Abstract: Thermally insulating ceramic coatings also known as
thermal barrier coatings (TBCs) have been essential technologies to
improve the performance and efficiency of advanced gas turbines in
service at extremely high temperatures. The damage mechanisms of
air-plasma sprayed YSZ thermal barrier coatings (TBC) with various
microstructures were studied by microscopic techniques after thermal
cycling. The typical degradation of plasma TBCs that occurs during
cyclic furnace testing of an YSZ and alumina coating on a Titanium
alloy are analyzed. During the present investigation the effects of
topcoat thickness, bond coat oxidation, thermal cycle lengths and test
temperature are investigated using thermal cycling. These results
were correlated with stresses measured by a spectroscopic technique
in order to understand specific damage mechanism. The failure
mechanism of former bond coats was found to involve fracture
initiation at the thermally grown oxide (TGO) interface and at the
TGO bond coat interface. The failure mechanism of the YZ was
found to involve combination of fracture along the interface between
TGO and bond coat.