to be replotted since these parameters may affect the discharge
ignition voltage. In this paper, we firstly investigate the domain of
validity of two corrective expressions on the Paschen-s law found in
the literature, in case of changing the air environment and known as
Peek and Dunbar corrections. Results show that these corrections are
no longer valid for combined variation of temperature and pressure.
After that, a new empirical expression for breakdown voltage is
proposed and is validated in the case of combined variations of
temperature and pressure.
Abstract: Hydrogen sulfide (H2S) is a very toxic gas that is produced in very large quantities in the oil and gas industry. It cannot be flared to the atmosphere and Claus process based gas plants are used to recover the sulfur and convert the hydrogen to water. In this paper, we present optical characterization of an atmospheric pressure microwave plasma torch for H2S dissociation into hydrogen and sulfur. The torch is operated at 2.45 GHz with power up to 2 kW. Three different gases can simultaneously be injected in the plasma torch. Visual imaging and optical emission spectroscopy are used to characterize the plasma for varying gas flow rates and microwave power. The plasma length, emission spectra and temperature are presented. The obtained experimental results validate our earlier published simulation results of plasma torch.
Abstract: Since atmosphere pressure field is an actual envoy of
climatic signal the atmospheric Highs and Lows should be attributed
to the key active focal points within the ocean-atmosphere interplay
system. Here we were set a task to determine how the dynamics of
those centres of action relates to the climate change both on regional
and global scales. For this target the near-surface temperature and
atmospheric pressure differences between the Icelandic Low and the
Azores High were considered. The secular term of phase states of the
system under consideration was found divided into three
nonintersecting subsets. Each of that was put in consequence with
one of three climatic scenarios related to the periods of 1905-1935
(relatively warm phase), 1940-1970 (cold phase) and 1980-2000
(warm phase).
Abstract: In this work, simulation algorithms for contact drying
of agitated particulate materials under vacuum and at atmospheric
pressure were developed. The implementation of algorithms gives a
predictive estimation of drying rate curves and bulk bed temperature
during contact drying. The calculations are based on the penetration
model to describe the drying process, where all process parameters
such as heat and mass transfer coefficients, effective bed properties,
gas and liquid phase properties are estimated with proper
correlations. Simulation results were compared with experimental
data from the literature. In both cases, simulation results were in good
agreement with experimental data. Few deviations were identified
and the limitations of the predictive capabilities of the models are
discussed. The programs give a good insight of the drying behaviour
of the analysed powders.
Abstract: This paper reports the influence of sucrose on the
preservation of CO2 hydrate crystal samples. The particle diameter of
hydrate samples were 1.0 and 5.6-8.0 mm. Mass fraction of sucrose in
the sample was 0.16. The samples were stored at the aerated condition
under atmospheric pressure and at the temperature of 253 or 258 K.
The results indicated that the mass fractions of CO2 hydrate in the
samples with sucrose were 0.10 ± 0.03 at the end of 3-week
preservation, regardless of temperature and particle diameter. Mass
fraction of CO2 hydrate in the samples with sucrose was higher than
that of pure CO2 hydrate for 1.0 mm particle diameter, while was
lower than that of pure CO2 hydrate for 5.6-8.0 mm particle diameter.
Discussion is made on the influence of sucrose on the dissociation of
CO2 hydrate and the resulting formation of ice.
Abstract: This study was to investigate the performance of
hybrid solvents blended between primary, secondary, or tertiary
amines and piperazine (PZ) for CO2 removal from flue gas in terms
of CO2 absorption capacity and regeneration efficiency at 90 oC.
Alkanolamines used in this work were monoethanolamine (MEA),
diethanolamine (DEA), and triethanolamine (TEA). The CO2
absorption was experimentally examined under atmospheric pressure
and room temperature. The results show that MEA blend with PZ
provided the maximum CO2 absorption capacity of 0.50 mol
CO2/mol amine while TEA provided the minimum CO2 absorption
capacity of 0.30 mol CO2/mol amine. TEA was easier to regenerate
for both first cycle and second cycle with less loss of absorption
capacity. The regeneration efficiency of TEA was 95.09 and 92.89 %,
for the first and second generation cycles, respectively.
Abstract: Combustion of sprays is of technological importance, but its flame behavior is not fully understood. Furthermore, the multiplicity of dependent variables such as pressure, temperature, equivalence ratio, and droplet sizes complicates the study of spray combustion. Fundamental study on the influence of the presence of liquid droplets has revealed that laminar flames within aerosol mixtures more readily become unstable than for gaseous ones and this increases the practical burning rate. However, fundamental studies on turbulent flames of aerosol mixtures are limited particularly those under near mono-dispersed droplet conditions. In the present work, centrally ignited expanding flames at near atmospheric pressures are employed to quantify the burning rates in gaseous and aerosol flames. Iso-octane-air aerosols are generated by expansion of the gaseous pre-mixture to produce a homogeneously distributed suspension of fuel droplets. The effects of the presence of droplets and turbulence velocity in relation to the burning rates of the flame are also investigated.
Abstract: The atmospheric pressure plasma torch with a direct
current arc discharge stabilized by water vapor vortex was
experimentally investigated. Overheated up to 450K water vapor was
used as plasma forming gas. Plasma torch design is one of the most
important factors leading to a stable operation of the device. The
electrical and thermal characteristics of the plasma torch were
determined during the experimental investigations. The design and
the basic characteristics of the water vapor plasma torch are presented
in the paper.
Plasma torches with the electric arc stabilized by water vapor
vortex provide special performance characteristics in some plasma
processing applications such as thermal plasma neutralization and
destruction of organic wastes enabling to extract high caloric value
synthesis gas as by-product of the process. Syngas could be used as a
surrogate fuel partly replacing the dependence on the fossil fuels or
used as a feedstock for hydrogen, methanol production.
Abstract: Team distillation assisted by microwave extraction
(SDAM) considered as accelerated technique extraction is a
combination of microwave heating and steam distillation, performed
at atmospheric pressure. SDAM has been compared with the same
technique coupled with the cryogrinding of seeds (SDAM -CG).
Isolation and concentration of volatile compounds are performed by a
single stage for the extraction of essential oil from Cuminum
cyminum seeds. The essential oils extracted by these two methods for
5 min were quantitatively (yield) and qualitatively (aromatic profile)
no similar. These methods yield an essential oil with higher amounts
of more valuable oxygenated compounds, and allow substantial
savings of costs, in terms of time, energy and plant material. SDAM
and SDAM-CG is a green technology and appears as a good
alternative for the extraction of essential oils from aromatic plants.