Abstract: The activation volume of 6082T6 aluminum is
investigated at different temperatures for grain size variants. The
deformation activation volume was computed on the basis of the
relationship between the Boltzmann’s constant k, the testing
temperatures, the material strain rate sensitivity and the material yield
stress grain size variants. The material strain rate sensitivity is
computed as a function of yield stress and strain rate grain size
variants. The effect of the material strain rate sensitivity and the
deformation activation volume of 6082T6 aluminum at different
temperatures of 3-D grain are discussed. It is shown that the strain rate sensitivities and activation volume
are negative for the grain size variants during the deformation of
nanostructured materials. It is also observed that the activation
volume vary in different ways with the equivalent radius, semi minor
axis radius, semi major axis radius and major axis radius. From the
obtained results it is shown that the variation of activation volume
increase and decrease with the testing temperature. It was revealed
that, increase in strain rate sensitivity led to decrease in activation
volume whereas increase in activation volume led to decrease in
strain rate sensitivity.
Abstract: Calcium Phosphate Cement (CPC) due to its high bioactivity and optimum bioresorbability shows excellent bone regeneration capability. Despite it has limited applications as bone implant due to its macro-porous microstructure causing its poor mechanical strength. The reinforcement of apatitic CPCs with biocompatible fibre glass phase is an attractive area of research to improve upon its mechanical strength. Here, we study the setting behaviour of Si-doped and un-doped α tri calcium phosphate (α - TCP) based CPC and its reinforcement with addition of E-glass fibre. Alpha Tri calcium phosphate powders were prepared by solid state sintering of CaCO3 , CaHPO4 and Tetra Ethyl Ortho Silicate (TEOS) was used as silicon source to synthesize Si doped α-TCP powders. Both initial and final setting time of the developed cement was delayed because of Si addition. Crystalline phases of HA (JCPDS 9- 432), α-TCP (JCPDS 29-359) and β-TCP (JCPDS 9-169) were detected in the X-ray diffraction (XRD) pattern after immersion of CPC in simulated body fluid (SBF) for 0 hours to 10 days. As Si incorporation in the crystal lattice stabilized the TCP phase, Si doped CPC showed little slower rate of conversion into HA phase as compared to un-doped CPC. The SEM image of the microstructure of hardened CPC showed lower grain size of HA in un-doped CPC because of premature setting and faster hydrolysis of un-doped CPC in SBF as compared that in Si-doped CPC. Premature setting caused generation of micro and macro porosity in un-doped CPC structure which resulted in its lower mechanical strength as compared to that in Si-doped CPC. It was found that addition of 10 wt% of E-glass fibre into Si-doped α-TCP increased the average DTS of CPC from 8 MPa to 15 MPa as the fibres could resists the propagation of crack by deflecting the crack tip. Our study shows that biocompatible E-glass fibre in optimum proportion in CPC matrix can enhance the mechanical strength of CPC without affecting its biocompatibility.
Abstract: Electrostatic interaction energy (ΔEEDL) is a part of the Extended Derjaguin-Landau-Verwey-Overbeek (XDLVO) theory, which, together with van der Waals (ΔEVDW) and acid base (ΔEAB) interaction energies, has been extensively used to investigate the initial adhesion of bacteria to surfaces. Electrostatic or electrical double layer interaction energy is considerably affected by surface potential; however it cannot be determined experimentally and is usually replaced by zeta (ζ) potential via electrophoretic mobility. This paper focusses on the effect of ionic concentration as a function of pH and the effect of mineral grain size on ζ potential. It was found that both ionic strength and mineral grain size play a major role in determining the value of ζ potential for the adhesion of P. putida to hematite and quartz surfaces. Higher ζ potential values lead to higher electrostatic interaction energies and eventually to higher total XDLVO interaction energy resulting in bacterial repulsion.
Abstract: The nickel-manganese (Ni-Mn) alloy coating prepared
from DC electrodeposition process in sulphamate bath was studied.
The effects of process parameters, such as current density and
electrolyte composition, on the cathodic current efficiency,
microstructure, internal stress and mechanical properties were
investigated. Because of its crucial effect on the application to the
electroforming of microelectronic components, the development of
low internal stress coating with high leveling power was emphasized.
It was found that both the coating’s manganese content and the
cathodic current efficiency increased with the raise in current density.
In addition, the internal stress of the deposited coating showed
compressive nature at low current densities while changed to tensile
one at higher current densities. Moreover, the metallographic
observation, X-ray diffraction measurement, and polarization curve
measurement were conducted. It was found that the Ni-Mn coating
consisted of nano-sized columnar grains and the maximum hardness of
the coating was associated with (111) preferred orientation in the
microstructure. The grain size was refined along with the increase in
the manganese content of the coating, which accordingly, raised its
hardness and resistance to annealing softening. In summary, the
Ni-Mn coating prepared at lower current density of 1-2 A/dm2 had low
internal stress, high leveling power, and better corrosion resistance.
Abstract: Cemented carbides, owing to their excellent
mechanical properties, have been of immense interest in the field of
hard materials for the past few decades. A number of processing
techniques have been developed to obtain high quality carbide tools,
with a wide range of grain size depending on the application and
requirements. Microwave sintering is one of the heating processes,
which has been used to prepare a wide range of materials including
ceramics. A deep understanding of microwave sintering and its
contribution towards control of grain growth and on deformation of
the resulting carbide materials requires further studies and attention.
In addition, the effect of binder materials and their behavior during
microwave sintering is another area that requires clear understanding.
This review aims to focus on microwave sintering, providing
information of how the process works and what type of materials it is
best suited for. In addition, a closer look at some microwave sintered
Tungsten Carbide-Cobalt samples will be taken and discussed,
highlighting some of the key issues and challenges faced in this
research area.
Abstract: Sol-enhanced Zn-Ni-Al2O3 nanocomposite coatings
were electroplated on mild steel by our newly developed solenhanced
electroplating method. In this method, transparent Al2O3 sol
was added into the acidic Zn-Ni bath to produced Zn-Ni-Al2O3nanocomposite
coatings. The chemical composition, microstructure and
mechanical properties of the composite and alloy coatings deposited
at two different agitation speed were investigated. The structure of all
coatings was single γ-Ni5Zn21 phase. The composite coatings possess
refined crystals with higher microhardness compared to Zn-Ni alloy
coatings. The wear resistance of Zn-Ni coatings was improved
significantly by incorporation of alumina nano particles into the
coatings. Higher agitation speed provided more uniform coatings
with smaller grain sized and slightly higher microhardness.
Considering composite coatings, high agitation speeds may facilitate
co-deposition of alumina in the coatings.
Abstract: A nanocrystalline thin film of ZnSe was successfully
electrodeposited on copper substrate using a non-aqueous solution
and subsequently annealed in air at 400°C. XRD analysis indicates
the polycrystalline deposit of (111) plane in both the cases. The
sharpness of the peak increases due to annealing of the film and
average grain size increases to 20 nm to 27nm. SEM photograph
indicate that grains are uniform and densely distributed over the
surface. Annealing increases the average grain size by 20%. The EDS
spectroscopy shows the ratio of Zn & Se is 1.1 in case of annealed
film. AFM analysis indicates the average roughness of the film
reduces from 181nm to 165nm due to annealing of the film. The
bandgap also decreases from 2.71eV to 2.62eV.
Abstract: The Cone Penetration Test (CPT) is a common in-situ
test which generally investigates a much greater volume of soil more
quickly than possible from sampling and laboratory tests. Therefore,
it has the potential to realize both cost savings and assessment of soil
properties rapidly and continuously. The principle objective of this
paper is to demonstrate the feasibility and efficiency of using
artificial neural networks (ANNs) to predict the soil angle of internal
friction (Φ) and the soil modulus of elasticity (E) from CPT results
considering the uncertainties and non-linearities of the soil. In
addition, ANNs are used to study the influence of different
parameters and recommend which parameters should be included as
input parameters to improve the prediction. Neural networks discover
relationships in the input data sets through the iterative presentation
of the data and intrinsic mapping characteristics of neural topologies.
General Regression Neural Network (GRNN) is one of the powerful
neural network architectures which is utilized in this study. A large
amount of field and experimental data including CPT results, plate
load tests, direct shear box, grain size distribution and calculated data
of overburden pressure was obtained from a large project in the
United Arab Emirates. This data was used for the training and the
validation of the neural network. A comparison was made between
the obtained results from the ANN's approach, and some common
traditional correlations that predict Φ and E from CPT results with
respect to the actual results of the collected data. The results show
that the ANN is a very powerful tool. Very good agreement was
obtained between estimated results from ANN and actual measured
results with comparison to other correlations available in the
literature. The study recommends some easily available parameters
that should be included in the estimation of the soil properties to
improve the prediction models. It is shown that the use of friction
ration in the estimation of Φ and the use of fines content in the
estimation of E considerable improve the prediction models.
Abstract: Equal channel angular pressing (ECAP) of
commercial Al-Mg-Si alloy was conducted using two strain rates.
The ECAP processing was conducted at room temperature and at
250°C. Route A was adopted up to a total number of four passes in
the present work. Structural evolution of the aluminum alloy discs
was investigated before and after ECAP processing using optical
microscopy (OM). Following ECAP, simple compression tests and
Vicker’s hardness were performed. OM micrographs showed that, the
average grain size of the as-received Al-Mg-Si disc tends to be larger
than the size of the ECAP processed discs. Moreover, significant
difference in the grain morphologies of the as-received and processed
discs was observed. Intensity of deformation was observed via the
alignment of the Al-Mg-Si consolidated particles (grains) in the
direction of shear, which increased with increasing the number of
passes via ECAP. Increasing the number of passes up to 4 resulted in
increasing the grains aspect ratio up to ~5. It was found that the
pressing temperature has a significant influence on the
microstructure, Hv-values, and compressive strength of the processed
discs. Hardness measurements demonstrated that 1-pass resulted in
increase of Hv-value by 42% compared to that of the as-received
alloy. 4-passes of ECAP processing resulted in additional increase in
the Hv-value. A similar trend was observed for the yield and
compressive strength. Experimental data of the Hv-values
demonstrated that there is a lack of any significant dependence on the
processing strain rate.
Abstract: Nanocrystalline powders of the lead-free piezoelectric
material, tantalum-substituted potassium sodium niobate
(K0.5Na0.5)(Nb0.9Ta0.1)O3 (KNNT), were produced using a Retsch
PM100 planetary ball mill by setting the milling time to 15h, 20h,
25h, 30h, 35h and 40h, at a fixed speed of 250rpm. The average
particle size of the milled powders was found to decrease from 12nm
to 3nm as the milling time increases from 15h to 25h, which is in
agreement with the existing theoretical model. An anomalous
increase to 98nm and then a drop to 3nm in the particle size were
observed as the milling time further increases to 30h and 40h
respectively. Various sizes of these starting KNNT powders were
used to investigate the effect of milling time on the microstructure,
dielectric properties, phase transitions and piezoelectric properties of
the resulting KNNT ceramics. The particle size of starting KNNT
was somewhat proportional to the grain size. As the milling time
increases from 15h to 25h, the resulting ceramics exhibit
enhancement in the values of relative density from 94.8% to 95.8%,
room temperature dielectric constant (εRT) from 878 to 1213, and
piezoelectric charge coefficient (d33) from 108pC/N to 128pC/N. For
this range of ceramic samples, grain size refinement suppresses the
maximum dielectric constant (εmax), shifts the Curie temperature (Tc)
to a lower temperature and the orthorhombic-tetragonal phase
transition (Tot) to a higher temperature. Further increase of milling
time from 25h to 40h produces a gradual degradation in the values of
relative density, εRT, and d33 of the resulting ceramics.
Abstract: Series of laboratory tests were carried out to study the
extent of scour caused by a three-dimensional wall jets exiting from a
square cross-section nozzle and into a non-cohesive sand beds.
Previous observations have indicated that the effect of the tail water
depth was significant for densimetric Froude number greater than ten.
However, the present results indicate that the cut off value could be
lower depending on the value of grain size-to-nozzle width ratio.
Numbers of equations are drawn out for a better scaling of numerous
scour parameters. Also suggested the empirical prediction of scour to
predict the scour centre line profile and plan view of scour profile at
any particular time.
Abstract: This entry concerned with dense silica bricks
microstructure was produced as a part of a project within the
Technology Agency of the Czech Republic which is being
implemented in cooperation of the biggest producer of refractories
the P-D Refractories CZ company with the research organisation
Brno University of Technology. The paper is focused on the
influence of mixture homogenisation and the influence of grain size
of the mineraliser on the resulting utility properties of the material as
well as its microstructure. It has a decisive influence on the durability
of the material in a building structure. This paper is a continuation of
a previously published study dealing with the suitability of various
types of mineralising agents in terms of density, strength and mineral
composition of silica brick.
The entry describes the influence of the method of mixture
homogenisation and the influence of granulometry of the applied Femineralising
agent on the resulting silica microstructure. Porosity,
density, phase composition and microstructure of the experimentally
prepared silica bricks samples were examined and the results were
discussed in context with the technology of homogenisation and
firing temperature used. The properties of silica bricks samples were
compared to the sample without any Fe-mineraliser.
Abstract: This research studies the electroplating of zinc coating
in the zinc chloride bath mixed with supercritical CO2. The sodium
fluoride (NaF) was used as the bath additive to change the structure
and property of the coating, and therefore the roughness and corrosion
resistance of the zinc coating was investigated. The surface
characterization was performed using optical microscope (OM), X-ray
diffractometer (XRD), and α-step profilometer. Moreover, the
potentiodynamic polarization measurement in 3% NaCl solution was
employed in the corrosion resistance evaluation. Because of the
emulsification of the electrolyte mixed in Sc-CO2, the electroplated
zinc produced the coating with smoother surface, smaller grain, better
throwing power and higher corrosion resistance. The main role played
by the NaF was to reduce the coating’s roughness and grain size. In
other words, the CO2 mixed with the electrolyte under the supercritical
condition performed the similar function as brighter and leveler in zinc
electroplating to enhance the throwing power and corrosion resistance
of the coating.
Abstract: Effect of aging treatment on microstructural aspects of interfacial layers of the Cu/Al clad sheet produced by differential speed rolling (DSR) process were studied by electron back scattered diffraction (EBSD). Clad sheet of Al/Cu has been fabricated by using DSR, which caused severe shear deformation between Al and Cu plate to easily bond to each other. Rolling was carried out at 100oC with speed ratio of 2, in which the total thickness reduction was 45%. Interface layers of clad sheet were analyzed by EBSD after subsequent annealing at 400oC for 30 to 120min. With increasing annealing time, thickness of interface layer and fraction of high angle grain boundary were increased and average grain size was decreased.
Abstract: The calcarenites carbonate rocks of the Quaternary ridges, which extend along the northwestern Mediterranean coastal plain of Egypt, represent an excellent model for the transformation of loose sediments to real sedimentary rocks by the different stages of meteoric diagenesis. The depositional and diagenetic fabrics of the rocks, in addition to the strata orientation, highly affect their ultimate compressive strength and other geotechnical properties.
There is a marked increase in the compressive strength (UCS) from the first to the fourth ridge rock samples. The lowest values are related to the loose packing, weakly cemented aragonitic ooid sediments with high porosity, besides the irregularly distributed of cement, which result in decreasing the ability of these rocks to withstand crushing under direct pressure. The high (UCS) values are attributed to the low porosity, the presence of micritic cement, the reduction in grain size and the occurrence of micritization and calcretization processes.
The strata orientation has a notable effect on the measured (UCS). The lowest values have been recorded for the samples cored in the inclined direction; whereas the highest values have been noticed in most samples cored in the vertical and parallel directions to bedding plane. In case of the inclined direction, the bedding planes were oriented close to the plane of maximum shear stress. The lowest and highest anisotropy values have been recorded for the first and the third ridges rock samples, respectively, which may attributed to the relatively homogeneity and well sorted grainstone of the first ridge rock samples, and relatively heterogeneity in grain and pore size distribution and degree of cementation of the third ridge rock samples, besides, the abundance of shell fragments with intraparticle pore spaces, which may produce lines of weakness within the rock.
Abstract: In this work, the bioclogging of two soils with different granulometries is presented. The durability of the clogging is also studied under cycles of hydraulic head and under cycles of desaturation-resaturation. The studied materials present continuous grain size distributions. The first one corresponding to the "material 1” presents grain sizes between 0.4 and 4mm. The second material called "material 2" is composed of grains with size varying between 1 and 10mm. The results show that clogging occurs very quickly after the injection of nutrition and an outlet flow near to 0 is observed. The critical hydraulic head is equal to 0.76 for "material 1", and 0.076 for "material 2". The durability tests show a good resistance to unclogging under cycles of hydraulic head and desaturation-resaturation for the "material 1". Indeed, the flow after the cycles is very low. In contrast, "material 2", shows a very bad resistance, especially under the hydraulic head cycles. The resistance under the cycles of desaturation-resaturation is better but an important increase of the flow is observed. The difference of behavior is due to the granulometry of the materials. Indeed, the large grain size contributes to the reduction of the efficiency of the bioclogging treatment in this material.
Abstract: This paper reports on the effects of heat treatment on 3CR12 and AISI 316 stainless steel grades. Heat treatment was conducted on the steel grades and cooled using two different media; air and water in order to study the effect of each medium on the evolving properties of the samples. The heat treated samples were characterized through the evolving microstructure and hardness. It was found that there was a significant grain size reduction in both the heat treated stainless steel specimens compared to the parent materials. The finer grain sizes were achieved as a result of impediment to growth of one phase by the other. The Vickers microhardness values of the heat treated samples were higher compared to the parent materials due to the fact that each of the steel grades had a proportion of martensitic structures in their microstructures thereby improving the integrity of the material.
Abstract: The present research study focuses on the investigation of the influence of sand blasting on formed mild steel samples. The investigation involved the examinations on the parent material and a sand blasted material. The results were compared to the mechanically formed materials (sand and non-sand blasted) as well as a laser formed material (sand and non-sand blasted). Each material was characterized for the grain sizes and hardness. The percentage change in the grain sizes was quantified and correlation to the microhardness values was established. The Ultimate Tensile Strength (UTS) of the materials was also quantified using the obtained hardness values. The investigations revealed that the sand blasting causes an increase in the Vickers microhardness values of all the materials which also led to an increase in the UTS. After the forming operation, the microstructure revealed elongated grains as compared to almost equiaxed obtained from the parent non-sand blasted materials.
Abstract: Preparation of size controlled nano-particles of silver catalyst on carbon substrate from e-waste has been investigated. Chemical route was developed by extraction of the metals available in nitric acid followed by treatment with hydrofluoric acid. Silver metal particles deposited with an average size 4-10 nm. A stabilizer concentration of 10- 40 g/l was used. The average size of the prepared silver decreased with increase of the anode current density. Size uniformity of the silver nano-particles was improved distinctly at higher current density no more than 20mA... Grain size increased with EK time whereby aggregation of particles was observed after 6 h of reaction.. The chemical method involves adsorption of silver nitrate on the carbon substrate. Adsorbed silver ions were directly reduced to metal particles using hydrazine hydrate. Another alternative method is by treatment with ammonia followed by heating the carbon loaded-silver hydroxide at 980°C. The product was characterized with the help of XRD, XRF, ICP, SEM and TEM techniques.
Abstract: Homogeneous composites of alumina and zirconia
with a small amount of MgO (99%) were obtained for ZTA ceramic containing 0.05 wt% MgO in
1500 °C.