Abstract: Nickel-based superalloys are generally known to be difficult to cut due to their strength, low thermal conductivity, and high work hardening tendency. Superalloy such as alloy 625 is often used in the oil and gas industry as a surfacing material to provide wear and corrosion resistance to components. The material is typically applied onto a metallic substrate through weld overlay cladding, an arc welding technique. Cladded surfaces are always rugged and carry a tough skin; this creates further difficulties to the machining process. The present work utilised design of experiment to optimise the internal cylindrical rough turning for weld overlay surfaces. An L27 orthogonal array was used to assess effects of the four selected key process variables: cutting insert, depth of cut, feed rate, and cutting speed. The optimal cutting conditions were determined based on productivity and the level of tool wear.
Abstract: This paper discusses the effects of sodium hypophosphite concentration, pH, and temperature on deposition rate. This paper also discusses the evaluation of coating strength, surface, and subsurface by varying the bath parameters, percentage of phosphate, plating temperature, and pH of the plating solution. Taguchi technique has been used for the analysis. In the experiment, nickel chloride which is a source of nickel when mixed with sodium hypophosphite has been used as the reducing agent and the source of phosphate and sodium hydroxide has been used to vary the pH of the coating bath. The coated samples are tested for impact energy by conducting impact test. Finally, the effects of coating bath parameters on the impact energy absorbed have been plotted, and analysis has been carried out. Further, percentage contribution of coating bath parameters using Design of Experiments approach (DOE) has been analysed. Finally, it can be concluded that the bath parameters of the Ni-P coating will certainly influence on the strength of the specimen.
Abstract: The environmental impacts arising from mining activities affect the air, water, and soil quality. Impacts may result in unexpected and adverse environmental outcomes. This study reports on the impact of coal production on sediment in Sydney region of Australia. The sediment samples upstream and downstream from the discharge points from three mines were taken, and 80 parameters were tested. The results were assessed against sediment quality based on presence of metals. The study revealed the increment of metal content in the sediment downstream of the reference locations. In many cases, the sediment was above the Australia and New Zealand Environment Conservation Council and international sediment quality guidelines value (SQGV). The major outliers to the guidelines were nickel (Ni) and zinc (Zn).
Abstract: The aim of our work is to develop an industrial bath of nickel alloy deposit on mild steel. The optimization of the operating parameters made it possible to obtain a stable Ni-P alloy deposition formulation. To understand the reaction mechanism of the deposition process, a kinetic study was performed by cyclic voltammetry and by electrochemical impedance spectroscopy (EIS). The coatings obtained have a very high corrosion resistance in a very aggressive acid medium which increases with the heat treatment.
Abstract: The cadmium sulfide nanoparticles were synthesized from the nickel-cadmium cake of a hydrometallurgical zinc producing plant and sodium sulfide as Cd2+ and S-2 sources, respectively. Also, the synthesis process was performed by using the secretions of Bacillus licheniformis as bio-surfactant. Initially, in order to obtain a cadmium rich solution, two following steps were carried out: 1) Alkaline leaching for the removal of zinc oxide from the cake, and 2) acidic leaching to dissolve cadmium from the remained solid residue. Afterward, the obtained CdSO4 solution was used for the nanoparticle biosynthesis. Nanoparticles were characterized by the energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) to confirm the formation of CdS crystals with cubic structure. Also, transmission electron microscopy (TEM) was applied to determine the particle sizes which were in 2-10 nm range. Moreover, the presence of the protein containing bio-surfactants was approved by using infrared analysis (FTIR). In addition, the absorbance below 400 nm confirms quantum particles’ size. Finally, it was shown that valuable CdS quantum dots could be obtained from the industrial waste products via environment-friendly biological approaches.
Abstract: Chromium in the environment is considered as one of the most toxic elements probably next only to mercury and arsenic. It is acutely toxic, mutagenic and carcinogenic in the environment. Chromium contamination of soil and underground water due to industrial activities is a very serious problem in several parts of India covering Karnataka, Tamil Nadu, Andhra Pradesh etc. Functionally modified Activated Carbon Fabrics (ACF) offer targeted chromium removal from drinking water and industrial effluents. Activated carbon fabric is a light weight adsorbing material with high surface area and low resistance to fluid flow. We have investigated surface modification of ACF using various acids in the laboratory through batch as well as through continuous flow column experiments with a view to develop the optimum conditions for chromium removal. Among the various acids investigated, phosphoric acid modified ACF gave best results with a removal efficiency of 95% under optimum conditions. Optimum pH was around 2 – 4 with 2 hours contact time. Continuous column experiments with an effective bed contact time (EBCT) of 5 minutes indicated that breakthrough occurred after 300 bed volumes. Adsorption data followed a Freundlich isotherm pattern. Nickel adsorbs preferentially and sulphate reduces chromium adsorption by 50%. The ACF could be regenerated up to 52.3% using 3 M NaOH under optimal conditions. The process is simple, economical, energy efficient and applicable to industrial effluents and drinking water.
Abstract: Cylindrical alumina microfiltration membrane (GMITM Corporation, inside diameter=9 mm, outside diameter=13 mm, length= 50 mm) with an average pore size of 0.5 micrometer and porosity of about 0.35 was used as the support for membrane reactor. This support was soaked in boehmite sols, and the mean particle size was adjusted in the range of 50 to 500 nm by carefully controlling hydrolysis time, and calcined at 650 °C for two hours. This process was repeated with different boehmite solutions in order to achieve an intermediate layer with an average pore size of about 50 nm. The resulting substrate was then coated with a thin and dense layer of silica by counter current chemical vapour deposition (CVD) method. A boehmite sol with 10 wt.% of nickel which was prepared by a standard procedure was used to make the catalytic layer. BET, SEM, and XRD analysis were used to characterize this layer. The catalytic membrane reactor was placed in an experimental setup to evaluate the permeation and hydrogen separation performance for a steam reforming reaction. The setup consisted of a tubular module in which the membrane was fixed, and the reforming reaction occurred at the inner side of the membrane. Methane stream, diluted with nitrogen, and deionized water with a steam to carbon (S/C) ratio of 3.0 entered the reactor after the reactor was heated up to 500 °C with a specified rate of 2 °C/ min and the catalytic layer was reduced at presence of hydrogen for 2.5 hours. Nitrogen flow was used as sweep gas through the outer side of the reactor. Any liquid produced was trapped and separated at reactor exit by a cold trap, and the produced gases were analyzed by an on-line gas chromatograph (Agilent 7890A) to measure total CH4 conversion and H2 permeation. BET analysis indicated uniform size distribution for catalyst with average pore size of 280 nm and average surface area of 275 m2.g-1. Single-component permeation tests were carried out for hydrogen, methane, and carbon dioxide at temperature range of 500-800 °C, and the results showed almost the same permeance and hydrogen selectivity values for hydrogen as the composite membrane without catalytic layer. Performance of the catalytic membrane was evaluated by applying membranes as a membrane reactor for methane steam reforming reaction at gas hourly space velocity (GHSV) of 10,000 h−1 and 2 bar. CH4 conversion increased from 50% to 85% with increasing reaction temperature from 600 °C to 750 °C, which is sufficiently above equilibrium curve at reaction conditions, but slightly lower than membrane reactor with packed nickel catalytic bed because of its higher surface area compared to the catalytic layer.
Abstract: The toxic metal contamination and their biomagnification in marine fishes is a serious public health concern specially, in the coastal areas and the small islands. In the present study, concentration of toxic heavy metals like zinc (Zn), cadmium (Cd), lead (Pb), nickel (Ni), cobalt (Co), chromium (Cr) and mercury (Hg) were determined in the tissues of tunas (T. albacores) caught from the area near to Lakshdweep Islands. The heavy metals are one of the indicators for the marine water pollution. Geochemical weathering, industrialization, agriculture run off, fishing, shipping and oil spills are the major pollutants. The presence of heavy toxic metals in the near coastal water fishes at both western coast and eastern coast of India has been well established. The present study was conducted assuming that the distant island will not have the metals presence in a way it is at the near main land coast. However, our study shows that there is a significant amount of the toxic metals present in the tissues of tuna samples. The gill, lever and flash samples were collected in waters around Lakshdweep Islands. They were analyzed using ICP–AES for the toxic metals after microwave digestion. The concentrations of the toxic metals were found in all fish samples and the general trend of presence was in decreasing order as Zn > Al > Cd > Pb > Cr > Ni > Hg. The amount of metals was found to higher in fish having more weight.
Abstract: Cane molasses is used as a raw material for the production of baker’s yeast (Saccharomyces cerevisiae) in Egypt. The high levels of heavy metals in molasses cause a critical problem during fermentation and cause various kinds of technological difficulties (yield and quality of yeast become lower). The aim of the present study was to determine heavy metal concentrations (cadmium, nickel, lead, and copper) in crude and treated molasses obtained from the storage tanks of the baker’s yeast factory through four seasons. Also, the effect of crude molasses treatment by different methods (at laboratory scale) on heavy metals reduction and its comparison with factory treated molasses were conducted. The molasses samples obtained at autumn season had the highest values of all the studied heavy metals. The molasses treated by cation exchange resin then sulfuric acid had the lowest concentrations of heavy metals compared with other treatments.
Abstract: In this study, nickel aluminide coatings were deposited onto CMSX-4 single crystal superalloy and pure Ni substrates by using in-situ chemical vapour deposition (CVD) technique. The microstructural evolutions and coating thickness (CT) were studied upon the variation of processing conditions i.e. time and temperature. The results demonstrated (under identical conditions) that coating formed on pure Ni contains no substrate entrapments and have lower CT in comparison to one deposited on the CMSX-4 counterpart. In addition, the interdiffusion zone (IDZ) of Ni substrate is a γ’-Ni3Al in comparison to the CMSX-4 alloy that is βNiAl phase. The higher CT on CMSX-4 superalloy is attributed to presence of γ-Ni/γ’-Ni3Al structure which contains ~ 15 at.% Al before deposition (that is already present in superalloy). Two main deposition parameters (time and temperature) of the coatings were also studied in addition to standard comparison of substrate effects. The coating formation time was found to exhibit profound effect on CT, whilst temperature was found to change coating activities. In addition, the CT showed linear trend from 800 to 1000 °C, thereafter reduction was observed. This was attributed to the change in coating activities.
Abstract: The performance of organophosphorus extractants Cyanex 272 and D2EHPA on the purification of concentrate nickel sulfate solutions was evaluated. Batch scale tests were carried out at pH range of 2 to 7 using a laboratory solution simulating concentrate nickel liquors as those typically obtained when sulfate intermediates from nickel laterite are re-leached and treated for the selective removal of cobalt, zinc, manganese and copper with Cyanex 272 ([Ca] = 0.57 g/L, [Mg] = 3.2 g/L, and [Ni] = 88 g/L). The increase on the concentration of D2EHPA favored the calcium extraction. The extraction of magnesium is dependent on the pH and of ratio of extractants D2EHPA and Cyanex 272 in the organic phase. The composition of the investigated organic phase did not affect nickel extraction. The number of stages is dependent on the magnesium extraction. The most favorable operating condition to selectively remove calcium and magnesium was determined.
Abstract: The microstructure, mechanical properties and metalgraphic characteristics of Ni plated AlN-Astaloy Cr-M powders were investigated using specimens produced by tube furnace sintering at 1000-1400 °C temperature. A uniform nickel layer on AlN powders was deposited prior to sintering using electroless plating technique. A composite consisting of ternary additions, metallic phase, Ni and ceramic phase AlN within a matrix of Astaloy Cr-M had been prepared under Ar shroud and then tube furnace sintered. The experimental results carried out by using XRD (X-Ray Diffraction) and SEM (Scanning Electron Microscope) for composition (10% AlN-Astaloy Cr-M) 10% Ni at 1400 °C suggest that the best properties as 132.45HB and permittivity were obtained at 1400 °C.
Abstract: The study assessed the effectiveness of Pawpaw
(Carica papaya) wood in reducing the concentrations of heavy
metals in wastewater acting as a bio-sorbent. The following heavy
metals were considered; Zinc, Cadmium, Lead, Copper, Iron,
Selenium, Nickel and Manganese. The physiochemical properties of
Carica papaya stem were studied. The experimental sample was
sourced from the trunk of a felled matured pawpaw tree. Wastewater
for experimental use was prepared by dissolving soil samples
collected from a dump site at Owerri, Imo state of Nigeria in water.
The concentration of each metal remaining in solution as residual
metal after bio-sorption was determined using Atomic absorption
Spectrometer. The effects of pH and initial heavy metal concentration
were studied in a batch reactor. The results of Spectrometer test
showed that there were different functional groups detected in the
Carica papaya stem biomass. There was increase in metal removal as
the pH increased for all the metals considered except for Nickel and
Manganese. Optimum bio-sorption occurred at pH 5.9 with 5g/100ml
solution of bio-sorbent. The results of the study showed that the
treated wastewater is fit for irrigation purpose based on Canada
wastewater quality guideline for the protection of Agricultural
standard. This approach thus provides a cost effective and
environmentally friendly option for treating wastewater.
Abstract: NiFe2O4 (nickel ferrite), ZnFe2O4 (zinc ferrite) and
Ni0.5Zn0.5Fe2O4 (nickel-zinc ferrite) were prepared by
mechanochemical route in a planetary ball mill starting from mixture
of the appropriate quantities of the Ni(OH)2/Fe(OH)3,
Zn(OH)2/Fe(OH)3 and Ni(OH)2/Zn(OH)2/Fe(OH)3 hydroxide
powders. In order to monitor the progress of chemical reaction and
confirm phase formation, powder samples obtained after 25 h, 18 h
and 10 h of milling were characterized by X-ray diffraction (XRD),
transmission electron microscopy (TEM), IR, Raman and Mössbauer
spectroscopy. It is shown that the soft mechanochemical method, i.e.
mechanochemical activation of hydroxides, produces high quality
single phase ferrite samples in much more efficient way. From the IR
spectroscopy of single phase samples it is obvious that energy of
modes depends on the ratio of cations. It is obvious that all samples
have more than 5 Raman active modes predicted by group theory in
the normal spinel structure. Deconvolution of measured spectra
allows one to conclude that all complex bands in the spectra are made
of individual peaks with the intensities that vary from spectrum to
spectrum. The deconvolution of Raman spectra allows to separate
contributions of different cations to a particular type of vibration and
to estimate the degree of inversion.
Abstract: Pure nickel coatings have been successfully
electrodeposited on copper substrates by the pulse plating technique.
The influence of current density, duty cycle and pulse frequency on
the surface morphology, crystal orientation, and microhardness was
determined. It was found that the crystallite size of the deposit
increases with increasing current density and duty cycle. The crystal
orientation progressively changed from a random texture at 1 A/dm2
to (200) texture at 10 A/dm2. Increasing pulse frequency resulted in
increased texture coefficient and peak intensity of (111) reflection.
An increase in duty cycle resulted in considerable increase in texture
coefficient and peak intensity of (311) reflection. Coatings obtained
at high current densities and duty cycle present a mixed morphology
of small and large grains. Maximum microhardness of 193 Hv was
achieved at 4 A/dm2, 10 Hz and duty cycle of 50%. Nickel coatings
with (200) texture are ductile while (111) texture improves the
microhardness of the coatings.
Abstract: The world crude oil demand is projected to rise to 108.5 million bbl/d by the year 2035. With reserves estimated at 869 billion tonnes worldwide, coal remains an abundant resource. The aim of this work was to produce a high value hydrocarbon liquid product using a Direct Coal Liquefaction (DCL) process at, relatively mild operating conditions. Via hydrogenation, the temperature-staged approach was investigated in a dual reactor lab-scale pilot plant facility. The objectives included maximising thermal dissolution of the coal in the presence of tetralin as the hydrogen donor solvent in the first stage with 2:1 and 3:1 solvent: coal ratios. Subsequently, in the second stage, hydrogen saturation, in particular, hydrodesulphurization (HDS) performance was assessed. Two commercial hydrotreating catalysts were investigated viz. NickelMolybdenum (Ni-Mo) and Cobalt-Molybdenum (Co-Mo). GC-MS results identified 77 compounds and various functional groups present in the first and second stage liquid product. In the first stage 3:1 ratios and liquid product yields catalysed by magnetite were favoured. The second stage product distribution showed an increase in the BTX (Benzene, Toluene, Xylene) quality of the liquid product, branched chain alkanes and a reduction in the sulphur concentration. As an HDS performer and selectivity to the production of long and branched chain alkanes, Ni-Mo had an improved performance over Co-Mo. Co-Mo is selective to a higher concentration of cyclohexane. For 16 days on stream each, Ni-Mo had a higher activity than Co-Mo. The potential to cover the demand for low–sulphur, crude diesel and solvents from the production of high value hydrocarbon liquid in the said process, is thus demonstrated.
Abstract: This paper presents the influences on the entrainment
of serpentines by grinding and reagents during copper–nickel sulfide
flotation. The previous bench flotation tests were performed to extract
the metallic values from the ore in Yunnan Mine, China and the
relatively satisfied results with recoveries of 86.92% Cu, 54.92% Ni,
and 74.73% Pt+Pd in the concentrate were harvested at their grades of
4.02%, 3.24% and 76.61 g/t, respectively. However, the content of
MgO in the concentrate was still more than 19%. Micro-flotation tests
were conducted with the objective of figuring out the influences on the
entrainment of serpentines into the concentrate by particle size,
flocculants or depressants and collectors, as well as visual
observations in suspension by OLYMPUS camera. All the tests results
pointed to the presences of both “entrapped-in” serpentines and its
coating on the hydrophobic flocs resulted from strong collectors
(combination of butyl xanthate, butyl ammonium dithophosphate,
even after adding carboxymethyl cellulose as effective depressant.
And fine grinding may escalate the entrainment of serpentines in the
concentrate.
Abstract: The nickel-manganese (Ni-Mn) alloy coating prepared
from DC electrodeposition process in sulphamate bath was studied.
The effects of process parameters, such as current density and
electrolyte composition, on the cathodic current efficiency,
microstructure, internal stress and mechanical properties were
investigated. Because of its crucial effect on the application to the
electroforming of microelectronic components, the development of
low internal stress coating with high leveling power was emphasized.
It was found that both the coating’s manganese content and the
cathodic current efficiency increased with the raise in current density.
In addition, the internal stress of the deposited coating showed
compressive nature at low current densities while changed to tensile
one at higher current densities. Moreover, the metallographic
observation, X-ray diffraction measurement, and polarization curve
measurement were conducted. It was found that the Ni-Mn coating
consisted of nano-sized columnar grains and the maximum hardness of
the coating was associated with (111) preferred orientation in the
microstructure. The grain size was refined along with the increase in
the manganese content of the coating, which accordingly, raised its
hardness and resistance to annealing softening. In summary, the
Ni-Mn coating prepared at lower current density of 1-2 A/dm2 had low
internal stress, high leveling power, and better corrosion resistance.
Abstract: Transparent nickel doped cobalt sulfide was fabricated
on a SnO2:F electrode and tested as an efficient electrocatalyst and as
an alternative to the expensive platinum counter electrode. In order to
investigate how this electrode could affect the electrical
characteristics of a dye-sensitized solar cell, we manufactured cells
with the same TiO2 photoanode sensitized with dye (N719) and
employing the same quasi-solid electrolyte, altering only the counter
electrode used. The cells were electrically and electrochemically
characterized and it was observed that the ones with the Ni doped
CoS2 outperformed the efficiency of the cells with the Pt counter
electrode (3.76% and 3.44% respectively). Particularly, the higher
efficiency of the cells with the Ni doped CoS2 counter electrode (CE)
is mainly because of the enhanced photocurrent density which is
attributed to the enhanced electrocatalytic ability of the CE and the
low charge transfer resistance at the CE/electrolyte interface.
Abstract: Through use of novel modern/rapid processing
techniques such as screen printing and Near-Infrared (NIR) radiative
curing, process time for the sintering of sintered nickel plaques,
applicable to alkaline nickel battery chemistries, has been drastically
reduced from in excess of 200 minutes with conventional convection
methods to below 2 minutes using NIR curing methods. Steps have
also been taken to remove the need for forming gas as a reducing
agent by implementing carbon as an in-situ reducing agent, within the
ink formulation.