Abstract: In order to avoid the potentially devastating
consequences of global warming and climate change, the carbon
dioxide “CO2" emissions caused due to anthropogenic activities must
be reduced considerably. This paper presents the first study
examining the feasibility of carbon sequestration in construction and
demolition “C&D" waste. Experiments were carried out in a self
fabricated Batch Reactor at 40ºC, relative humidity of 50-70%, and
flow rate of CO2 at 10L/min for 1 hour for water-to-solids ratio of 0.2
to 1.2. The effect of surface area was found by comparing the
theoretical extent of carbonation of two different sieve sizes (0.3mm
and 2.36mm) of C&D waste. A 38.44% of the theoretical extent of
carbonation equating to 4% CO2 sequestration extent was obtained
for C&D waste sample for 0.3mm sieve size. Qualitative,
quantitative and morphological analyses were done to validate
carbonate formation using X-ray diffraction “X.R.D.," thermal
gravimetric analysis “T.G.A., “X-Ray Fluorescence Spectroscopy
“X.R.F.," and scanning electron microscopy “S.E.M".
Abstract: A simple approach is demonstrated for growing large
scale, nearly vertically aligned ZnO nanowire arrays by thermal
oxidation method. To reveal effect of temperature on growth and
physical properties of the ZnO nanowires, gold coated zinc substrates
were annealed at 300 °C and 400 °C for 4 hours duration in air. Xray
diffraction patterns of annealed samples indicated a set of well
defined diffraction peaks, indexed to the wurtzite hexagonal phase of
ZnO. The scanning electron microscopy studies show formation of
ZnO nanowires having length of several microns and average of
diameter less than 500 nm. It is found that the areal density of wires
is relatively higher, when the annealing is carried out at higher
temperature i.e. at 400°C. From the field emission studies, the values
of the turn-on and threshold field, required to draw emission current
density of 10 μA/cm2 and 100 μA/cm2 are observed to be 1.2 V/μm
and 1.7 V/μm for the samples annealed at 300 °C and 2.9 V/μm and
3.7 V/μm for that annealed at 400 °C, respectively. The field
emission current stability, investigated over duration of more than 2
hours at the preset value of 1 μA, is found to be fairly good in both
cases. The simplicity of the synthesis route coupled with the
promising field emission properties offer unprecedented advantage
for the use of ZnO field emitters for high current density
applications.
Abstract: Chemical vapor deposition method was used to
produce carbon nanotubes on an iron based catalyst from acetylene.
Gas-phase samples collected from the different positions of the tubular reactor were analyzed by GC/MS. A variety of species ranging from hydrogen to naphthalene were observed and changes in their concentrations were plotted against the reactor position. Briefly benzene, toluene, styrene, indene and naphthalene were the main
higher molecular weight species and vinylacetylene and diacetylene were the important intermediates. Nanotube characterization was performed by scanning electron microscopy and transmission electron microscopy.
Abstract: Platinum oxide nanoparticles were prepared by a
simple hydrothermal route and chemical reduction using
carbohydrates (Fructose and sucrose) as the reducing and
stabilizing agents. The crystallite size of these nanoparticles was
evaluated from X-ray diffraction (XRD), atomic force microscopy
(AFM) and transmission electron microscopy (TEM) and was
found to be 10 nm as shown in figure 1, which is the
demonstration of EM bright field and transmission electron
microscopy. The effect of carbohydrates on the morphology of the
nanoparticles was studied using TEM (Figure 1). The
nanoparticles (100 μg/ml) were administered to the Pseudomonas
Stutzeri and Lactobacillus cultures and the incubation was done at
35 oC for 24 hours. The nanocomposites exhibited interesting
inhibitory as well as bactericidal activity against P. Stutzeri and
and Lactobacillus species. Incorporation of nanoparticles also
increased the thermal stability of the carbohydrates.
Abstract: Nanowire arrays of copper with uniform diameters have
been synthesized by potentiostatic electrochemical metal deposition
(EMD) of copper sulphate and potassium chloride solution within
the nano-channels of porous Indium-Tin Oxide (ITO), also known as
Tin doped Indium Oxide templates. The nanowires developed were
fairly continuous with diameters ranging from 110-140 nm along
the entire length. Single as well as poly-crystalline copper wires
have been prepared by application of appropriate potential during the
EMD process. Scanning electron microscopy (SEM), high resolution
transmission electron microscopy (HRTEM), small angle electron
diffraction (SAED) and atomic force microscopy (AFM) were used
to characterize the synthesized nano wires at room temperature. The
electrochemical response of synthesized products was evaluated by
cyclic voltammetry while surface energy analysis was carried out
using a Goniometer.
Abstract: Among the many promising nanomaterials with antifungal properties, metal nanoparticles (silver nanoparticles) stand out due to their high chemical activity. Therefore, the aim of this study was to evaluate the effect of silver nanoparticles (AgNPs) against Phomopsis sp. AgNPs were synthesized by silver nitrate reduction with sodium citrate and stabilized with ammonia. The synthesized AgNPs have further been characterized by UV/Visible spectroscopy, Biophysical techniques like Dynamic light scattering (DLS) and Scanning Electron Microscopy (SEM). The average diameter of the prepared silver colloidal nanoparticles was about 52 nm. Absolute inhibitions (100%) were observed on treated with a 270 and 540 µg ml-1 concentration of AgNPs. The results from the study of the AgNPs antifungal effect are significant and suggest that the synthesized silver nanoparticles may have an advantage compared with conventional fungicides.
Abstract: Silver/polylactide nanocomposites (Ag/PLA-NCs) were
synthesized via chemical reduction method in diphase solvent. Silver
nitrate and sodium borohydride were used as a silver precursor
and reducing agent in the polylactide (PLA). The properties of
Ag/PLA-NCs were studied as a function of the weight percentages
of silver nanoparticles (8, 16 and 32 wt% of Ag-NPs) relative to
the weight of PLA. The Ag/PLA-NCs were characterized by Xray
diffraction (XRD), transmission electron microscopy (TEM),
electro-optical microscopy (EOM), UV-visible spectroscopy (UV-vis)
and Fourier transform infrared spectroscopy (FT-IR). XRD patterns
confirmed that Ag-NPs crystallographic planes were face centered
cubic (fcc) type. TEM images showed that mean diameters of Ag-NPs
were 3.30, 3.80 and 4.80 nm. Electro-optical microscopy revealed
excellent dispersion and interaction between Ag-NPs and PLA films.
The generation of silver nanoparticles was confirmed from the UVvisible
spectra. FT-IR spectra showed that there were no significant
differences between PLA and Ag/PLA-NCs films. The synthesized
Ag/PLA-NCs were stable in organic solution over a long period of
time without sign of precipitation.
Abstract: A novel physico-chemical route to produce few layer graphene nanoribbons with atomically smooth edges is reported, via acid treatment (H2SO4:HNO3) followed by characteristic thermal shock processes involving extremely cold substances. Samples were studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Raman spectroscopy and X-ray photoelectron spectroscopy. This method demonstrates the importance of having the nanotubes open ended for an efficient uniform unzipping along the nanotube axis. The average dimensions of these nanoribbons are approximately ca. 210 nm wide and consist of few layers, as observed by transmission electron microscopy. The produced nanoribbons exhibit different chiralities, as observed by high resolution transmission electron microscopy. This method is able to provide graphene nanoribbons with atomically smooth edges which could be used in various applications including sensors, gas adsorption materials, composite fillers, among others.
Abstract: This paper investigates the influence of various
parameters on the behaviour of water droplets on polymeric surfaces
under high electric fields. An inclined plane test was carried out to
understand the droplet behaviour in strong electric field. Parameters
such as water droplet conductivity, droplet volume, polymeric
surface roughness and droplet positioning with respect to the
electrodes were studied. The flashover voltage is affected by all
aforementioned parameters. The droplet positioning is in some cases
more vital than the droplet volume. Surface damages were analysed
using Scanning Electron Microscopy (SEM) studies and by Energy
dispersive X-ray Analysis (EDAX). It is observes that magnitude of
discharge have direct influence on amount of surface da
Abstract: In our recent study, we have used ZnO nanoparticles assisted with UV light irradiation to investigate the photocatalytic degradation of Phenol Red (PR). The ZnO photocatalyst was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), specific surface area analysis (BET) and UVvisible spectroscopy. X-ray diffractometry result for the ZnO nanoparticles exhibit normal crystalline phase features. All observed peaks can be indexed to the pure hexagonal wurtzite crystal structures, with the space group of P63mc. There are no other impurities in the diffraction peak. In addition, TEM measurement shows that most of the nanoparticles are rod-like and spherical in shape and fairly monodispersed. A significant degradation of the PR was observed when the catalyst was added into the solution even without the UV light exposure. In addition, the photodegradation increases with the photocatalyst loading. The surface area of the ZnO nanomaterials from the BET measurement was 11.9 m2/g. Besides the photocatalyst loading, the effect of some parameters on the photodegradation efficiency such as initial PR concentration and pH were also studied.
Abstract: Reinforced Concrete (RC) structures strengthened
with fiber reinforced polymer (FRP) lack in thermal resistance under
elevated temperatures in the event of fire. This phenomenon led to
the lining of strengthened concrete with thin high performance
cementitious composites (THPCC) to protect the substrate against
elevated temperature. Elevated temperature effects on THPCC, based
on different cementitious materials have been studied in the past but
high-alumina cement (HAC)-based THPCC have not been well
characterized. This research study will focus on the THPCC based on
HAC replaced by 60%, 70%, 80% and 85% of ground granulated
blast furnace slag (GGBS). Samples were evaluated by the
measurement of their mechanical strength (28 & 56 days of curing)
after exposed to 400°C, 600°C and 28°C of room temperature for
comparison and corroborated by their microstructure study. Results
showed that among all mixtures, the mix containing only HAC
showed the highest compressive strength after exposed to 600°C as
compared to other mixtures. However, the tensile strength of THPCC
made of HAC and 60% GGBS content was comparable to the
THPCC with HAC only after exposed to 600°C. Field emission
scanning electron microscopy (FESEM) images of THPCC
accompanying Energy Dispersive X-ray (EDX) microanalysis
revealed that the microstructure deteriorated considerably after
exposure to elevated temperatures which led to the decrease in
mechanical strength.
Abstract: The characterization of κ-carrageenan could provide a
better understanding of its functions in biological, medical and
industrial applications. Chemical and physical analyses of
carrageenan from seaweeds, Euchema cottonii L., were done to offer
information on its properties and the effects of Co-60 γ-irradiation on
its thermochemical characteristics. The structural and morphological
characteristics of κ-carrageenan were determined using scanning
electron microscopy (SEM) while the composition, molecular weight
and thermal properties were determined using attenuated total
reflectance Fourier transform infrared spectroscopy (ATR-FTIR), gel
permeation chromatography (GPC), thermal gravimetric analysis
(TGA) and differential scanning calorimetry (DSC). Further chemical
analysis was done using hydrogen-1 nuclear magnetic resonance (1H
NMR) and functional characteristics in terms of biocompatibility
were evaluated using cytotoxicity test.
Abstract: In this paper, the residual stress of thermal spray
coatings in gas turbine component by curvature method has been
studied. The samples and shaft were coated by hard WC-12Co
cermets using high velocity oxy fuel (HVOF) after preparation in
same conditions. The curvature of coated samples was measured by
using of coordinate measurement machine (CMM). The metallurgical
and Tribological studies has been made on the coated shaft using
optical microscopy and scanning electron microscopy (SEM)
Abstract: We study the problem of reconstructing a three dimensional binary matrices whose interiors are only accessible through few projections. Such question is prominently motivated by the demand in material science for developing tool for reconstruction of crystalline structures from their images obtained by high-resolution transmission electron microscopy. Various approaches have been suggested to reconstruct 3D-object (crystalline structure) by reconstructing slice of the 3D-object. To handle the ill-posedness of the problem, a priori information such as convexity, connectivity and periodicity are used to limit the number of possible solutions. Formally, 3Dobject (crystalline structure) having a priory information is modeled by a class of 3D-binary matrices satisfying a priori information. We consider 3D-binary matrices with periodicity constraints, and we propose a polynomial time algorithm to reconstruct 3D-binary matrices with periodicity constraints from two orthogonal projections.
Abstract: Bacterial cellulose, a biopolysaccharide, is produced by the bacterium, Gluconacetobacter xylinus. Static batch fermentation for bacterial cellulose production was studied in sucrose and date syrup solutions (Bx. 10%) at 28 °C using G. xylinus (PTCC, 1734). Results showed that the maximum yields of bacterial cellulose (BC) were 4.35 and 1.69 g/l00 ml for date syrup and sucrose medium after 336 hours fermentation period, respectively. Comparison of FTIR spectrum of cellulose with BC indicated appropriate coincidence which proved that the component produced by G. xylinus was cellulose. Determination of the area under X-ray diffractometry patterns demonstrated that the crystallinity amount of cellulose (83.61%) was more than that for the BC (60.73%). The scanning electron microscopy imaging of BC and cellulose were carried out in two magnifications of 1 and 6K. Results showed that the diameter ratio of BC to cellulose was approximately 1/30 which indicated more delicacy of BC fibers relative to cellulose.
Abstract: In this study, Li4SiO4 powder was successfully
synthesized via sol gel method followed by drying at 150oC. Lithium
oxide, Li2O and silicon oxide, SiO2 were used as the starting
materials with citric acid as the chelating agent. The obtained powder
was then sintered at various temperatures. Crystallographic phase
analysis, morphology and ionic conductivity were investigated
systematically employing X-ray diffraction, Fourier Transform
Infrared, Scanning Electron Microscopy and AC impedance
spectroscopy. XRD result showed the formation of pure monoclinic
Li4SiO4 crystal structure with lattice parameters a = 5.140 Å, b =
6.094 Å, c = 5.293 Å, β = 90o in the sample sintered at 750oC. This
observation was confirmed by FTIR analysis. The bulk conductivity
of this sample at room temperature was 3.35 × 10-6 S cm-1 and the
highest bulk conductivity of 1.16 × 10-4 S cm-1 was obtained at
100°C. The results indicated that, the Li4SiO4 compound has
potential to be used as host for LISICON structured solid electrolyte
for low temperature application.
Abstract: Electro Chemical Discharge Machining (ECDM) is an
emerging hybrid machining process used in precision machining of hard and brittle non-conducting materials. The present paper gives a
critical review on materials machined by ECDM under the prevailing machining conditions; capability indicators of the process are
reported. Some results obtained while performing experiments in micro-channeling on soda lime glass using ECDM are also presented. In these experiments, Tool Wear (TW) and Material Removal (MR)
were studied using design of experiments and L–4 orthogonal array. Experimental results showed that the applied voltage was the most influencing parameter in both MR and TW studies. Field
emission scanning electron microscopy (FESEM) results obtained on the microchannels confirmed the presence of micro-cracks, primarily responsible for MR. Chemical etching was also seen along the edges.
The Energy dispersive spectroscopy (EDS) results were used to detect the elements present in the debris and specimens.
Abstract: Electrochemical-oxidation of Reactive Black-5 (RB- 5) was conducted for degradation using DSA type Ti/RuO2-SnO2- Sb2O5 electrode. In the study, for electro-oxidation, electrode was indigenously fabricated in laboratory using titanium as substrate. This substrate was coated using different metal oxides RuO2, Sb2O5 and SnO2 by thermal decomposition method. Laboratory scale batch reactor was used for degradation and decolorization studies at pH 2, 7 and 11. Current density (50mA/cm2) and distance between electrodes (8mm) were kept constant for all experiments. Under identical conditions, removal of color, COD and TOC at initial pH 2 was 99.40%, 55% and 37% respectively for initial concentration of 100 mg/L RB-5. Surface morphology and composition of the fabricated electrode coatings were characterized using scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDX) respectively. Coating microstructure was analyzed by X-ray diffraction (XRD). Results of this study further revealed that almost 90% of oxidation occurred within 5-10 minutes.
Abstract: The use of magnetic and magnetic/gold core/shell
nanoparticles in biotechnology or medicine has shown good promise
due to their hybrid nature which possesses superior magnetic and
optical properties. Some of these potential applications include
hyperthermia treatment, bio-separations, diagnostics, drug delivery
and toxin removal. Synthesis refinement to control geometric and
magnetic/optical properties, and finding functional surfactants for
biomolecular attachment, are requirements to meet application
specifics.
Various high-temperature preparative methods were used for the
synthesis of iron oxide and gold-coated iron oxide nanoparticles.
Different surface functionalities, such as 11-aminoundecanoic and
11-mercaptoundecanoic acid, were introduced on the surface of the
particles to facilitate further attachment of biomolecular functionality
and drug-like molecules. Nanoparticle thermal stability, composition,
state of aggregation, size and morphology were investigated and the
results from techniques such as Fourier Transform-Infra Red
spectroscopy (FT-IR), Ultraviolet visible spectroscopy (UV-vis),
Transmission Electron Microscopy (TEM) and thermal analysis are
discussed.
Abstract: The mechanical and tribological properties in WC-Co
coatings are strongly affected by hardness and elasticity
specifications. The results revealed the effect of spraying distance on
microhardness and elasticity modulus of coatings. The metallurgical
studies have been made on coated samples using optical microscopy,
scanning electron microscopy (SEM).