Abstract: Nanocrystalline thin film of Na0.1V2O5.nH2O xerogel
obtained by sol gel synthesis was used as gas sensor. Gas sensing
properties of different gases such as hydrogen, petroleum and
humidity were investigated. Applying XRD and TEM the size of the
nanocrystals is found to be 7.5 nm. SEM shows a highly porous
structure with submicron meter-sized voids present throughout the
sample. FTIR measurement shows different chemical groups
identifying the obtained series of gels. The sample was n-type
semiconductor according to the thermoelectric power and electrical
conductivity. It can be seen that the sensor response curves from
130oC to 150oC show a rapid increase in sensitivity for all types of
gas injection, low response values for heating period and the rapid
high response values for cooling period. This result may suggest that
this material is able to act as gas sensor during the heating and
cooling process.
Abstract: A simple and dexterous in situ method was introduced to load CdS nanocrystals into organofunctionalized mesoporous, which used an ion-exchange method. The products were extensively characterized by combined spectroscopic methods. X- ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) demonstrated both the maintenance of pore symmetry (space group p6mm) of SBA-15 and the presence of CdS nanocrystals with uniform sizes of about 6 - 8 nm inside the functionalized SBA-15 channels. These mesoporous silica-supported CdS composites showed room temperature photoluminescence properties with a blue shift, indicating the quantum size effect of nanocrystalline CdS.
Abstract: Sol-gel method has been used to fabricate
nanocomposite films on glass substrates composed halloysite clay
mineral and nanocrystalline TiO2. The methodology for the synthesis
involves a simple chemistry method utilized nonionic surfactant
molecule as pore directing agent along with the acetic acid-based solgel
route with the absence of water molecules. The thermal treatment
of composite films at 450oC ensures elimination of organic material
and lead to the formation of TiO2 nanoparticles onto the surface of
the halloysite nanotubes. Microscopy techniques and porosimetry
methods used in order to delineate the structural characteristics of the
materials. The nanocomposite films produced have no cracks and
active anatase crystal phase with small crystallite size were deposited
on halloysite nanotubes. The photocatalytic properties for the new
materials were examined for the decomposition of the Basic Blue 41
azo dye in solution. These, nanotechnology based composite films
show high efficiency for dye’s discoloration in spite of different
halloysite quantities and small amount of halloysite/TiO2 catalyst
immobilized onto glass substrates. Moreover, we examined the
modification of the halloysite/TiO2 films with silver particles in order
to improve the photocatalytic properties of the films. Indeed, the
presence of silver nanoparticles enhances the discoloration rate of the
Basic Blue 41 compared to the efficiencies obtained for unmodified
films.