Abstract: Fibre-reinforced polymer (FRP) strengthened reinforced concrete (RC) structures are susceptible to intense deterioration when exposed to elevated temperatures, particularly in the incident of fire. FRP has the tendency to lose bond with the substrate due to the low glass transition temperature of epoxy; the key component of FRP matrix. In the past few decades, various types of high performance cementitious composites (HPCC) were explored for the protection of RC structural members against elevated temperature. However, there is an inadequate information on the influence of elevated temperature on the ultra high performance fibre-reinforced cementitious composites (UHPFRCC) containing ground granulated blast furnace slag (GGBS) as a replacement of high alumina cement (HAC) in conjunction with hybrid fibres (basalt and polypropylene fibres), which could be a prospective fire resisting material for the structural components. The influence of elevated temperatures on the compressive as well as flexural strength of UHPFRCC, made of HAC-GGBS and hybrid fibres, were examined in this study. Besides control sample (without fibres), three other samples, containing 0.5%, 1% and 1.5% of basalt fibres by total weight of mix and 1 kg/m3 of polypropylene fibres, were prepared and tested. Another mix was also prepared with only 1 kg/m3 of polypropylene fibres. Each of the samples were retained at ambient temperature as well as exposed to 400, 700 and 1000 °C followed by testing after 28 and 56 days of conventional curing. Investigation of results disclosed that the use of hybrid fibres significantly helped to improve the ambient temperature compressive and flexural strength of UHPFRCC, which was found to be 80 and 14.3 MPa respectively. However, the optimum residual compressive strength was marked by UHPFRCC-CP (with polypropylene fibres only), equally after both curing days (28 and 56 days), i.e. 41%. In addition, the utmost residual flexural strength, after 28 and 56 days of curing, was marked by UHPFRCC– CP and UHPFRCC– CB2 (1 kg/m3 of PP fibres + 1% of basalt fibres) i.e. 39% and 48.5% respectively.
Abstract: The main objective of the study is focused in
producing slag based geopolymer concrete obtained with the addition
of alkali activator. Test results indicated that the reaction of silicates
in slag is based on the reaction potential of sodium hydroxide and the
formation of alumino-silicates. The study also comprises on the
evaluation of the efficiency of polymer reaction in terms of the
strength gain properties for different geopolymer mixtures.
Geopolymer mixture proportions were designed for different binder
to total aggregate ratio (0.3 & 0.45) and fine to coarse aggregate ratio
(0.4 & 0.8). Geopolymer concrete specimens casted with normal
curing conditions reported a maximum 28 days compressive strength
of 54.75 MPa. The addition of glued steel fibres at 1.0% Vf in
geopolymer concrete showed reasonable improvements on the
compressive strength, split tensile strength and flexural properties of
different geopolymer mixtures. Further, comparative assessment was
made for different geopolymer mixtures and the reinforcing effects of
steel fibres were investigated in different concrete matrix.
Abstract: Reinforced concrete has good durability and excellent structural performance. But there are cases of early deterioration due to a number of factors, one prominent factor being corrosion of steel reinforcement. The process of corrosion sets in due to ingress of moisture, oxygen and other ingredients into the body of concrete, which is unsound, permeable and absorbent. Cracks due to structural and other causes such as creep, shrinkage, etc also allow ingress of moisture and other harmful ingredients and thus accelerate the rate of corrosion. There are several interactive factors both external and internal, which lead to corrosion of reinforcement and ultimately failure of structures. Suitable addition of mineral admixture like silica fume (SF) in concrete improves the strength and durability of concrete due to considerable improvement in the microstructure of concrete composites, especially at the transition zone. Secondary reinforcement in the form of fibre is added to concrete, which provides three dimensional random reinforcement in the entire mass of concrete. Reinforced concrete beams of size 0.1 m X 0.15 m and length 1m have been cast using M 35 grade of concrete. The beams after curing process were subjected to corrosion process by impressing an external Direct Current (Galvanostatic Method) for a period of 15 days under stressed and unstressed conditions. The corroded beams were tested by applying two point loads to determine the ultimate load carrying capacity and cracking pattern and the results of specimens were compared with that of the companion specimens. Gravimetric method is used to quantify corrosion that has occurred.
Abstract: The article presents findings from the study and
analysis of the results of an experimental programme focused on the
production of concrete and fibre reinforced concrete in which natural
aggregate has been substituted with brick or concrete recyclate. The
research results are analyzed to monitor the effect of mechanicalphysical
characteristics on the durability properties of tested
cementitious composites. The key parts of the fibre reinforced
concrete mix are the basic components: aggregates – recyclate,
cement, fly ash, water and fibres. Their specific ratios and the
properties of individual components principally affect the resulting
behaviour of fresh fibre reinforced concrete and the characteristics of
the final product. The article builds on the sources dealing with the
use of recycled aggregates from construction and demolition waste in
the production of fibre reinforced concrete. The implemented
procedure of testing the composite contributes to the building
sustainability in environmental engineering.
Abstract: This paper presents the experiment results of investigating the effects of adding various types and proportions of fibre on mechanical strength and permeability characteristics of recycled aggregate concrete (RAC), which was produced with treated coarse recycled concrete aggregate (RCA). Two types of synthetic fibres (i.e., barchip and polypropylene fibre) with various volume fractions were added to the RAC, which was calculated by the weight of the cement. The hardened RAC properties such as compressive strength, flexural strength, ultrasonic pulse velocity, water absorption and total porosity at the curing ages of 7 and 28 days were evaluated and compared with the properties of the control specimens. Results indicate that the treated coarse RCA enhances the mechanical strength and permeability properties of RAC and adding barchip fibre further optimises the results. Adding 1.2% barchip fibre has the best effect on the mechanical strength performance of the RAC.