Abstract: In general, it is desirable to finish the weld quickly,
before a large volume of surrounding metal heats up and expands.
The welding process used, type, welding current and speed of travel,
thus, affect the degree of shrinkage and distortion of a weldment. The
use of mechanized welding equipment reduces welding time, metal
affected zone and consequently distortion. This article helps to define
what weld distortion is and then provide a practical understanding of
the causes of distortion, effects of shrinkage in butt joint welded
assemblies using TI6AL4VA and Aluminium AA2024 alloy sheet.
The beam offset position to the joint interface towards titanium and
aluminium side. The factors affecting distortion during welding is
also given. Test results reveal that welding speed is the significant
parameter to decide the extent of distortion. Also welding from Al
side reduces the distortion while Ti side increases the distortion.
Abstract: Ultrasonic metal welding has been the subject of ongoing research and development, most recently concentrating on metal joining in miniature devices, for example to allow solder-free wire bonding. As well as at the small scale, there are also opportunities to research the joining of thicker sheet metals and to widen the range of similar and dissimilar materials that can be successfully joined using this technology. This study presents the design, characterisation and test of a lateral-drive ultrasonic metal spot welding device. The ultrasonic metal spot welding horn is modelled using finite element analysis (FEA) and its vibration behaviour is characterised experimentally to ensure ultrasonic energy is delivered effectively to the weld coupon. The welding stack and fixtures are then designed and mounted on a test machine to allow a series of experiments to be conducted for various welding and ultrasonic parameters. Weld strength is subsequently analysed using tensile-shear tests. The results show how the weld strength is particularly sensitive to the combination of clamping force and ultrasonic vibration amplitude of the welding tip, but there are optimal combinations of these and also limits that must be clearly identified.
Abstract: A Friction stir welding tool is a critical component to
the success of the process. The tool typically consists of a rotating
round shoulder and a threaded cylindrical pin that heats the work
piece, mostly by friction, and moves the softened alloy around it to
form the joint. In this research work, an attempt has been made to
investigate the relationship between FSW variables mainly tool
profile, rotating speed, welding speed and the mechanical properties
(tensile strength, yield strength, percentage elongation, and micro
hardness) of friction stir welded aluminum alloy 5083 joints. From
the experimental details, it can be assessed that the joint produced by
using Triflute profile tool has contribute superior mechanical and
structural properties as compared to Tapered unthreaded & Threaded
tool for 1000rpm.
Abstract: This research paper portrays a comparative analysis of
thermomechanical behaviour of Shielded Metal Arc Welding
(SMAW) and Gas Tungsten Arc Welding (GTAW) of low carbon
steel of AISI 1020 grade butt joints. The thermal history has been
obtained by experimental work. We have focused on temperature
dependent cooling rate as depicted by Adam’s two-dimensional
model. The effect of moving point heat source of SMAW and GTAW
on mechanical properties has been judged by optical and scanning
electron micrographs of different regions in weld joints. The
microhardness study has been carried to visualize the joint strength
due to formation of different phases.
Abstract: The purposes of hydraulic gate are to maintain the
functions of storing and draining water. It bears long-term hydraulic
pressure and earthquake force and is very important for reservoir and
waterpower plant. The high tensile strength of steel plate is used as
constructional material of hydraulic gate. The cracks and rusts,
induced by the defects of material, bad construction and seismic
excitation and under water respectively, thus, the mechanics
phenomena of gate with crack are probing into the cause of stress
concentration, induced high crack increase rate, affect the safety and
usage of hydroelectric power plant. Stress distribution analysis is a
very important and essential surveying technique to analyze
bi-material and singular point problems. The finite difference
infinitely small element method has been demonstrated, suitable for
analyzing the buckling phenomena of welding seam and steel plate
with crack. Especially, this method can easily analyze the singularity
of kink crack. Nevertheless, the construction form and deformation
shape of some gates are three-dimensional system. Therefore, the
three-dimensional Digital Image Correlation (DIC) has been
developed and applied to analyze the strain variation of steel plate with
crack at weld joint. The proposed Digital image correlation (DIC)
technique is an only non-contact method for measuring the variation of
test object. According to rapid development of digital camera, the cost
of this digital image correlation technique has been reduced.
Otherwise, this DIC method provides with the advantages of widely
practical application of indoor test and field test without the restriction
on the size of test object. Thus, the research purpose of this research is
to develop and apply this technique to monitor mechanics crack
variations of weld steel hydraulic gate and its conformation under
action of loading. The imagines can be picked from real time
monitoring process to analyze the strain change of each loading stage.
The proposed 3-Dimensional digital image correlation method,
developed in the study, is applied to analyze the post-buckling
phenomenon and buckling tendency of welded steel plate with crack.
Then, the stress intensity of 3-dimensional analysis of different
materials and enhanced materials in steel plate has been analyzed in
this paper. The test results show that this proposed three-dimensional
DIC method can precisely detect the crack variation of welded steel
plate under different loading stages. Especially, this proposed DIC
method can detect and identify the crack position and the other flaws
of the welded steel plate that the traditional test methods hardly detect
these kind phenomena. Therefore, this proposed three-dimensional
DIC method can apply to observe the mechanics phenomena of
composite materials subjected to loading and operating.
Abstract: The wider growing Finite Element Method (FEM)
application is caused by its benefits of cost saving and environment
friendly. Also, by using FEM a deep understanding of certain
phenomenon can be achieved. This paper observed the role of
material properties and volumetric change when Solid State Phase
Transformation (SSPT) takes place in residual stress formation due to
a welding process of ferritic steels through coupled Thermo-
Metallurgy-Mechanical (TMM) analysis. The correctness of FEM residual stress prediction was validated by
experiment. From parametric study of the FEM model, it can be
concluded that the material properties change tend to over-predicts
residual stress in the weld center whilst volumetric change tend to
underestimates it. The best final result is the compromise of both by
incorporates them in the model which has a better result compared to
a model without SSPT.
Abstract: The aim of this study is to identify the suitability of
Virtual Learning Environment (VLE) in welding simulator
application towards Computer-Based Training (CBT) in developing
skills upon new students at the Advanced Technology Training
Center (ADTEC) Batu Pahat, Johor, Malaysia and GIATMARA,
Batu Pahat, Johor, Malaysia. The significance of the study is to create
a computer-based skills development approach in welding technology
among new students in ADTEC and GIATMARA as well as to
cultivate the elements of general skills among them. This study is
also important in elevating the number of individual knowledge
workers (K-workers) working in manufacturing industry in order to
achieve a national vision which is to be an industrial nation in the
year of 2020. The design of the study is a survey type of research
which using questionnaires as the instruments and some 136 students
from ADTEC and GIATMARA were interviewed. Descriptive
analysis is used to identify the frequency and mean values. The
findings of the study show that the welding technology has developed
skills in the students because of the application of VLE simulated at a
high level and the respondents agreed that the skills could be
embedded through the application of the VLE simulator. In summary,
the VLE simulator is suitable in welding skills development training
in terms of exposing new students with the relevant characteristics of
welding skills and at the same time spurring the students’ interest
towards learning more about the skills.
Abstract: Friction stir welding and tungsten inert gas welding
techniques were employed to weld armor grade aluminum alloy to
investigate the effect of welding processes on tensile behavior of
weld joints. Tensile tests, Vicker microhardness tests and optical
microscopy were performed on developed weld joints and base metal.
Welding process influenced tensile behavior and microstructure of
weld joints. Friction stir welded joints showed tensile behavior better
than tungsten inert gas weld joints.
Abstract: A large variety of pipe flange is required in marine
and construction industry. Pipe flanges are usually welded or screwed
to the pipe end and are connected with bolts. This approach is very
simple and widely used for a long time; however, it results in high
development cost and low productivity, and the productions made by
this approach usually have safety problem at the welding area. In this
research, a new approach of forming pipe flange based on cold
forging and floating die concept is presented. This innovative
approach increases the effectiveness of the material usage and save
the time cost compared with conventional welding method. To ensure the dimensional accuracy of the final product, the finite
element analysis (FEA) was carried out to simulate the process of
cold forging, and the orthogonal experiment methods were used to
investigate the influence of four manufacturing factors (pin die angle,
pipe flange angle, rpm, pin die distance from clamp jig) and predicted
the best combination of them. The manufacturing factors were
obtained by numerical and experimental studies and it shows that the
approach is very useful and effective for the forming of pipe flange,
and can be widely used later.
Abstract: During welding or flame cutting of metals, the
prediction of heat affected zone (HAZ) is critical. There is need to
develop a simple mathematical model to calculate the temperature
variation in HAZ and derivative analysis can be used for this purpose.
This study presents analytical solution for heat transfer through
conduction in mild steel plate. The homogeneous and nonhomogeneous
boundary conditions are single variables. The full field
analytical solutions of temperature measurement, subjected to local
heating source, are derived first by method of separation of variables
followed with the experimental visualization using infrared imaging.
Based on the present work, it is suggested that appropriate heat input
characteristics controls the temperature distribution in and around
HAZ.
Abstract: In this study, failure analysis of pipe system at a micro
hydroelectric power plant is investigated. Failure occurred at the pipe
system in the powerhouse during shut down operation of the water
flow by a valve. This locking had caused a sudden shock wave, also
called “Water-hammer effect”, resulting in noise and inside pressure
increase. After visual investigation of the effect of the shock wave on
the system, a circumference crack was observed at the pipe flange
weld region. To establish the reason for crack formation, calculations
of pressure and stress values at pipe, flange and welding seams were
carried out and concluded that safety factor was high (2.2), indicating
that no faulty design existed. By further analysis, pipe system and
hydroelectric power plant was examined. After observations it is
determined that the plant did not include a ventilation nozzle (air
trap), that prevents the system of sudden pressure increase inside the
pipes which is caused by water-hammer effect. Analyses were carried
out to identify the influence of water-hammer effect on inside
pressure increase and it was concluded that, according Jowkowsky’s
equation, shut down time is effective on inside pressure increase. The
valve closing time was uncertain but by a shut down time of even one
minute, inside pressure would increase by 7.6 bar (working pressure
was 34.6 bar). Detailed investigations were also carried out on the
assembly of the pipe-flange system by considering technical
drawings. It was concluded that the pipe-flange system was not
installed according to the instructions. Two of five weld seams were
not applied and one weld was carried out faulty. This incorrect and
inadequate weld seams resulted in; insufficient connection of the pipe
to the flange constituting a strong notch effect at weld seam regions,
increase in stress values and the decrease of strength and safety
factor.
Abstract: Since 1920, the industry has almost completely
changed the rivets production techniques for the manufacture of
permanent welding join production of structures and manufacture of
other products. The welding arc is the process more widely used in
industries. This is accomplished by the heat of an electric arc which
melts the base metal while the molten metal droplets are transferred
through the arc to the welding pool, protected from the atmosphere
by a gas curtain. The GMAW (Gas metal arc welding) process is
influenced by variables such as: current, polarity, welding speed,
electrode: extension, position, moving direction; type of joint,
welder's ability, among others. It is remarkable that the knowledge
and control of these variables are essential for obtaining satisfactory
quality welds, knowing that are interconnected so that changes in one
of them requiring changes in one or more of the other to produce the
desired results. The optimum values are affected by the type of base
metal, the electrode composition, the welding position and the quality
requirements. Thus, this paper proposes a new methodology, adding
the variable vibration through a mechanism developed for GMAW
welding, in order to improve the mechanical and metallurgical
properties which does not affect the ability of the welder and enables
repeatability of the welds made. For confirmation metallographic
analysis and mechanical tests were made.
Abstract: Submerged arc welding is a very complex process. It
is a very efficient and high performance welding process. In this
present study an attempt have been done to reduce the welding
distortion by increased amount of oxide flux through TiO2 in
submerged arc welding process. Care has been taken to avoid the
excessiveness of the adding agent for attainment of significant
results. Data Envelopment Analysis (DEA) based BAT algorithm is
used for the parametric optimization purpose in which DEA is used
to convert multi response parameters into a single response
parameter. The present study also helps to know the effectiveness of
the addition of TiO2 in active flux during submerged arc welding
process.
Abstract: Encapsulated O-rings are specifically designed to address the problem of sealing the most hostile chemicals and extreme temperature applications. Ultrasonic vibration hot embossing and ultrasonic welding techniques provide a fast and reliable method to fabricate encapsulated O-ring. This paper performs the design and analysis method of the acoustic horns with double extrusion to process tube double side flange simultaneously. The paper deals with study through Finite Element Method (FEM) of ultrasonic stepped horn used to process a capsulated O-ring, the theoretical dimensions of horns, and their natural frequencies and amplitudes are obtained through the simulations of COMOSOL software. Furthermore, real horns were fabricated, tested and verified to proof the practical utility of these horns.
Abstract: In this paper we propose a computer-aided solution
with Genetic Algorithms in order to reduce the drafting of reports:
FMEA analysis and Control Plan required in the manufacture of the
product launch and improved knowledge development teams for
future projects. The solution allows to the design team to introduce
data entry required to FMEA. The actual analysis is performed using
Genetic Algorithms to find optimum between RPN risk factor and
cost of production. A feature of Genetic Algorithms is that they are
used as a means of finding solutions for multi criteria optimization
problems. In our case, along with three specific FMEA risk factors is
considered and reduce production cost. Analysis tool will generate
final reports for all FMEA processes. The data obtained in FMEA
reports are automatically integrated with other entered parameters in
Control Plan. Implementation of the solution is in the form of an
application running in an intranet on two servers: one containing
analysis and plan generation engine and the other containing the
database where the initial parameters and results are stored. The
results can then be used as starting solutions in the synthesis of other
projects. The solution was applied to welding processes, laser cutting
and bending to manufacture chassis for buses. Advantages of the
solution are efficient elaboration of documents in the current project
by automatically generating reports FMEA and Control Plan using
multiple criteria optimization of production and build a solid
knowledge base for future projects. The solution which we propose is
a cheap alternative to other solutions on the market using Open
Source tools in implementation.
Abstract: Potassium borates, which are widely used in welding
and metal refining industry, as a lubricating oil additive, cement
additive, fiberglass additive and insulation compound, are one of the
important groups of borate minerals. In this study the production of a
potassium borate mineral via hydrothermal method is aimed. The
potassium source of potassium nitrate (KNO3) was used along with a
sodium source of sodium hydroxide (NaOH) and boron source of
boric acid (H3BO3). The constant parameters of reaction temperature
and reaction time were determined as 80°C and 1 h, respectively. The
molar ratios of 1:1:3 (as KNO3:NaOH:H3BO3), 1:1:4, 1:1:5, 1:1:6
and 1:1:7 were used. Following the synthesis the identifications of
the produced products were conducted by X-Ray Diffraction (XRD),
Fourier Transform Infrared Spectroscopy (FT-IR) and Raman
Spectroscopy. The results of the experiments and analysis showed in
the ratio of 1:1:6, the Santite mineral with powder diffraction file
number (pdf no.) of 01-072-1688, which is known as potassium
pentaborate (KB5O8·4H2O) was synthesized as best.
Abstract: Super steel materials play a vital role in the
construction and fabrication of structural, piping and pipeline
components. In assuring the integrity of onshore and offshore
operating systems, they enable life cycle costs to be minimized. In
this context, Duplex stainless steel (DSS) material related welding on
constructions and fabrications plays a significant role in maintaining
and assuring integrity at an optimal expenditure over the life cycle of
production and process systems as well as associated structures. In
DSS welding, factors such as gap geometry, shielding gas supply
rate, welding current, and type of the welding process are vital to the
final joint performance. Hence, an experimental investigation has
been performed using an engineering robust design approach
(ERDA) to investigate the optimal settings that generate optimal
super DSS (i.e. UNS S32750) joint performance. This manuscript
illustrates the mathematical approach and experimental design,
optimal parameter settings and results of the verification experiment.
Abstract: To understand the friction stir welding process, it is
very important to know the nature of the material flow in and around
the tool. The process is a combination of both thermal as well as
mechanical work i.e. it is a coupled thermo-mechanical process.
Numerical simulations are very much essential in order to obtain a
complete knowledge of the process as well as the physics underlying
it. In the present work a model based approach is adopted in order to
study material flow. A thermo-mechanical based CFD model is
developed using a Finite Element package, Comsol Multiphysics.
The fluid flow analysis is done. The model simultaneously predicts
shear strain fields, shear strain rates and shear stress over the entire
workpiece for the given conditions. The flow fields generated by the
streamline plot give an idea of the material flow. The variation of
dynamic viscosity, velocity field and shear strain fields with various
welding parameters is studied. Finally the result obtained from the
above mentioned conditions is discussed elaborately and concluded.
Abstract: This paper shows in detail the mathematical model of
direct and inverse kinematics for a robot manipulator (welding type)
with four degrees of freedom. Using the D-H parameters, screw
theory, numerical, geometric and interpolation methods, the
theoretical and practical values of the position of robot were
determined using an optimized algorithm for inverse kinematics
obtaining the values of the particular joints in order to determine the
virtual paths in a relatively short time.
Abstract: The number of persons with implanted cardiac
pacemakers (PM) has increased in Western countries. The aim of this
paper is to investigate the possible situations where persons with a
PM may be exposed to extremely low frequency (ELF) electric (EF)
and magnetic fields (MF) that may disturb their PM. Based on our
earlier studies, it is possible to find such high public exposure to EFs
only in some places near 400 kV power lines, where an EF may
disturb a PM in unipolar mode. Such EFs cannot be found near 110
kV power lines. Disturbing MFs can be found near welding
machines. However, we do not have measurement data from welding.
Based on literature and earlier studies at Tampere University of
Technology, it is difficult to find public EF or MF exposure that is
high enough to interfere with PMs.