Abstract: Thermally insulating ceramic coatings also known as
thermal barrier coatings (TBCs) have been essential technologies to
improve the performance and efficiency of advanced gas turbines in
service at extremely high temperatures. The damage mechanisms of
air-plasma sprayed YSZ thermal barrier coatings (TBC) with various
microstructures were studied by microscopic techniques after thermal
cycling. The typical degradation of plasma TBCs that occurs during
cyclic furnace testing of an YSZ and alumina coating on a Titanium
alloy are analyzed. During the present investigation the effects of
topcoat thickness, bond coat oxidation, thermal cycle lengths and test
temperature are investigated using thermal cycling. These results
were correlated with stresses measured by a spectroscopic technique
in order to understand specific damage mechanism. The failure
mechanism of former bond coats was found to involve fracture
initiation at the thermally grown oxide (TGO) interface and at the
TGO bond coat interface. The failure mechanism of the YZ was
found to involve combination of fracture along the interface between
TGO and bond coat.
Abstract: This presentation reviews recent advances in superalloys and thermal barrier coating (TBC) for application in hot sections of energy-efficient gas-turbine engines. It has been reviewed that in the modern combined-cycle gas turbines (CCGT) applying single-crystal energy materials (SC superalloys) and thermal barrier coatings (TBC), and – in one design – closed-loop steam cooling, thermal efficiency can reach more than 60%. These technological advancements contribute to profitable and clean power generation with reduced emission. Alternatively, the use of advanced superalloys (e.g. GTD-111 superalloy, Allvac 718Plus superalloy) and advanced thermal barrier coatings (TBC) in modern gas-turbines has been shown to yield higher energy-efficiency in power generation.
Abstract: A numerical study on the heat transfer in the thermal
barrier coatings and the substrates of a parallel-plate enclosure is
carried out. Some of the thermal barrier coatings, such as ceramics, are
semitransparent and are of interest for high-temperature applications
where radiation effects are significant. The radiative transfer equations
and the energy equations are solved by using the discrete ordinates
method and the finite difference method. Illustrative results are
presented for temperature distributions in the coatings and the opaque
walls under various heating conditions. The results show that the
temperature distribution is more uniform in the interior portion of each
coating away from its boundary for the case with a larger average of
varying refractive index and a positive gradient of refractive index
enhances radiative transfer to the substrates.