Abstract: The process of modification of ed-20 epoxy resin synthesized by vinyl-containing compounds is considered. It is shown that the introduction of vinyl-containing compounds into the composition based on epoxy resin ED-20 allows adjusting the technological and operational characteristics of the binder. For improvement of the properties of epoxy resin, following modifiers were selected: polyvinylformalethyl, polyvinyl butyral and composition of linear and aromatic amines (Аramine) as a hardener. Now the big range of hardeners of epoxy resins exists that allows varying technological properties of compositions, and also thermophysical and strength indicators. The nature of the aramin type hardener has a significant impact on the spatial parameters of the mesh, glass transition temperature, and strength characteristics. Epoxy composite materials based on ED-20 modified with polyvinyl butyral were obtained and investigated. It is shown that the composition of resins based on derivatives of polyvinyl butyral and ED-20 allows obtaining composite materials with a higher complex of deformation-strength, adhesion and thermal properties, better water resistance, frost resistance, chemical resistance, and impact strength. The magnitude of the effect depends on the chemical structure, temperature and curing time. In the area of concentrations, where the effect of composite synergy is appearing, the values of strength and stiffness significantly exceed the similar parameters of the individual components of the mixture. The polymer-polymer compositions form their class of materials with diverse specific properties that ensure their competitive application. Coatings with high performance under cyclic loading have been obtained based on epoxy oligomers modified with vinyl-containing compounds.
Abstract: After the recent devastating flood in Kashmir in 2014, dredging of the local water bodies, especially Jhelum River has become a priority for the government. Local government under the project name of 'Comprehensive Flood Management Programme' plans to undertake an increase in discharge of existing flood channels by removal of encroachments and acquisition of additional land, dredging and other works of the water bodies. The total quantity of soil to be dredged will be 16.15 lac cumecs. Dredged soil is a major component that would result from the project which requires disposal/utilization. This study analyses the effect of cement and sand on the engineering properties of soil. The tests were conducted with variable additions of sand (10%, 20% and 30%), whereas cement was added at 12%. Samples with following compositions: soil-cement (12%) and soil-sand (30%) were tested as well. Laboratory experiments were conducted to determine the engineering characteristics of soil, i.e., compaction, strength, and CBR characteristics. The strength characteristics of the soil were determined by unconfined compressive strength test and direct shear test. Unconfined compressive strength of the soil was tested immediately and for a curing period of seven days. CBR test was performed for unsoaked, soaked (worst condition- 4 days) and cured (4 days) samples.
Abstract: Today, with developments in science and technology, there is an excessive potential for the use of nanomaterials in various fields of geotechnical project such as soil stabilization. This study investigates the effect of Nano-SiO2 solution on the unconfined compression strength and Young's elastic modulus of Kaolinite. For this purpose, nano-SiO2 was mixed with kaolinite in five different contents: 1, 2, 3, 4 and 5% by weight of the dry soil and a series of the unconfined compression test with curing time of one-day was selected as laboratory test. Analyses of the tests results show that stabilization of kaolinite with Nano-SiO2 solution can improve effectively the unconfined compression strength of modified soil up to 1.43 times compared to the pure soil.
Abstract: Road performance and traffic safety are highly influenced by improper water drainage system performance, particularly within intersection areas. So, the aim of the presented paper is the evaluation of pervious concrete made with two types and two aggregate fractions for potential utilization in intersection drainage areas. Although the studied pervious concrete mixtures achieved proper drainage but lower strength characteristics, this pervious concrete has a good potential for enhancing pavement drainage systems if it is embedded on limited intersection areas.
Abstract: Among other traditional and non-traditional
additives, polymers have shown an efficient performance in the field
and improved sustainability. Polyacrylamide (PAM) is one such
additive that has demonstrated many advantages including a
reduction in permeability, an increase in durability and the provision
of strength characteristics. However, information about its effect on
the improved geotechnical characteristics is very limited to the field
performance monitoring. Therefore, a laboratory investigation was
carried out to examine the basic and engineering behaviors of three
types of soils treated with a PAM additive. The results showed an
increase in dry density and unconfined compressive strength for all
the soils. The results further demonstrated an increase in unsoaked
CBR and a reduction in permeability for all stabilized samples.
Abstract: Thin-walled elements with a matrix set on a base of
high-valuable Portland cement with dispersed reinforcement from
alkali-resistant glass fibres are used in a range of applications as
claddings of buildings and infrastructure constructions as well as
various architectural elements of residential buildings.
Even though their elementary thickness and therefore total weight
is quite low, architects and building companies demand on even
further decreasing of the bulk density of these fibre-cement elements
for the reason of loading elimination of connected superstructures
and easier assembling in demand conditions.
By the means of various kinds of light-weight aggregates it is
possible to achieve light-weighing of these composite elements.
From the range of possible fillers with different material properties
granulated expanded glass worked the best.
By the means of laboratory testing an effect of two fillers based on
expanded glass on the fibre reinforced cement composite was
verified.
Practical applicability was tested in the production of commonly
manufactured glass fibre reinforced concrete elements, such as
channels for electrical cable deposition, products for urban equipment
and especially various cladding elements.
Even though these are not structural elements, it is necessary to
evaluate also strength characteristics and resistance to environment
for their durability in certain applications.
Abstract: In this article our research focused on study of basic physical and mechanical parameters of polymer-cement repair materials is presented. Namely the influence of applied aggregates in combination with active admixture is specially considered. New formulas which were exposed in ambient with temperature even to 1000°C were suggested. Subsequently densities and strength characteristics including their changes were evaluated. Selected samples were analyzed using electron microscope. The positive influence of porous aggregates based on sintered ash was definitely demonstrated. Further it was found than in terms of thermal resistance the effective micro silica amount represents 5% to 7.5% of cement weight.
Abstract: The outstanding mechanical properties of Carbon
nanotubes (CNTs) have generated great interest for their potential as
reinforcements in high performance cementitious composites. The
main challenge in research is the proper dispersion of carbon
nanotubes in the cement matrix. The present work discusses the role
of dispersion of multiwalled carbon nanotubes (MWCNTs) on the
compressive strength characteristics of hydrated Portland IS 1489
cement paste. Cement-MWCNT composites with different mixing
techniques were prepared by adding 0.2% (by weight) of MWCNTs
to Portland IS 1489 cement. Rectangle specimens of size
approximately 40mm × 40mm ×160mm were prepared and curing of
samples was done for 7, 14, 28 and 35days. An appreciable increase
in compressive strength with both techniques; mixture of MWCNTs
with cement in powder form and mixture of MWCNTs with cement
in hydrated form 7 to 28 days of curing time for all the samples was
observed.
Abstract: The results reported in this paper are the part of an extensive laboratory investigation undertaken to study the effects of fibre parameters on the permeability and strength characteristics of steel fibre reinforced concrete (SFRC). The effect of varying fibre content and curing age on the water permeability, compressive and split tensile strengths of SFRC was investigated using straight steel fibres having an aspect ratio of 65. Samples containing three different weight fractions of 1.0%, 2.0% and 4.0% were cast and tested for permeability and strength after 7, 14, 28 and 60 days of curing. Plain concrete samples were also cast and tested for reference purposes.
Permeability was observed to decrease significantly with the addition of steel fibres and continued to decrease with increasing fibre content and increasing curing age. An exponential relationship was observed between permeability and compressive and split tensile strengths for SFRC as well as PCC. To evaluate the effect of fibre content on the permeability and strength characteristics, the Analysis of Variance (ANOVA) statistical method was used. An a level (probability of error) of 0.05 was used for ANOVA test. Regression analysis was carried out to develop relationship between permeability, compressive strength and curing age.
Abstract: Alkali Activated Slag Concrete (AASC) mixes are manufactured by activating ground granulated blast furnace slag (GGBFS) using sodium hydroxide and sodium silicate solutions. The aim of the present experimental research was to investigate the effect of increasing the dosages of sodium oxide (Na2O, in the range of 4 to 8%) and the activator modulus (Ms) (i.e. the SiO2/Na2O ratio, in the range of 0.5 to 1.5) of the alkaline solutions, on the workability and strength characteristics of self-cured (air-cured) alkali activated Indian slag concrete mixes. Further the split tensile and flexure strengths for optimal mixes were studied for each dosage of Na2O.It is observed that increase in Na2O concentration increases the compressive, split-tensile and flexural strengths, both at the early and later-ages, while increase in Ms, decreases the workability of the mixes. An optimal Ms of 1.25 is found at various Na2O dosages. No significant differences in the strength performances were observed between AASCs manufactured with alkali solutions prepared using either of potable and de-ionized water.
Abstract: In view of geological origin, formation of the shallow
gas reservoir of the Hangzhou Bay, northern Zhejiang Province,
eastern China, and original occurrence characteristics of the gassy
sand are analyzed. Generally, gassy sand in scale gas reservoirs is in
the state of residual moisture content and the approximate scope of
initial matric suction of sand ranges about from 0kPa to100kPa.
Results based on GDS triaxial tests show that the classical shear
strength formulas of unsaturated soil can not effectively describe basic
strength characteristics of gassy sand; the relationship between
apparent cohesion and matric suction of gassy sand agrees well with
the power function, which can reasonably be used to describe the
strength of gassy sand. In the stress path of gas release, shear strength
of gassy sand will increase and experimental results show the formula
proposed in this paper can effectively predict the strength increment.
When saturated strength indexes of the sand are used in engineering
design, moderate reduction should be considered.