Abstract: In this paper, the effects of fiber types and elevated
temperatures on compressive strength, modulus of rapture and the
bond characteristics of fiber reinforced concretes (FRC) are
presented. By using the three different types of fibers (steel fiber-SF,
polypropylene-PPF and polyvinyl alcohol-PVA), FRC specimens
were produced and exposed to elevated temperatures up to 800 ºC for
1.5 hours. In addition, a plain concrete (without fiber) was produced
and used as a control. Test results obtained showed that the steel fiber
reinforced concrete (SFRC) had the highest compressive strength,
modulus of rapture and bond stress values at room temperatures, the
residual bond, flexural and compressive strengths of both FRC and
plain concrete dropped sharply after exposure to high temperatures.
The results also indicated that the reduction of bond, flexural and
compressive strengths with increasing the exposed temperature was
relatively less for SFRC than for plain, and FRC with PPF and PVA.
Abstract: Gypsum (CaSO4.2H2O) is a mineral that is found in
large quantities in the Turkey and in the World. In this study, the
dissolution of this mineral in the diammonium hydrogen phosphate
solutions has been studied. The dissolution and dissolution kinetics of
gypsum in diammonium hydrogen phosphate solutions will be useful
for evaluating of solid wastes containing gypsum. Parameters such as
diammonium hydrogen phosphate concentration, temperature and
stirring speed affecting on the dissolution rate of the gypsum in
diammonium hydrogen phosphate solutions were investigated. In
experimental studies have researched effectiveness of the selected
parameters. The dissolution of gypsum were examined in two parts at
low and high temperatures. The experimental results were
successfully correlated by linear regression using Statistica program.
Dissolution curves were evaluated shrinking core models for solidfluid
systems. The activation energy was found to be 34.58 kJ/mol
and 44.45 kJ/mol for the low and the high temperatures. The
dissolution of gypsum was controlled by chemical reaction both low
temperatures and high temperatures.
Abstract: Oases are complex and fragile agro-ecosystems. They
have always existed in environments characterized by an arid climate,
scarcity of rainfall, high temperatures and high evaporation. These
palms have grown up despite the severity of the physical
characteristics thanks to the water's existence and irrigation practice.
The oases are generally spread along non-perennial rivers (wadis),
shallow water table or deep artesian groundwater. However, the
sustainability of oasis system is threatened by water scarcity and
declining of water table levels particularly in arid areas. Located in
the southern east area of Morocco, Tafilalet plain encompasses one of
the largest palm groves in the kingdom. In recent years, this area has
become increasingly threatened by water shortage and has seen a
sharp deterioration under the effect of several combined
anthropogenic and climatic factors. The Bayoud disease, successive
years of drought, Hassan Addakhil dam construction etc are all
factors that have affected both water and phoenicicole heritage of the
area. The objective of this study is to understand the interaction
between qualitative and quantitative degradation of groundwater
resources, and the palm grove dynamics, while reviewing the
assumption that groundwater resources contribute in a direct way to
the conservation of this oasis agroecosystem. A historical analysis
tracing both the oasis dynamics and the groundwater evolution has
been established. Data were collected from satellite images, surveys
with different actors (farmers, Regional Office for Agricultural
Development, Basin agency...). They were complemented by a
synthesis of numerous technical reports in the area. The results
showed that within 40 years, the thickness of the groundwater table
has dropped in 50 %. Along with this, there has been a downsizing of
date palm by 50 %. Areas with higher groundwater level were the
least affected by the downsizing. So we can say that the shallow
groundwater contribute significantly and directly to the water supply
of date palm through its root system, and largely ensures the oasis
ecosystem sustainability.
Abstract: This paper is concerning the issues of behaviour of
lightweight expanded clay aggregates concrete exposed to high
temperature. Lightweight aggregates from expanded clay are
produced by firing of row material up to temperature 1050°C.
Lightweight aggregates have suitable properties in terms of volume
stability, when exposed to temperatures up to 1050°C, which could
indicate their suitability for construction applications with higher risk
of fire. The test samples were exposed to heat by using the standard
temperature-time curve ISO 834. Negative changes in resulting
mechanical properties, such as compressive strength, tensile strength,
and flexural strength were evaluated. Also visual evaluation of the
specimen was performed. On specimen exposed to excessive heat, an
explosive spalling could be observed, due to evaporation of
considerable amount of unbounded water from the inner structure of
the concrete.
Abstract: As the human race will continue to explore the space
by creating new space transportation means and sending them to other
planets, the enhance of atmospheric reentry study is crucial. In this
context, an analysis of mass recession rate of ablative materials for
thermal shields of reentry spacecrafts is important to be carried out.
The paper describes a new estimation method for calculating the mass
recession of an ablator system made of carbon fiber reinforced plastic
materials. This method is based on Arrhenius equation for low
temperatures and, for high temperatures, on a theory applied for the
recession phenomenon of carbon fiber reinforced plastic materials,
theory which takes into account the presence of the resin inside the
materials. The space mission of USERS spacecraft is considered as a
case study.
Abstract: The use of permanent magnets (PM) is increasing in
permanent magnet synchronous machines (PMSM) to fulfill the
requirements of high efficiency machines in modern industry. PMSM
are widely used in industrial applications, wind power plants and the
automotive industry. Since PMSM are used in different
environmental conditions, the long-term effect of NdFeB-based
magnets at high temperatures and their corrosion behavior have to be
studied due to the irreversible loss of magnetic properties.
In this paper, the effect of magnetic properties due to corrosion
and increasing temperature in a climatic chamber has been presented.
The magnetic moment and magnetic field of the magnets were
studied experimentally.
Abstract: Al-Si-Mg-Ni(-Cu) alloys are widely used in the automotive industry. They have the advantage of low weight associated with low coefficient of thermal expansion and excellent mechanical properties – mainly at high temperatures. The corrosion resistance of these alloys in coastal area, particularly sea water, however is not yet known. In this investigation, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization have been used to evaluate the corrosion resistance of Al-6Si-0.5Mg-2Ni (-2Cu) alloys in simulated sea water environments. The potentiodynamic polarization curves reveal that 2 wt% Cu content alloy (Alloy-2) is more prone to corrosion than the Cu free alloy (Alloy-1). But the EIS test results showed that corrosion resistance or charge transfer resistance (Rct) increases with the addition of Cu. Due to addition of Cu and thermal treatment, the magnitude of open circuit potential (OCP), corrosion potential (Ecorr) and pitting corrosion potential (Epit) of Al-6Si-0.5Mg-2Ni alloy in NaCl solution were shifted to the more noble direction.
Abstract: In this article our research focused on study of basic physical and mechanical parameters of polymer-cement repair materials is presented. Namely the influence of applied aggregates in combination with active admixture is specially considered. New formulas which were exposed in ambient with temperature even to 1000°C were suggested. Subsequently densities and strength characteristics including their changes were evaluated. Selected samples were analyzed using electron microscope. The positive influence of porous aggregates based on sintered ash was definitely demonstrated. Further it was found than in terms of thermal resistance the effective micro silica amount represents 5% to 7.5% of cement weight.
Abstract: Thermal radiation plays a very important role in the heat transfer combination through the various components of the SOFC fuel cell operating at high temperatures. Lattice Boltzmann method is used for treating conduction-radiation heat transfer in the electrolyte. The thermal radiation heat transfer is coupled to the overall energy conservation equations through the divergence of the local radiative flux. The equation of energy in one dimension is numerically resolved by using the Lattice Boltzmann method. A computing program (FORTRAN) is developed locally for this purpose in order to obtain fields of temperature in every element of the cell. The parameters investigated are: functioning temperature, cell voltages and electrolyte thickness. The results show that the radiation effect increases with increasing the electrolyte thickness, also increases with increasing the functioning temperature and decreases with the increase of the voltage of the cell.
Abstract: Developments in turbine cooling technology play an important role in increasing the thermal efficiency and the power output of recent gas turbines, in particular the turbojets.
Advanced turbojets operate at high temperatures to improve thermal efficiency and power output. These temperatures are far above the permissible metal temperatures. Therefore, there is a critical need to cool the blades in order to give theirs a maximum life period for safe operation.
The focused objective of this work is to calculate the turbojet performances, as well as the calculation of turbine blades cooling.
The developed application able the calculation of turbojet performances to different altitudes in order to find a point of optimal use making possible to maintain the turbine blades at an acceptable maximum temperature and to limit the local variations in temperatures in order to guarantee their integrity during all the lifespan of the engine.
Abstract: The high temperatures during sensitive growth phases are changing rice morphology as well as influencing yield. In the glass house study, the treatments were growing conditions [normal growing (32oC+2) and heat stress (38oC+2) day time and 22oC+2 night time], growth stages (booting, flowering and ripening) and four cultivars (Hovaze, Hashemi, Fajr, as exotic and MR219 as indigenous). The heat chamber was prepared covered with plastic, and automatic heater was adjusted for two weeks in every growth stages. Rice morphological and yield under the influence of heat stress during various growth stages showed taller plants in Hashemi due to its tall character. The total tillers per hill were significantly higher in Fajr. In all growing conditions, Hashemi recorded higher panicle exertion. The flag leaf width in all situations was found higher in Hovaze. The total tillers per hill were more in Fajr, although heat stress was imposed during booting and flowering stages. The indigenous MR219 in all situations of growing conditions, growth stages recorded higher grain yield. However, its grain yield decreased when heat stress was imposed during booting and flowering. However, plants had no effect on heat stress during ripening stage.
Abstract: When concrete is exposed to high temperatures, some changes may occur in its physical and mechanical properties. Especially, high strength concrete (HSC), may exhibit damages such as cracks and spallings. To overcome this problem, incorporating polymer fibers such as polypropylene (PP) in concrete is a well-known method. In high temperatures, PP decomposes and releases harmful gases such as CO and CO2. This study researches the use of raw rice husk (RRH) as a sustainable material, instead of PP fibers considering its several favorable properties, and its usability in HSC. RRH and PP fibers were incorporated in concrete at 0.5-3% and 0.2-0.5% by weight of cement, respectively. Concrete specimens were exposed to 20 (control), 300, 600 and 900°C. Under these temperatures, residual compressive and splitting tensile strength was determined. During the high temperature effect, the amount of released harmful gases was measured by a gas detector.
Abstract: Recently, a growing interest has emerged on the development of new and efficient energy sources, due to the inevitable extinction of the nonrenewable energy reserves. One of these alternative sources which have a great potential and sustainability to meet up the energy demand is biomass energy. This significant energy source can be utilized with various energy conversion technologies, one of which is biomass gasification in supercritical water.
Water, being the most important solvent in nature, has very important characteristics as a reaction solvent under supercritical circumstances. At temperatures above its critical point (374.8oC and 22.1MPa), water becomes more acidic and its diffusivity increases. Working with water at high temperatures increases the thermal reaction rate, which in consequence leads to a better dissolving of the organic matters and a fast reaction with oxygen. Hence, supercritical water offers a control mechanism depending on solubility, excellent transport properties based on its high diffusion ability and new reaction possibilities for hydrolysis or oxidation.
In this study the gasification of a real biomass, namely olive mill wastewater (OMW), in supercritical water conditions is investigated with the use of Ru/Al2O3 catalyst. OMW is a by-product obtained during olive oil production, which has a complex nature characterized by a high content of organic compounds and polyphenols. These properties impose OMW a significant pollution potential, but at the same time, the high content of organics makes OMW a desirable biomass candidate for energy production.
The catalytic gasification experiments were made with five different reaction temperatures (400, 450, 500, 550 and 600°C) and five reaction times (30, 60, 90, 120 and 150s), under a constant pressure of 25MPa. Through these experiments, the effects of reaction temperature and time on the gasification yield, gaseous product composition and OMW treatment efficiency were investigated.
Abstract: In this work we study the thermodynamic behavior of some ventilated facades under summer operating conditions in Southern Spain. Under these climatic conditions, indoor comfort implies a high energetic demand due to high temperatures that usually are reached in this season in the considered geographical area.
The aim of this work is to determine if during summer operating conditions in Southern Spain, ventilated façades provide some energy saving compared to the non-ventilated façades and to deduce their behavior patterns in terms of energy efficiency.
The modelization of the air flow in the channel has been performed by using Navier-Stokes equations for thermodynamic flows. Numerical simulations have been carried out with a 2D Finite Element approach.
This way, we analyze the behavior of ventilated façades under different weather conditions as variable wind, variable temperature and different levels of solar irradiation.
CFD computations show the combined effect of the shading of the external wall and the ventilation by the natural convection into the air gap achieve a reduction of the heat load during the summer period. This reduction has been evaluated by comparing the thermodynamic performances of two ventilated and two unventilated façades with the same geometry and thermophysical characteristics.
Abstract: In this work, the influence of temperature on the
different parameters of solar cells based on organic semiconductors
are studied. The short circuit current Isc increases so monotonous
with temperature and then saturates to a maximum value before
decreasing at high temperatures. The open circuit voltage Vco
decreases linearly with temperature. The fill factor FF and efficiency,
which are directly related with Isc and Vco follow the variations of
the letters. The phenomena are explained by the behaviour of the
mobility which is a temperature activated process.
Abstract: Thermally insulating ceramic coatings also known as
thermal barrier coatings (TBCs) have been essential technologies to
improve the performance and efficiency of advanced gas turbines in
service at extremely high temperatures. The damage mechanisms of
air-plasma sprayed YSZ thermal barrier coatings (TBC) with various
microstructures were studied by microscopic techniques after thermal
cycling. The typical degradation of plasma TBCs that occurs during
cyclic furnace testing of an YSZ and alumina coating on a Titanium
alloy are analyzed. During the present investigation the effects of
topcoat thickness, bond coat oxidation, thermal cycle lengths and test
temperature are investigated using thermal cycling. These results
were correlated with stresses measured by a spectroscopic technique
in order to understand specific damage mechanism. The failure
mechanism of former bond coats was found to involve fracture
initiation at the thermally grown oxide (TGO) interface and at the
TGO bond coat interface. The failure mechanism of the YZ was
found to involve combination of fracture along the interface between
TGO and bond coat.
Abstract: Tubular process equipment is often damaged in
industrial processes. The damage occurs both on devices working at
high temperatures and also on less exposed devices. In case of sudden
damage of key equipment a shutdown of the whole production unit
and resulting significant economic losses are imminent. This paper
presents a solution of several types of tubular process equipment. The
causes of damage and suggestions of correction actions are discussed
in all cases. Very important part is the analysis of operational
conditions, determination of unfavourable working states decreasing
lifetime of devices and suggestions of correction actions. Lately very
popular numerical methods are used for analysis of the equipment.
Abstract: The tubes in an Ammonia primary reformer furnace
operate close to the limits of materials technology in terms of the
stress induced as a result of very high temperatures, combined with
large differential pressures across the tube wall. Operation at tube
wall temperatures significantly above design can result in a rapid
increase in the number of tube failures, since tube life is very
sensitive to the absolute operating temperature of the tube. Clearly it
is important to measure tube wall temperatures accurately in order to
prevent premature tube failure by overheating.. In the present study,
the catalyst tubes in an Ammonia primary reformer has been modeled
taking into consideration heat, mass and momentum transfer as well
as reformer characteristics.. The investigations concern the effects of
tube characteristics and superficial tube wall temperatures on of the
percentage of heat flux, unconverted methane and production of
Hydrogen for various values of steam to carbon ratios. The results
show the impact of catalyst tubes length and diameters on the
performance of operating parameters in ammonia primary reformers.
Abstract: Vinegar is a precious food additive and complement as well as effective preservative against food spoilage. Recently traditional vinegar production has been improved using various natural substrates and fruits such as grape, palm, cherry, coconut, date, sugarcane, rice and balsam. These neoclassical fermentations resulted in several vinegar types with different tastes, fragrances and nutritional values because of applying various acetic acid bacteria as starters. Acetic acid bacteria include genera Acetobacter, Gluconacetobacter and Gluconobacter according to latest edition of Bergy-s Manual of Systematic Bacteriology that classifies genera on the basis of their 16s RNA differences. Acetobacter spp as the main vinegar starters belong to family Acetobacteraceae that are gram negative obligate aerobes, chemoorganotrophic bacilli that are oxidase negative and oxidize ethanol to acetic acid. In this research we isolated and identified a native Acetobacter strain with high acetic acid productivity and tolerance against high ethanol concentrations from Iranian peach as a summer delicious fruit that is very susceptible to food spoilage and decay. We used selective and specific laboratorial culture media such as Standard GYC, Frateur and Carr medium. Also we used a new industrial culture medium and a miniature fermentor with a new aeration system innovated by Pars Yeema Biotechnologists Co., Isfahan Science and Technology Town (ISTT), Isfahan, Iran. The isolated strain was successfully cultivated in modified Carr media with 2.5% and 5% ethanol simultaneously in high temperatures, 34 - 40º C after 96 hours of incubation period. We showed that the increase of ethanol concentration resulted in rising of strain sensitivity to high temperature. In conclusion we isolated and characterized a new Acetobacter strain from Iranian peach that could be considered as a potential strain for production of a new vinegar type, peach vinegar, with a delicious taste and advantageous nutritional value in food biotechnology and industrial microbiology.
Abstract: Metal cutting is a severe plastic deformation process
involving large strains, high strain rates, and high temperatures.
Conventional analysis of the chip formation process is based on bulk
material deformation disregarding the inhomogeneous nature of the
material microstructure. A series of orthogonal cutting tests of AISI
1045 and 1144 steel were conducted which yielded similar process
characteristics and chip formations. With similar shear angles and cut
chip thicknesses, shear strains for both chips were found to range
from 2.0 up to 2.8. The manganese-sulfide (MnS) precipitate in the
1144 steel has a very distinct and uniform shape which allows for
comparison before and after chip formation. From close observations
of MnS precipitates in the cut chips it is shown that the conventional
approach underestimates plastic strains in metal cutting.
Experimental findings revealed local shear strains around a value of
6. These findings and their implications are presented and discussed.