Abstract: Samples of CoFe2-xCrxO4 where x varies from 0.0 to 0.5 were prepared by co-precipitation route. These samples were sintered at 750°C for 2 hours. These particles were characterized by X-ray diffraction (XRD) at room temperature. The FCC spinel structure was confirmed by XRD patterns of the samples. The crystallite sizes of these particles were calculated from the most intense peak by Scherrer formula. The crystallite sizes lie in the range of 37-60 nm. The lattice parameter was found decreasing upon substitution of Cr. DC electrical resistivity was measured as a function of temperature. The room temperature thermoelectric power was measured for the prepared samples. The magnitude of Seebeck coefficient depends on the composition and resistivity of the samples.
Abstract: The systematic manipulations of shapes and sizes of
inorganic compounds greatly benefit the various application fields
including optics, magnetic, electronics, catalysis and medicine.
However shape control has been much more difficult to achieve.
Hence exploration of novel method for the preparation of differently
shaped nanoparticles is challenging research area. II-VI group of
semiconductor cadmium sulphide (CdS) nanostructure with different
morphologies (such as, acicular like, mesoporous, spherical shapes)
and of crystallite sizes vary from 11 to 16 nm were successfully
synthesized by chemical aqueous precipitation of Cd2+ ions with
homogeneously released S2- ions from decomposition of cadmium
sulphate (CdSO4) and thioacetamide (CH3CSNH2) by annealing at
different radiations (microwave, ultrasonic and sunlight) with matter
and systematic research has been done for various factors affecting
the controlled growth rate of CdS nanoparticles. The obtained
nanomaterials have been characterized by X-ray Diffraction (XRD),
Fourier Transform Infrared Spectroscopy (FTIR),
Thermogravometric (DSC-TGA) analysis and Scanning Electron
Microscopy (SEM). The result indicates that on increasing the
reaction time particle size increases but on increasing the molar ratios
grain size decreases.
Abstract: TiO2 supported nano-ZnO catalyst was prepared by
deposition-precipitation and tested for the trans-esterification
reaction of soybean oil to biodiesel. The TiO2 support stabilized the
nano-ZnO in a dispersed form with limited crystallite size compared
to the unsupported ZnO. The final ZnO dispersion and crystallite size
and the material transfer resistance in the catalyst significantly
influenced the supported nano-ZnO catalyst performance.
Abstract: Sol-gel method has been used to fabricate
nanocomposite films on glass substrates composed halloysite clay
mineral and nanocrystalline TiO2. The methodology for the synthesis
involves a simple chemistry method utilized nonionic surfactant
molecule as pore directing agent along with the acetic acid-based solgel
route with the absence of water molecules. The thermal treatment
of composite films at 450oC ensures elimination of organic material
and lead to the formation of TiO2 nanoparticles onto the surface of
the halloysite nanotubes. Microscopy techniques and porosimetry
methods used in order to delineate the structural characteristics of the
materials. The nanocomposite films produced have no cracks and
active anatase crystal phase with small crystallite size were deposited
on halloysite nanotubes. The photocatalytic properties for the new
materials were examined for the decomposition of the Basic Blue 41
azo dye in solution. These, nanotechnology based composite films
show high efficiency for dye’s discoloration in spite of different
halloysite quantities and small amount of halloysite/TiO2 catalyst
immobilized onto glass substrates. Moreover, we examined the
modification of the halloysite/TiO2 films with silver particles in order
to improve the photocatalytic properties of the films. Indeed, the
presence of silver nanoparticles enhances the discoloration rate of the
Basic Blue 41 compared to the efficiencies obtained for unmodified
films.