Abstract: The thermoelectric properties of nano-scaled In2O3:Sn films deposited by spray pyrolysis are considered in the present report. It is shown that multicomponent In2O3:Sn-based films are promising material for the application in thermoelectric devices. It is established that the increase in the efficiency of thermoelectric conversion at CSn~5% occurred due to nano-scaled structure of the films studied and the effect of the grain boundary filtering of the low energy electrons. There are also analyzed the limitations that may appear during such material using in devices developed for the market of thermoelectric generators and refrigerators. Studies showed that the stability of nano-scaled film’s parameters is the main problem which can limit the application of these materials in high temperature thermoelectric converters.
Abstract: CuO thin films were deposited by spray ultrasonic
pyrolysis with different precursor solution. Two staring solution slats
were used namely: copper acetate and copper chloride. The influence
of these solutions on CuO thin films proprieties of is instigated. The
X rays diffraction (XDR) analysis indicated that the films deposed
with copper acetate are amorphous however the films elaborated with
copper chloride have monoclinic structure. UV- Visible transmission
spectra showed a strong absorbance of the deposited CuO thin films
in the visible region. Electrical characterization has shown that CuO
thin films prepared with copper acetate have a higher electrical
conductivity.
Abstract: Selective oxidation of H2S to elemental sulfur in a
fixed bed reactor over newly synthesized alumina nanocatalysts was
physio-chemically investigated and results compared with a
commercial Claus catalyst. Amongst these new materials, Al2O3-
supported sodium oxide prepared with wet chemical technique and
Al2O3 nanocatalyst prepared with spray pyrolysis method were the
most active catalysts for selective oxidation of H2S to elemental
sulfur. Other prepared nanocatalysts were quickly deactivated,
mainly due to the interaction with H2S and conversion into sulfides.
Abstract: Noble metal participation in nanostructured
semiconductor catalysts has drawn much interest because of their
improved properties. Recently, it has been discussed by many
researchers that Ag participation in TiO2, CuO, ZnO semiconductors
showed improved photocatalytic and optical properties. In this
research, Ag/ZnO nanocomposite particles were prepared by
Ultrasonic Spray Pyrolysis(USP) Method. 0.1M silver and zinc
nitrate aqueous solutions were used as precursor solutions. The
Ag:Zn atomic ratio of the solution was selected 1:1. Experiments
were taken place under constant air flow of 400 mL/min at 800°C
furnace temperature. Particles were characterized by X-Ray
Diffraction (XRD), Scanning Electron Microscope (SEM) and
Energy Dispersive Spectroscopy (EDS). The crystallite sizes of Ag
and ZnO in composite particles are 24.6 nm, 19.7 nm respectively.
Although, spherical nanocomposite particles are in a range of 300-
800 nm, these particles are formed by the aggregation of primary
particles which are in a range of 20-60 nm.
Abstract: Titanium oxide hollow microspheres were synthesized from organic precursor titanium tetraisopropoxide (TTIP) using continuous spray pyrolysis reactor. Effects of precursor concentration, applied voltage and annealing have been investigated. It was observed that the annealing of the as-synthesized TiO2 hollow microspheres at 2500C, which had an average external diameter of 200 nm, leads to an increase in the size and also more spherical shape. The precursor concentration was found to have a direct impact on the size of the microspheres, which is also evident in the absorption spectrum. The as-prepared TiO2 hollow microspheres exhibited good photocatalytic activity for the degradation of MO.