Abstract: Selective oxidation of H2S to elemental sulfur in a
fixed bed reactor over newly synthesized alumina nanocatalysts was
physio-chemically investigated and results compared with a
commercial Claus catalyst. Amongst these new materials, Al2O3-
supported sodium oxide prepared with wet chemical technique and
Al2O3 nanocatalyst prepared with spray pyrolysis method were the
most active catalysts for selective oxidation of H2S to elemental
sulfur. Other prepared nanocatalysts were quickly deactivated,
mainly due to the interaction with H2S and conversion into sulfides.
Abstract: Hydrogen sulfide (H2S) is a very toxic gas that is produced in very large quantities in the oil and gas industry. It cannot be flared to the atmosphere and Claus process based gas plants are used to recover the sulfur and convert the hydrogen to water. In this paper, we present optical characterization of an atmospheric pressure microwave plasma torch for H2S dissociation into hydrogen and sulfur. The torch is operated at 2.45 GHz with power up to 2 kW. Three different gases can simultaneously be injected in the plasma torch. Visual imaging and optical emission spectroscopy are used to characterize the plasma for varying gas flow rates and microwave power. The plasma length, emission spectra and temperature are presented. The obtained experimental results validate our earlier published simulation results of plasma torch.
Abstract: IFP Group Technology “Sulfrex process" was used in
Iran-s South Pars Gas Complex Refineries for removing sulfur
compounds such as mercaptans, carbonyl sulfide and hydrogen
sulfide, which uses sulfonated cobalt phthalocyanine dispersed in
alkaline solution as catalyst. In this technology, catalyst and alkaline
solution were used circularly. However the stability of catalyst due to
effect of some parameters would reduce with the running of the unit
and therefore sweetening efficiency would be decreased. Hence, the
aim of this research is study the factors effecting on the stability of
catalyst.
Abstract: Copper sulfide nanoparticles (CuS) were successfully synthesized by the pulsed plasma in liquid method, using two copper rod electrodes submerged in molten sulfur. Low electrical energy and no high temperature were applied for synthesis. Obtained CuS nanoparticles were then analyzed by means of X-ray diffraction, Low and High Resolution Transmission Electron Microscopy, Electron Diffraction, X-ray Photoelectron, Raman Spectroscopies and Field Emission Scanning Electron Microscopy. XRD analysis revealed peaks for CuS with hexagonal phase composition. TEM and HRTEM studies showed that sizes of CuS nanoparticles ranged between 10-60 nm, with the average size of about 20 nm. Copper sulfide nanoparticles have short nanorod-like structure. Raman spectroscopy found peak for CuS at 474.2cm-1of Raman region.