Abstract: In order to apply partially filled steel grid composite deck as the horizontal supporting structure of various kinds of infrastructures, the variation of its flexural strength according to design parameters such as cross and longitudinal bars constituting the steel grid and the type of shear connection is evaluated and compared experimentally. The result shows that the design sensitivity of the deck to the spacing of the cross bars is insignificant in the case of structure with low risk of punching failure or without load distribution problem. By means of shear connection composed by transverse rebar and longitudinal bar without additional shear stud bolts, the complete interaction between steel grid and concrete slab is able to be achieved and the composite deck can develop its bending resistance capacity.
Abstract: The composite materials were prepared by sawdust, cassava starch and natural rubber latex (NR). The mixtures of 15%w/v gelatinized cassava starch and 15%w/v PVOH were used as the binder of these composite materials. The concentrated rubber latex was added to the mixtures. They were mixed rigorously to the treated sawdust in the ratio of 70:30 until achive uniform dispersion. The batters were subjected to the hot compression moulding at the temperature of 160°C and 3,000 psi pressure for 5 min. The experimental results showed that the mechanical properties of composite materials, which contained the gelatinized cassava starch and PVOH in the ratio of 2:1, 20% NR latex by weight of the dry starch and treated sawdust with 5%NaOH or 1% BPO, were the best. It contributed the maximal compression strength (341.10 + 26.11 N), puncture resistance (8.79 + 0.98 N/mm2) and flexural strength (3.99 + 0.72N/mm2). It is also found that the physicochemical and mechanical properties of composites strongly depends on the interface quality of sawdust, cassava starch and NR latex.
Abstract: Concrete pavement has superior durability and longer
structural life than asphalt pavement. Concrete pavement requires
less maintenance compared to asphalt pavement which requires maintenance and major rehabilitation. Use of the concrete pavement
has been grown over the past decade in developing countries. Fibre reinforced concrete (FRC) has been successfully used in design of concrete pavement in past decade. In this research, the effect of fibre
volume fraction in modulus of rupture, load-deflection, equivalent flexural strength (fe,3) and the equivalent flexural strength ratio (Re,3)
has been used in different fibre volume fraction. Crimped-type flat
steel fibre of size 50 x 2.0 x 0.6 mm was used with 1.0%, 1.5% and 2.0% volume fraction. Beam specimens of size 500 x 100 x 100 mm were used for flexural as well as with JCI method for analysis flexural toughness, equivalent flexural strength. It was obtained as the 2% fibre volume fractions; reduce 45% of the concrete pavement
thickness.
Abstract: Eight steel reinforced concrete beams (SRC), were
fabricated and tested under earthquake type cyclic loading. The
effectiveness of intermediate stiffeners, such as mid-span stiffener and
plastic hinge zone stiffeners, in enhancing composite action and
ductility of SRC beams was investigated. The effectiveness of
strengthened beam-to-column (SBC) and weakened beam-to-column
(WBC) connections in enhancing beam ductility was also studied. It
was found that: (1) All the specimens possessed fairly high flexural
ductility and were found adequate for structures in high seismic zones.
(2) WBC connections induced stress concentration which caused extra
damage to concrete near the flange tapering zone. This extra damage
inhibited the flexural strength development and the ductility of the
specimens with WBC connections to some extent. (3) Specimens with
SBC connections demonstrated higher flexural strength and ductility
compared to specimens with WBC connections. (4) The intermediate
stiffeners, especially combination of plastic hinge zone stiffener and
mid span stiffeners, have an obvious effect in enhancing the ductility
of the beams with SBC connection.
Abstract: The primary objective of this research is to improve the flexural capacity of FRP strengthened RC Beam structures with Aluminum and Titanium laminates. FRP rupture of flexural strengthened RC beams using FRP plates generally occurs at the interface between FRP plate and the beam. Therefore, in order to prevent brittle rupture and improve the ductility of the system, this research was performed by using Aluminum and Titanium materials between the two different structural systems. The research also aims to provide various strengthening/retrofitting methods for RC beam structures and to conduct a preliminary analysis of the demands on the structural systems. This was achieved by estimation using the experimental data from this research to identify a flexural capacity for the systems. Ultimately, the preliminary analysis of current study showed that the flexural capacity and system demand ductility was significantly improved by the systems inserted with Aluminum and Titanium anchor plates. Further verification of the experimental research is currently on its way to develop a new or reliable design guideline to retrofit/strengthen the concrete-FRP structural system can be evaluated.
Abstract: Self-compacting concrete (SCC), a new kind of high
performance concrete (HPC) have been first developed in Japan in
1986. The development of SCC has made casting of dense
reinforcement and mass concrete convenient, has minimized noise.
Fresh self-compacting concrete (SCC) flows into formwork and
around obstructions under its own weight to fill it completely and
self-compact (without any need for vibration), without any
segregation and blocking. The elimination of the need for
compaction leads to better quality concrete and substantial
improvement of working conditions. SCC mixes generally have a
much higher content of fine fillers, including cement, and produce
excessively high compressive strength concrete, which restricts its
field of application to special concrete only. To use SCC mixes in
general concrete construction practice, requires low cost materials to
make inexpensive concrete.
Rice husk ash (RHA) has been used as a highly reactive
pozzolanic material to improve the microstructure of the interfacial
transition zone (ITZ) between the cement paste and the aggregate in
self compacting concrete. Mechanical experiments of RHA blended
Portland cement concretes revealed that in addition to the pozzolanic
reactivity of RHA (chemical aspect), the particle grading (physical
aspect) of cement and RHA mixtures also exerted significant
influences on the blending efficiency.
The scope of this research was to determine the usefulness of Rice
husk ash (RHA) in the development of economical self compacting
concrete (SCC). The cost of materials will be decreased by reducing
the cement content by using waste material like rice husk ash instead
of.
This paper presents a study on the development of Mechanical
properties up to 180 days of self compacting and ordinary concretes
with rice-husk ash (RHA), from a rice paddy milling industry in
Rasht (Iran). Two different replacement percentages of cement by
RHA, 10%, and 20%, and two different water/cementicious material
ratios (0.40 and 0.35), were used for both of self compacting and
normal concrete specimens. The results are compared with those of
the self compacting concrete without RHA, with compressive,
flexural strength and modulus of elasticity. It is concluded that RHA
provides a positive effect on the Mechanical properties at age after
60 days.
Base of the result self compacting concrete specimens have higher
value than normal concrete specimens in all test except modulus of
elasticity. Also specimens with 20% replacement of cement by RHA
have the best performance.
Abstract: In this paper, a parametric experimental study for producing paving blocks using fine and coarse waste glass is presented. Some of the physical and mechanical properties of paving blocks having various levels of fine glass (FG) and coarse glass (CG) replacements with fine aggregate (FA) are investigated. The test results show that the replacement of FG by FA at level of 20% by weight has a significant effect on the compressive strength, flexural strength, splitting tensile strength and abrasion resistance of the paving blocks as compared with the control sample because of puzzolanic nature of FG. The compressive strength, flexural strength, splitting tensile strength and abrasion resistance of the paving block samples in the FG replacement level of 20% are 69%, 90%, 47% and 15 % higher as compared with the control sample respectively. It is reported in the earlier works the replacement of FG by FA at level of 20% by weight suppress the alkali-silica reaction (ASR) in the concrete. The test results show that the FG at level of 20% has a potential to be used in the production of paving blocks. The beneficial effect on these properties of CG replacement with FA is little as compared with FG.
Abstract: The main aim of this research is to study the possible
use of recycled fine aggregate made from waste rubble wall to
substitute partially for the natural sand used in the production of
cement and sand bricks. The bricks specimens were prepared by
using 100% natural sand; they were then replaced by recycled fine
aggregate at 25, 50, 75, and 100% by weight of natural sand. A series
of tests was carried out to study the effect of using recycled aggregate
on the physical and mechanical properties of bricks, such as density,
drying shrinkage, water absorption characteristic, compressive and
flexural strength. Test results indicate that it is possible to
manufacture bricks containing recycled fine aggregate with good
characteristics that are similar in physical and mechanical properties
to those of bricks with natural aggregate, provided that the percentage
of recycled fine aggregates is limited up to 50-75%.
Abstract: The use of additions in cement in manufacturing,
mortar and concrete offers economic and ecological advantages. Cements with additions such as limestone, slag and natural
pouzzolana are produced in cement factories in Algeria. Several studies analyzed the effect of these additions on the physical and
mechanical properties as well as the durability of concrete. However,
few studies were conducted on the effect of local metakaolin on
mechanical properties and durability of concrete. The main purpose
of this paper is to analyze the performance of mortar and concrete with local metakaolin. The preparation of the metakaolin was carried
out by calcination of kaolin at a temperature of 850 °C for a period of 3 hours. The experimental results have shown that the rates of
substitutions of 10 and 15% metakaolin increases the compressive
strength and flexural strength at both early age and long term. The durability and the permeability were also improved by reducing the
coefficient of sorptivity.
Abstract: This paper presents the experiment results of investigating the effects of adding various types and proportions of fibre on mechanical strength and permeability characteristics of recycled aggregate concrete (RAC), which was produced with treated coarse recycled concrete aggregate (RCA). Two types of synthetic fibres (i.e., barchip and polypropylene fibre) with various volume fractions were added to the RAC, which was calculated by the weight of the cement. The hardened RAC properties such as compressive strength, flexural strength, ultrasonic pulse velocity, water absorption and total porosity at the curing ages of 7 and 28 days were evaluated and compared with the properties of the control specimens. Results indicate that the treated coarse RCA enhances the mechanical strength and permeability properties of RAC and adding barchip fibre further optimises the results. Adding 1.2% barchip fibre has the best effect on the mechanical strength performance of the RAC.
Abstract: In order to calculate the flexural strength of
normal-strength concrete (NSC) beams, the nonlinear actual concrete
stress distribution within the compression zone is normally replaced
by an equivalent rectangular stress block, with two coefficients of α
and β to regulate the intensity and depth of the equivalent stress
respectively. For NSC beams design, α and β are usually assumed
constant as 0.85 and 0.80 in reinforced concrete (RC) codes. From an
earlier investigation of the authors, α is not a constant but significantly
affected by flexural strain gradient, and increases with the increasing
of strain gradient till a maximum value. It indicates that larger
concrete stress can be developed in flexure than that stipulated by
design codes. As an extension and application of the authors- previous
study, the modified equivalent concrete stress block is used here to
produce a series of design charts showing the maximum design limits
of flexural strength and ductility of singly- and doubly- NSC beams,
through which both strength and ductility design limits are improved
by taking into account strain gradient effect.
Abstract: This paper in essence presents comparative
experimental data on the mechanical performance of steel and
synthetic fibre-reinforced concrete under compression, tensile split
and flexure. URW1050 steel fibre and HPP45 synthetic fibre, both
with the same concrete design mix, have been used to make cube
specimens for a compression test, cylinders for a tensile split test and
beam specimens for a flexural test. The experimental data
demonstrated steel fibre reinforced concrete to be stronger in flexure
at early stages, whilst both fibre reinforced concrete types displayed
comparatively the same performance in compression, tensile splitting
and 28-day flexural strength. In terms of post-crack controlHPP45
was preferable.
Abstract: High strength concrete has been used in situations
where it may be exposed to elevated temperatures. Numerous authors
have shown the significant contribution of polypropylene fiber to the
spalling resistance of high strength concrete.
When cement-based composite that reinforced by polypropylene
fibers heated up to 170 °C, polypropylene fibers readily melt and
volatilize, creating additional porosity and small channels in to the
matrix that cause the poor structure and low strength.
This investigation develops on the mechanical properties of mortar
incorporating polypropylene fibers exposed to high temperature.
Also effects of different pozzolans on strength behaviour of samples
at elevated temperature have been studied.
To reach this purpose, the specimens were produced by partial
replacement of cement with finely ground glass, silica fume and rice
husk ash as high reactive pozzolans. The amount of this replacement
was 10% by weight of cement to find the effects of pozzolans as a
partial replacement of cement on the mechanical properties of
mortars. In this way, lots of mixtures with 0%, 0.5%, 1% and 1.5% of
polypropylene fibers were cast and tested for compressive and
flexural strength, accordance to ASTM standard. After that
specimens being heated to temperatures of 300, 600 °C, respectively,
the mechanical properties of heated samples were tested.
Mechanical tests showed significant reduction in compressive
strength which could be due to polypropylene fiber melting. Also
pozzolans improve the mechanical properties of sampels.
Abstract: Use of fly ash as a supplementary cementing material
in large volumes can bring both technological and economic benefits
for concrete industry. In this investigation mix proportions for high
volume fly ash concrete were determined at cement replacement
levels of 50%, 55%, 60% and 65% with low calcium fly ash. Flexural
and compressive strengths of different mixes were measured at ages
of 7, 28 and 90 days. Flexural strength of composite section prepared
from pavement quality and lean high volume fly ash concrete was
determined at the age of 28 days. High volume fly ash concrete mixes
exhibited higher rate of strength gain and age factors than
corresponding reference concrete mixes. The optimum cement
replacement level for pavement quality concrete was found to be
60%. The consideration of bond between pavement quality and lean
of high volume fly ash concrete will be beneficial in design of rigid
pavements.
Abstract: There is a acute water problem especially in the dry
season in and around Perundurai (Erode district, Tamil Nadu, India)
where there are more number of tannery units. Hence an attempt was
made to use the waste water from tannery industry for construction
purpose. The mechanical properties such as compressive strength,
tensile strength, flexural strength etc were studied by casting various
concrete specimens in form of cube, cylinders and beams etc and
were found to be satisfactory. Hence some special properties such as
chloride attack, sulphate attack and chemical attack are considered
and comparatively studied with the conventional potable water. In
this experimental study the results of specimens prepared by using
treated and untreated tannery effluent were compared with the
concrete specimens prepared by using potable water. It was observed
that the concrete had some reduction in strength while subjected to
chloride attack, sulphate attack and chemical attack. So admixtures
were selected and optimized in suitable proportion to counter act the
adverse effects and the results were found to be satisfactory.
Abstract: The term hybrid composite refers to the composite
containing more than one type of fiber material as reinforcing fillers.
It has become attractive structural material due to the ability of
providing better combination of properties with respect to single fiber
containing composite. The eco-friendly nature as well as processing
advantage, light weight and low cost have enhanced the attraction
and interest of natural fiber reinforced composite. The objective of
present research is to study the mechanical properties of jute-coir
fiber reinforced hybrid polypropylene (PP) composite according to
filler loading variation. In the present work composites were
manufactured by using hot press machine at four levels of fiber
loading (5, 10, 15 and 20 wt %). Jute and coir fibers were utilized at a
ratio of (1:1) during composite manufacturing. Tensile, flexural,
impact and hardness tests were conducted for mechanical
characterization. Tensile test of composite showed a decreasing trend
of tensile strength and increasing trend of the Young-s modulus with
increasing fiber content. During flexural, impact and hardness tests,
the flexural strength, flexural modulus, impact strength and hardness
were found to be increased with increasing fiber loading. Based on
the fiber loading used in this study, 20% fiber reinforced composite
resulted the best set of mechanical properties.
Abstract: Over a million tonnes of cigarette butts (CBs) are produced worldwide annually. These CBs accumulate in the environment due to the poor biodegradability of the cellulose acetate filters and pose a serious environmental risk. This paper presents some of the results from a continuing study on recycling CBs into fired clay bricks. Properties including compressive strength, flexural strength, density, water absorption and thermal conductivity of fired clay bricks are reported and discussed. Furthermore, leaching of heavy metals from the manufactured clay bricks was tested. The results show that the density of fired bricks was reduced by about 8 – 30 %, depending on the percentage of CBs incorporated into the raw materials. The compressive strength of bricks tested was 12.57, 5.22 and 3.00 MPa for 2.5, 5.0 and 10 % CB content respectively. Water absorption and initial rate of absorption values increased as density, and hence porosity, of bricks decreased with increasing CB volume. The leaching test results revealed trace amounts of heavy metals.
Abstract: A research program is conducted to evaluate the
mechanical properties of Ultra High Performance Concrete, target
compressive strength at the age of 28 days being more than 150 MPa.
The methodology to develop such mix has been explained. The
material properties, mix design and curing regime are determined.
The material attributes are understood by studying the stress strain
behaviour of UHPC cylinders under uniaxial compressive loading.
The load –crack mouth opening displacement (cmod) of UHPC
beams, flexural strength and fracture energy was evaluated using
third point loading test. Compressive strength and Split tensile
strength results are determined to find out the compressive and tensile
behaviour. Residual strength parameters are presented vividly
explaining the flexural performance, toughness of concrete.Durability
studies were also done to compare the effect of fibre to that of a
control mix For all the studies the Mechanical properties were
evaluated by varying the percentage and aspect ratio of steel fibres
The results reflected that higher aspect ratio and fibre volume
produced drastic changes in the cube strength, cylinder strength, post
peak response, load-cmod, fracture energy flexural strength, split
tensile strength, residual strength and durability. In regards to null
application of UHPC in India, an initiative is undertaken to
comprehend the mechanical behaviour of UHPC, which will be vital
for longer run in commercialization for structural applications.