Abstract: Natural fibers are used in polymer composites to
improve mechanical properties to replace inorganic reinforcing
agents produced by non-renewable resources. The present study
investigates the tensile and flexural behaviors of palm fibers-high
density polyethylene (HDPE) composite as a function of volume
fraction. The surface of the fibers was treated by mercerization
treatments to improve the wetting behavior of the apolar HDPE. The
treatment characterization was obtained by scanning electron
microscopy, X-Ray diffraction and infrared spectroscopy. Results
evidences that a good adhesion interfacial between fibers-matrix
caused an increase strength and modulus flexural as well as tensile
strength in the modified fibers/HDPE composites when compared to
the pure HDPE and untreated fibers reinforced composites.
Abstract: In recent years, the use of the aluminum based alloys
in the industry and technology are increasing. Alloying elements in
aluminum have further been improving the strength and stiffness
properties that provide superior compared to other metals. In this
study, investigation of physical properties (microstructure,
microhardness, tensile strength, electrical conductivity and thermal
properties) in the Al-12.6wt.%Si-%2wt.Ni ternary alloy were
investigated. Al-Si-Ni alloy was prepared in vacuum atmosphere. The
samples were directionally solidified upwards with different growth
rate V (8.3−165.45 μm/s) at constant temperature gradient G (7.73
K/mm). The flake spacings (λ), microhardness (HV), ultimate tensile
strength (σ), electrical resistivity (ρ) and thermal properties (H, Cp,
Tm) of the samples were measured. Influence of the growth rate and
spacings on microhardness, ultimate tensile strength and electrical
resistivity were investigated and relationships between them were
obtained. According to results, λ values decrease with increasing V,
but HV, σ and ρ values increase with increasing V. Variations of
electrical resistivity (ρ) of solidified samples were also measured.
The enthalpy of fusion (H) and specific heat (Cp) for the alloy was
also determined by differential scanning calorimeter (DSC) from
heating trace during the transformation from liquid to solid. The
results in this work were compared with the previous similar
experimental results.
Abstract: In present global scenario, aluminum alloys are
coining the attention of many innovators as competing structural
materials for automotive and space applications. Comparing to other
challenging alloys, especially, 7xxx series aluminum alloys have
been studied seriously because of benefits such as moderate strength;
better deforming characteristics and affordable cost. It is expected
that substitution of aluminum alloys for steels will result in great
improvements in energy economy, durability and recyclability.
However, it is necessary to improve the strength and the formability
levels at low temperatures in aluminum alloys for still better
applications. Aluminum–Zinc–Magnesium with or without other
wetting agent denoted as 7XXX series alloys are medium strength
heat treatable alloys. In addition to Zn, Mg as major alloying
additions, Cu, Mn and Si are the other solute elements which
contribute for the improvement in mechanical properties by suitable
heat treatment process. Subjecting to suitable treatments like age
hardening or cold deformation assisted heat treatments; known as low
temperature thermomechanical treatments (LTMT) the challenging
properties might be incorporated. T6 is the age hardening or
precipitation hardening process with artificial aging cycle whereas T8
comprises of LTMT treatment aged artificially with X% cold
deformation. When the cold deformation is provided after solution
treatment, there is increase in hardness related properties such as
wear resistance, yield and ultimate strength, toughness with the
expense of ductility. During precipitation hardening both hardness
and strength of the samples are increasing. The hardness value may
further improve when room temperature deformation is positively
supported with age hardening known as thermomechanical treatment.
It is intended to perform heat treatment and evaluate hardness, tensile
strength, wear resistance and distribution pattern of reinforcement in
the matrix. 2 to 2.5 and 3 to 3.5 times increase in hardness is reported
in age hardening and LTMT treatments respectively as compared to
as-cast composite. There was better distribution of reinforcements in
the matrix, nearly two fold increase in strength levels and up to 5
times increase in wear resistance are also observed in the present
study.
Abstract: This paper attempts to evaluate the effect of fire
damage on concrete by using nonlinear resonance vibration method,
one of the nonlinear nondestructive method. Concrete exhibits not
only nonlinear stress-strain relation but also hysteresis and discrete
memory effect which are contained in consolidated materials.
Hysteretic materials typically show the linear resonance frequency
shift. Also, the shift of resonance frequency is changed according to
the degree of micro damage. The degree of the shift can be obtained
through nonlinear resonance vibration method. Five exposure
scenarios were considered in order to make different internal micro
damage. Also, the effect of post-fire-curing on fire-damaged concrete
was taken into account to conform the change in internal damage.
Hysteretic nonlinearity parameter was obtained by amplitudedependent
resonance frequency shift after specific curing periods. In
addition, splitting tensile strength was measured on each sample to
characterize the variation of residual strength. Then, a correlation
between the hysteretic nonlinearity parameter and residual strength
was proposed from each test result.
Abstract: Natural fibres have emerged as the potential reinforcement material for composites and thus gain attraction by many researchers. This is mainly due to their applicable benefits as they offer low density, low cost, renewable, biodegradability and environmentally harmless and also comparable mechanical properties with synthetic fibre composites. The properties of hybrid composites highly depends on several factors, including the interaction of fillers with the polymeric matrix, shape and size (aspect ratio), and orientation of fillers [1]. In this study, natural fibre kenaf composites and kenaf/fibreglass hybrid composites were fabricated by a combination of hand lay-up method and cold-press method. The effect of different fibre types (powder, short and long) on the tensile properties of composites is investigated. The kenaf composites with and without the addition of fibreglass were then characterized by tensile testing and scanning electron microscopy. A significant improvement in tensile strength and modulus were indicated by the introduction of long kenaf/woven fibreglass hybrid composite. However, the opposite trends are observed in kenaf powder composite. Fractographic observation shows that fibre/matrix debonding causes the fibres pull out. This phenomenon results in the fibre and matrix fracture.
Abstract: This work was conducted to improve the level of
resistant starch (RS) in a rice noodle using unripe banana flour and to
investigate the effect of substitution of unripe banana flour for rice
flour on the physical properties of rice noodle. In order to prepare
rice noodles, the unripe banana flour were replaced the rice flour
with different degrees of substitutions including 0, 20, 40, 60, 80, and
100%. The results indicated that substitution of unripe banana flour
was significantly affected the viscosity properties of noodle flour,
color, cooking loss, RS and total starch content of noodle. It was
found that the noodle prepared from 100% unripe banana indicated
the greatest changes on the viscosity properties and color profiles. It
also showed the highest values of cooking loss (2.53%), tensile
strength (129.03%), and RS content (13.15%).
Abstract: Gold coated silica core nanoparticles have an optical
response dictated by the plasmon resonance. The wavelength at
which the resonance occurs depends on the core and shell sizes,
allowing nanoshells to be tailored for particular applications. The
purposes of this study was to synthesize and use different
concentration of gold nanoshells as exogenous material for skin
tissue soldering and also to examine the effect of laser soldering
parameters on the properties of repaired skin. Two mixtures of
albumin solder and different concentration of gold nanoshells were
prepared. A full thickness incision of 2×20 mm2 was made on the
surface and after addition of mixtures it was irradiated by an 810nm
diode laser at different power densities. The changes of tensile
strength σt due to temperature rise, number of scan (Ns), and scan
velocity (Vs) were investigated. The results showed at constant laser
power density (I), σt of repaired incisions increases by increasing the
concentration of gold nanoshells, Ns and decreasing Vs. It is therefore
important to consider the trade off between the scan velocity and the
surface temperature for achieving an optimum operating condition. In
our case this corresponds to σt =1610 gr/cm2 at I~ 60 Wcm-2, T ~
65ºC, Ns =10 and Vs=0.2mms-1.
Abstract: This paper reports the tensile fracture location
characterizations of dissimilar friction stir welds between 5754
aluminium alloy and C11000 copper. The welds were produced using
three shoulder diameter tools; namely, 15, 18 and 25 mm by varying
the process parameters. The rotational speeds considered were 600,
950 and 1200 rpm while the feed rates employed were 50, 150 and
300 mm/min to represent the low, medium and high settings
respectively. The tensile fracture locations were evaluated using the
optical microscope to identify the fracture locations and were
characterized. It was observed that 70% of the tensile samples failed
in the Thermo Mechanically Affected Zone (TMAZ) of copper at the
weld joints. Further evaluation of the fracture surfaces of the pulled
tensile samples revealed that welds with low Ultimate Tensile
Strength either have defects or intermetallics present at their joint
interfaces.