Abstract: In this research, zinc coatings were fabricated by electroplating process in a sulfate solution under direct and pulse current conditions. In direct and pulse current conditions, effect of maximum current was investigated on the coating properties. Also a comparison was made between the obtained coatings under direct and pulse current. Morphology of the coatings was investigated by scanning electron microscopy (SEM). Corrosion behavior of the coatings was investigated by potentiodynamic polarization test. In pulse current conditions, the effect of pulse frequency and duty cycle was also studied. The effect of these conditions and parameters were also investigated on morphology and corrosion behavior. All of DC plated coatings are showing a distinct passivation area in -1 to -0.4 V range. Pulsed current coatings possessed a higher corrosion resistance. The results showed that current density is the most important factor regarding the fabrication process. Furthermore, a rise in duty cycle deteriorated corrosion resistance of coatings. Pulsed plated coatings performed almost 10 times better than DC plated coatings.
Abstract: Pure nickel coatings have been successfully
electrodeposited on copper substrates by the pulse plating technique.
The influence of current density, duty cycle and pulse frequency on
the surface morphology, crystal orientation, and microhardness was
determined. It was found that the crystallite size of the deposit
increases with increasing current density and duty cycle. The crystal
orientation progressively changed from a random texture at 1 A/dm2
to (200) texture at 10 A/dm2. Increasing pulse frequency resulted in
increased texture coefficient and peak intensity of (111) reflection.
An increase in duty cycle resulted in considerable increase in texture
coefficient and peak intensity of (311) reflection. Coatings obtained
at high current densities and duty cycle present a mixed morphology
of small and large grains. Maximum microhardness of 193 Hv was
achieved at 4 A/dm2, 10 Hz and duty cycle of 50%. Nickel coatings
with (200) texture are ductile while (111) texture improves the
microhardness of the coatings.