Abstract: Manganese steel (Hadfield) is one of the important
alloys in industry due to its special properties. High work hardening
ability with appropriate toughness and ductility are the properties that
caused this alloy to be used in wear resistance parts and in high
strength condition. Heat treatment is the main process through which
the desired mechanical properties and microstructures are obtained in
Hadfield steel. In this study various heat treatment cycles, differing in
austenising temperature, time and quenching solution are applied. For
this purpose, the same samples of manganese steel was heat treated in
9 different cycles, and then the mechanical properties and
microstructures were investigated. Based on the results of the study,
the optimum heat treatment cycle was obtained.
Abstract: Within this work High Temperature Single Impact
Studies were performed to evaluate deformation mechanisms at
different energy and momentum levels. To show the influence of
different microstructures and hardness levels and their response to
single impacts four different materials were tested at various
temperatures up to 700°C. One carbide reinforced NiCrBSi based
Metal Matrix Composite and three different steels were tested. The
aim of this work is to determine critical energies for fracture
appearance and the materials response at different energy and
momenta levels. Critical impact loadings were examined at elevated
temperatures to limit operating conditions in impact dominated
regimes at elevated temperatures. The investigations on the
mechanisms were performed using different means of microscopy at
the surface and in metallographic cross sections. Results indicate
temperature dependence of the occurrence of cracks in hardphase
rich materials, such as Metal Matrix Composites High Speed Steels
and the influence of different impact momenta at constant energies
on the deformation of different steels.
Abstract: The aluminum bronze matrix alumina composites using hot press and resin infiltration were investigated to study their porosities, hardness, bending strengths, and microstructures. The experiment results show that the hardness of the sintered composites with the decrease of porosity increases. The composites without and with resin infiltration have about HRF 42-61 of about 34-40% of porosity and about HRF 62-83 of about 30-36% of porosity, respectively. Besides, the alumina composites contain a more amount of iron and nickel powders would cause a lower bending strength due to forming some weaker bonding among the iron, nickel, copper, aluminum under this hot pressing of shorter time.
Abstract: Highly ordered TiO2 nanotube (TNT) arrays were
fabricated onto a pre-treated titanium foil by anodic oxidation with a
voltage of 20V in phosphoric acid/sodium fluoride electrolyte. A pretreatment
of titanium foil involved washing with acetone,
isopropanol, ethanol and deionized water. Carbon doped TiO2
nanotubes (C-TNT) was fabricated 'in-situ' with the same method in
the presence of polyvinyl alcohol and urea as carbon sources. The
affects of polyvinyl alcohol concentration and oxidation time on the
composition, morphology and structure of the C-TN were studied by
FE-SEM, EDX and XRD techniques. FESEM images of the
nanotubes showed uniform arrays of C-TNTs. The density and
microstructures of the nanotubes were greatly affected by the content
of PVA. The introduction of the polyvinyl alcohol into the electrolyte
increases the amount of C content inside TiO2 nanotube arrays
uniformly. The influence of carbon content on the photo-current of
C-TNT was investigated and the I-V profiles of the nanotubes were
established. The preliminary results indicated that the 'in-situ'
doping technique produced a superior quality nanotubes compared to
post doping techniques.
Abstract: Titanium oxide hollow microspheres were synthesized from organic precursor titanium tetraisopropoxide (TTIP) using continuous spray pyrolysis reactor. Effects of precursor concentration, applied voltage and annealing have been investigated. It was observed that the annealing of the as-synthesized TiO2 hollow microspheres at 2500C, which had an average external diameter of 200 nm, leads to an increase in the size and also more spherical shape. The precursor concentration was found to have a direct impact on the size of the microspheres, which is also evident in the absorption spectrum. The as-prepared TiO2 hollow microspheres exhibited good photocatalytic activity for the degradation of MO.
Abstract: In this study, hydroxyapatite (HA) composites are
prepared on addition of 30%CaO-30%P2O5-40%Na2 O based glass to
pure HA, in proportion of 2, 5, and 10 wt %. Each composition was
sintered over a range of temperatures. The quantitative phase
analysis was carried out using XRD and the microstructures were
studied using SEM. The density, microhardness, and compressive
strength have shown increase with the increasing amount of glass
addition. The resulting composites have chemical compositions that
are similar to the inorganic constituent of the mineral part of bone,
and constitutes trace elements like Na. X-ray diffraction showed no
decomposition of HA to secondary phases, however, the glass
reinforced-HA composites contained a HA phase and variable
amounts of tricalcium phosphate phase, depending on the amount of
bioglass added. The HA-composite material exhibited higher
compressive strength compared to sintered HA. The HA composite
reinforced with 10 wt % bioglass showed highest bioactivity level.
Abstract: To understand the material characteristics of singleand
poly-crystals of pure copper, the respective relationships between
crystallographic orientations and microstructures, and the bending
and mechanical properties were examined. And texture distribution
is also analyzed. A bending test is performed in a SEM apparatus and
while its behaviors are observed in situ. Furthermore, some
analytical results related to crystal direction maps, inverse pole
figures, and textures were obtained from EBSD analyses.
Abstract: Group-III nitride material as particularly AlxGa1-xN is
one of promising optoelectronic materials to require for shortwavelength
devices. To achieve the high-quality AlxGa1-xN films for
a high performance of such devices, AlN-nucleation layers are the
important factor. To improve the AlN-nucleation layers with a
variation of Ga-addition, XRD measurements were conducted to
analyze the crystalline quality of the subsequent Al0.1Ga0.9N with the
minimum ω-FWHMs of (0002) and (10-10) reflections of 425 arcsec
and 750 arcsec, respectively. SEM and AFM measurements were
performed to observe the surface morphology and TEM
measurements to identify the microstructures and orientations.
Results showed that the optimized Ga-atoms in the Al(Ga)Nnucleation
layers improved the surface diffusion to form moreuniform
crystallites in structure and size, better alignment of each
crystallite, and better homogeneity of island distribution. This, hence,
improves the orientation of epilayers on the Si-surface and finally
improves the crystalline quality and reduces the residual strain of
subsequent Al0.1Ga0.9N layers.
Abstract: To improve the material characteristics of single- and
poly-crystals of pure copper, the respective relationships between crystallographic orientations and microstructures, and the bending and mechanical properties were examined. And texture distribution is also
analyzed. A grain refinement procedure was performed to obtain a
grained structure. Furthermore, some analytical results related to
crystal direction maps, inverse pole figures, and textures were obtained from SEM-EBSD analyses. Results showed that these
grained metallic materials have peculiar springback characteristics with various bending angles.