Abstract: This paper shows researches in order to extract Cr, Cu and Ni from the polluted soils. Research is based on preliminary studies regarding the usage of Thiobacillus ferrooxidans bacterium (9K medium) for bioleaching of soil polluted with heavy metal (Cu, Cr and Ni). The microorganisms (Thiobacillus ferooxidans) selected directly from polluted soil samples were used in this experimental work. Soil samples used in the experimental research were taken from an area polluted with heavy metals from Romania. The soil samples are subjected to the cleaning process using the 9K medium solution (20 mL and 40 mL, respectively), stirred 200 rpm for 20 hours at a controlled temperature (30 ˚C). During the experiment (0, 2, 4, 8 and 20 h), liquid samples have been extracted and analyzed using the Atomic Absorption Spectrophotometer AA-6800 (AAS) in order to determine the Cr, Cu and Ni concentration. Experiments led to the conclusion that these soils can be depolluted by bioleaching, being a biological treatment method involving the use of microorganisms to favor the extraction of Cr, Cu and Ni from polluted soils.
Abstract: Among the diverse types of pollutants produced by anthropogenic activities, metals represent a serious threat, due to their accumulation in ecosystems and their elevated toxicity. The mine tailings of abandoned mines contain high levels of metals such as arsenic (As), zinc (Zn), copper (Cu), and lead (Pb), which do not suffer any degradation process, they are accumulated in environment. Abandoned mine tailings potentially could contaminate rivers and aquifers representing a risk for human health due to their high metal content. In an attempt to remove the metals and thereby mitigate the environmental pollution, an environmentally friendly and economical method of bioremediation has been introduced. Bioleaching has been actively studied over the last several years, and it is one of the bioremediation solutions used to treat heavy metals contained in sewage sludge, sediment and contaminated soil. Acidithiobacillus thiooxidans, an extremely acidophilic, chemolithoautotrophic, gram-negative, rod shaped microorganism, which is typically related to Cu mining operations (bioleaching), has been well studied for industrial applications. The sulfuric acid produced plays a major role in bioleaching. Specifically, Acidithiobacillus thiooxidans strain DSM 26636 has been able to leach Al, Ni, V, Fe, Mg, Si, and Ni contained in slags from coal combustion wastes. The present study reports the ability of A. thiooxidans DSM 26636 for the bioleaching of metals contained in two different mine tailing samples (MT1 and MT2). It was observed that Al, Fe, and Mn were removed in 36.3±1.7, 191.2±1.6, and 4.5±0.2 mg/kg for MT1, and in 74.5±0.3, 208.3±0.5, and 20.9±0.1 for MT2. Besides, < 1.5 mg/kg of Au and Ru were also bioleached from MT1; in MT2, bioleaching of Zn was observed at 55.7±1.3 mg/kg, besides removal of < 1.5 mg/kg was observed for As, Ir, Li, and 0.6 for Os in this residue. These results show the potential of strain DSM 26636 for the bioleaching of metals that came from different mine tailings.
Abstract: Spent catalysts are considered as hazardous residues of major concern, mainly due to the simultaneous presence of several metals in elevated concentrations. Although hydrometallurgical, pyrometallurgical and chelating agent methods are available to remove and recover some metals contained in spent catalysts; these procedures generate potentially hazardous wastes and the emission of harmful gases. Thus, biotechnological treatments are currently gaining importance to avoid the negative impacts of chemical technologies. To this end, diverse microorganisms have been used to assess the removal of metals from spent catalysts, comprising bacteria, archaea and fungi, whose resistance and metal uptake capabilities differ depending on the microorganism tested. Acidophilic sulfur oxidizing bacteria have been used to investigate the biotreatment and extraction of valuable metals from spent catalysts, namely Acidithiobacillus thiooxidans and Acidithiobacillus ferroxidans, as they present the ability to produce leaching agents such as sulfuric acid and sulfur oxidation intermediates. In the present work, the ability of A. thiooxidans DSM 26636 for the bioleaching of metals contained in five different spent catalysts was assessed by growing the culture in modified Starkey mineral medium (with elemental sulfur at 1%, w/v), and 1% (w/v) pulp density of each residue for up to 21 days at 30 °C and 150 rpm. Sulfur-oxidizing activity was periodically evaluated by determining sulfate concentration in the supernatants according to the NMX-k-436-1977 method. The production of sulfuric acid was assessed in the supernatants as well, by a titration procedure using NaOH 0.5 M with bromothymol blue as acid-base indicator, and by measuring pH using a digital potentiometer. On the other hand, Inductively Coupled Plasma - Optical Emission Spectrometry was used to analyze metal removal from the five different spent catalysts by A. thiooxidans DSM 26636. Results obtained show that, as could be expected, sulfuric acid production is directly related to the diminish of pH, and also to highest metal removal efficiencies. It was observed that Al and Fe are recurrently removed from refinery spent catalysts regardless of their origin and previous usage, although these removals may vary from 9.5 ± 2.2 to 439 ± 3.9 mg/kg for Al, and from 7.13 ± 0.31 to 368.4 ± 47.8 mg/kg for Fe, depending on the spent catalyst proven. Besides, bioleaching of metals like Mg, Ni, and Si was also obtained from automotive spent catalysts, which removals were of up to 66 ± 2.2, 6.2±0.07, and 100±2.4, respectively. Hence, the data presented here exhibit the potential of A. thiooxidans DSM 26636 for the simultaneous bioleaching of metals contained in spent catalysts from diverse provenance.
Abstract: Sulphur oxidizing bacteria (SOB) have marked their significant role in perspectives of maintaining healthy environment as researchers from all over the world tested and apply these in waste water treatment plants, bioleaching of heavy metals, deterioration of bridge structures, concrete and for bioremediation purposes, etc. Also, these SOB are well adapted in all kinds of environment ranging from normal soil, water habitats to extreme natural sources like geothermal areas, volcanic eruptions, black shale and acid rock drainage (ARD). SOB have been isolated from low pH environment of anthropogenic origin like acid mine drainage (AMD) and bioleaching heaps, hence these can work efficiently in different environmental conditions. Besides having many applications in field of environment science, they may be proven to be very beneficial in area of agriculture as sulphur is the fourth major macronutrients required for the growth of plants. More amount of sulphur is needed by pulses and oilseed crops with respect to the cereal grains. Due to continuous use of land for overproduction of more demanding sulphur utilizing crops and without application of sulphur fertilizers, its concentration is decreasing day by day, and thus, sulphur deficiency is becoming a great problem as it affects the crop productivity and quality. Sulphur is generally found in soils in many forms which are unavailable for plants (cannot be use by plants) like elemental sulphur, thiosulphate which can be taken up by bacteria and converted into simpler forms usable by plants by undergoing a series of transformations. So, keeping the importance of sulphur in view for various soil types, oilseed crops and role of microorganisms in making them available to plants, we made an effort to isolate, optimize, and characterize SOB. Three potential strains of bacteria were isolated, namely SSF7, SSA21, and SSS6, showing sulphate production of concentration, i.e. 2.268, 3.102, and 2.785 mM, respectively. Also, these were optimized for various culture conditions like carbon, nitrogen source, pH, temperature, and incubation time, and characterization was also done.
Abstract: The efficiency of heavy metals removal from sewage
sludge in bioleaching processes with heterotrophic, chemoautotrophic
(sulphur-oxidizing) sludge cenoses and chemical leaching (in
distilled water, weakly acidic or alkaline medium) was compared.
The efficacy of heavy metals removal from sewage sludge varies
from 83 % (Zn) up to 14 % (Cr) and follows the order: Zn > Mn > Cu
> Ni > Co > Pb > Cr. The advantages of metals bioleaching process
at heterotrophic metabolism were shown. A new process for
bioconversation of sewage sludge into fertilizer at middle
temperatures after partial heavy metals removal was developed. This
process is based on enhancing vital ability of heterotrophic
microorganisms by adding easily metabolized nutrients and synthesis
of metabolites by growing sludge cenoses. These metabolites possess
the properties of heavy metals extractants and flocculants which
provide the enhancement of sludge flocks sedimentation. The process
results in biomineral fertilizer of prolonged action with immobilized
sludge bioelements. The fertilizer satisfies the EU limits for the
sewage sludge of agricultural utilization. High efficiency of the
biomineral fertilizer obtained has been demonstrated in vegetation
experiments.
Abstract: The present investigation deals with bioleaching of spent petroleum catalyst using At. ferrooxidans and At. thiooxidans. The spent catalyst used in the present study was pretreated with acetone to remove the oily hydrocarbons. FESEM and XPS analysis indicated the presence of metals in sulfide and oxide forms in spent catalyst. Both At. ferrooxidans and At. thiooxidans were found to be highly effective in producing the acid. Bioleaching with At. ferrooxidans and At. thiooxidans led to higher recovery of metals compare to control. During bioleaching similar recoveries of metals were obtained using At. ferrooxidans and At. thiooxidans. This might be due to the presence of metals as soluble oxides and sulphides in the spent catalyst. At the end of bioleaching, about 87-90% Ni, 34% Al, 65-73% Mo and 92-97% V were leached using above bacteria. It is elucidated that bioleaching with At. thiooxidans is comparatively more advantageous due to lower cost of sulphur.
Abstract: In the present study, the effect of ferrous sulfate concentration and total solids on bioleaching of heavy metals from sewage sludge has been examined using indigenous iron-oxidizing microorganisms. The experiments on effects of ferrous sulfate concentrations on bioleaching were carried out using ferrous sulfate of different concentrations (5-20 g L-1) to optimize the concentration of ferrous sulfate for maximum bioleaching. A rapid change in the pH and ORP took place in first 2 days followed by a slow change till 16th day in all the sludge samples. A 10 g L-1 ferrous sulfate concentration was found to be sufficient in metal bioleaching in the following order: Zn: 69%>Cu: 52%>Cr: 46%>Ni: 45. Further, bioleaching using 10 g/L ferrous sulfate was found to be efficient up to 20 g L-1 sludge solids concentration. The results of the present study strongly indicate that using 10 g L-1 ferrous sulfate indigenous iron-oxidizing microorganisms can bring down pH to a value needed for significant metal solubilization.
Abstract: Bioleaching of spent catalyst using moderate thermophilic chemolithotrophic acidophiles in growth medium without Fe source was investigated with two different pulp densities and three different size fractions. All the experiments were conducted on shake flasks at a temperature of 65 °C. The leaching yield of Ni and Al was found to be promising with very high leaching yield of 92-96% followed by Al as 41-76%, which means both Ni and Al leaching were favored by the moderate thermophilic bioleaching compared to the mesophilic bioleaching. The acid consumption was comparatively higher for the 10% pulp density experiments. Comparatively minimal difference in the leaching yield with different size fractions and different pulp densities show no requirement of grinding and using low pulp density less than 10%. This process would rather be economical as well as eco-friendly process for future optimization of the recovery of metal values from spent catalyst.
Abstract: The recovery of metal values and safe disposal of
spent catalyst is gaining interest due to both its hazardous nature and
increased regulation associated with disposal methods. Prior to the
recovery of the valuable metals, removal of entrained deposits limit
the diffusion of lixiviate resulting in low recovery of metals must be
taken into consideration. Therefore, petroleum refinery spent catalyst
was subjected to acetone washing and roasting at 500oC. The treated
samples were investigated for metals bioleaching using
Acidithiobacillus ferrooxidans in batch reactors and the leaching
efficiencies were compared. It was found out that acetone washed
spent catalysts results in better metal recovery compare to roasted
spent. About 83% Ni, 20% Al, 50% Mo and 73% V were leached
using the acetone washed spent catalyst. In both the cases, Ni, V and
Mo was high compared to Al.
Abstract: In this study, the ability of Aspergillus niger and
Penicillium simplicissimum to extract heavy metals from a spent
refinery catalyst was investigated. For the first step, a spent
processing catalyst from one of the oil refineries in Iran was
physically and chemically characterized. Aspergillus niger and
Penicillium simplicissimum were used to mobilize Al/Co/Mo/Ni from
hazardous spent catalysts. The fungi were adapted to the mixture of
metals at 100-800 mg L-1 with increments in concentration of 100 mg
L-1. Bioleaching experiments were carried out in batch cultures. To
investigate the production of organic acids in sucrose medium,
analyses of the culture medium by HPLC were performed at specific
time intervals after inoculation. The results obtained from Inductive
coupled plasma-optical emission spectrometry (ICP-OES) showed
that after the one-step bioleaching process using Aspergillus niger,
maximum removal efficiencies of 27%, 66%, 62% and 38% were
achieved for Al, Co, Mo and Ni, respectively. However, the highest
removal efficiencies using Penicillium simplicissimum were of 32%,
67%, 65% and 38% for Al, Co, Mo and Ni, respectively
Abstract: Spent petroleum catalyst from Korean petrochemical
industry contains trace amount of metals such as Ni, V and Mo.
Therefore an attempt was made to recover those trace metal using
bioleaching process. Different leaching parameters such as Fe(II)
concentration, pulp density, pH, temperature and particle size of
spent catalyst particle were studied to evaluate their effects on the
leaching efficiency. All the three metal ions like Ni, V and Mo
followed dual kinetics, i.e., initial faster followed by slower rate. The
percentage of leaching efficiency of Ni and V were higher than Mo.
The leaching process followed a diffusion controlled model and the
product layer was observed to be impervious due to formation of
ammonium jarosite (NH4)Fe3(SO4)2(OH)6. In addition, the lower
leaching efficiency of Mo was observed due to a hydrophobic coating
of elemental sulfur over Mo matrix in the spent catalyst.