Abstract: The four-stroke single cylinder diesel engine has been used in this study, the pistons and valves of the engine have been stabilized, the aluminum oxide (Al2O3) in different ratios has been added in the power of zirconium (ZrO2) magnesium oxide (MgO), and has been coated with the plasma spray method. The pistons and valves of the combustion chamber of the engine are coated with 5 different (ZrO2 + MgO), (ZrO2 + MgO + 25% Al2O3), (ZrO2 + MgO + 50% Al2O3), (ZrO2 + MgO + 75% Al2O3), (Al2O3) sample. The material tests have been made for each of the coated engine parts with the scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD) using Cu Kα radiation surface analysis methods. The engine tests have been repeated for each sample in any electric dynamometer in full power 1600 rpm, 2000 rpm, 2400 rpm and 2800 rpm engine speeds. The material analysis and engine tests have shown that the best performance has been performed with (ZrO2 + MgO + 50% Al2O3). Thus, there is no significant change in HC and Smoke emissions, but NOx emission is increased, as the engine improves power, torque, specific fuel consumption and CO emissions in the tests made with sample A3.
Abstract: The effect of additional magnesium oxide (MgO) was
investigated by using the tungsten oxide supported on silica catalyst
(WOx/SiO2) physically mixed with MgO in a weight ratio 1:1. The
both fresh and spent catalysts were characterized by FT-Raman
spectrometer, UV-Vis spectrometer, X-Ray diffraction (XRD) and
temperature programmed oxidation (TPO). The results indicated that
the additional MgO could enhance the conversion of trans-2-butene
due to isomerization reaction. However, adding MgO would increase
the amount of coke deposit on the WOx/SiO2 catalyst. The TPO
profile presented two peaks when the WOx/SiO2 catalyst was
physically mixed with MgO. The further peak was suggested that
came from coke precursor could be produced by isomerization
reaction of undesired product. Then, the occurred coke precursor
could deposit and form coke on the acid catalyst.
Abstract: Due to their strong mechanical and thermal properties magnesium borates have a wide usage area such as ceramic industry, detergent production, friction reducing additive and grease production. In this study, microwave synthesis of magnesium borates from MgCl2.6H2O (Magnesium chloride hexahydrate), MgO (Magnesium oxide) and H3BO3 (Boric acid) for different reaction times is researched. X-ray Diffraction (XRD) and Fourier Transform Infrared (FT-IR) Spectroscopy are used to find out how the reaction time sways on the products. The superficial properties are investigated with Scanning Electron Microscopy (SEM). According to XRD analysis, the synthesized compounds are 00-041-1407 pdf coded Shabinite (Mg5(BO3)4Cl2(OH)5.4(H2O)) and 01-073-2158 pdf coded Karlite (Mg7(BO3)3(OH,Cl)5).
Abstract: Carbon nanotubes (CNTs) with their high mechanical,
electrical, thermal and chemical properties are regarded as promising
materials for many different potential applications. Having unique
properties they can be used in a wide range of fields such as
electronic devices, electrodes, drug delivery systems, hydrogen
storage, textile etc. Catalytic chemical vapor deposition (CCVD) is a
common method for CNT production especially for mass production.
Catalysts impregnated on a suitable substrate are important for
production with chemical vapor deposition (CVD) method. Iron
catalyst and MgO substrate is one of most common catalyst-substrate
combination used for CNT. In this study, CNTs were produced by
CCVD of acetylene (C2H2) on magnesium oxide (MgO) powder
substrate impregnated by iron nitrate (Fe(NO3)3•9H2O) solution. The
CNT synthesis conditions were as follows: at synthesis temperatures
of 500 and 800°C multiwall and single wall CNTs were produced
respectively. Iron (Fe) catalysts were prepared by with Fe:MgO ratio
of 1:100, 5:100 and 10:100. The duration of syntheses were 30 and
60 minutes for all temperatures and catalyst percentages. The
synthesized materials were characterized by thermal gravimetric
analysis (TGA), transmission electron microscopy (TEM) and Raman
spectroscopy.
Abstract: Carbon nanotubes (CNTs) possess unique structural,
mechanical, thermal and electronic properties, and have been
proposed to be used for applications in many fields. However, to
reach the full potential of the CNTs, many problems still need to be
solved, including the development of an easy and effective
purification procedure, since synthesized CNTs contain impurities,
such as amorphous carbon, carbon nanoparticles and metal particles.
Different purification methods yield different CNT characteristics
and may be suitable for the production of different types of CNTs. In
this study, the effect of different purification chemicals on carbon
nanotube quality was investigated. CNTs were firstly synthesized by
chemical vapor deposition (CVD) of acetylene (C2H2) on a
magnesium oxide (MgO) powder impregnated with an iron nitrate
(Fe(NO3)3·9H2O) solution. The synthesis parameters were selected
as: the synthesis temperature of 800°C, the iron content in the
precursor of 5% and the synthesis time of 30 min. The liquid phase
oxidation method was applied for the purification of the synthesized
CNT materials. Three different acid chemicals (HNO3, H2SO4, and
HCl) were used in the removal of the metal catalysts from the
synthesized CNT material to investigate the possible effects of each
acid solution to the purification step. Purification experiments were
carried out at two different temperatures (75 and 120 °C), two
different acid concentrations (3 and 6 M) and for three different time
intervals (6, 8 and 15 h). A 30% H2O2 : 3M HCl (1:1 v%) solution
was also used in the purification step to remove both the metal
catalysts and the amorphous carbon. The purifications using this
solution were performed at the temperature of 75°C for 8 hours.
Purification efficiencies at different conditions were evaluated by
thermogravimetric analysis. Thermal and electrical properties of
CNTs were also determined. It was found that the obtained electrical
conductivity values for the carbon nanotubes were typical for organic
semiconductor materials and thermal stabilities were changed
depending on the purification chemicals.
Abstract: TiO2/MgO composite films were prepared by coating
the magnesium acetate solution in the pores of mesoporous TiO2
films using a dip coating method. Concentrations of magnesium
acetate solution were varied in a range of 1x10-4 – 1x10-1 M. The
TiO2/MgO composite films were characterized by scanning electron
microscopy (SEM), transmission electron microscropy (TEM),
electrochemical impedance spectroscopy(EIS) , transient voltage
decay and I-V test. The TiO2 films and TiO2/MgO composite films
were immersed in a 0.3 mM N719 dye solution. The Dye-sensitized
solar cells with the TiO2/MgO/N719 structure showed an optimal
concentration of magnesium acetate solution of 1x10-3 M resulting in
the MgO film estimated thickness of 0.0963 nm and giving the
maximum efficiency of 4.85%. The improved efficiency of dyesensitized
solar cell was due to the magnesium oxide film as the wide
band gap coating decays the electron back transfer to the triiodide
electrolyte and reduce charge recombination.
Abstract: The aim of this study was to synthesize the single
walled carbon nanotubes (SWCNTs) and determine their hydrogen
storage capacities. SWCNTs were firstly synthesized by chemical
vapor deposition (CVD) of acetylene (C2H2) on a magnesium oxide
(MgO) powder impregnated with an iron nitrate (Fe(NO3)3·9H2O)
solution. The synthesis parameters were selected as: the synthesis
temperature of 800°C, the iron content in the precursor of 5% and the
synthesis time of 30 min. Purification process of SWCNTs was
fulfilled by microwave digestion at three different temperatures (120,
150 and 200 °C), three different acid concentrations (0.5, 1 and 1.5
M) and for three different time intervals (15, 30 and 60 min). Nitric
acid (HNO3) was used in the removal of the metal catalysts. The
hydrogen storage capacities of the purified materials were measured
using volumetric method at the liquid nitrogen temperature and gas
pressure up to 100 bar. The effects of the purification conditions such
as temperature, time and acid concentration on hydrogen adsorption
were investigated.