Abstract: Delamination between layers in composite materials is a major structural failure. The delamination resistance is quantified by the critical strain energy release rate (SERR). The present investigation deals with the strain energy release rate of two woven fabric composites. Materials used are made of two types of glass fiber (360 gsm and 600 gsm) of plain weave and epoxy as matrix. The fracture behavior is studied using the mode I, double cantilever beam test and the mode II, end notched flexure test, in order to determine the energy required for the initiation and growth of an artificial crack. The delamination energy of these two materials is compared in order to study the effect of weave and reinforcement on mechanical properties. The fracture mechanism is also analyzed by means of scanning electron microscopy (SEM). It is observed that the plain weave fabric composite with lesser strand width has higher inter laminar fracture properties compared to the plain weave fabric composite with more strand width.
Abstract: The accomplished study is based on the appointment
and identification of ageing effects and according to this absorption
of moisture of aircraft cabin components over the life-cycle. In the
first step of the study ceiling panels from same age and from the
same aircraft cabin have been examined according to weight changes
depending on the position in the aircraft cabin. In the second step of
the study different aged ceiling panels have been examined
concerning deflection, weight changes and the acoustic sound
transmission loss. To prove the assumption of water absorption
within the study and with the theoretical background from literature
and scientific papers, an older test panel was exposed extreme
thermal conditions (humidity and temperature) within a climate
chamber to show that there is a general ingress of water to cabin
components and that this ingress of water leads to the change of
different mechanical properties.
Abstract: The mechanical properties of blends consisting of
plasticized poly(vinyl butyral) (PVB) and plasticized poly(vinyl
chloride) (PVC) are studied, in order to evaluate the possibility of
using recycled PVB waste derived from windshields. PVC was
plasticized with 38% of diisononyl phthalate (DINP), while PVB was
plasticized with 28% of triethylene glycol, bis(2-ethylhexanoate)
(3GO). The optimal process conditions for the PVB/PVC blend in 1:1
ratio were determined. Entropy was used in order to theoretically
predict the blends miscibility. The PVB content of each blend
composition used was ranging from zero to 100%. Tensile strength
and strain were tested. In addition, a comparison between recycled
and original PVB, used as constituents of the blend, was performed.
Abstract: Martensitic stainless steels have been extensively used for their good corrosion resistance and better mechanical properties. Heat treatment was suggested as one of the most excellent ways to this regard; hence, it affects the microstructure, mechanical and corrosion properties of the steel. In the current research work the microstructural changes and corrosion behavior in an AISI 420A stainless steel exposed to temperatures in the 980-1035oC range were investigated. The heat treatment is carried out in vacuum furnace within the said temperature range. The quenching of the samples was carried out in oil, brine and water media. The formation and stability of passive film was studied by Open Circuit Potential, Potentiodynamic polarization and Electrochemical Scratch Tests. The Electrochemical Impedance Spectroscopy results simulated with Equivalent Electrical Circuit suggested bilayer structure of outer porous and inner barrier oxide films. The quantitative data showed thick inner barrier oxide film retarded electrochemical reactions. Micrographs of the quenched samples showed sigma and chromium carbide phases which prove the corrosion resistance of steel alloy.
Abstract: Multifunctional structures are a potentially disruptive
technology that allows for significant mass savings on spacecraft.
The specific concept addressed herein is that of a multifunctional
power structure. In this paper, a parametric optimisation of the
design of such a structure that uses commercially available battery
cells is presented. Using numerical modelling, it was found that there
exists several trade-offs aboutthe conflict between the capacity of the
panel and its mechanical properties. It was found that there is no
universal optimal location for the cells. Placing them close to the
mechanical interfaces increases loading in the mechanically weak
cells whereas placing them at the centre of the panel increases the
stress inthe panel and reduces the stiffness of the structure.
Abstract: Environmental awareness and depletion of the
petroleum resources are among vital factors that motivate a number
of researchers to explore the potential of reusing natural fiber as an
alternative composite material in industries such as packaging,
automotive and building constructions. Natural fibers are available in
abundance, low cost, lightweight polymer composite and most
importance its biodegradability features, which often called “ecofriendly"
materials. However, their applications are still limited due
to several factors like moisture absorption, poor wettability and large
scattering in mechanical properties. Among the main challenges on
natural fibers reinforced matrices composite is their inclination to
entangle and form fibers agglomerates during processing due to
fiber-fiber interaction. This tends to prevent better dispersion of the
fibers into the matrix, resulting in poor interfacial adhesion between
the hydrophobic matrix and the hydrophilic reinforced natural fiber.
Therefore, to overcome this challenge, fiber treatment process is one
common alternative that can be use to modify the fiber surface
topology by chemically, physically or mechanically technique.
Nevertheless, this paper attempt to focus on the effect of
mercerization treatment on mechanical properties enhancement of
natural fiber reinforced composite or so-called bio composite. It
specifically discussed on mercerization parameters, and natural fiber
reinforced composite mechanical properties enhancement.
Abstract: This current research focused on development of degradable starch based packaging film with enhanced mechanical properties. A series of low density polyethylene (LDPE)/tapioca starch compounds with various tapioca starch contents were prepared by twin screw extrusion with the addition of maleic anhydride grafted polyethylene as compatibilizer. Palm cooking oil was used as processing aid to ease the blown film process, thus, degradable film can be processed via conventional blown film machine. Studies on their characteristics, mechanical properties and biodegradation were carried out by Fourier Transform Infrared (FTIR) spectroscopy and optical properties, tensile test and exposure to fungi environment respectively. The presence of high starch contents had an adverse effect on the tensile properties of LDPE/tapioca starch blends. However, the addition of compatibilizer to the blends improved the interfacial adhesion between the two materials, hence, improved the tensile properties of the films. High content of starch amount also was found to increase the rate of biodegradability of LDPE/tapioca starch films. It can be proved by exposure of the film to fungi environment. A growth of microbes colony can be seen on the surface of LDPE/tapioca starch film indicates that the granular starch present on the surface of the polymer film is attacked by microorganisms, until most of it is assimilated as a carbon source.
Abstract: Solidification cracking and hydrogen cracking are some defects generated in the fusion welding of ultrahigh carbon steels. However, friction stir welding (FSW) of such steels, being a solid-state technique, has been demonstrated to alleviate such problems encountered in traditional welding. FSW include different process parameters that must be carefully defined prior processing. These parameters included but not restricted to: tool feed, tool RPM, tool geometry, tool tilt angle. These parameters form a key factor behind avoiding warm holes and voids behind the tool and in achieving a defect-free weld. More importantly, these parameters directly affect the microstructure of the weld and hence the final mechanical properties of weld. For that, 3D finite element (FE) thermo-mechanical model was developed using DEFORM 3D to simulate FSW of carbon steel. At points of interest in the joint, tracking is done for history of critical state variables such as temperature, stresses, and strain rates. Typical results found include the ability to simulate different weld zones. Simulations predictions were successfully compared to experimental FSW tests. It is believed that such a numerical model can be used to optimize FSW processing parameters to favor desirable defect free weld with better mechanical properties.
Abstract: In areas of low to moderate seismicity many building contents and equipment are not positively fixed to the floor or tied to adjacent walls. Under seismic induced horizontal vibration, such contents and equipment can suffer from damage by either overturning or impact associated with rocking. This paper focuses on the estimation of shock on typical contents and equipment due to rocking. A simplified analytical model is outlined that can be used to estimate the maximum acceleration on a rocking object given its basic geometric and mechanical properties. The developed model was validated against experimental results. The experimental results revealed that the maximum shock acceleration can be underestimated if the static stiffness of the materials at the interface between the rocking object and floor is used rather than the dynamic stiffness. Excellent agreement between the model and experimental results was found when the dynamic stiffness for the interface material was used, which was found to be generally much higher than corresponding static stiffness under different investigated boundary conditions of the cushion. The proposed model can be a beneficial tool in performing a rapid assessment of shock sensitive components considered for possible seismic rectification.
Abstract: The purpose of this research study is to investigate the manner in which various loads affect the mechanical properties of the formed mild steel plates. The investigation focuses on examining the cross-sectional area of the metal plate at the centre of the formed mild steel plate. Six mild steel plates were deformed with different loads. The loads applied on the plates had a magnitude of 5 kg, 10 kg, 15 kg, 20 kg, 25 kg and 30 kg. The radius of the punching die was 120 mm and the loads were applied at room temperature. The investigations established that the applied load causes the Vickers microhardness at the cross-sectional area of the plate to increase due to strain hardening. Hence, the percentage increase of the hardness due to the load was found to be directly proportional to the increase in the load. Furthermore, the tensile test results for the parent material showed that the average Ultimate Tensile Strength (UTS) for the three samples was 308 MPa while the average Yield Strength and Percentage Elongation were 227 MPa and 38 % respectively. Similarly, the UTS of the formed components increased after the deformation of the plate, as such it can be concluded that the forming loads alter the mechanical properties of the materials by improving and strengthening the material properties.
Abstract: Novel acrylated epoxidized hemp oil (AEHO) based
bioresins were successfully synthesised, characterized and applied to
biocomposites reinforced with woven jute fibre. Characterisation of
the synthesised AEHO consisted of acid number titrations and FTIR
spectroscopy to assess the success of the acrylation reaction. Three
different matrices were produced (vinylester (VE), 50/50 blend of
AEHO/VE and 100% AEHO) and reinforced with jute fibre to form
three different types of biocomposite samples. Mechanical properties
in the form of flexural and interlaminar shear strength (ILSS) were
investigated and compared for the different samples. Results from the
mechanical tests showed that AEHO and 50/50 based neat bioresins
displayed lower flexural properties compared with the VE samples.
However when applied to biocomposites and compared with VE
based samples, AEHO biocomposites demonstrated comparable
flexural performance and improved ILSS. These results are attributed
to improved fibre-matrix interfacial adhesion due to surface-chemical
compatibility between the natural fibres and bioresin.
Abstract: The term hybrid composite refers to the composite
containing more than one type of fiber material as reinforcing fillers.
It has become attractive structural material due to the ability of
providing better combination of properties with respect to single fiber
containing composite. The eco-friendly nature as well as processing
advantage, light weight and low cost have enhanced the attraction
and interest of natural fiber reinforced composite. The objective of
present research is to study the mechanical properties of jute-coir
fiber reinforced hybrid polypropylene (PP) composite according to
filler loading variation. In the present work composites were
manufactured by using hot press machine at four levels of fiber
loading (5, 10, 15 and 20 wt %). Jute and coir fibers were utilized at a
ratio of (1:1) during composite manufacturing. Tensile, flexural,
impact and hardness tests were conducted for mechanical
characterization. Tensile test of composite showed a decreasing trend
of tensile strength and increasing trend of the Young-s modulus with
increasing fiber content. During flexural, impact and hardness tests,
the flexural strength, flexural modulus, impact strength and hardness
were found to be increased with increasing fiber loading. Based on
the fiber loading used in this study, 20% fiber reinforced composite
resulted the best set of mechanical properties.