Synthesis, Characterization and PL Properties of Cds Nanoparticles Confined within a Functionalized SBA-15 Mesoprous

A simple and dexterous in situ method was introduced to load CdS nanocrystals into organofunctionalized mesoporous, which used an ion-exchange method. The products were extensively characterized by combined spectroscopic methods. X- ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM) demonstrated both the maintenance of pore symmetry (space group p6mm) of SBA-15 and the presence of CdS nanocrystals with uniform sizes of about 6 - 8 nm inside the functionalized SBA-15 channels. These mesoporous silica-supported CdS composites showed room temperature photoluminescence properties with a blue shift, indicating the quantum size effect of nanocrystalline CdS.





References:
[1] Beck J S, Vartuli J C, Roth W J, Leonowicz M E, Kresge C T, Schmitt
K D, J. Am. Chem. Soc. 1992; 114: 10834- 10843.
[2] Zhao D, Feng J, Huo Q, Melosh N, Fredrickson G H, Chmelka B F, et
al., Science 1998; 279: 548- 552.
[3] Vartuli J C, Kresge C T, Leonowicz M E, Chu A S, McCullen S B,
Johnson I D, et al., Chem. Mater. 1994; 6: 2070- -2077.
[4] Morishige K, Ito M, J. Chem. Phys. 2002; 117: 8036- 8041.
[5] Pickett N L, Brien P O-, Chem. Rec. 2001; 1 : 467- 479.
[6] Parala H, Winkler H, Kolbe M, Wohlfart A, Fischer R A, Schmechel R,
et al. , Adv. Mater. 2000; 12:1050-1055.
[7] Zhou H J, Cai W P, Zhang L D, Mater. Res. Bull. 1999; 34 :845-849..
[8] Chomski E, Dag O, Kuperman A, Coombs N, Ozin G A, Chem. Vap.
Deposition 1996; 2 :8- 13.
[9] Zhang W H, Shi J L, Chen H R, Hua Z L, Yan D S, Chem. Mater.
2001; 13 :648- 654.
[10] Wang S Z, Choi D, Yang S M, Adv. Mater. 2002;14: 1311- 1314.
[11] ShanY , Gao L, Mat. Chem. Phys. 2005; 89 :412-416.
[12] Marler B, Oberhagemann U, Vortmann S, Gies H, Microporous Mater.
1996; 6 :375-383.
[13] Chae W-S, Ko J-H, Hwang I-W, Kim Y-R, Chem. Phys.Lett. 2002;
365:49- 56.
[14] Pearson R G, Inorg.Chem. 1988; 27:734-740.