Abstract: The present research study focuses on the investigation of the influence of sand blasting on formed mild steel samples. The investigation involved the examinations on the parent material and a sand blasted material. The results were compared to the mechanically formed materials (sand and non-sand blasted) as well as a laser formed material (sand and non-sand blasted). Each material was characterized for the grain sizes and hardness. The percentage change in the grain sizes was quantified and correlation to the microhardness values was established. The Ultimate Tensile Strength (UTS) of the materials was also quantified using the obtained hardness values. The investigations revealed that the sand blasting causes an increase in the Vickers microhardness values of all the materials which also led to an increase in the UTS. After the forming operation, the microstructure revealed elongated grains as compared to almost equiaxed obtained from the parent non-sand blasted materials.
Abstract: The functional performance of machined components, often, depends on surface topography, hardness, nature of stress and strain induced on the surface, etc. Invariably, surfaces of metallic components obtained by turning, milling, etc., consist of irregularities such as machining marks are responsible for the above. Surface finishing/coating processes used to produce improved surface quality/textures are classified as chip-removal and chip-less processes. Burnishing is chip-less cold working process carried out to improve surface finish, hardness and resistance to fatigue and corrosion; not obtainable by other surface coating and surface treatment processes. It is a very simple, but effective method which improves surface characteristics and is reported to introduce compressive stresses.
Of late, considerable attention is paid to post-machining, finishing operations, such as burnishing. During burnishing the micro-irregularities start to deform plastically, initially the crests are gradually flattened and zones of reduced deformation are formed. When all the crests are deformed, the valleys between the micro-irregularities start moving in the direction of the newly formed surface. The grain structure is then condensed, producing a smoother and harder surface with superior load-carrying and wear-resistant capabilities.
Burnishing can be performed on a lathe with a highly polished ball or roller type tool which is traversed under force over a rotating/stationary work piece. Often, several passes are used to obtain the work piece surface with the desired finish and hardness.
This paper presents the findings of an experimental investigation on the effect of ball burnishing parameters such as, burnishing speed, feed, force and number of passes; on surface roughness (Ra) and micro-hardness (Hv) of a 60/40 copper/zinc alloy, using a 2-level fractional factorial design of experiments (DoE). Mathematical models were developed to predict surface roughness and hardness generated by burnishing in terms of the above process parameters. A ball-type tool, designed and constructed from a high chrome steel material (HRC=63 and Ra=0.012 µm), was used for burnishing of fine-turned cylindrical bars (0.68-0.78µm and 145Hv). They are given by,
Ra= 0.305-0.005X1 - 0.0175X2 + 0.0525X4 + 0.0125X1X4 -0.02X2X4 - 0.0375X3X4
Hv=160.625 -2.37 5X1 + 5.125X2 + 1.875X3 + 4.375X4 - 1.625X1X4 + 4.375X2X4 - 2.375X3X4
High surface microhardness (175HV) was obtained at 400rpm, 2passes, 0.05mm/rev and 15kgf., and high surface finish (0.20µm) was achieved at 30kgf, 0.1mm/rev, 112rpm and single pass. In other words, surface finish improved by 350% and microhardness improved by 21% compared to as machined conditions.
Abstract: Single crystals of Magnesium alloys such as pure Mg,
Mg-1Zn-0.5Y, Mg-0.1Y, and Mg-0.1Ce alloys were successfully
fabricated in this study by employing the modified Bridgman method.
To determine the exact orientation of crystals, pole figure
measurement using X-ray diffraction were carried out on each single
crystal. Hardness and compression tests were conducted followed by
subsequent recrysatllization annealing. Recrystallization kinetics of
Mg alloy single crystals has been investigated. Fabricated single
crystals were cut into rectangular shaped specimen and solution
treated at 400oC for 24 hrs, and then deformed in compression mode
by 30% reduction. Annealing treatment for recrystallization has been
conducted on these cold-rolled plates at temperatures of 300oC for
various times from 1 to 20 mins. The microstructure observation and
hardness measurement conducted on the recrystallized specimens
revealed that static recrystallization of ternary alloy single crystal was
very slow, while recrystallization behavior of binary alloy single
crystals appeared to be very fast.
Abstract: Soursop (Anona muricata) is one of the underutilized tropical fruits containing nutrients, particularly dietary fibre and antioxidant properties that are beneficial to human health. This objective of this study is to investigate the feasibility of matured soursop pulp flour (SPF) to be substituted with high-protein wheat flour in bread. Bread formulation was substituted with different levels of SPF (0%, 5%, 10% and 15%). The effect on physicochemical properties and sensory attributes were evaluated. Higher substitution level of SPF resulted in significantly higher (p
Abstract: Experiments were carried out on the survival and growth of Rasbora daniconius, Puntius ticto and Puntius conchonius. The motivation of the study was to obtain information for growing the fish on a commercial scale for their use as biological control agents against mosquito larvae. The effects of temperature, total hardness, DO, pH and feed on the growth of fish were also investigated. Excessive value of total hardness was found because very rich calcium ion is present in Chitrakoot area. There was significant increases in growth rates of fish as temperature was increased from 280C to 300C. Further increases in temperature up to 320C, did not further affect growth. The positive and highly significant correlations 0.991488, 0.9581 and 0.9935 were found between length and weight of P. ticto, P. conchonius and R. daniconius respectively. The regression was significant at 5% level of probability.
Abstract: Deep cold rolling (DCR) is a cold working process, which easily produces a smooth and work-hardened surface by plastic deformation of surface irregularities. In the present study, the influence of main deep cold rolling process parameters on the surface roughness and the hardness of AISI 4140 steel were studied by using fractional factorial design of experiments. The assessment of the surface integrity aspects on work material was done, in terms of identifying the predominant factor amongst the selected parameters, their order of significance and setting the levels of the factors for minimizing surface roughness and/or maximizing surface hardness. It was found that the ball diameter, rolling force, initial surface roughness and number of tool passes are the most pronounced parameters, which have great effects on the work piece-s surface during the deep cold rolling process. A simple, inexpensive and newly developed DCR tool, with interchangeable collet for using different ball diameters, was used throughout the experimental work presented in this paper.
Abstract: Particulate reinforced metal matrix composites
(MMCs) are potential materials for various applications due to their
advantageous of physical and mechanical properties. This paper
presents a study on the performance of stir cast Al2O3 SiC reinforced
metal matrix composite materials. The results indicate that the
composite materials exhibit improved physical and mechanical
properties, such as, low coefficient of thermal expansion, high
ultimate tensile strength, high impact strength, and hardness. It has
been found that with the increase of weight percentage of
reinforcement particles in the aluminium metal matrix, the new
material exhibits lower wear rate against abrasive wearing. Being
extremely lighter than the conventional gray cast iron material, the
Al-Al2O3 and Al-SiC composites could be potential green materials
for applications in the automobile industry, for instance, in making
car disc brake rotors.
Abstract: The textural parameters, together with appearance and
flavor, are sensory attributes of great importance for the product to be
accepted by the consumer. The objective of the present study was the
evaluation of the textural attributes of Packhams pears in the fresh
state, after drying in a chamber with forced convection at 50ºC,
lyophilized and re-hydrated. In texture analysis it was used the
method of Texture Profile Analysis (TPA). The parameters analyzed
were hardness, cohesiveness, adhesiveness, elasticity and chewiness.
From the results obtained is possible to see that the drying operation
greatly affected some textural properties of the pears, so that the
hardness diminished very much with drying, for both drying
methods.
Abstract: The objective of the research was to evaluate the
hardness stability of milk pomade sweets packed in several
packaging materials (OPP, Multibarrier 60 HFP, BIALON 65
HFP, BIALON 50 HFP, ECOLEAN) by several packaging
technologies – modified atmosphere (MAP) (consisting of
30% CO2+70% N2; 30% N2+70% CO2 and 100% CO2) and
control – in air ambiance. Samples were stored at the room
temperature +21±1 °C. The studies of the samples were
carried out before packaging and after 2, 4, 6, 8, and 10
storage weeks.
Abstract: A study has been carried out to determine the effect of
coating two commercial glass-ionomer cements in either petroleum
jelly or wax. After coating, specimens were stored in water for 24 or
168 hours, then the coating removed and the surface examined.
Coating in wax was found to increase the surface hardness
significantly compared with the uncoated control, whereas coating
the specimens in petroleum jelly led to only a slight increase in
surface hardness. Coating in wax led to no detectable ion release
after either 24 or 168 hours, though there was some ion release after
the coating had been removed and the specimens exposed to water
for a further 24 hours. This shows that soluble species remained in
these specimens. Overall, this study confirms the idea that immature
glass-ionomers should be protected from early exposure to moisture,
and that the protection offered by petroleum jelly is only modest.
Abstract: The paper presents the results of microhardness and
microstructure of low carbon steel surface melted using carbon
dioxide laser with a wavelength of 10.6μm and a maximum output
power of 2000W. The processing parameters such as the laser power,
and the scanning rate were investigated in this study. After surface
melting two distinct regions formed corresponding to the melted zone
MZ, and the heat affected zone HAZ. The laser melted region
displayed a cellular fine structures while the HAZ displayed
martensite or bainite structure. At different processing parameters,
the original microstructure of this steel (Ferrite+Pearlite) has been
transformed to new phases of martensitic and bainitic structures. The
fine structure and the high microhardness are evidence of the high
cooling rates which follow the laser melting. The melting pool and
the transformed microstructure in the laser surface melted region of
carbon steel showed clear dependence on laser power and scanning
rate.
Abstract: Aluminum alloy has an extensive range of industrial application due to its consistent mechanical properties and structural integrity. The heat treatment by precipitation technique affected the Magnesium, Silicon Manganese and copper crystals dissolved in the Aluminum alloy. The crystals dislocated to precipitate on the crystal’s boundaries of the Aluminum alloy when given a thermal energy increased its hardness. In this project various times and temperature were varied to find out the best combination of these variables to increase the precipitation of the metals on the Aluminum crystal’s boundaries which will lead to get the highest hardness. These specimens are then tested for their hardness and tensile strength. It is noticed that when the temperature increases, the precipitation increases and consequently the hardness increases. A threshold temperature value (264C0) of Aluminum alloy should not be reached due to the occurrence of recrystalization which causes the crystal to grow. This recrystalization process affected the ductility of the alloy and decrease hardness. In addition, and while increasing the temperature the alloy’s mechanical properties will decrease. The mechanical properties, namely tensile and hardness properties are investigated according to standard procedures. In this research, different temperature and time have been applied to increase hardening.The highest hardness at 100°c in 6 hours equals to 207.31 HBR, while at the same temperature and time the lowest elongation equals to 146.5.
Abstract: This research was conducted to develop a correlation
between microstructure of HSLA steel and the mechanical properties
that occur as a result of both laser and mechanical forming processes
of the metal. The technique of forming flat metals by applying laser
beams is a relatively new concept in the manufacturing industry.
However, the effects of laser energy on the stability of metal alloy
phases have not yet been elucidated in terms of phase
transformations and microhardness. In this work, CO2 laser source
was used to irradiate the surface of a flat metal then the
microstructure and microhardness of the metal were studied on the
formed specimen. The extent to which the microstructure changed
depended on the heat inputs of up to 1000 J/cm2 with cooling rates of
about 4.8E+02 K/s. Experimental results revealed that the irradiated
surface of a HSLA steel had transformed to austenitic structure
during the heating process.
Abstract: The present study aims at determining the effect of ageing on the impact toughness and microstructure of 2024 Al-Cu - Mg alloy. Following the 2 h solutionizing treatment at 450°C and water quench, the specimens were aged at 200°C for various periods (1 to 18 h). The precipitation stages during ageing were monitored by hardness measurements. For each specimen group, Charpy impact and hardness tests were carried out. During ageing the impact toughness of the alloy first increased, and then, following a maxima decreased due to the precipitation of intermediate phases, finally it reached its minimum at the peak hardness. Correlations between hardness and impact toughness were investigated.
Abstract: The present work is concerned with the effect of turning process parameters (cutting speed, feed rate, and depth of cut) and distance from the center of work piece as input variables on the chip micro-hardness as response or output. Three experiments were conducted; they were used to investigate the chip micro-hardness behavior at diameter of work piece for 30[mm], 40[mm], and 50[mm]. Response surface methodology (R.S.M) is used to determine and present the cause and effect of the relationship between true mean response and input control variables influencing the response as a two or three dimensional hyper surface. R.S.M has been used for designing a three factor with five level central composite rotatable factors design in order to construct statistical models capable of accurate prediction of responses. The results obtained showed that the application of R.S.M can predict the effect of machining parameters on chip micro-hardness. The five level factorial designs can be employed easily for developing statistical models to predict chip micro-hardness by controllable machining parameters. Results obtained showed that the combined effect of cutting speed at it?s lower level, feed rate and depth of cut at their higher values, and larger work piece diameter can result increasing chi micro-hardness.
Abstract: The present study was designed to demonstrate the seasonal variations in physico-chemical parameters of fish farm at Govt. Nursery Unit, Muzaffargarh, Department of Fisheries Govt. of Punjab, Pakistan for a period of eight months from January to August 2008. Water samples were collected on fifteen days basis and have been analyzed for estimation of Air temperature, Water temperature, Light penetration, pH, Total dissolved oxygen, Clouds, Carbonates, Bicarbonates, Total carbonates, Total dissolved solids, Chlorides, Calcium and Hardness. Seasonal fluctuations were observed in all the physico-chemical parameters of fish farm. The overall physicochemical parameters of fish pond water remained within the tolerable range throughout the study period.
Abstract: Deep cold rolling (DCR) and low plasticity burnishing (LPB) process are cold working processes, which easily produce a smooth and work-hardened surface by plastic deformation of surface irregularities. The present study focuses on the surface roughness and surface hardness aspects of AISI 4140 work material, using fractional factorial design of experiments. The assessment of the surface integrity aspects on work material was done, in order to identify the predominant factors amongst the selected parameters. They were then categorized in order of significance followed by setting the levels of the factors for minimizing surface roughness and/or maximizing surface hardness. In the present work, the influence of main process parameters (force, feed rate, number of tool passes/overruns, initial roughness of the work piece, ball material, ball diameter and lubricant used) on the surface roughness and the hardness of AISI 4140 steel were studied for both LPB and DCR process and the results are compared. It was observed that by using LPB process surface hardness has been improved by 167% and in DCR process surface hardness has been improved by 442%. It was also found that the force, ball diameter, number of tool passes and initial roughness of the workpiece are the most pronounced parameters, which has a significant effect on the work piece-s surface during deep cold rolling and low plasticity burnishing process.
Abstract: In the present work, a comparative study on the
microstructure and mechanical properties of as cast, cast aged and
forged aged A356 alloy has been investigated. The study reveals that
mechanical properties of A356 alloy are highly influenced by melt
treatment and solid state processing. Cast aged alloys achieve highest
strength and hardness compared to as cast and forge aged ones. Ones
treated with combined addition of grain refiners and modifiers
achieve maximum strength and hardness. Cast aged A356 alloy
possesses higher wear resistance compared to as cast and forge aged
ones. Forging improves both strength and ductility of alloys over as
cast ones. However, the improvement in ductility is perceptible only
for properly grain refined and modified alloys. Ones refined with
0.65% Al-3Ti shows highest improvement in ductility while ones
treated with 0.20% Al-10Sr exhibits less improvement in ductility.
Abstract: The peculiarities of the nanoscale structure-phase
states formed after electroexplosive carburizing and subsequent
electron-beam treatment of technically pure titanium surface in different regimes are established by methods of transmission electron
diffraction microscopy and physical mechanisms are discussed. Electroexplosive carburizing leads to surface layer formation
(40 m thickness) with increased (in 3.5 times) microhardness. It consists of β-titanium, graphite (monocrystals 100-150 nm,
polycrystals 5-10 nm, amorphous particles 3-5nm), TiC (5-10 nm), β-Ti02 (2-20nm). After electron-beam treatment additionally increasing the microhardness the surface layer consists of TiC.