Abstract: In this paper, Zinc Oxide (ZnO) thin films are deposited on glass substrate by sol-gel method. The ZnO thin films with well defined orientation were acquired by spin coating of zinc acetate dehydrate monoethanolamine (MEA), de-ionized water and isopropanol alcohol. These films were pre-heated at 275°C for 10 min and then annealed at 350°C, 450°C and 550°C for 80 min. The effect of annealing temperature and different thickness on structure and surface morphology of the thin films were verified by Atomic Force Microscopy (AFM). It was found that there was a significant effect of annealing temperature on the structural parameters of the films such as roughness exponent, fractal dimension and interface width. Thin films also were characterizied by X-ray Diffractometery (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure and show the c-axis grain orientation. Increasing annealing temperature increased the crystallite size and the c-axis orientation of the film after 450°C. Also In this study, ZnO thin films in different thickness have been prepared by sol-gel method on the glass substrate at room temperature. The thicknesses of films are 100, 150 and 250 nm. Using fractal analysis, morphological characteristics of surface films thickness in amorphous state were investigated. The results show that with increasing thickness, surface roughness (RMS) and lateral correlation length (ξ) are decreased. Also, the roughness exponent (α) and growth exponent (β) were determined to be 0.74±0.02 and 0.11±0.02, respectively.
Abstract: Zinc borates can be used as multi-functional
synergistic additives with flame retardant additives in polymers. Zinc
borate is white, non-hygroscopic and powder type product. The most
important properties are low solubility in water and high dehydration
temperature. Zinc borates dehydrate above 290°C and anhydrous zinc
borate has thermal resistance about 400°C. Zinc borates can be
synthesized using several methods such as hydrothermal and solidstate
processes. In this study, the solid-state method was applied at
low temperatures of 600oC and 700oC using the starting materials of
ZnO and H3BO3 with several mole ratios. The reaction time was
determined as 4 hours after some preliminary experiments. After the
synthesis, the crystal structure and the morphology of the products
were examined by X-Ray Diffraction (XRD) and Fourier Transform
Infrared Spectroscopy (FT-IR). As a result the forms of ZnB4O7,
Zn3(BO3)2, ZnB2O4 were synthesized and obtained along with the
unreacted ZnO.
Abstract: Magnetic and semiconductor nanomaterials exhibit
novel magnetic and optical properties owing to their unique size and
shape-dependent effects. With shrinking the size down to nanoscale
region, various anomalous properties that normally not present in bulk
start to dominate. Ability in harnessing of these anomalous properties
for the design of various advance electronic devices is strictly
dependent on synthetic strategies. Hence, current research has focused
on developing a rational synthetic control to produce high quality
nanocrystals by using organometallic approach to tune both size and
shape of the nanomaterials. In order to elucidate the growth
mechanism, transmission electron microscopy was employed as a
powerful tool in performing real time-resolved morphologies and
structural characterization of magnetic (Fe3O4) and semiconductor
(ZnO) nanocrystals. The current synthetic approach is found able to
produce nanostructures with well-defined shapes. We have found that
oleic acid is an effective capping ligand in preparing oxide-based
nanostructures without any agglomerations, even at high temperature.
The oleate-based precursors and capping ligands are fatty acid
compounds, which are respectively originated from natural palm oil
with low toxicity. In comparison with other synthetic approaches in
producing nanostructures, current synthetic method offers an effective
route to produce oxide-based nanomaterials with well-defined shapes
and good monodispersity. The nanocystals are well-separated with
each other without any stacking effect. In addition, the as-synthesized
nanopellets are stable in terms of chemically and physically if
compared to those nanomaterials that are previous reported. Further
development and extension of current synthetic strategy are being
pursued to combine both of these materials into nanocomposite form
that will be used as “smart magnetic nanophotocatalyst" for industry
waste water treatment.
Abstract: Vertical ZnO nanowire array films were synthesized
based on aqueous method for sensing applications. ZnO nanowires
were investigated structurally using X-ray diffraction (XRD) and
scanning electron microscopy (SEM). The gas-sensing properties of
ZnO nanowires array films are studied. It is found that the ZnO
nanowires array film sensor exhibits excellent sensing properties
towards O2 and CO2 at 100 °C with the response time shorter than 5
s. High surface area / volume ratio of vertical ZnO nanowire and high
mobility accounts for the fast response and recovery. The sensor
response was measured in the range from 100 to 500 ppm O2 and CO2
in this study.
Abstract: ZnO heteronanostructured nanowires arrays have
been fabricated by low temperature solution method. Various
heterostructures were synthesized including CdS/ZnO,
CdSe/CdS/ZnO nanowires and Co3O4/ZnO, ZnO/SiC
nanowires. These multifunctional heterostructure nanowires
showed important applications in photocatalysts, sensors,
wettability control and solar energy conversion.
Abstract: A filter is used to remove undesirable frequency information from a dynamic signal. This paper shows that the Znotch filter filtering technique can be applied to remove the noise nuisance from a machining signal. In machining, the noise components were identified from the sound produced by the operation of machine components itself such as hydraulic system, motor, machine environment and etc. By correlating the noise components with the measured machining signal, the interested components of the measured machining signal which was less interfered by the noise, can be extracted. Thus, the filtered signal is more reliable to be analysed in terms of noise content compared to the unfiltered signal. Significantly, the I-kaz method i.e. comprises of three dimensional graphical representation and I-kaz coefficient, Z∞ could differentiate between the filtered and the unfiltered signal. The bigger space of scattering and the higher value of Z∞ demonstrated that the signal was highly interrupted by noise. This method can be utilised as a proactive tool in evaluating the noise content in a signal. The evaluation of noise content is very important as well as the elimination especially for machining operation fault diagnosis purpose. The Z-notch filtering technique was reliable in extracting noise component from the measured machining signal with high efficiency. Even though the measured signal was exposed to high noise disruption, the signal generated from the interaction between cutting tool and work piece still can be acquired. Therefore, the interruption of noise that could change the original signal feature and consequently can deteriorate the useful sensory information can be eliminated.
Abstract: Post growth annealing of solution grown ZnO
nanowire array is performed under controlled oxygen ambience. The
role of annealing over surface defects and their consequence on
dark/photo-conductivity and photosensitivity of nanowire array is
investigated. Surface defect properties are explored using various
measurement tools such as contact angle, photoluminescence, Raman
spectroscopy and XPS measurements. The contact angle of the NW
films reduces due to oxygen annealing and nanowire film surface
changes from hydrophobic (96°) to hydrophilic (16°). Raman and
XPS spectroscopy reveal that oxygen annealing improves the crystal
quality of the nanowire films. The defect band emission intensity
(relative to band edge emission, ID/IUV) reduces from 1.3 to 0.2 after
annealing at 600 °C at 10 SCCM flow of oxygen. An order
enhancement in dark conductivity is observed in O2 annealed
samples, while photoconductivity is found to be slightly reduced due
to lower concentration of surface related oxygen defects.
Abstract: Based on an analysis of the mechanism of degradation of optical characteristics of the ZnO-pigmented white paint by electron irradiation, a model of single molecular color centers is built. An equation that explains the relationship between the changes of variation of the ZnO-pigmented white paint-s spectrum absorptance and electron fluence is derived. The uncertain parameters in the equation can be calculated using the curve fitting by experimental data. The result indicates that the model can be applied to predict the degradation of optical characteristics of ZnO-pigmented white paint by electron radiation.
Abstract: We report here structural, mechanical and I-V
characteristics of Zn1-xMxO ceramic samples with various x and M.
It is found that the considered dopants does not influence the wellknown
peaks related to wurtzite structure of ZnO ceramics, while the
shape and size of grains are clearly affected. Average crystalline
diameters, deduced from XRD are between 42 nm and 54 nm, which
are 70 times lower than those obtained from SEM micrographs.
Interestingly, the potential barrier could be formed by adding Cu up
to 0.20, and it is completely deformed by 0.025 Ni additions. The
breakdown field could be enhanced up to 4138 V/cm by 0.025 Cu
additions, followed by a decrease with further increase of Cu . On
the other hand a gradual decrease in VHN is reported for both
dopants and their values are higher in Ni samples as compared to Cu
samples. The electrical conductivity is generally improved by Ni,
while addition of Cu improved it only in the over doped region (≥
0.10). These results are discussed in terms of the difference of
valency and ferromagnetic ordering for both dopants as compared to
undoped sample.
Abstract: TiO2 supported nano-ZnO catalyst was prepared by
deposition-precipitation and tested for the trans-esterification
reaction of soybean oil to biodiesel. The TiO2 support stabilized the
nano-ZnO in a dispersed form with limited crystallite size compared
to the unsupported ZnO. The final ZnO dispersion and crystallite size
and the material transfer resistance in the catalyst significantly
influenced the supported nano-ZnO catalyst performance.
Abstract: The paper reports the preparation and photocatalytic
activity of ZnO/SnO2 and SnO2 nanoparticles. These nanoparticles
were synthesized by hydrothermal method. The products were
characterized by X-ray diffraction (XRD) and scanning electron
microscopy (SEM). Their grain sizes are about 50-100 nm. The
photocatalytic activities of these materials were investigated for
congo red removal from aqueous solution under UV light irradiation.
It was shown that the use of ZnO/SnO2 as photocatalyst have better
photocatalytic activity for degradation of congo red than SnO2 or
TiO2 (anatase, particle size: 30nm) alone.
Abstract: ZnO+Ga2O3 functionally graded thin films (FGTFs)
were examined for their potential use as Solar cell and organic light
emitting diodes (OLEDs). FGTF transparent conducting oxides (TCO)
were fabricated by combinatorial RF magnetron sputtering. The
composition gradient was controlled up to 10% by changing the
plasma power of the two sputter guns. A Ga2O3+ZnO graded region
was placed on the top layer of ZnO. The FGTFs showed up to 80%
transmittance. Their surface resistances were reduced to < 10% by
increasing the Ga2O3: pure ZnO ratio in the TCO. The FGTFs- work
functions could be controlled within a range of 0.18 eV. The
controlled work function is a very promising technology because it
reduces the contact resistance between the anode and Hall transport
layers of OLED and solar cell devices.