Abstract: In this study, fiberless reactive powder concrete (RPC) was produced with high pressure and flexural strength. C30/37 concrete was chosen as the control sample. In this study, 9 different cure types were applied to fiberless RPC. the most suitable combined cure type was selected according to the pressure and flexure strength. Pressure and flexural strength tests were applied to these samples after curing. As a result of the study, the combined cure type with the highest pressure resistance was obtained. The highest pressure resistance was achieved with consecutive standard water cure at 20 °C for 7 days – hot water cure at 90 °C for 2 days - drying oven cure at 180 °C for 2 days. As a result of the study, the highest pressure resistance of fiberless RPC was found as 123 MPa with water cure at 20 °C for 7 days - hot water cure at 90 °C for 2 days - drying oven cure at 180 °C for 2 days; and the highest flexural resistance was found as 8.37 MPa for the same combined cure type.
Abstract: Fly ash-slag based Geopolymer Cement (GPC) is presenting mechanical properties and environmental advantages that make it the predominant “green” alternative to Portland Cement (PC). Although numerous life-cycle analyses praising its environmental advantages, disposal after the end of its life remains as an issue that has been barely explored. The present study is investigating the recyclability of fly ash-slag GPC as aggregate in mortars. The purpose of the study was to evaluate the effect of GPC fine Recycled Aggregates (RA), at replacement levels of 25% and 50%, on the main mechanical properties of PC and GPC mortar mixes. The results were compared with those obtained by corresponding mixes incorporating natural and PC-RA. The main physical properties of GPC-RA were examined and proven to be comparable to those of PC-RA and slightly inferior to those of natural sand. A negligible effect was observed at 28-day compressive and flexural strength of PC mortars with GPC aggregates having a milder effect than PC. As far as GPC mortars are concerned, the influence of GPC aggregates was enhancing for the investigated mechanical properties. Additionally, a screening test showed that recycled geopolymer aggregates are not prone of inducing alkali silica reaction.
Abstract: This paper reports an experimental work that aimed to investigate the effects of clay brick waste, as part of fine aggregate, on rendering mortar performance. The brick, in crushed form, was from a local brick manufacturer that was rejected due to being of-standard. It was used to replace 33.33 %, 50 %, 66.66 % and 100 % by weight of the quarry sand in mortar. Effects of the brick replacement on the mortar key properties intended for wall plastering were investigated; these are workability, compressive strength, flexural strength, linear shrinkage, water absorption by total immersion and by capillary suction. The results showed that as the brick replacement level increased, the mortar workability reduced. The linear shrinkage increases over time and decreases with the introduction of brick waste. The compressive and flexural strengths decrease with the increase of brick waste because of their great water absorption.
Abstract: Experimental and analytical studies were carried out to investigate the structural behavior of precast foamed concrete sandwich panels (PFCSP) of total number (6) as one-way action slab tested under lateral load. The details of the test setup and procedures were illustrated. The results obtained from the experimental tests were discussed which include the observation of cracking patterns and influence of aspect ratio (L/b). Analytical study of finite element analysis was implemented and degree of composite action of the test panels was also examined in both experimental and analytical studies. Result shows that crack patterns appeared in only one-direction, similar to reports on solid slabs, particularly when both concrete wythes act in a composite manner. Foamed concrete was briefly reviewed and experimental results were compared with the finite element analyses data which gives a reasonable degree of accuracy. Therefore, based on the results obtained, PFCSP slab can be used as an alternative to conventional flooring system.
Abstract: E-glass-epoxy laminated composites having different fiber volume fractions (40, 50, 60 and 70) were fabricated with and without the addition of nanoclay. Flexural strength and tensile strength of the composite laminates were determined. It was observed that, with increasing the fiber volume fraction (Vf) of fiber from 40 to 60, the ability of nanoclay to enhance the tensile and flexural strength of E-glass-epoxy composites decreases significantly. At 70Vf, the tensile and flexural strength of the nanoclay reinforced E-glass-epoxy were found to be lowest when compared to the E-glass-epoxy composite made without the addition of nanoclay. Based on the obtained data and microstructure of the tested samples, plausible mechanism for the observed trends has been proposed. The enhanced mechanical properties for nanoclay reinforced E-glass-epoxy composites for 40-60 Vf, due to higher interface toughness coupled with strong interfilament bonding may have ensured the homogeneous load distribution across all the glass fibers. Results in the decrease in mechanical properties at 70Vf, may be due to the inability of the matrix to bind the nanoclay and glass-fibers.
Abstract: Earth structures constructed of marine clay soils have
tendency to crack. In order to improve the flexural strength and
brittleness, a technique of mixing short fibers is introduced to the soil
lime mixture. Coir fiber was used in this study as reinforcing
elements. An experimental investigation consisting primarily of
flexural tensile tests was conducted to examine the influence of coir
fibers on the flexural behaviour of the reinforced soils. The test
results that the coir fibers were effective in improving the flexural
strength and Young’s modulus of all soils examined and ductility
after peak strength for reinforced marine clay soil treated by lime. 5%
lime treated soil and 1% coir fiber reinforced soil specimens’
demonstrated good strength and durability when submerged in water
and retained 45% of their air-cured strengths.
Abstract: This experimental study consists of a characterization
of epoxy grout where an amount of 2% of graphene nanoplatelets
particles were added to commercial epoxy resin to evaluate their
behavior regarding neat epoxy resin. Compressive tests, tensile tests
and flexural tests were conducted to study the effect of graphene
nanoplatelets on neat epoxy resin. By comparing graphene-based and
neat epoxy grout, there is no significant increase of strength due to
weak interface in the graphene nanoplatelets/epoxy composites.
From this experiment, the tension and flexural strength of graphenebased
epoxy grouts is slightly lower than ones of neat epoxy grout.
Nevertheless, the addition of graphene has produced more consistent
results according to a smaller standard deviation of strength.
Furthermore, the graphene has also improved the ductility of the
grout, hence reducing its brittle behaviour. This shows that the
performance of graphene-based grout is reliably predictable and able
to minimise sudden rupture. This is important since repair design of
damaged pipeline is of deterministic nature.
Abstract: The quality of concrete is usually defined by compressive strength, but flexural strength is the most important characteristic of concrete in a pavement which control the mix design of concrete instead of compressive strength. Therefore, the aggregates which are selected for the pavements are affected by higher flexural strength. Roller Compacting Concrete Pavement (RCCP) is not a new construction method. The other characteristic of this method is no bleeding and less shrinkage due to the lower amount of water. For this purpose, a roller is needed for placing and compacting. The surface of RCCP is not smooth; therefore, the most common use of this pavement is in an industrial zone with slower traffic speed which requires durable and tough pavement. For preparing a smoother surface, it can be achieved by asphalt paver. RCCP decrease the finishing cost because there are no bars, formwork, and the lesser labor need for placing the concrete. In this paper, different aspect of RCCP such as mix design, flexural, compressive strength and focus on the different part of RCCP on detail have been investigated.
Abstract: The objective of this study was to synthesize and
characterize the poly(alkenoic acid)s with different molecular
structures, use these polymers to formulate a dental cement
restorative, and study the effect of molecular structures on reaction
kinetics, viscosity, and mechanical strengths of the formed polymers
and cement restoratives. In this study, poly(alkenoic acid)s with
different molecular structures were synthesized. The purified
polymers were formulated with commercial Fuji II LC glass fillers to
form the experimental cement restoratives. The reaction kinetics was
studied via 1HNMR spectroscopy. The formed restoratives were
evaluated using compressive strength, diametral tensile strength,
flexural strength, hardness and wear-resistance tests. Specimens were
conditioned in distilled water at 37oC for 24 h prior to testing. Fuji II
LC restorative was used as control. The results show that the higher
the arm number and initiator concentration, the faster the reaction
was. It was also found that the higher the arm number and branching
that the polymer had, the lower the viscosity of the polymer in water
and the lower the mechanical strengths of the formed restorative. The
experimental restoratives were 31-53% in compressive strength, 37-
55% in compressive modulus, 80-126% in diametral tensile strength,
76-94% in flexural strength, 4-21% in fracture toughness and 53-96%
in hardness higher than Fuji II LC. For wear test, the experimental
restoratives were only 5.4-13% of abrasive and 6.4-12% of attritional
wear depths of Fuji II LC in each wear cycle. The aging study also
showed that all the experimental restoratives increased their strength
continuously during 30 days, unlike Fuji II LC. It is concluded that
polymer molecular structures have significant and positive impact on
mechanical properties of dental cement restoratives.
Abstract: Concrete is strong in compression however weak in
tension. The tensile strength as well as ductile property of concrete
could be improved by addition of short dispersed fibers. Polyethylene
terephthalate (PET) fiber obtained from hand cutting or mechanical
slitting of plastic sheets generally used as discrete reinforcement in
substitution of steel fiber. PET fiber obtained from the former process
is in the form of straight slit sheet pattern that impart weaker
mechanical bonding behavior in the concrete matrix. To improve the
limitation of straight slit sheet fiber the present study considered two
additional geometry of fiber namely (a) flattened end slit sheet and
(b) deformed slit sheet. The mix for plain concrete was design for a
compressive strength of 25 MPa at 28 days curing time with a watercement
ratio of 0.5. Cylindrical and beam specimens with 0.5% fibers
volume fraction and without fibers were cast to investigate the
influence of geometry on the mechanical properties of concrete. The
performance parameters mainly studied include flexural strength,
splitting tensile strength, compressive strength and ultrasonic pulse
velocity (UPV). Test results show that geometry of fiber has a
marginal effect on the workability of concrete. However, it plays a
significant role in achieving a good compressive and tensile strength
of concrete. Further, significant improvement in term of flexural and
energy dissipation capacity were observed from other fibers as
compared to the straight slit sheet pattern. Also, the inclusion of PET
fiber improved the ability in absorbing energy in the post-cracking
state of the specimen as well as no significant porous structures.
Abstract: Fly ash (FA) thanks to the significant presence of SiO2
and Al2O3 as the main components is a potential raw material for
geopolymers production. Mechanical activation is a method for
improving FA reactivity and also the porosity of final mixture; those
parameters can be analysed through sorption properties. They have
direct impact on the durability of fly ash based geopolymer mortars.
In the paper, effect of FA fineness on sorption properties of
geopolymers based on sodium silicate, as well as relationship
between fly ash fineness and apparent density, compressive and
flexural strength of geopolymers are presented. The best results in the
evaluated area reached the sample H1, which contents the highest
portion of particle under 20μm (100% of GFA). The interdependence
of individual tested properties was confirmed for geopolymer
mixtures corresponding to those in the cement based mixtures: higher
is portion of fine particles < 20μm, higher is strength, density and
lower are sorption properties. The compressive strength as well as
sorption parameters of the geopolymer can be reasonably controlled
by grinding process and also ensured by the higher share of fine
particle (to 20μm) in total mass of the material.
Abstract: Rice husk and kenaf filled with calcium carbonate
(CaCO3) and high density polyethylene (HDPE) composite were
prepared separately using twin-screw extruder at 50rpm. Different
filler loading up to 30 parts of rice husk particulate and kenaf fiber
were mixed with the fixed 30% amount of CaCO3 mineral filler to
produce rice husk/CaCO3/HDPE and kenaf/CaCO3/HDPE hybrid
composites. In this study, the effects of natural fiber for both rice
husk and kenaf in CaCO3/HDPE composite on physical, mechanical
and morphology properties were investigated. Field Emission
Scanning Microscope (FeSEM) was used to investigate the impact
fracture surfaces of the hybrid composite. The property analyses
showed that water absorption increased with the presence of kenaf
and rice husk fillers. Natural fibers in composite significantly
influence water absorption properties due to natural characters of
fibers which contain cellulose, hemicellulose and lignin structures.
The result showed that 10% of additional natural fibers into hybrid
composite had caused decreased flexural strength, however additional
of high natural fiber (>10%) filler loading has proved to increase its
flexural strength.
Abstract: Properties of Portland cement mixtures with various
fractions of metakaolin were studied. 10% of Portland cement CEM I
42.5 R was replaced by different fractions of high reactivity
metakaolin with defined chemical and mineralogical properties.
Various fractions of metakaolin were prepared by jet mill classifying
system. There is a clear trend between fineness of metakaolin and
hydration heat development. Due to metakaolin presence in mixtures
the compressive strength development of mortars is rather slower for
coarser fractions but 28-day flexural strengths are improved for all
fractions of metakaoline used in mixtures compared to reference
sample of pure Portland cement. Yield point, plastic viscosity and
adhesion of fresh pastes are considerably influenced by fineness of
metakaolin used in cement pastes.
Abstract: To determine the potential of a low cost Irish
engineered timber product to replace high cost solid timber for use in
bending active structures such as gridshells a single Irish engineered
timber product in the form of orientated strand board (OSB) was
selected. A comparative study of OSB and solid timber was carried
out to determine the optimum properties that make a material suitable
for use in gridshells. Three parameters were identified to be relevant
in the selection of a material for gridshells. These three parameters
are the strength to stiffness ratio, the flexural stiffness of
commercially available sections, and the variability of material and
section properties. It is shown that when comparing OSB against
solid timber, OSB is a more suitable material for use in gridshells that
are at the smaller end of the scale and that have tight radii of
curvature. Typically, for solid timber materials, stiffness is used as an
indicator for strength and engineered timber is no different. Thus, low
flexural stiffness would mean low flexural strength. However, when
it comes to bending active gridshells, OSB offers a significant
advantage. By the addition of multiple layers, an increased section
size is created, thus endowing the structure with higher stiffness and
higher strength from initial low stiffness and low strength materials
while still maintaining tight radii of curvature. This allows OSB to
compete with solid timber on large scale gridshells. Additionally, a
preliminary sustainability study using a set of sustainability indicators
was carried out to determine the relative sustainability of building a
large-scale gridshell in Ireland with a primary focus on economic
viability but a mention is also given to social and environmental
aspects. For this, the Savill garden gridshell in the UK was used as
the functional unit with the sustainability of the structural roof
skeleton constructed from UK larch solid timber being compared
with the same structure using Irish OSB. Albeit that the advantages of
using commercially available OSB in a bending active gridshell are
marginal and limited to specific gridshell applications, further study
into an optimised engineered timber product is merited.
Abstract: Sustainability and eco-friendly requirement of
engineering materials are sort for in recent times, thus giving rise to
the development of bio-composites. However, the natural fibres to
matrix interface interactions remain a key issue in getting the desired
mechanical properties from such composites. Treatment of natural
fibres is essential in improving matrix to filler adhesion, hence
improving its mechanical properties. In this study, investigations
were carried out to determine the effect of sodium hydroxide
treatment on the tensile, flexural, impact and hardness properties of
crushed and uncrushed Luffa cylindrica fibre reinforced recycled low
density polyethylene composites. The LC (Luffa cylindrica) fibres
were treated with 0%, 2%, 4%, 6%, 8% and 10% wt. sodium
hydroxide (NaOH) concentrations for a period of 24 hours under
room temperature conditions. A formulation ratio of 80/20 g (matrix
to reinforcement) was maintained for all developed samples. Analysis
of the results showed that the uncrushed luffa fibre samples gave
better mechanical properties compared with the crushed luffa fibre
samples. The uncrushed luffa fibre composites had a maximum
tensile and flexural strength of 7.65 MPa and 17.08 Mpa respectively
corresponding to a young modulus and flexural modulus of 21.08
MPa and 232.22 MPa for the 8% and 4% wt. NaOH concentration
respectively. Results obtained in the research showed that NaOH
treatment with the 8% NaOH concentration improved the mechanical
properties of the LC fibre reinforced composites when compared with
other NaOH treatment concentration values.
Abstract: Waste silicon carbide (waste SiC) filled high-density
polyethylene (HDPE) with and without surface modifiers were
studied. Two types of surface modifiers namely; high-density
polyethylene-grafted-maleic anhydride (HDPE-g-MA) and 3-aminopropyltriethoxysilane have been used in this study. The
composites were produced using a two roll mill, extruder and shaped
in a hydraulic compression molding machine. The mechanical
properties of polymer composites such as flexural strength and
modulus, impact strength, tensile strength, stiffness and hardness
were investigated over a range of compositions. It was found that,
flexural strength and modulus, tensile modulus and hardness
increased, whereas impact strength and tensile strength decreased
with the increasing in filler contents, compared to the neat HDPE. At
similar filler content, the effect of both surface modifiers increased
flexural modulus, impact strength, tensile strength and stiffness but
reduced the flexural strength. Morphological investigation using
SEM revealed that the improvement in mechanical properties was
due to enhancement of the interfacial adhesion between waste SiC
and HDPE.
Abstract: Sandwich structure composites produced by epoxy
core and aluminium skin were developed as potential building
materials. Interface bonding between core and skin was controlled by
varying kenaf content. Five different weight percentage of kenaf
loading ranging from 10 wt% to 50 wt% were employed in the core
manufacturing in order to study the mechanical properties of the
sandwich composite. Properties of skin aluminium with epoxy were
found to be affected by drying time of the adhesive. Mechanical
behavior of manufactured sandwich composites in relation with
properties of constituent materials was studied. It was found that 30
wt% of kenaf loading contributed to increase the flexural strength and
flexural modulus up to 102 MPa and 32 GPa, respectively. Analysis
were done on the flatwise and edgewise compression test. For
flatwise test, it was found that 30 wt% of fiber loading could
withstand maximum force until 250 kN, with compressive strength
results at 96.94 MPa. However, at edgewise compression test, the
sandwich composite with same fiber loading only can withstand 31
kN of the maximum load with 62 MPa of compressive strength
results.
Abstract: Bio-composites derived from plant fiber and/or bioderived
polymer, are likely more ecofriendly and demonstrate
competitive performance with petroleum based composites. In this
research, the bio phenol-formaldehyde (bio-PF) was used as a matrix
and oil palm empty fruit bunch fiber (EFB) as reinforcement. The
matrix was synthesized via liquefaction and condensation to enhance
the combination of phenol and formaldehyde, during the process.
Then, the bio-PF was mixed with different percentage of EFB (5%,
10%, 15% and 20%) and molded at 180oC. The samples that viewed
under scanning electron microscopy (SEM) showed an excellent
wettability and interaction between EFB and matrix. Samples of 10%
EFB gave the optimum properties of impact and hardness meanwhile
sample 15% of EFB gave the highest reading of flexural modulus
(MOE) and flexural strength (MOR). For thermal stability analysis, it
was found that the weight loss and the activation energy (Ea) of the
bio-composites samples were decreased as the filler content
increased.
Abstract: In this paper, a nonlinear Finite Element Analysis
(FEA) was carried out using ANSYS software to build a model able
of predicting the behavior of Reinforced Concrete (RC) beams with
unbonded reinforcement. The FEA model was compared to existing
experimental data by other researchers. The existing experimental
data consisted of 16 beams that varied from structurally sound beams
to beams with unbonded reinforcement with different unbonded
lengths and reinforcement ratios. The model was able to predict the
ultimate flexural strength, load-deflection curve, and crack pattern of
concrete beams with unbonded reinforcement. It was concluded that
when the when the unbonded length is less than 45% of the span,
there will be no decrease in the ultimate flexural strength due to the
loss of bond between the steel reinforcement and the surrounding
concrete regardless of the reinforcement ratio. Moreover, when the
reinforcement ratio is relatively low, there will be no decrease in
ultimate flexural strength regardless of the length of unbond.
Abstract: The main objective of this paper is study the influence
of carbon nano-tubes fibers and nano silica fibers on the
characteristic compressive strength and flexural strength on concrete
and cement mortar. Twelve tested specimens were tested with square
section its dimensions (4040 160) mm, divided into four groups.
The first and second group studied the effect of carbon nano-tubes
(CNTs) fibers with different percentage equal to 0.0, 0.11%, 0.22%,
and 0.33% by weight of cement and effect of nano-silica (nS) fibers
with different percentages equal to 0.0, 1.0%, 2.0%, and 3.0% by
weight of cement on the cement mortar. The third and fourth groups
studied the effect of CNTs fiber with different percentage equal to
0.0%, 0.11%, and 0.22% by weight of cement, and effect of nS fibers
with different percentages were equal to 0.0%, 1.0%, and 2.0% by
weight of cement on the concrete. The compressive strength and
flexural strength at 7, 28, and 90 days is determined. From analysis of
tested results concluded that the nano-fibers is more effective when
used with cement mortar more than used with concrete because of
increasing the surface area, decreasing the pore and the collection of
nano-fibers. And also by adding nano-fibers the improvement of
flexural strength of concrete and cement mortar is more than
improvement of compressive strength.