Abstract: In the present study, the properties of Al-Al2O3
nanocomposite hollow sphere structures were investigated. For this
reason, the Al-based nanocomposite hollow spheres with different
amounts of nano-alumina reinforcement (0-10wt %) and different
ratio of thickness to diameter (t/D: 0.06-0.3) were prepared via a
powder metallurgy method. Then, the effect of mentioned parameters
was studied on physical and quasi static mechanical properties of
their related prepared structures (open/closed cell) such as density,
hardness, strength, and energy absorption. It was found that, as the
t/D ratio increases the relative density, compressive strength and
energy absorption increase. The highest values of strength and energy
absorption were obtained from the specimen with 5 wt. % of
nanoparticle reinforcement, t/D of 0.3 (t=1 mm, D=400μm) as 22.88
MPa and 13.24 MJ/m3, respectively. The moderate specific strength
of prepared composites in the present study showed the good
consistency with the properties of others low carbon steel composite
with similar structure.
Abstract: A bauxite ore can be utilized in Bayer Process, if the
mass ratio of Al2O3 to SiO2 is greater than 10. Otherwise, its FexOy
and SiO2 content should be removed. On the other hand, removal of
TiO2 from the bauxite ore would be beneficial because of both
lowering the red mud residue and obtaining a valuable raw material
containing TiO2 mineral. In this study, the low grade diasporic
bauxite ore of Yalvaç, Isparta, Turkey was roasted under reducing
atmosphere and subjected to magnetic separation. According to the
experimental results, 800°C for reduction temperature and 20000
Gauss of magnetic intensity were found to be the optimum
parameters for removal of iron oxide and rutile from the nonmagnetic
ore. On the other hand, 600°C and 5000 Gauss were
determined to be the optimum parameters for removal of silica from
the non-magnetic ore.
Abstract: In recent research copper and manganese systems
were found to be the most active in CO and organic compounds
oxidation among the base catalysts. The mixed copper manganese
oxide has been widely studied in oxidation reactions because of their
higher activity at low temperatures in comparison with single oxide
catalysts. The results showed that the formation of spinel
CuxMn3−xO4 in the oxidized catalyst is responsible for the activity
even at room temperature. That is why the most of the investigations
are focused on the hopcalite catalyst (CuMn2O4) as the best coppermanganese
catalyst. Now it’s known that this is true only for CO
oxidation, but not for mixture of CO and VOCs. The purpose of this
study is to investigate the alumina supported copper-manganese
catalysts with different Cu/Mn molar ratio in terms of oxidation of
CO, methanol and dimethyl ether. The catalysts were prepared by impregnation of γ-Al2O3 with
copper and manganese nitrates and the catalytic activity
measurements were carried out in two stage continuous flow
equipment with an adiabatic reactor for simultaneous oxidation of all
compounds under the conditions closest possible to the industrial. Gas
mixtures on the input and output of the reactor were analyzed with a
gas chromatograph, equipped with FID and TCD detectors. The
texture characteristics were determined by low-temperature (- 196oС)
nitrogen adsorption in a Quantachrome Instruments NOVA 1200e
(USA) specific surface area & pore analyzer. Thermal, XRD and
TPR analyses were performed. It was established that the active component of the mixed Cu-
Mn/γ–alumina catalysts strongly depends on the Cu/Mn molar ratio.
Highly active alumina supported Cu-Mn catalysts for CO, methanol
and DME oxidation were synthesized. While the hopcalite is the best
catalyst for CO oxidation, the best compromise for simultaneous
oxidation of all components is the catalyst with Cu/Mn molar ratio
1:5.
Abstract: Zn alloy and composite coatings are widely used in
buildings and structures, automobile and fasteners industries to
protect steel component from corrosion. In this paper, Zn-Ni-Al2O3
nanocomposite coatings were electrodeposited on mild steel using a
novel sol enhanced electroplating method. In this method, transparent
Al2O3 sol was added into the acidic Zn-Ni bath to produced Zn-Ni-
Al2O3 nanocomposite coatings. The effect of alumina sol on the
electrodeposition process, and coating properties was investigated
using cyclic voltammetry, XRD, ESEM and Tafel test. Results from
XRD tests showed that the structure of all coatings was single γ-
Ni5Zn21 phase. Cyclic voltammetry results showed that the
electrodeposition overpotential was lower in the presence of alumina
sol in the bath, and caused the reduction potential of Zn-Ni to shift to
more positive values. Zn-Ni-Al2O3 nanocomposite coatings produced
more uniform and compact deposits, with fine grained microstructure
when compared to Zn-Ni coatings. The corrosion resistance of Zn-Ni
coatings was improved significantly by incorporation of alumina
nanoparticles into the coatings.
Abstract: Sol-enhanced Zn-Ni-Al2O3 nanocomposite coatings
were electroplated on mild steel by our newly developed solenhanced
electroplating method. In this method, transparent Al2O3 sol
was added into the acidic Zn-Ni bath to produced Zn-Ni-Al2O3nanocomposite
coatings. The chemical composition, microstructure and
mechanical properties of the composite and alloy coatings deposited
at two different agitation speed were investigated. The structure of all
coatings was single γ-Ni5Zn21 phase. The composite coatings possess
refined crystals with higher microhardness compared to Zn-Ni alloy
coatings. The wear resistance of Zn-Ni coatings was improved
significantly by incorporation of alumina nano particles into the
coatings. Higher agitation speed provided more uniform coatings
with smaller grain sized and slightly higher microhardness.
Considering composite coatings, high agitation speeds may facilitate
co-deposition of alumina in the coatings.
Abstract: This paper analyses the heat transfer performance and
fluid flow using different nanofluids in a square enclosure. The
energy equation and Navier-Stokes equation are solved numerically
using finite volume scheme. The effect of volume fraction
concentration on the enhancement of heat transfer has been studied
icorporating the Brownian motion; the influence of effective thermal
conductivity on the enhancement was also investigated for a range of
volume fraction concentration. The velocity profile for different
Rayleigh number. Water-Cu, water AL2O3 and water-TiO2 were
tested.
Abstract: Pt/γ-Al2O3 membrane catalysts were prepared via an
evaporative-crystallization deposition method. The obtained Pt/γ-
Al2O3 catalyst activity was tested after characterization (SEM-EDAX
observation, BET measurement, permeability assessment) in the
catalytic oxidation of selected volatile organic compound (VOC) i.e.
propane, fed in mixture of oxygen. The VOC conversion (nearly
90%) obtained by varying the operating temperature showed that
flow-through membrane reactor might do better in the abatement of
VOCs.
Abstract: Fly ash (FA) thanks to the significant presence of SiO2
and Al2O3 as the main components is a potential raw material for
geopolymers production. Mechanical activation is a method for
improving FA reactivity and also the porosity of final mixture; those
parameters can be analysed through sorption properties. They have
direct impact on the durability of fly ash based geopolymer mortars.
In the paper, effect of FA fineness on sorption properties of
geopolymers based on sodium silicate, as well as relationship
between fly ash fineness and apparent density, compressive and
flexural strength of geopolymers are presented. The best results in the
evaluated area reached the sample H1, which contents the highest
portion of particle under 20μm (100% of GFA). The interdependence
of individual tested properties was confirmed for geopolymer
mixtures corresponding to those in the cement based mixtures: higher
is portion of fine particles < 20μm, higher is strength, density and
lower are sorption properties. The compressive strength as well as
sorption parameters of the geopolymer can be reasonably controlled
by grinding process and also ensured by the higher share of fine
particle (to 20μm) in total mass of the material.
Abstract: Nanofibers of PVA /nickel nitrate/silica/alumina
izopropoxide/boric acid composite were prepared by using sol-gel
processing and electrospinning technique. By high temperature
calcinations of the above precursor fibers, nanofibers of
NiO/Al2O3/B2O3/SiO2 composite with diameters about 500 nm
could be successfully obtained. The fibers were characterized by
XRD and SEM analyses.
Abstract: The effect of transition metal doping on Pt/Al2O3
catalyst used in propane dehydrogenation reaction at 500°C was
studied. The preparation methods investigated were sequential
impregnation (Pt followed by the 2nd metal or the 2nd metal followed
by Pt) and co-impregnation. The metal contents of these catalysts
were fixed as the weight ratio of Pt per the 2nd metal of around 0.075.
These catalysts were characterized by N2-physisorption, TPR, COchemisorption
and NH3-TPD. It was found that the impregnated 2nd
metal had an effect upon reducibility of Pt due to its interaction with
transition metal-containing structure. This was in agreement with the
CO-chemisorption result that the presence of Pt metal, which is a
result from Pt species reduction, was decreased. The total acidity of
bimetallic catalysts is decreased but the strong acidity is slightly
increased. It was found that the stability of bimetallic catalysts
prepared by co-impregnation and sequential impregnation where the
2nd metal was impregnated before Pt were better than that of
monometallic catalyst (undoped Pt one) due to the forming of Pt sites
located on the transition metal-oxide modified surface. Among all
preparation methods, the sequential impregnation method- having Pt
impregnated before the 2nd metal gave the worst stability because this
catalyst lacked the modified Pt sites and some fraction of Pt sites was
covered by the 2nd metal.
Abstract: The development of active and stable catalysts
without noble metals for low temperature oxidation of exhaust gases
remains a significant challenge. The purpose of this study is to
determine the influence of the preparation method on the catalytic
activity of the supported copper-manganese mixed oxides in terms of
VOCs oxidation. The catalysts were prepared by impregnation of γ-
Al2O3 with copper and manganese nitrates and acetates and the
possibilities for CO, CH3OH and dimethyl ether (DME) oxidation
were evaluated using continuous flow equipment with a four-channel
isothermal stainless steel reactor. Effect of the support, Cu/Mn mole
ratio, heat treatment of the precursor and active component loading
were investigated. Highly active alumina supported Cu-Mn catalysts
for CO and VOCs oxidation were synthesized. The effect of
preparation conditions on the activity behavior of the catalysts was
discussed.
The synergetic interaction between copper and manganese species
increases the activity for complete oxidation over mixed catalysts.
Type of support, calcination temperature and active component
loading along with catalyst composition are important factors,
determining catalytic activity. Cu/Mn molar ratio of 1:5, heat
treatment at 450oC and 20 % active component loading are the best
compromise for production of active catalyst for simultaneous
combustion of CO, CH3OH and DME.
Abstract: Catalytic combustion of methane is imperative due to
stability of methane at low temperature. Methane (CH4), therefore,
remains unconverted in vehicle exhausts thereby causing greenhouse
gas GHG emission problem. In this study, heterogeneous catalysts of
palladium with bio-char (2 wt% Pd/Bc) and Al2O3 (2wt% Pd/ Al2O3)
supports were prepared by incipient wetness impregnation and then
subsequently tested for catalytic combustion of CH4. Support-porous
heterogeneous catalytic combustion (HCC) material were selected
based on factors such as surface area, porosity, thermal stability,
thermal conductivity, reactivity with reactants or products, chemical
stability, catalytic activity, and catalyst life. Sustainable and
renewable support-material of bio-mass char derived from palm shell
waste material was compared with those from the conventional
support-porous materials. Kinetic rate of reaction was determined for
combustion of methane on Palladium (Pd) based catalyst with Al2O3
support and bio-char (Bc). Material characterization was done using
TGA, SEM, and BET surface area. The performance test was
accomplished using tubular quartz reactor with gas mixture ratio of
3% methane and 97% air. The methane porous-HCC conversion was
carried out using online gas analyzer connected to the reactor that
performed porous-HCC. BET surface area for prepared 2 wt% Pd/Bc
is smaller than prepared 2wt% Pd/ Al2O3 due to its low porosity
between particles. The order of catalyst activity based on kinetic rate
on reaction of catalysts in low temperature was 2wt%
Pd/Bc>calcined 2wt% Pd/ Al2O3> 2wt% Pd/ Al2O3>calcined 2wt%
Pd/Bc. Hence agro waste material can successfully be utilized as an
inexpensive catalyst support material for enhanced CH4 catalytic
combustion.
Abstract: Co metal supported on SiO2 and Al2O3 catalysts with
a metal loading varied from 30 of 70 wt.% were evaluated for
decomposition of methane to COx free hydrogen and carbon
nanomaterials. The catalytic runs were carried out from 550-800oC
under atmospheric pressure using fixed bed vertical flow reactor. The
fresh and spent catalysts were characterized by BET surface area
analyzer, XRD, SEM, TEM and TG analysis. The data showed that
50% Co/Al2O3 catalyst exhibited remarkable higher activity at 800oC
with respect to H2 production compared to rest of the catalysts.
However, the catalytic activity and durability was greatly declined at
higher temperature. The main reason for the catalytic inhibition of Co
containing SiO2 catalysts is the higher reduction temperature of
Co2SiO4. TEM images illustrate that the carbon materials with
various morphologies, carbon nanofibers (CNFs), helical-shaped
CNFs and branched CNFs depending on the catalyst composition and
reaction temperature were obtained.
Abstract: The borate glasses are known by their structural
characterized by existence of unit’s structural composed by triangles
and tetrahedrons boron in different configurations depending on the
percentage of B2O3 in the glass chemical composition. In this paper,
effect of lithium oxide addition on the thermal and physical
properties of an alumina borate glass, was investigated. It was found
that the boron abnormality has a significant effect in the change of
glass properties according to the addition rate of lithium oxide.
Abstract: The temperature dependence of wettability (wetting
angle, Θ (T)) for Ag-based melts on graphite and Al2O3 substrates is
compared. Typical alloying effects are found, as the Ag host metal is
gradually replaced by various metallic elements. The essence of
alloying lies in the change of the electron/atom (e/a) ratio. This ratio
is also manifested in the shift of wetting angles on the same substrate.
Nevertheless, the effects are partially smeared by other
(metallurgical) factors, like the interaction between the oxygenalloying
elements and by the graphite substrate-oxygen interaction. In
contrast, such effects are not pronounced in the case of Al2O3
substrates. As a consequence, Θ(T) exhibits an opposite trend in the
case of two substrates. Crossovers of the Θ(T) curves were often
found. The positions of crossovers depend on the chemical character
and concentration of solute atoms. Segregation and epitaxial texture
formation after solidification were also observed in certain alloy
drops, especially in high concentration range. This phenomenon is
not yet explained in every detail.
Abstract: In the present study, mixed convection in a horizontal
rectangular duct using Al2O3 is numerically investigated. The effects
of different Rayleigh number, Reynolds number and radiation on
flow and heat transfer characteristics are studied in detail. This study
covers Rayleigh number in the range of 2 × 10^6 ≤ Ra ≤ 2 × 10^7 and
Reynolds number in the range of 100 ≤ Re ≤ 1100. Results reveal that
the Nusselt number increases as Reynolds and Rayleigh numbers
increase. It is also found that the dimensionless temperature
distribution increases as Rayleigh number increases.
Abstract: In order to manufacture short gap single Si nanowire
(NW) field effect transistor (FET) by imprinting and transferring
method, we introduce the method using Al2O3 sacrificial layer. The
diameters of cylindrical Si NW addressed between Au electrodes by
dielectrophoretic (DEP) alignment method are controlled to 106, 128,
and 148 nm. After imprinting and transfer process, cylindrical Si NW
is embedded in PVP adhesive and dielectric layer. By curing
transferred cylindrical Si NW and Au electrodes on PVP-coated p++ Si
substrate with 200nm-thick SiO2, 3μm gap Si NW FET fabrication
was completed. As the diameter of embedded Si NW increases, the
mobility of FET increases from 80.51 to 121.24 cm2/V·s and the
threshold voltage moves from –7.17 to –2.44 V because the ratio of
surface to volume gets reduced.
Abstract: Two Lithium Disilicate (LD) glass ceramics based on
SiO2-Li2O-K2O-Al2O3 system were prepared through a glass melting
method. The glass rods were then fabricated into dental crowns via a
hot pressing at 900˚C and 850˚C in order to study the effect of the
pressing temperatures on the phase formation and microstructure of
the glasses. Different samples of as cast glass and heat treated
samples (600˚C and 700˚C) were used to press for investigating the
effect of an initial microstructure on the hot pressing technique. Xray
diffraction (XRD) and scanning electron microscopy (SEM) were
performed to determine the phase formation and microstructure of the
samples, respectively. XRD results show that the main crystalline
structure was Li2Si2O5 by having Li3PO4, Li0.6Al0.6Si2O6, Li2SiO3,
Ca5 (PO4)3F and SiO2 as minor phases. Glass compositions with
different heat treatment temperatures exhibited a difference phase
formations but have less effect during pressing. SEM micrographs
showed the microstructure of Li2Si2O5 as lath-like shape in all
glasses. With increasing the initial heat treatment temperature, the
longer the lath-like crystals of lithium disilicate were increased
especially when using glass heat treatment at 700˚C followed by
pressing at 900˚C. This could be suggested that LD1 heat treatment at
700˚C which pressing at 900˚C presented the best formation by the
hot pressing and compiled microstructure.
Abstract: With demand for primary energy continuously
growing, search for renewable and efficient energy sources has been
high on agenda of our society. One of the most promising energy
sources is biogas technology. Residues coming from dairy industry
and milk processing could be used in biogas production; however,
low efficiency and high cost impede wide application of such
technology. One of the main problems is management and conversion
of organic residues through the anaerobic digestion process which is
characterized by acidic environment due to the low whey pH (
Abstract: Ni-based catalysts with different amounts of Na as
promoter from 2 to 6 wt % were prepared by solution combustion
method. The catalytic activity was investigated in syngas methanation
reaction. Carbon oxides conversion and methane selectivity are greatly
influenced by sodium loading. Adding 2 wt% Na remarkably improves
catalytic activity and long-term stability, attributed to its smaller mean
NiO particle size, better distribution, and milder metal-support
interaction. However, excess addition of Na results in deactivation
distinctly due to the blockage of active sites.