Abstract: In this current contribution, authors are dedicated to
investigate influence of the crystal lamellae orientation on
electromechanical behaviors of relaxor ferroelectric Poly
(vinylidene fluoride –trifluoroethylene -chlorotrifluoroethylene)
(P(VDF-TrFE-CTFE)) films by control of polymer microstructure,
aiming to picture the full map of structure-property relationship. In
order to define their crystal orientation films, terpolymer films were
fabricated by solution-casting, stretching and hot-pressing process.
Differential scanning calorimetry, impedance analyzer, and tensile
strength techniques were employed to characterize crystallographic
parameters, dielectric permittivity, and elastic Young’s modulus
respectively. In addition, large electrical induced out-of-plane
electrostrictive strain was obtained by cantilever beam mode.
Consequently, as-casted pristine films exhibited surprisingly high
electrostrictive strain 0.1774% due to considerably small value of
elastic Young’s modulus although relatively low dielectric
permittivity. Such reasons contributed to large mechanical elastic
energy density. Instead, due to 2 folds increase of elastic Young’s
modulus and less than 50% augmentation of dielectric constant, fullycrystallized
film showed weak electrostrictive behavior and
mechanical energy density as well. And subjected to mechanical
stretching process, Film C exhibited stronger dielectric constant and
out-performed electrostrictive strain over Film B because edge-on
crystal lamellae orientation induced by uniaxially mechanical stretch.
Hot-press films were compared in term of cooling rate. Rather large
electrostrictive strain of 0.2788% for hot-pressed Film D in
quenching process was observed although its dielectric permittivity
equivalent to that of pristine as-casted Film A, showing highest
mechanical elastic energy density value of 359.5 J/m3. In hot-press
cooling process, dielectric permittivity of Film E saw values at 48.8
concomitant with ca.100% increase of Young’s modulus. Films with
intermediate mechanical energy density were obtained.
Abstract: This work aims to investigate the structure–property
relationship in ternary nanocomposites consisting of polypropylene
as the matrix, polyamide 66 as the minor phase and treated nanoclay
DELLITE 67G as the reinforcement. All PP/PA66/Nanoclay systems
with polypropylene grafted maleic anhydride PP-g-MAH as a
compatibilizer were prepared via melt compounding and
characterized in terms of nanoclay content. Morphological structure
was investigated by scanning electron microscopy. The rheological
behavior of the nanocomposites was determined by various methods,
viz melt flow index (MFI) and parallel plate rheological
measurements. The PP/PP-g-MAH/PA66 nanocomposites showed a homogeneous
morphology supporting the compatibility improvement between PP,
PA66, and nanoclay. SEM results revealed the formation of
nanocomposites as the nanoclay was intercalated and exfoliated. In
the ternary nanocomposites, the rheological behavior showed that, the
complex viscosity is increased with increasing the nanoclay. The results showed that the use of nanoclay affects the variations
of storage modulus (G′), loss modulus (G″) and the melt elasticity.
Abstract: This paper presents the effects of mixing procedures
on mechanical properties of flyash-based geopolymer matrices
containing nanosilica (NS) at 0.5%, 1.0%, 2.0%, and 3.0% by weight.
Comparison is made with conventional mechanical dry-mixing of NS
with flyash and wet-mixing of NS in alkaline solutions. Physical and
mechanical properties are investigated using X-Ray Diffraction
(XRD) and Scanning Electron Microscope (SEM). Results show that
generally the addition of NS particles enhanced the microstructure
and improved flexural and compressive strengths of geopolymer
nanocomposites. However, samples, prepared using dry-mixing
approach, demonstrate better physical and mechanical properties
comparing to wet-mixing samples.
Abstract: Polymeric composites are being increasingly used as
repair material for repairing critical infrastructures such as building,
bridge, pressure vessel, piping and pipeline. Technique in repairing
damaged pipes is one of the major concerns of pipeline owners.
Considerable researches have been carried out on the repair of
corroded pipes using composite materials. This article attempts a
short review of the subject matter to provide insight into various
techniques used in repairing corroded pipes, focusing on a wide range
of composite repair systems. These systems including pre-cured
layered, flexible wet lay-up, pre-impregnated, split composite sleeve
and flexible tape systems. Both advantages and limitations of these
repair systems were highlighted. Critical technical aspects have been
discussed through the current standards and practices. Research gaps
and future study scopes in achieving more effective design
philosophy are also presented.
Abstract: Over the last two decades, externally bonded fiber
reinforced polymer (FRP) composites bonded to concrete substrates
has become a popular method for strengthening reinforced concrete
(RC) highway and railway bridges. Such structures are exposed to
severe cyclic loading throughout their lifetime often resulting in
fatigue damage to structural components and a reduction in the
service life of the structure. Since experimental and numerical results
on the fatigue performance of FRP-to-concrete joints are still limited,
the current research focuses on assessing the fatigue performance of
externally bonded FRP-to-concrete joints using a direct shear test.
Some early results indicate that the stress ratio and the applied cyclic
stress level have a direct influence on the fatigue life of the externally
bonded FRP. In addition, a calibrated finite element model is
developed to provide further insight into the influence of certain
parameters such as: concrete strength, FRP thickness, number of
cycles, frequency, and stiffness on the fatigue life of the FRP-toconcrete
joints.
Abstract: This paper presents numerical analysis in terms of
buckling resistance of GFRP sandwich infill panels system under the
influence of increased temperature on the foam core. Failure mode
under in-plane compression is studied by means of numerical analysis
with ABAQUS platform. Parameters considered in this study are
contact length and both the type of foam for core and the variation of
its module elastic under the thermal influence. Increment of
temperature is considered in static cases and only applied to core.
Indeed, it is proven that the effect of temperature alters the mechanical
properties of the entire panel system. Moreover, the rises of
temperature result in a decrease in strength of the panel. This is due to
the polymeric nature of this material. Additionally, the contact length
also displays the effect on performance of infill panel. Their
significance factors are based on type of polymer for core. Therefore,
by comparing difference type of core material, the variation can be
reducing.
Abstract: Hydrogen produced by means of polymer electrolyte
membrane electrolyzer (PEME) is one of the most promising
methods due to clean and renewable energy source. In the process,
some energy loss due to mass transfer through a PEM is caused by
diffusion, electro-osmotic drag, and the pressure difference between
the cathode channel and anode channel. In PEME, water molecules
and ionic particles transferred between the electrodes from anode to
cathode, Extensive mixing of the hydrogen and oxygen at anode
channel due to gases cross-over must be avoided. In recent times the
consciousness of safety issue in high pressure PEME where the
oxygen mix with hydrogen at anode channel could create, explosive
conditions have generated a lot of concern. In this paper, the steady
state and simulation analysis of gases crossover in PEME on the
temperature and pressure effect are presented. The simulations have
been analysis in MATLAB based on the well-known Fick’s Law of
molecular diffusion. The simulation results indicated that as
temperature increases, there is a significant decrease in operating
voltage.
Abstract: Geopolymer composites reinforced with flax fabrics
and nanoclay are fabricated and studied for physical and mechanical
properties using X-Ray Diffraction (XRD), Fourier Transform
Infrared Spectroscopy (FTIR), and Scanning Electron Microscope
(SEM). Nanoclay platelets at a weight of 1.0%, 2.0%, and 3.0% were
added to geopolymer pastes. Nanoclay at 2.0 wt.% was found to
improve density and decrease porosity while improving flexural
strength and post-peak toughness. A microstructural analysis
indicated that nanoclay behaves as filler and as an activator
supporting geopolymeric reaction while producing a higher content
geopolymer gel improving the microstructure of binders. The process
enhances adhesion between the geopolymer matrix and flax fibres.
Abstract: In this paper, a robust fault detection and isolation
(FDI) scheme is developed to monitor a multivariable nonlinear
chemical process called the Chylla-Haase polymerization reactor,
when it is under the cascade PI control. The scheme employs a radial
basis function neural network (RBFNN) in an independent mode to
model the process dynamics, and using the weighted sum-squared
prediction error as the residual. The Recursive Orthogonal Least
Squares algorithm (ROLS) is employed to train the model to
overcome the training difficulty of the independent mode of the
network. Then, another RBFNN is used as a fault classifier to isolate
faults from different features involved in the residual vector. Several
actuator and sensor faults are simulated in a nonlinear simulation of
the reactor in Simulink. The scheme is used to detect and isolate the
faults on-line. The simulation results show the effectiveness of the
scheme even the process is subjected to disturbances and
uncertainties including significant changes in the monomer feed rate,
fouling factor, impurity factor, ambient temperature, and
measurement noise. The simulation results are presented to illustrate
the effectiveness and robustness of the proposed method.
Abstract: In order to investigate the prebiotic potential of
oligosaccharides prepared by chemical hydrolysis of water-soluble
polysaccharides (WSP) from Zizyphus lotus leaves, the effect of
oligosaccharides on bacterial growth was studied. The chemical
composition of WSP was evaluated by colorimetric assays revealed
the average values: 7.05±0.73% proteins and 86.21±0.74%
carbohydrates, among them 64.81±0.42% is neutral sugar and the rest
16.25±1.62% is uronic acids. The characterization of
monosaccharides was determined by high performance anion
exchange chromatography with pulsed amperometric detection
(HPAEC-PAD) was found to be composed of galactose (23.95%),
glucose (21.30%), rhamnose (20.28%), arabinose (9.55%), and
glucuronic acid (22.95%). The effects of oligosaccharides on the
growth of lactic acid bacteria were compared with those of fructooligosaccharide
(RP95). The oligosaccharides concentration was
1g/L of Man, Rogosa, Sharpe broth. Bacterial growth was assessed
during 2, 4.5, 6.5, 9, 12, 16 and 24 h by measuring the optical density
of the cultures at 600 nm (OD600) and pH values. During
fermentation, pH in broth cultures decreased from 6.7 to 5.87±0.15.
The enumeration of lactic acid bacteria indicated that
oligosaccharides led to a significant increase in bacteria (P≤0.05)
compared to the control. The fermentative metabolism appeared to be
faster on RP95 than on oligosaccharides from Zizyphus lotus leaves.
Both RP95 and oligosaccharides showed clear prebiotic effects, but
had differences in fermentation kinetics because of to the different
degree of polymerization. This study shows the prebiotic
effectiveness of oligosaccharides, and provides proof for the selection
of leaves of Zizyphus lotus for use as functional food ingredients.
Abstract: According to IR, 13C and 1H NMR, APT, 1D NOE,
2D heteronuclear 1H/13C HSQC and 2D DOSY experiments the main
chemical constituent of high-molecular preparations from Symphytum
asperum, S. caucasicum, S. officinale and Anchusa italica
(Boraginaceae) was found to be caffeic acid-derived polyether,
namely poly[3-(3,4-dihydroxyphenyl)glyceric acid] (PDPGA) or
poly[oxy-1-carboxy-2-(3,4-dihydroxyphenyl)ethylene]. Most
carboxylic groups of this polymer of A. italica are methylated.
Abstract: Green concrete are generally composed of recycling
materials as hundred or partial percent substitutes for aggregate,
cement, and admixture in concrete. To reduce greenhouse gas
emissions, efforts are needed to develop environmentally friendly
construction materials. Using of fly ash based geopolymer as an
alternative binder can help reduce CO2 emission of concrete. The
binder of geopolymer concrete is different from the ordinary Portland
cement concrete. Geopolymer Concrete specimens were prepared
with different concentration of NaOH solution M10, M14, and, M16
and cured at 60ºC in duration of 24 hours and 8 hours, in addition to
the curing in direct sunlight. Thus, it is necessary to study the effects
of the geopolymer binder on the behavior of concrete. Concrete is
made by using geopolymer technology is environmental friendly and
could be considered as part of the sustainable development. In this
study, the Local Alkaline Activator in Egypt and crashed stone as
coarse aggregate in fly ash based-geopolymer concrete was
investigated. This paper illustrates the development of mechanical
properties. Since the gained compressive strength for geopolymer
concrete at 28 days was in the range of 22.5MPa – 43.9MPa.
Abstract: Local steel slag is produced as a by-product during the
oxidation of steel pellets in an electric arc furnace. Using local steel
slag waste as a hundred substitutes of crashed stone in construction
materials would resolve the environmental problems caused by the
large-scale depletion of the natural sources of crashed stone. This
paper reports the experimental study to investigate the influence of a
hundred replacement of crashed stone as a coarse aggregate with
local steel slag, on the fresh and hardened geopolymer concrete
properties. The investigation includes traditional testing of hardening
concrete, for selected mixes of cement and geopolymer concrete. It
was found that local steel slag as a coarse aggregate enhanced the
slump test of the fresh state of cement and geopolymer concretes.
Nevertheless, the unit weight of concretes was affected. Meanwhile,
the good performance was observed when fly ash used as geopolymer
concrete based.
Abstract: Novel wind-lens turbine designs can augment power
output. Vacuum-Assisted Resin Transfer Molding (VARTM) is used
to form large and complex structures from a Carbon Fiber Reinforced
Polymer (CFRP) composite. Typically, wind-lens turbine structures
are fabricated in segments, and then bonded to form the final structure.
This paper introduces five new adhesive joints, divided into two
groups: one is constructed between dry carbon and CFRP fabrics, and
the other is constructed with two dry carbon fibers. All joints and
CFRP fabrics were made in our laboratory using VARTM
manufacturing techniques. Specimens were prepared for tensile testing
to measure joint performance. The results showed that the second
group of joints achieved a higher tensile strength than the first group.
On the other hand, the tensile fracture behavior of the two groups
showed the same pattern of crack originating near the joint ends
followed by crack propagation until fracture.
Abstract: The objective of this study was to synthesize and
characterize the poly(alkenoic acid)s with different molecular
structures, use these polymers to formulate a dental cement
restorative, and study the effect of molecular structures on reaction
kinetics, viscosity, and mechanical strengths of the formed polymers
and cement restoratives. In this study, poly(alkenoic acid)s with
different molecular structures were synthesized. The purified
polymers were formulated with commercial Fuji II LC glass fillers to
form the experimental cement restoratives. The reaction kinetics was
studied via 1HNMR spectroscopy. The formed restoratives were
evaluated using compressive strength, diametral tensile strength,
flexural strength, hardness and wear-resistance tests. Specimens were
conditioned in distilled water at 37oC for 24 h prior to testing. Fuji II
LC restorative was used as control. The results show that the higher
the arm number and initiator concentration, the faster the reaction
was. It was also found that the higher the arm number and branching
that the polymer had, the lower the viscosity of the polymer in water
and the lower the mechanical strengths of the formed restorative. The
experimental restoratives were 31-53% in compressive strength, 37-
55% in compressive modulus, 80-126% in diametral tensile strength,
76-94% in flexural strength, 4-21% in fracture toughness and 53-96%
in hardness higher than Fuji II LC. For wear test, the experimental
restoratives were only 5.4-13% of abrasive and 6.4-12% of attritional
wear depths of Fuji II LC in each wear cycle. The aging study also
showed that all the experimental restoratives increased their strength
continuously during 30 days, unlike Fuji II LC. It is concluded that
polymer molecular structures have significant and positive impact on
mechanical properties of dental cement restoratives.
Abstract: Hydrogels are three-dimensional, hydrophilic,
polymeric networks composed of homopolymers or copolymers and
are insoluble in water due to the presence of chemical or physical
cross-links. When hydrogels come in contact with aqueous solutions,
they can effectively sorb and retain the dissolved substances,
depending on the nature of the monomeric units comprising the
hydrogel. For this reason, hydrogels have been proposed in several
studies as water purification agents. At the present work anionic
hydrogels bearing negatively charged –COO- groups were prepared
and investigated. These gels are based on sodium acrylate (ANa),
either homopolymerized (poly(sodiumacrylate), PANa) or
copolymerized (P(DMAM-co-ANa)) with N,N Dimethylacrylamide
(DMAM). The hydrogels were used to extract some model organic
dyes from water. It is found that cationic dyes are strongly sorbed and
retained by the hydrogels, while sorption of anionic dyes was
negligible. In all cases it was found that both maximum sorption
capacity and equilibrium binding constant varied from one dye to the
other depending on the chemical structure of the dye, the presence of
functional chemical groups and the hydrophobic-hydrophilic balance.
Finally, the nonionic hydrogel of the homopolymer poly(N,Ndimethylacrylamide),
PDMAM, was also used for reasons of
comparison.
Abstract: Polylactic acid (PLA) is the most commercially
available bio-based and biodegradable plastic at present. PLA has
been used in plastic related industries including single-used
containers, disposable and environmentally friendly packaging owing
to its renewability, compostability, biodegradability, and safety.
Although PLA demonstrates reasonably good optical, physical,
mechanical and barrier properties comparable to the existing
petroleum-based plastics, its brittleness and mold shrinkage as well as
its price are the points to be concerned for the production of rigid and
semi-rigid packaging. Blending PLA with other bio-based polymers
including thermoplastic starch (TPS) is an alternative not only to
achieve a complete bio-based plastic, but also to reduce the
brittleness, shrinkage during molding and production cost of the
PLA-based products. TPS is a material produced mainly from starch
which is cheap, renewable, biodegradable, compostable, and nontoxic.
It is commonly prepared by a plasticization of starch under
applying heat and shear force. Although glycerol has been reported as
one of the most plasticizers used for preparing TPS, its migration
caused the surface stickiness of the TPS products. In some cases,
mixed plasticizers or natural fibers have been applied to impede the
retrogradation of starch or reduce the migration of glycerol. The
introduction of fibers into TPS-based materials could reinforce the
polymer matrix as well. Therefore, the objective of the present
research is to study the effect of starch type (i.e. native starch and
phosphate starch), plasticizer type (i.e. glycerol and xylitol with a
weight ratio of glycerol to xylitol of 100:0, 75:25, 50:50, 25:75 and
0:100) and fiber content (i.e. in the range of 1-25 %wt) on properties
of PLA/TPS blend and composite. PLA/TPS blends and composites
were prepared using a twin-screw extruder and then converted into
dumbbell-shaped specimens using an injection molding machine. The
PLA/TPS blends prepared by using phosphate starch showed higher
tensile strength and stiffness than the blends prepared by using native
one. In contrast, the blends from native starch exhibited higher
extensibility and heat distortion temperature (HDT) than those from
the modified starch. Increasing xylitol content resulted in enhanced
tensile strength, stiffness and water resistance, but decreased
extensibility and HDT of the PLA/TPS blend. Tensile properties and
hydrophobicity of the blend could be improved by incorporating
silane treated-jute fibers.
Abstract: The development of composite materials and the
related design and manufacturing technologies is one of the most
important advances in the history of materials. Composites are
multifunctional materials having unprecedented mechanical and
physical properties that can be tailored to meet the requirements of a
particular application. Some composites also exhibit great resistance
to high-temperature corrosion, oxidation, and wear. Polymers are
widely used indoors and outdoors, therefore they are exposed to a
chemical environment which may include atmospheric oxygen, acidic
fumes, acidic rain, moisture heat and thermal shock, ultra-violet light,
high energy radiation, etc. Different polymers are affected differently
by these factors even though the amorphous polymers are more
sensitive. Ageing is also important and it is defined as the process of
deterioration of engineering materials resulting from the combined
effects of atmospheric radiation, heat, oxygen, water, microorganisms
and other atmospheric factors.
Abstract: The study conducted a simulation of the effect of sea
water to the bonding capacity of GFRP sheet on the concrete beams
using a simulation tank. Fiber reinforced polymer (FRP) has been
developed and applied in many fields civil engineering structures on
the new structures and also for strengthening of the deteriorated
structures. The FRP has advantages such as its corrosion resistance as
well as high tensile strength to weight ratio. Compared to the other
FRP materials, Glass composed FRP (GFRP) is relatively cheaper.
GFRP sheet is applied externally by bonding it on the concrete surface.
The studies regarding the application of GFRP sheet have been
conducted such as strengthening system, bonding behavior of GFRP
sheet including the application as reinforcement in new structures. For
application to the structures with direct contact to sea environment, a
study regarding the effect of sea water to the bonding capacity of
GFRP sheet is important to be clarified. To achieve the objective of the
study, a series of concrete beams strengthened with GFRP sheet on
extreme tension surface were prepared. The beams then were stored on
the sea water tank for six months. Results indicated the bonding
capacity decreased after six month exposed to the sea water.
Abstract: The high-molecular water-soluble preparations from
several species of two genera (Symphytum and Anchusa) of
Boraginaceae family Symphytum asperum, S. caucasicum, S.officinale
and Anchusa italica were isolated. According to IR, 13C and 1H
NMR, APT, 1D NOE, 2D heteronuclear 1H/13C HSQC and 2D
DOSY experiments, the main chemical constituent of these
preparations was found to be caffeic acid-derived polyether, namely
poly[3-(3,4-dihydroxyphenyl)glyceric acid] (PDPGA) or poly[oxy-1-
carboxy-2-(3,4-dihydroxyphenyl)ethylene]. Most carboxylic groups
of this caffeic acid-derived polymer of A. italica are methylated.