Abstract: The massive demolition of old buildings in recent years has generated tons of waste, especially brick waste. Thus, a concern of recent research is the use of this waste for the production of environmentally friendly concrete. At the same time, corrosion of the reinforcement steel rebar in classical concrete is a current problem. In this context, in the present paper a study was carried out on the corrosion of metal reinforcement in cement mortars with added brick waste. The corrosion process was analyzed on four compositions of mortars without and with 15%, 25% and 35% brick waste replacing the sand. The brick waste has majority content in SiO2, Al2O3, FeO3 and CaO. The grain size distribution of brick waste was close to that of the sand (dmax = 2 mm). The preparation method of the samples was similar to ordinary mortars. The corrosion action on the rebar in concrete, at different brick waste concentrations, was investigated by electrochemical measurements (polarization curves and electrochemical impedance spectroscopy (EIS)) at 1 month and 26 months. The results obtained at 26 months revealed that the addition of the brick waste in mortar improved the anticorrosion properties in the case of all samples compared with the etalon mortar. The best results were obtained in the case of the sample with 15% brick waste (the efficiency was ≈ 90%). The corrosion intermediary layer formed on the rebar surface was evidenced by SEM-EDX.
Abstract: Catalytic oxidation of benzene assisted by ozone, on alumina, silica, and boehmite-supported Ni/Pd catalysts was investigated at 353 K to assess the influence of the support on the reaction. Three bimetallic Ni/Pd nanosized samples with loading 4.7% of Ni and 0.17% of Pd supported on SiO2, AlOOH and Al2O3 were synthesized by the extractive-pyrolytic method. The phase composition was characterized by means of XRD and the surface area and pore size were estimated using Brunauer–Emmett–Teller (BET) and Barrett–Joyner–Halenda (BJH) methods. At the beginning of the reaction, catalysts were significantly deactivated due to the accumulation of intermediates on the catalyst surface and after 60 minutes it turned stable. Ni/Pd/AlOOH catalyst showed the highest steady-state activity in comparison with the Ni/Pd/SiO2 and Ni/Pd/Al2O3 catalysts. Their activity depends on the ozone decomposition potential of the catalysts because of generating oxidizing active species. The sample with the highest ozone decomposition ability which correlated to the surface area of the support oxidizes benzene to the highest extent.
Abstract: In structural-health monitoring of fiber reinforced plastics (FRPs), every single inorganic fiber sensor that are integrated into the bulk material requires an electrical insulation around itself, when the surrounding reinforcing fibers are electrically conductive. This results in a more accurate data acquisition only from the sensor fiber without any electrical interventions. For this purpose, thin nano-films of aluminium oxide (Al2O3)-based electrical-insulation coatings have been fabricated around the Silicon Carbide (SiC) single fiber sensors through reactive DC magnetron sputtering technique. The sputtered coatings were amorphous in nature and the thickness of the coatings increased with an increase in the sputter time. Microstructural characterization of the coated fibers performed using scanning electron microscopy (SEM) confirmed a homogeneous circumferential coating with no detectable defects or cracks on the surface. X-ray diffraction (XRD) analyses of the as-sputtered and 2 hours annealed coatings (825 & 1125 ˚C) revealed the amorphous and crystalline phases of Al2O3 respectively. Raman spectroscopic analyses produced no characteristic bands of Al2O3, as the thickness of the films was in the nanometer (nm) range, which is too small to overcome the actual penetration depth of the laser used. In addition, the influence of the insulation coatings on the mechanical properties of the SiC sensor fibers has been analyzed.
Abstract: The deployable descent technology is a lightweight entry method using an inflatable heat shield. The heatshield consists of a pressurized core which is covered by different layers of thermal insulation and flexible ablative materials in order to protect against the thermal loads. In this paper, both aluminum and silicon-aluminum aerogels were prepared by freeze-drying method. The latter material has bigger specific surface area and nano-scale pores. Mullite fibers are used as the reinforcing fibers to prepare the aerogel matrix to improve composite flexibility. The flexible composite materials were performed as an insulation layer to an underlying aramid fabric by a thermal shock test at a heat flux density of 120 kW/m2 and uniaxial tensile test. These results show that the aramid fabric with untreated mullite fibers as the thermal protective layer is completely carbonized at the heat of about 60 s. The aramid fabric as a thermal resistance layer of the composite material still has good mechanical properties at the same heat condition.
Abstract: In this paper, the effect of the additive content in the Al2O3-TiO2-MnO system on the sintering of composite ceramics based on corundum was studied. The samples were pressed by uniaxial semi-dry pressing under 100 MPa and sintered at 1500 °С and 1550 °С. The properties of composite ceramics for porosity and flexural strength were studied. When the amount of additives increases, the properties of composite ceramic samples are better than samples without additives.
Abstract: By using a combination of new technologies together with an unconventional use of different types of materials, specific mechanical properties and structures of the material can be achieved. Some possibilities are enabled by a combination of powder metallurgy in the preparation of a metal matrix with dispersed stable particles achieved by mechanical alloying and hot consolidation. This paper explains the thermomechanical properties of new generation of Oxide Dispersion Strengthened alloys (ODS) within three ranges of temperature with specified deformation profiles. The results show that the mechanical properties of new ODS alloys are significantly affected by the thermomechanical treatment.
Abstract: The present work focuses on the preparation and the stabilization of Al2O3-water based nanofluids. Though they have been widely considered in the past, to the best of our knowledge, there is no clear consensus about a proper way to prepare and stabilize them by the appropriate surfactant. In this paper, a careful experimental investigation is performed to quantify the combined influence of pH and the surfactant on the stability of Al2O3-water based nanofluids. Two volume concentrations of nanoparticles and three nanoparticle sizes have been considered. The good preparation and stability of these nanofluids are evaluated through thermal conductivity measurements. The results show that the optimum value for the thermal conductivity is obtained mainly by controlling the pH of the mixture and surfactants are not necessary to stabilize the solution.
Abstract: In this numerical work, natural convection and entropy generation of Al2O3–water nanofluid in square cavity have been studied. A two-dimensional steady laminar natural convection in a differentially heated square cavity of length L, filled with a nanofluid is investigated numerically. The horizontal walls are considered adiabatic. Vertical walls corresponding to x=0 and x=L are respectively maintained at hot temperature, Th and cold temperature, Tc. The resolution is performed by the CFD code "FLUENT" in combination with GAMBIT as mesh generator. These simulations are performed by maintaining the Rayleigh numbers varied as 103 ≤ Ra ≤ 106, while the solid volume fraction varied from 1% to 5%, the particle size is fixed at dp=33 nm and a range of the temperature from 20 to 70 °C. We used models of thermophysical nanofluids properties based on experimental measurements for studying the effect of adding solid particle into water in natural convection heat transfer and entropy generation of nanofluid. Such as models of thermal conductivity and dynamic viscosity which are dependent on solid volume fraction, particle size and temperature. The average Nusselt number is calculated at the hot wall of the cavity in a different solid volume fraction. The most important results is that at low temperatures (less than 40 °C), the addition of nanosolids Al2O3 into water leads to a decrease in heat transfer and entropy generation instead of the expected increase, whereas at high temperature, heat transfer and entropy generation increase with the addition of nanosolids. This behavior is due to the contradictory effects of viscosity and thermal conductivity of the nanofluid. These effects are discussed in this work.
Abstract: Alumina supported PtSn catalysts with cylindrical particles were prepared and characterized by using low temperature N2 adsorption/desorption and X-ray diffraction. Low temperature N2 adsorption/desorption demonstrate that the tableting changed the texture properties of catalysts. XRD pattern indicate that the crystal structure of supports had no change after reaction. The performances over particles of PtSn/Al2O3 catalysts were investigated with regards to reaction temperature, pressure, and H2/AcOH mole ratio. After tableting, the conversion of acetic acid and selectivity of ethanol and acetyl acetate decreased. High reaction temperature and pressure can improve conversion of acetic acid. H2/AcOH mole ratio of 9.36 showed the best performance on acetic acid hydrogenation. High pressure had benefits for the selectivity of ethanol and other two parameters had no obvious effect on selectivity.
Abstract: Alumina supported platinum and tin catalysts with different loadings of Pt and Sn were prepared and characterized by low temperature N2 adsorption/desorption, H2-temperature programed reduction and CO pulse chemisorption. Pt and Sn below 1% loading were suitable for acetic acid hydrogenation. The best performance over 0.75Pt1Sn/Al2O3 can reach 87.55% conversion of acetic acid and 47.39% selectivity of ethanol. The operating conditions of acetic acid hydrogenation over 1Pt1Sn/Al2O3 were investigated. High reaction temperature can enhance the conversion of acetic acid, but it decreased total selectivity of ethanol and acetyl acetate. High pressure and low weight hourly space velocity were beneficial to both conversion of acetic acid and selectivity to ethanol.
Abstract: In this work, obtaining methods of ultrafine alumina
powdery composites and high temperature pressing technology of
matrix ceramic composites with different compositions have been
discussed. Alumina was obtained by solution combustion synthesis
and sol-gel methods. Metal carbides containing powdery composites
were obtained by homogenization of finishing powders in nanomills,
as well as by their single-step high temperature synthesis .Different
types of matrix ceramics composites (α-Al2O3-ZrO2-Y2O3, α-Al2O3-
Y2O3-MgO, α-Al2O3-SiC-Y2O3, α-Al2O3-WC-Co-Y2O3, α-Al2O3-
B4C-Y2O3, α-Al2O3- B4C-TiB2 etc.) were obtained by using OXYGON
furnace. Consolidation of powders were carried out at 1550-
1750°C (hold time - 1 h, pressure - 50 MPa). Corundum ceramics
samples have been obtained and characterized by high hardness and
fracture toughness, absence of open porosity, high corrosion
resistance. Their density reaches 99.5-99.6% TD. During the work,
the following devices have been used: High temperature vacuum
furnace OXY-GON Industries Inc (USA), Electronic Scanning
Microscopes Nikon Eclipse LV 150, Optical Microscope NMM-
800TRF, Planetary mill Pulverisette 7 premium line, Shimadzu
Dynamic Ultra Micro Hardness Tester DUH-211S, Analysette 12
Dynasizer.
Abstract: This research provides a systematic way to study and
better understand double nano-tubular structure of alunina (Al2O3) and
titania (TiO2). The TiO2 NT was prepared by immersing Al2O3
template in 0.02 M titanium fluoride (TiF4) solution (pH=3) at 25 °C
for 120 min, followed by annealing at 450 °C for 1 h to obtain anatase
TiO2 NT in the Al2O3 template. Large-scale development of film for
nanotube-based CO2 capture and conversion can potentially result in
more efficient energy harvesting. In addition, the production process
will be relatively environmentally friendly. The knowledge generated
by this research will significantly advance research in the area of
Al2O3, TiO2, CaO, and Ca2O3 nano-structure film fabrication and
applications for CO2 capture and conversion. This green energy source
will potentially reduce reliance on carbon-based energy resources and
increase interest in science and engineering careers.
Abstract: TiO2 particles have been added in molten aluminium to result in aluminium based cast Al/Al3Ti-Al2O3 composite, which has been added then to molten magnesium to synthesize magnesium based cast Mg-Al/Al3Ti-Al2O3 composite. The nominal compositions in terms of Mg, Al, and TiO2 contents in the magnesium based composites are Mg-9Al-0.6TiO2, Mg-9Al-0.8TiO2, Mg-9Al-1.0TiO2 and Mg-9Al-1.2TiO2 designated respectively as MA6T, MA8T, MA10T and MA12T. The microstructure of the cast magnesium based composite shows grayish rods of intermetallics Al3Ti, inherited from aluminium based composite but these rods, on hot forging, breaks into smaller lengths decreasing the average aspect ratio (length to diameter) from 7.5 to 3.0. There are also cavities in between the broken segments of rods. β-phase in cast microstructure, Mg17Al12, dissolves during heating prior to forging and re-precipitates as relatively finer particles on cooling. The amount of β-phase also decreases on forging as segregation is removed. In both the cast and forged composite, the Brinell hardness increases rapidly with increasing addition of TiO2 but the hardness is higher in forged composites by about 80 BHN. With addition of higher level of TiO2 in magnesium based cast composite, yield strength decreases progressively but there is marginal increase in yield strength over that of the cast Mg-9 wt. pct. Al, designated as MA alloy. But the ultimate tensile strength (UTS) in the cast composites decreases with the increasing particle content indicating possibly an early initiation of crack in the brittle inter-dendritic region and their easy propagation through the interfaces of the particles. In forged composites, there is a significant improvement in both yield strength and UTS with increasing TiO2 addition and also, over those observed in their cast counterpart, but at higher addition it decreases. It may also be noted that as in forged MA alloy, incomplete recovery of forging strain increases the strength of the matrix in the composites and the ductility decreases both in the forged alloy and the composites. Initiation fracture toughness, JIC, decreases drastically in cast composites compared to that in MA alloy due to the presence of intermetallic Al3Ti and Al2O3 particles in the composite. There is drastic reduction of JIC on forging both in the alloy and the composites, possibly due to incomplete recovery of forging strain in both as well as breaking of Al3Ti rods and the voids between the broken segments of Al3Ti rods in composites. The ratio of tearing modulus to elastic modulus in cast composites show higher ratio, which increases with the increasing TiO2 addition. The ratio decreases comparatively more on forging of cast MA alloy than those in forged composites.
Abstract: Unsteady flow and heat transfer from a circular
cylinder in cross-flow is studied numerically. The governing
equations are solved by using finite volume method. Reynolds
number varies in range of 50 to 200; in this range flow is considered
to be laminar and unsteady. Al2O3 nanoparticle with volume fraction
in range of 5% to 20% is added to pure water. Effects of adding
nanoparticle to pure water on lift and drag coefficient and Nusselt
number is presented. Addition of Al2O3 has inconsiderable effect on
the value of drags and lift coefficient. However, it has significant
effect on heat transfer; results show that heat transfer of Al2O3
nanofluid is about 9% to 36% higher than pure water.
Abstract: In this numerical study, effects of using Al2O3-water
nanofluid on the rate of heat transfer have been investigated. Physical
model is a square enclosure with insulated top and bottom horizontal
walls, while the vertical walls are kept at different constant
temperatures. Two appropriate models are used to evaluate the
viscosity and thermal conductivity of nanofluid. The governing
stream-vorticity equations are solved using a second order central
finite difference scheme, coupled to the conservation of mass and
energy. The study has been carried out for the nanoparticle diameter
30, 60 and 90 nm and the solid volume fraction 0 to 0.04. Results are
presented by average Nusselt number and normalized Nusselt number
in different range of φ and D for mixed convection dominated
regime. It is found that different heat transfer rate is predicted when
the effect of nanoparticle diameter is taken into account.
Abstract: Rice Husk (RH) is the major byproduct in the
processing of paddy rice. The management of this waste has become
a big challenge to some of the rice producers, some of these wastes
are left in open dumps while some are burn in the open space, and
these two actions have been contributing to environmental pollution.
This study evaluates an alternative waste management of this
agricultural product for use as a civil engineering material. The RH
was burn in a controlled environment to form Rice Husk Ash (RHA).
The RHA was mix with lateritic clay at 0, 2, 4, 6, 8, and 10%
proportion by weight. Chemical test was conducted on the open burn
and controlled burn RHA with the lateritic clay. Physical test such as
particle size distribution, Atterberg limits test, and density test were
carried out on the mix material. The chemical composition obtained
for the RHA showed that the total percentage compositions of Fe2O3,
SiO2 and Al2O3 were found to be above 70% (class “F” pozzolan)
which qualifies it as a very good pozzolan. The coefficient of
uniformity (Cu) was 8 and coefficient of curvature (Cc) was 2 for the
soil sample. The Plasticity Index (PI) for the 0, 2, 4, 6, 8. 10% was
21.0, 18.8, 16.7, 14.4, 12.4 and 10.7 respectively. The work
concluded that RHA can be effectively used in hydraulic barriers and
as a stabilizing agent in soil stabilization.
Abstract: Ceramic obtained on the base of aluminum oxide has
wide application range, because it has unique properties, for example,
wear-resistance, dielectric characteristics, and exploitation ability at
high temperatures and in corrosive atmosphere. Low temperature
synthesis of α-Al2O3 is energo-economical process and it is topical
for developing technologies of corundum ceramics fabrication. In the present work possibilities of low temperature transformation
of oxyhydroxides in α-Al2O3, during the presence of small amount of
rare–earth elements compounds (also Th, Re), have been discussed.
Aluminum unstable oxyhydroxides have been obtained by hydrolysis
of aluminium isopropoxide, nitrates, sulphate, and chloride in
alkaline environment at 80-90ºC temperatures. β-Al(OH)3 has been
received from aluminum powder by ultrasonic development. Drying
of oxyhydroxide sol has been conducted with presence of various
types seeds, which amount reaches 0,1-0,2% (mas). Neodymium,
holmium, thorium, lanthanum, cerium, gadolinium, disprosium
nitrates and rhenium carbonyls have been used as seeds and they
have been added to the sol specimens in amount of 0.1-0.2% (mas)
calculated on metals. Annealing of obtained gels is carried out at 70–
1100ºC for 2 hrs. The same specimen transforms in α-Al2O3 at
1100ºC. At this temperature in case of presence of lanthanum and
gadolinium transformation takes place by 70-85%. In case of
presence of thorium stabilization of γ-and θ-phases takes place. It is
established, that thorium causes inhibition of α-phase generation at
1100ºC, and at the time when in all other doped specimens α-phase is
generated at lower temperatures (1000-1050ºC). Synthesis of various
type compounds and simultaneous consolidation has developed in the
furnace of OXY-GON. Composite materials containing oxide and
non-oxide components close to theoretical data have been obtained in
this furnace respectively. During the work the following devices have
been used: X-ray diffractometer DRON-3M (Cu-Kα, Ni filter,
2º/min), High temperature vacuum furnace OXY-GON, electronic
scanning microscopes Nikon ECLIPSE LV 150, NMM-800TRF,
planetary mill Pulverisette 7 premium line, SHIMADZU Dynamic
Ultra Micro Hardness Tester, DUH-211S, Analysette 12 Dyna sizer.
Abstract: Thermal enhancement of a single mini channel in
Proton Exchange Membrane Fuel Cell (PEMFC) cooling plate is
numerically investigated. In this study, low concentration of Al2O3 in
Water - Ethylene Glycol mixtures is used as coolant in single channel
of carbon graphite plate to mimic the mini channels in PEMFC
cooling plate. A steady and incompressible flow with constant heat
flux is assumed in the channel of 1mm x 5mm x 100mm. Nano
particle of Al2O3 used ranges from 0.1, 0.3 and 0.5 vol %
concentration and then dispersed in 60:40 (water: Ethylene Glycol)
mixture. The effect of different flow rates to fluid flow and heat
transfer enhancement in Re number range of 20 to 140 was observed.
The result showed that heat transfer coefficient was improved by
18.11%, 9.86% and 5.37% for 0.5, 0.3 and 0.1 vol. % Al2O3 in 60:40
(water: EG) as compared to base fluid of 60:40 (water: EG). It is also
showed that the higher vol. % concentration of Al2O3 performed
better in term of thermal enhancement but at the expense of higher
pumping power required due to increase in pressure drop
experienced. Maximum additional pumping power of 0.0012W was
required for 0.5 vol % Al2O3 in 60:40 (water: EG) at Re number 140.
Abstract: This paper reports the viability of developing Zn-27Al
alloy matrix hybrid composites reinforced with alumina, graphite and
fly ash (solid waste bye product of coal in thermal power plants).
This research work was aimed at developing low cost-high
performance Zn-27Al matrix composite with low density. Alumina
particulates (Al2O3), graphite added with 0, 2, 3, 4 and 5 wt% fly ash
were utilized to prepare 10wt% reinforcing phase with Zn-27Al alloy
as matrix using two-step stir casting method. Density measurement,
estimated percentage porosity, tensile testing, micro hardness
measurement and optical microscopy were used to assess the
performance of the composites produced. The results show that the
hardness, ultimate tensile strength, and percent elongation of the
hybrid composites decrease with increase in fly ash content. The
maximum decrease in hardness and ultimate tensile strength of
13.72% and 15.25% respectively were observed for composite grade
containing 5wt% fly ash. The percentage elongation of composite
sample without fly ash is 8.9% which is comparable with that of the
sample containing 2wt% fly ash with percentage elongation of 8.8%.
The fracture toughness of the fly ash containing composites was
however superior to those of composites without fly ash with 5wt%
fly ash containing composite exhibiting the highest fracture
toughness. The results show that fly ash can be utilized as
complementary reinforcement in ZA-27 alloy matrix composite to
reduce cost.
Abstract: This paper aims to study the heat transfer and fluid
flow characteristics of nanofluids used in spray cooling systems. The
effect of spray height, type of nanofluids and concentration of
nanofluids are numerically investigated. Five different nanofluids
such as AgH2O, Al2O3, CuO, SiO2 and TiO2 with volume fraction
range of 0.5% to 2.5% are used. The results revealed that the heat
transfer performance decreases as spray height increases. It is found
that TiO2 has the highest transfer coefficient among other nanofluids.
In dilute spray conditions, low concentration of nanofluids is
observed to be more effective in heat removal in a spray cooling
system.