Abstract: TiO2/Ag composite films were prepared by
incorporating Ag in the pores of mesoporous TiO2 films using a
photoreduction method. The Ag nanoparticle sizes were in a range of
3.66-38.56 nm. The TiO2/Ag composite films were characterized by
X-ray diffraction (XRD), scanning electron microscopy (SEM) and
transmission electron microscropy (TEM). The TiO2 films and
TiO2/Ag composite films were immersed in a 0.3 mM N719 dye
solution and characterized by UV-Vis spectrophotometer. The
TiO2/Ag/N719 composite film showed that an optimal size of Ag
nanoparticles was 19.12 nm and, hence, gave the maximum optical
absorption spectra. The improved absorption was due to surface
plasmon resonance induced by the Ag nanoparticles to enhance the
absorption coefficient of the dye.
Abstract: TiO2/MgO composite films were prepared by coating
the magnesium acetate solution in the pores of mesoporous TiO2
films using a dip coating method. Concentrations of magnesium
acetate solution were varied in a range of 1x10-4 – 1x10-1 M. The
TiO2/MgO composite films were characterized by scanning electron
microscopy (SEM), transmission electron microscropy (TEM),
electrochemical impedance spectroscopy(EIS) , transient voltage
decay and I-V test. The TiO2 films and TiO2/MgO composite films
were immersed in a 0.3 mM N719 dye solution. The Dye-sensitized
solar cells with the TiO2/MgO/N719 structure showed an optimal
concentration of magnesium acetate solution of 1x10-3 M resulting in
the MgO film estimated thickness of 0.0963 nm and giving the
maximum efficiency of 4.85%. The improved efficiency of dyesensitized
solar cell was due to the magnesium oxide film as the wide
band gap coating decays the electron back transfer to the triiodide
electrolyte and reduce charge recombination.