Abstract: Nanocrystalline thin film of Na0.1V2O5.nH2O xerogel
obtained by sol gel synthesis was used as gas sensor. Gas sensing
properties of different gases such as hydrogen, petroleum and
humidity were investigated. Applying XRD and TEM the size of the
nanocrystals is found to be 7.5 nm. SEM shows a highly porous
structure with submicron meter-sized voids present throughout the
sample. FTIR measurement shows different chemical groups
identifying the obtained series of gels. The sample was n-type
semiconductor according to the thermoelectric power and electrical
conductivity. It can be seen that the sensor response curves from
130oC to 150oC show a rapid increase in sensitivity for all types of
gas injection, low response values for heating period and the rapid
high response values for cooling period. This result may suggest that
this material is able to act as gas sensor during the heating and
cooling process.