Abstract: The purpose of the analysis is estimation of viability and profitability of kenaf plant farming in Kelantan State. The monetary information was gathered through interviewing kenaf growers as well group discussion. In addition, the production statistics were collected from Kenaf factory administrative group. The monetary data were analyzed using the Precision financial Calculator. For kenaf production per hectare three scenarios of productivity were adopted, they were 15, 12 and ten; the research results exposed that, when kenaf productivity was 15 ton and the agronomist received financial supports from kenaf administration, the margin profit reached up to 37% which is almost dual profitability that is expected without government support. The financial analysis explains that, the adopted scenarios of the productivity are feasible when Benefit Cost Ratio (BCR) was used as financial indicator. Nonetheless, the kenaf productivity of 15 ton is the superlative viable among the others and payback period is 5 years which equals to middle period time to return the invested amount back. The study concluded that for the farmer to increase the productivity of kenaf per hectare the well farming practices as well as continuously farmers financial support are highly needed.
Abstract: This paper investigates the effect of alkali treatment and mechanical properties of kenaf (Hibiscus cannabinus) fibre for the development of yarn. Two different fibre sources are used for the yarn production. Kenaf fibres were treated with sodium hydroxide (NaOH) in the concentration of 3, 6, 9, and 12% prior to fibre opening process and tested for their tensile strength and Young’s modulus. Then, the selected fibres were introduced to fibre opener at three different opening processing parameters; namely, speed of roller feeder, small drum, and big drum. The diameter size, surface morphology, and fibre durability towards machine of the fibres were characterized. The results show that concentrations of NaOH used have greater effects on fibre mechanical properties. From this study, the tensile and modulus properties of the treated fibres for both types have improved significantly as compared to untreated fibres, especially at the optimum level of 6% NaOH. It is also interesting to highlight that 6% NaOH is the optimum concentration for the alkaline treatment. The untreated and treated fibres at 6% NaOH were then introduced to fibre opener, and it was found that the treated fibre produced higher fibre diameter with better surface morphology compared to the untreated fibre. Higher speed parameter during opening was found to produce higher yield of opened-kenaf fibres.
Abstract: Rice husk and kenaf filled with calcium carbonate
(CaCO3) and high density polyethylene (HDPE) composite were
prepared separately using twin-screw extruder at 50rpm. Different
filler loading up to 30 parts of rice husk particulate and kenaf fiber
were mixed with the fixed 30% amount of CaCO3 mineral filler to
produce rice husk/CaCO3/HDPE and kenaf/CaCO3/HDPE hybrid
composites. In this study, the effects of natural fiber for both rice
husk and kenaf in CaCO3/HDPE composite on physical, mechanical
and morphology properties were investigated. Field Emission
Scanning Microscope (FeSEM) was used to investigate the impact
fracture surfaces of the hybrid composite. The property analyses
showed that water absorption increased with the presence of kenaf
and rice husk fillers. Natural fibers in composite significantly
influence water absorption properties due to natural characters of
fibers which contain cellulose, hemicellulose and lignin structures.
The result showed that 10% of additional natural fibers into hybrid
composite had caused decreased flexural strength, however additional
of high natural fiber (>10%) filler loading has proved to increase its
flexural strength.
Abstract: Sandwich structure composites produced by epoxy
core and aluminium skin were developed as potential building
materials. Interface bonding between core and skin was controlled by
varying kenaf content. Five different weight percentage of kenaf
loading ranging from 10 wt% to 50 wt% were employed in the core
manufacturing in order to study the mechanical properties of the
sandwich composite. Properties of skin aluminium with epoxy were
found to be affected by drying time of the adhesive. Mechanical
behavior of manufactured sandwich composites in relation with
properties of constituent materials was studied. It was found that 30
wt% of kenaf loading contributed to increase the flexural strength and
flexural modulus up to 102 MPa and 32 GPa, respectively. Analysis
were done on the flatwise and edgewise compression test. For
flatwise test, it was found that 30 wt% of fiber loading could
withstand maximum force until 250 kN, with compressive strength
results at 96.94 MPa. However, at edgewise compression test, the
sandwich composite with same fiber loading only can withstand 31
kN of the maximum load with 62 MPa of compressive strength
results.
Abstract: An experimental study was conducted on foamed concrete with synthetic and natural fibres consisting of AR-glas, polypropylene, steel, kenaf and oil palm fibre. The foamed concrete mixtures produced had a target density of 1000kg/m3 and a mix ratio of (1:1.5:0.45). The fibres were used as additives. The inclusion of fibre was maintained at a volumetric fraction of 0.25 and 0.4%. The water absorption, thermal and shrinkage were determined to study the effect of the fibre on the durability properties of foamed concrete. The results showed that AR-glass fibre has the lowest percentage value of drying shrinkage compared to others.
Abstract: Fiber cross sectional area value is a crucial factor in determining the strength properties of natural fiber. Furthermore, unlike synthetic fiber, a diameter and cross sectional area of natural fiber has a large variation along and between the fibers. This study aims to determine the main and interaction effects of alkali treatment conditions which influence kenaf bast fiber mean cross sectional area. Three alkali treatment conditions at two different levels were selected. The conditions setting were alkali concentrations at 2 and 10 w/v %; fiber immersed temperature at room temperature and 1000C; and fiber immersed duration for 30 and 480 minutes. Untreated kenaf fiber was used as a control unit. Kenaf bast fiber bundle mounting tab was prepared according to ASTM C1557-03. Cross sectional area was measured using a Leica video analyzer. The study result showed that kenaf fiber bundle mean cross sectional area was reduced 6.77% to 29.88% after alkali treatment. From analysis of variance, it shows that interaction of alkali concentration and immersed time has a higher magnitude at 0.1619 compared to alkali concentration and immersed temperature interaction which was 0.0896. For the main effect, alkali concentration factor contributes to the higher magnitude at 0.1372 which indicated are decrease pattern of variability when the level was change from lower to higher level. Then, it was followed by immersed temperature at 0.1261 and immersed time at 0.0696 magnitudes.
Abstract: Natural fibres have emerged as the potential reinforcement material for composites and thus gain attraction by many researchers. This is mainly due to their applicable benefits as they offer low density, low cost, renewable, biodegradability and environmentally harmless and also comparable mechanical properties with synthetic fibre composites. The properties of hybrid composites highly depends on several factors, including the interaction of fillers with the polymeric matrix, shape and size (aspect ratio), and orientation of fillers [1]. In this study, natural fibre kenaf composites and kenaf/fibreglass hybrid composites were fabricated by a combination of hand lay-up method and cold-press method. The effect of different fibre types (powder, short and long) on the tensile properties of composites is investigated. The kenaf composites with and without the addition of fibreglass were then characterized by tensile testing and scanning electron microscopy. A significant improvement in tensile strength and modulus were indicated by the introduction of long kenaf/woven fibreglass hybrid composite. However, the opposite trends are observed in kenaf powder composite. Fractographic observation shows that fibre/matrix debonding causes the fibres pull out. This phenomenon results in the fibre and matrix fracture.
Abstract: Textile structures are engineered and fabricated to
meet worldwide structural applications. Nevertheless, research
varying textile structure on natural fibre as composite reinforcement
was found to be very limited. Most of the research is focusing on
short fibre and random discontinuous orientation of the reinforcement
structure. Realizing that natural fibre (NF) composite had been
widely developed to be used as synthetic fibre composite
replacement, this research attempted to examine the influence of
woven and cross-ply laminated structure towards its mechanical
performances. Laminated natural fibre composites were developed
using hand lay-up and vacuum bagging technique. Impact and
flexural strength were investigated as a function of fibre type (coir
and kenaf) and reinforcement structure (imbalanced plain woven,
0°/90° cross-ply and +45°/-45° cross-ply). Multi-level full factorial
design of experiment (DOE) and analysis of variance (ANOVA) was
employed to impart data as to how fibre type and reinforcement
structure parameters affect the mechanical properties of the
composites. This systematic experimentation has led to determination
of significant factors that predominant influences the impact and
flexural properties of the textile composites. It was proven that both
fibre type and reinforcement structure demonstrated significant
difference results. Overall results indicated that coir composite and
woven structure exhibited better impact and flexural strength. Yet,
cross-ply composite structure demonstrated better fracture resistance.
Abstract: This work presents the experimental results obtained
at a pilot plant which works with a slow, wet and catalytic pyrolysis
process of dry fowl manure. This kind of process mainly consists in
the cracking of the organic matrix and in the following reaction of
carbon with water, which is either already contained in the organic
feed or added, to produce carbon monoxide and hydrogen. Reactions
are conducted in a rotating reactor maintained at a temperature of
500°C; the required amount of water is about 30% of the dry organic
feed. This operation yields a gas containing about 59% (on a volume
basis) of hydrogen, 17% of carbon monoxide and other products such
as light hydrocarbons (methane, ethane, propane) and carbon
monoxide in lesser amounts. The gas coming from the reactor can be
used to produce not only electricity, through internal combustion
engines, but also heat, through direct combustion in industrial
boilers. Furthermore, as the produced gas is devoid of both solid
particles and pollutant species (such as dioxins and furans), the
process (in this case applied to fowl manure) can be considered as an
optimal way for the disposal and the contemporary energetic
valorization of organic materials, in such a way that is not damaging
to the environment.