Abstract: Anthropogenic sources of zinc (Zn), including industrial emissions and effluents, Zn–rich fertilizer materials and pesticides containing Zn, can contribute to increasing the concentration of soluble Zn at levels toxic to plants in acid sandy soils. The application of municipal sewage sludge or biosolids (MBS) which contain metal immobilizing agents on coarse-textured soils could improve the metal sorption capacity of the low-CEC soils. The purpose of this experiment was to evaluate the sorption of Zn in surface samples (0-15 cm) of six Quebec (Canada) soils amended with MBS (pH 6.9) from Val d’Or (Quebec, Canada). Soil samples amended with increasing amounts (0 to 20%) of MBS were equilibrated with various amounts of Zn as ZnCl2 in 0.01 M CaCl2 for 48 hours at room temperature. Sorbed Zn was calculated from the difference between the initial and final Zn concentration in solution. Zn sorption data conformed to the linear form of Freundlich equation. The amount of sorbed Zn increased considerably with increasing MBS rate. Analysis of variance revealed a highly significant effect (p ≤ 0.001) of soil texture and MBS rate on the amount of sorbed Zn. The average values of the Zn-sorption capacity of MBS-amended coarse-textured soils were lower than those of MBS-amended fine textured soils. The two sandy soils (86-99% sand) amended with MBS retained 2- to 5-fold Zn than those without MBS (control). Significant Pearson correlation coefficients between the Zn sorption isotherm parameter, i.e. the Freundlich sorption isotherm (KF), and commonly measured physical and chemical entities were obtained. Among all the soil properties measured, soil pH gave the best significant correlation coefficients (p ≤ 0.001) for soils receiving 0, 5 and 10% MBS. Furthermore, KF values were positively correlated with soil clay content, exchangeable basic cations (Ca, Mg or K), CEC and clay content to CEC ratio. From these results, it can be concluded that (i) municipal biosolids provide sorption sites that have a strong affinity for Zn, (ii) both soil texture, especially clay content, and soil pH are the main factors controlling anthropogenic Zn sorption in the municipal biosolids-amended soils, and (iii) the effect of municipal biosolids on Zn sorption will be more pronounced for a sandy soil than for a clay soil.
Abstract: The safflower seed contains about 25-40% solvent extract and 20-33% fiber. It is well known that dietary phospholipids lower serum cholesterol levels effectively. The nutrient composition of safflower seed changes depending on region, soil and genotypes. This research was made by using of six natural selected (A22, A29, A30, C12, E1, F4, G8, G12, J27) and three commercial (Remzibey, Dincer, Black Sun1) varieties of safflower genotypes. The research was conducted on field conditions for two years (2009 and 2010) in randomized complete block design with three replications in Konya-Turkey ecological conditions. Oil contents, mineral contents and their correlations were determined in the research. According to the results, oil content was ranged from 22.38% to 34.26%, while the minerals were in between the following values: 1469, 04-2068.07 mg kg-1 for Ca, 7.24-11.71 mg kg-1 for B, 13.29-17.41 mg kg-1 for Cu, 51.00-79.35 mg kg-1 for Fe, 3988-6638.34 mg kg-1 for K, 1418.61-2306.06 mg kg-1 for Mg, 11.37-17.76 mg kg-1 for Mn, 4172.33-7059.58 mg kg-1 for P and 32.60-59.00 mg kg-1 for Zn. Correlation analysis that was made separately for the commercial varieties and wild lines showed that high level of oil content was negatively affected by all the investigated minerals except for K and Zn in the commercial varieties.
Abstract: Effect of Zn addition on the microstructure and
mechanical properties of Mg-Zn alloys with Zn contents from 6 to 10
weight percent was investigated in this study. Through calculation of
phase equilibria of Mg-Zn alloys, carried out by using FactSage® and
FTLite database, solution treatment temperature was decided as
temperatures from 300 to 400oC, where supersaturated solid solution
can be obtained. Solid solution treatment of Mg-Zn alloys was
successfully conducted at 380oC and supersaturated microstructure
with all beta phase resolved into matrix was obtained. After solution
treatment, hot rolling was successfully conducted by reduction of
60%. Compression and tension tests were carried out at room
temperature on the samples as-cast, solution treated, hot-rolled and
recrystallized after rolling. After solid solution treatment, each alloy
was annealed at temperatures of 180 and 200oC for time intervals from
1 min to 48 hrs and hardness of each condition was measured by
micro-Vickers method. Peak aging conditions were deduced as at the
temperature of 200oC for 10 hrs. By addition of Zn by 10 weight
percent, hardness and strength were enhanced.
Abstract: Zinc borates are used as a multi-functional flame
retardant additive for its high dehydration temperature. In this study,
the method of ultrasonic mixing was used in the synthesis of zinc
borates. The reactants of zinc oxide (ZnO) and boric acid (H3BO3)
were used at the constant reaction parameters of 90°C reaction
temperature and 55 min of reaction time. Several molar ratios of
ZnO:H3BO3 (1:1, 1:2, 1:3, 1:4 and 1:5) were conducted for the
determination of the optimum reaction ratio. Prior to synthesis the
characterization of the synthesized zinc borates were made by X-Ray
Diffraction (XRD) and Fourier Transform Infrared Spectroscopy
(FT-IR). From the results Zinc Oxide Borate Hydrate
[Zn3B6O12.3.5H2O], were synthesized optimum at the molar ratio of
1:3, with a reaction efficiency of 95.2%.
Abstract: In this paper, the unstable angle of attack of a
FOXTROT aircraft is controlled by using Genetic Algorithm based
flight controller and the result is compared with the conventional
techniques like Tyreus-Luyben (TL), Ziegler-Nichols (ZN) and
Interpolation Rule (IR) for tuning the PID controller. In addition, the
performance indices like Mean Square Error (MSE), Integral Square
Error (ISE), and Integral Absolute Time Error (IATE) etc. are
improved by using Genetic Algorithm. It was established that the
error by using GA is very less as compared to the conventional
techniques thereby improving the performance indices of the
dynamic system.
Abstract: NiFe2O4 (nickel ferrite), ZnFe2O4 (zinc ferrite) and
Ni0.5Zn0.5Fe2O4 (nickel-zinc ferrite) were prepared by
mechanochemical route in a planetary ball mill starting from mixture
of the appropriate quantities of the Ni(OH)2/Fe(OH)3,
Zn(OH)2/Fe(OH)3 and Ni(OH)2/Zn(OH)2/Fe(OH)3 hydroxide
powders. In order to monitor the progress of chemical reaction and
confirm phase formation, powder samples obtained after 25 h, 18 h
and 10 h of milling were characterized by X-ray diffraction (XRD),
transmission electron microscopy (TEM), IR, Raman and Mössbauer
spectroscopy. It is shown that the soft mechanochemical method, i.e.
mechanochemical activation of hydroxides, produces high quality
single phase ferrite samples in much more efficient way. From the IR
spectroscopy of single phase samples it is obvious that energy of
modes depends on the ratio of cations. It is obvious that all samples
have more than 5 Raman active modes predicted by group theory in
the normal spinel structure. Deconvolution of measured spectra
allows one to conclude that all complex bands in the spectra are made
of individual peaks with the intensities that vary from spectrum to
spectrum. The deconvolution of Raman spectra allows to separate
contributions of different cations to a particular type of vibration and
to estimate the degree of inversion.
Abstract: During machining process, chatter is an unavoidable
phenomenon. Boring bars possess the cantilever shape and due to
this, it is subjected to chatter. The adverse effect of chatter includes
the increase in temperature which will leads to excess tool wear. To
overcome these problems, in this investigation, Cartridge brass (Cu –
70% and Zn – 30%) is passively fixed on the boring bar and also
clearance is provided in order to reduce the displacement, tool wear
and cutting temperature. A conventional all geared lathe is attached
with vibrometer and pyrometer is used to measure the displacement
and temperature. The influence of input parameters such as cutting
speed, depth of cut and clearance on temperature, tool wear and
displacement are investigated for various cutting conditions. From
the result, the optimum conditions to obtain better damping in boring
process for chatter reduction is identified.
Abstract: The ferrites ZnFe2O4, CdFe2O4 and CuFe2O4 are
synthesized in laboratory conditions using ceramic technology. Their
homogeneity and structure are proven by X-Ray diffraction analysis
and Mössbauer spectroscopy. The synthesized ferrites are subjected
to strong acid and high temperature leaching with solutions of H2SO4,
HCl and HNO3. The results indicate that the highest degree of
leaching of Zn, Cd and Cu from the ferrites is achieved by use of
HCl. The charging of five zinc sulfide concentrates was optimized using
the criterion of minimal amount of zinc ferrite produced when
roasting the concentrates in a fluidized bed. The results obtained are
interpreted in terms of the hydrometallurgical zinc production and
maximum recovery of zinc, copper and cadmium from initial zinc
concentrates after their roasting.
Abstract: Zinc borate is an important inorganic hydrate borate
material, which can be used as a flame retardant agent and corrosion
resistance material. This compound can loss its structural water
content at higher than 290°C. Due to thermal stability; Zinc Borate
can be used as flame retardant at high temperature process of plastic
and gum. In this study, the ultrasonic reaction of zinc borates were
studied using hydrozincite (Zn5(CO3)2·(OH)6) and boric acid
(H3BO3) raw materials. Before the synthesis raw materials were
characterized by X-Ray Diffraction (XRD) and Fourier Transform
Infrared Spectroscopy (FT-IR). Ultrasonic method is a new
application on the zinc borate synthesis. The synthesis parameters
were set to 90°C reaction temperature and 55 minutes of reaction
time, with 1:1, 1:2, 1:3, 1:4 and 1:5 molar ratio of starting materials
(Zn5(CO3)2·(OH)6 : H3BO3). After the zinc borate synthesis, the
products were analyzed by XRD and FT-IR. As a result, optimum
molar ratio of 1:5 is determined for the synthesis of zinc borates with
ultrasonic method.
Abstract: This paper reports the viability of developing Zn-27Al
alloy matrix hybrid composites reinforced with alumina, graphite and
fly ash (solid waste bye product of coal in thermal power plants).
This research work was aimed at developing low cost-high
performance Zn-27Al matrix composite with low density. Alumina
particulates (Al2O3), graphite added with 0, 2, 3, 4 and 5 wt% fly ash
were utilized to prepare 10wt% reinforcing phase with Zn-27Al alloy
as matrix using two-step stir casting method. Density measurement,
estimated percentage porosity, tensile testing, micro hardness
measurement and optical microscopy were used to assess the
performance of the composites produced. The results show that the
hardness, ultimate tensile strength, and percent elongation of the
hybrid composites decrease with increase in fly ash content. The
maximum decrease in hardness and ultimate tensile strength of
13.72% and 15.25% respectively were observed for composite grade
containing 5wt% fly ash. The percentage elongation of composite
sample without fly ash is 8.9% which is comparable with that of the
sample containing 2wt% fly ash with percentage elongation of 8.8%.
The fracture toughness of the fly ash containing composites was
however superior to those of composites without fly ash with 5wt%
fly ash containing composite exhibiting the highest fracture
toughness. The results show that fly ash can be utilized as
complementary reinforcement in ZA-27 alloy matrix composite to
reduce cost.
Abstract: We investigated ecotoxicity and performed experiment
for removing ZnO nanoparticles in water. Short term exposure of
hatching test using fertilized eggs (O. latipes) showed deformity in
5ppm of ZnO nanoparticles solution. And in 10ppm ZnO nanoparticles
solution delayed hatching was observed. Hereine, chemical
precipitation method was suggested for removing ZnO nanoparticles
in water. The precipitated ZnO nanoparticles showed the form of ZnS
after addition of Na2S, and the form of Zn3(PO4)2 for Na2HPO4. The
removal efficiency of ZnO nanoparticles in water was closed to 100%
for two cases. In ecotoxicity evaluation of as-precipitated ZnS and
Zn3(PO4)2, they did not cause any acute toxicity for D. magna. It is
noted that this precipitation treatment of ZnO is effective to reduce the
potential cytotoxicity.
Abstract: Different designs of attenuator systems have been
studied in this research; new analysis have been done on existed
designs considering fibers effect on air flow; it was comprehended
that, at fibers presence, there is an air flow which agglomerates fibers
as a negative effect. So some new representations have been designed
and CFD analysis has been done on them. Afterwards, one of these
representations selected as the most optimum and effective design
which is brought in this paper.
Abstract: RF magnetron sputtering is used on the ceramic targets,
each of which contains zinc oxide (ZnO), zinc oxide doped with
aluminum (AZO) and zinc oxide doped with gallium (GZO). The XRD
analysis showed a preferred orientation along the (002) plane for ZnO,
AZO, and GZO films. The AZO film had the best electrical properties;
it had the lowest resistivity of 6.6 × 10-4 cm, the best sheet resistance of
2.2 × 10-1 Ω/square, and the highest carrier concentration of 4.3 × 1020
cm-3, as compared to the ZnO and GZO films.
Abstract: In present global scenario, aluminum alloys are
coining the attention of many innovators as competing structural
materials for automotive and space applications. Comparing to other
challenging alloys, especially, 7xxx series aluminum alloys have
been studied seriously because of benefits such as moderate strength;
better deforming characteristics and affordable cost. It is expected
that substitution of aluminum alloys for steels will result in great
improvements in energy economy, durability and recyclability.
However, it is necessary to improve the strength and the formability
levels at low temperatures in aluminum alloys for still better
applications. Aluminum–Zinc–Magnesium with or without other
wetting agent denoted as 7XXX series alloys are medium strength
heat treatable alloys. In addition to Zn, Mg as major alloying
additions, Cu, Mn and Si are the other solute elements which
contribute for the improvement in mechanical properties by suitable
heat treatment process. Subjecting to suitable treatments like age
hardening or cold deformation assisted heat treatments; known as low
temperature thermomechanical treatments (LTMT) the challenging
properties might be incorporated. T6 is the age hardening or
precipitation hardening process with artificial aging cycle whereas T8
comprises of LTMT treatment aged artificially with X% cold
deformation. When the cold deformation is provided after solution
treatment, there is increase in hardness related properties such as
wear resistance, yield and ultimate strength, toughness with the
expense of ductility. During precipitation hardening both hardness
and strength of the samples are increasing. The hardness value may
further improve when room temperature deformation is positively
supported with age hardening known as thermomechanical treatment.
It is intended to perform heat treatment and evaluate hardness, tensile
strength, wear resistance and distribution pattern of reinforcement in
the matrix. 2 to 2.5 and 3 to 3.5 times increase in hardness is reported
in age hardening and LTMT treatments respectively as compared to
as-cast composite. There was better distribution of reinforcements in
the matrix, nearly two fold increase in strength levels and up to 5
times increase in wear resistance are also observed in the present
study.
Abstract: The goal of this experiment is to evaluate the
effectiveness of different leachate pre-treatment options in terms of
COD and ammonia removal. This research focused on the evaluation
of physical-chemical methods for pre-treatment of leachate that
would be effective and rapid in order to satisfy the requirements of
the sewer discharge by-laws. The four pre-treatment options
evaluated were: air stripping, chemical coagulation, electrocoagulation
and advanced oxidation with sodium ferrate. Chemical
coagulation reported the best COD removal rate at 43%, compared to
18% for both air stripping and electro-coagulation, and 20% for
oxidation with sodium ferrate. On the other hand, air stripping was
far superior to the other treatment options in terms of ammonia
removal with 86%. Oxidation with sodium ferrate reached only 16%,
while chemical coagulation and electro-coagulation removed less
than 10%. When combined, air stripping and chemical coagulation
removed up to 50% COD and 85% ammonia.
Abstract: Zn alloy and composite coatings are widely used in
buildings and structures, automobile and fasteners industries to
protect steel component from corrosion. In this paper, Zn-Ni-Al2O3
nanocomposite coatings were electrodeposited on mild steel using a
novel sol enhanced electroplating method. In this method, transparent
Al2O3 sol was added into the acidic Zn-Ni bath to produced Zn-Ni-
Al2O3 nanocomposite coatings. The effect of alumina sol on the
electrodeposition process, and coating properties was investigated
using cyclic voltammetry, XRD, ESEM and Tafel test. Results from
XRD tests showed that the structure of all coatings was single γ-
Ni5Zn21 phase. Cyclic voltammetry results showed that the
electrodeposition overpotential was lower in the presence of alumina
sol in the bath, and caused the reduction potential of Zn-Ni to shift to
more positive values. Zn-Ni-Al2O3 nanocomposite coatings produced
more uniform and compact deposits, with fine grained microstructure
when compared to Zn-Ni coatings. The corrosion resistance of Zn-Ni
coatings was improved significantly by incorporation of alumina
nanoparticles into the coatings.
Abstract: The Chair of Thermal Engineering at Poznan
University of Technology has been conducted research works on the
possibilities of using carbon nanostructures in energy and mechanics
applications for a couple of years. Those studies have provided results in a form of co-operation with foreign research centres, numerous publications and patent
applications.
Authors of this paper have studied the influence of multi-walled
carbon nanostructures on changes in static friction arising when steel
surfaces were moved. Tests were made using the original test stand
consisting of automatically controlled inclined plane driven by
precise stepper motors. Computer program created in the LabView
environment was responsible for monitoring of the stand operation,
accuracy of measurements and archiving the obtained results. Such a
solution enabled to obtain high accuracy and repeatability of all
conducted experiments.
Tests and analysis of the obtained results allowed us to determine
how additional layers of carbon nanostructures influenced on changes
of static friction coefficients. At the same time, we analyzed the
potential possibilities of applying nanostructures under consideration
in mechanics.
Abstract: Obesity and osteoporosis are the two diseases whose
increasing prevalence and high impact on the global morbidity and
mortality, during the two recent decades, have gained a status of
major health threats worldwide. Obesity purports to affect the bone
metabolism through complex mechanisms. Debated data on the
connection between the bone mineral density and fracture prevalence
in the obese patients are widely presented in literature. There is
evidence that the correlation of weight and fracture risk is sitespecific.
This study is aimed at determining the connection between
the bone mineral density (BMD) and trabecular bone score (TBS)
parameters in Ukrainian women suffering from obesity. We
examined 1025 40-89-year-old women, divided them into the groups
according to their body mass index: Group A included 360 women
with obesity whose BMI was ≥30 kg/m2, and Group B – 665 women
with no obesity and BMI of
Abstract: The heavy metal pollution of the soils around the mining area near Shamlugh town and related risks to human health were assessed. The investigations showed that the soils were polluted with heavy metals that can be ranked by anthropogenic pollution degree as follows: Cu>Pb>As>Co>Ni>Zn. The main sources of the anthropogenic metal pollution of the soils were the copper mining area near Shamlugh town, the Chochkan tailings storage facility and the trucks transferring ore from the mining area. Copper pollution degree in some observation sites was unallowable for agricultural production. The total non-carcinogenic chronic hazard index (THI) values in some places, including observation sites in Shamlugh town, were above the safe level (THI
Abstract: Sol-enhanced Zn-Ni-Al2O3 nanocomposite coatings
were electroplated on mild steel by our newly developed solenhanced
electroplating method. In this method, transparent Al2O3 sol
was added into the acidic Zn-Ni bath to produced Zn-Ni-Al2O3nanocomposite
coatings. The chemical composition, microstructure and
mechanical properties of the composite and alloy coatings deposited
at two different agitation speed were investigated. The structure of all
coatings was single γ-Ni5Zn21 phase. The composite coatings possess
refined crystals with higher microhardness compared to Zn-Ni alloy
coatings. The wear resistance of Zn-Ni coatings was improved
significantly by incorporation of alumina nano particles into the
coatings. Higher agitation speed provided more uniform coatings
with smaller grain sized and slightly higher microhardness.
Considering composite coatings, high agitation speeds may facilitate
co-deposition of alumina in the coatings.