Abstract: The mechanical properties of blends consisting of
plasticized poly(vinyl butyral) (PVB) and plasticized poly(vinyl
chloride) (PVC) are studied, in order to evaluate the possibility of
using recycled PVB waste derived from windshields. PVC was
plasticized with 38% of diisononyl phthalate (DINP), while PVB was
plasticized with 28% of triethylene glycol, bis(2-ethylhexanoate)
(3GO). The optimal process conditions for the PVB/PVC blend in 1:1
ratio were determined. Entropy was used in order to theoretically
predict the blends miscibility. The PVB content of each blend
composition used was ranging from zero to 100%. Tensile strength
and strain were tested. In addition, a comparison between recycled
and original PVB, used as constituents of the blend, was performed.
Abstract: Polylactic acid-g-polyvinyl acetate (PLLA-g-PVAc)
was used as a compatibilizer for 50/50 starch/PLLA blend. PLLA-g-
PVAc with different mol% of PVAc contents were prepared by
grafting PVAc onto PLLA backbone via free radical polymerization
in solution process. Various conditions such as type and the amount
of initiator, monomer concentration, polymerization time and
temperature were studied. Results showed that the highest mol% of
PVAc grafting (16 mol%) was achieved by conducting graft
copolymerization in toluene at 110°C for 10 h using DCP as an
initiator. Chemical structure of the PVAc grafted PLLA was
confirmed by 1H NMR. Blending of modified starch and PLLA in the
presence compatibilizer with different amounts and mol% PVAc was
acquired using internal mixer at 160°C for 15 min. Effects of PVAc
content and the amount of compatibilizer on mechanical properties of
polymer blend were studied. Results revealed that tensile strength and
tensile modulus of polymer blend with higher PVAc grafting content
compatibilizer showed better properties than that of lower PVAc
grafting content compatibilizer. The amount of compatibilizer was
found optimized in the range of 0.5-1.0 Wt% depending on the mol%
PVAc.
Abstract: The state of melt viscosity in injection process is significantly influenced by the setting parameters due to that the shear rate of injection process is higher than other processes. How to determine plastic melt viscosity during injection process is important to understand the influence of setting parameters on the melt viscosity. An apparatus named as pressure sensor bushing (PSB) module that is used to evaluate the melt viscosity during injection process is developed in this work. The formulations to coupling melt viscosity with fill time and injection pressure are derived and then the melt viscosity is determined. A test mold is prepared to evaluate the accuracy on viscosity calculations between the PSB module and the conventional approaches. The influence of melt viscosity on the tensile strength of molded part is proposed to study the consistency of injection quality.
Abstract: The present work consecutively on synthesis and
characterization of composites, Al/Al alloy A 384.1 as matrix in
which the main ingredient as Al/Al-5% MgO alloy based metal
matrix composite. As practical implications the low cost processing
route for the fabrication of Al alloy A 384.1 and operational
difficulties of presently available manufacturing processes based in
liquid manipulation methods. As all new developments, complete
understanding of the influence of processing variables upon the final
quality of the product. And the composite is applied comprehensively
to the acquaintance for achieving superiority of information
concerning the specific heat measurement of a material through the
aid of thermographs. Products are evaluated concerning relative
particle size and mechanical behavior under tensile strength.
Furthermore, Taguchi technique was employed to examine the
experimental optimum results are achieved, owing to effectiveness of
this approach.
Abstract: Carbon fibers are fabricated from different materials,
such as special polyacrylonitrile (PAN) fibers, rayon fibers and pitch.
Among these three groups of materials, PAN fibers are the most
widely used precursor for the manufacture of carbon fibers. The
process of fabrication carbon fibers from special PAN fibers includes
two steps; oxidative stabilization at low temperature and
carbonization at high temperatures in an inert atmosphere. Due to the
high price of raw materials (special PAN fibers), carbon fibers are
still expensive.
In the present work the main goal is making carbon fibers from
low price commercial PAN fibers with modified chemical
compositions. The results show that in case of conducting completes
stabilization process, it is possible to produce carbon fibers with
desirable tensile strength from this type of PAN fibers. To this
matter, thermal characteristics of commercial PAN fibers were
investigated and based upon the obtained results, with some changes
in conventional procedure of stabilization in terms of temperature
and time variables; the desirable conditions of complete stabilization
is achieved.
Abstract: An effect of rolling temperature on the mechanical properties and microstructural evolution of an Al-Mg-Si alloy was studied. The material was rolled up to a true strain of ~0.7 at three different temperatures viz; room temperature, liquid propanol and liquid nitrogen. The liquid nitrogen rolled sample exhibited superior properties with a yield and tensile strength of 332 MPa and 364 MPa, respectively, with a reasonably good ductility of ~9%. The liquid nitrogen rolled sample showed around 54 MPa increase in tensile strength without much reduction in the ductility as compared to the as received T6 condition alloy. The microstructural details revealed equiaxed grains in the annealed and solutionized sample and elongated grains in the rolled samples. In addition, the cryorolled samples exhibited fine grain structure compared to the room temperature rolled samples.
Abstract: In this study, an ablation, mechanical and thermal properties of a rocket motor insulation from phenolic/ fiber matrix composites forming a laminate with different fiber between fiberglass and locally available synthetic fibers. The phenolic/ fiber matrix composites was mechanics and thermal properties by means of tensile strength, ablation, TGA and DSC. The design of thermal insulation involves several factors.Determined the mechanical properties according to MIL-I-24768: Density >1.3 g/cm3, Tensile strength >103 MPa and Ablation
Abstract: In this study, the thermal and mechanical properties of
basalt fibre reinforced concrete were investigated. The volume
fractions of basalt fibre of (0.1, 0.2, 0.3, and 0.5% by total mix
volume) were used. Properties such as heat transfer, compressive and
splitting tensile strengths were examined. Results indicated that the
strength increases with increase the fibre content till 0.3% then there
is a slight reduction when 0.5% fibre used. Lower amount of heat
conducted through the thickness of concrete specimens than the
conventional concrete was also recorded.
Abstract: The objective of this work is to study the influence of the properties of the substrate on the retrofit (thin repair) of damaged concrete elements, with the SCC. Fluidity, principal characteristic of the SCC, would enable it to cover and adhere to the concrete to be repaired. Two aspects of repair are considered, the bond (Adhesion) and the tensile strength and the cracking. The investigation is experimental; It was conducted over test specimens made up of ordinary concrete prepared and hardened in advance (the material to be repaired) over which a self compacting concrete layer is cast. Three alternatives of SC concrete and one ordinary concrete (comparison) were tested. It appears that the self-compacting concrete constitutes a good material for repairing. It follows perfectly the surfaces- forms to be repaired and allows a perfect bond. Fracture tests made on specimens of self-compacting concrete show a brittle behaviour. However when a small percentage of fibres is added, the resistance to cracking is very much improve.
Abstract: Laser soldering is based on applying some soldering material (albumin) onto the approximated edges of the cut and heating the solder (and the underlying tissues) by a laser beam. Endogenous and exogenous materials such as indocyanine green (ICG) are often added to solders to enhance light absorption. Gold nanoshells are new materials which have an optical response dictated by the plasmon resonance. The wavelength at which the resonance occurs depends on the core and shell sizes, allowing nanoshells to be tailored for particular applications. The purposes of this study was use combination of ICG and different concentration of gold nanoshells for skin tissue soldering and also to examine the effect of laser soldering parameters on the properties of repaired skin. Two mixtures of albumin solder and different combinations of ICG and gold nanoshells were prepared. A full thickness incision of 2×20 mm2 was made on the surface and after addition of mixtures it was irradiated by an 810nm diode laser at different power densities. The changes of tensile strength σt due to temperature rise, number of scan (Ns), and scan velocity (Vs) were investigated. The results showed at constant laser power density (I), σt of repaired incisions increases by increasing the concentration of gold nanoshells in solder, Ns and decreasing Vs. It is therefore important to consider the tradeoff between the scan velocity and the surface temperature for achieving an optimum operating condition. In our case this corresponds to σt =1800 gr/cm2 at I~ 47 Wcm-2, T ~ 85ºC, Ns =10 and Vs=0.3mms-1.
Abstract: In present study, two kinds of thermal power plant ashes; one the fly ash and the other waste ash are mixed with adhesive tragacanth and cement to produce new composite materials. 48 new samples are produced by varying the percentages of the fly ash, waste ash, cement and tragacanth. The new samples are subjected to some tests to find out their properties such as thermal conductivity, compressive strength, tensile strength and sucking capability of water. It is found that; the thermal conductivity decreases with increasing amount of tragacanth in the mixture. The compressive, tensile strength increases when the rate of tragacanth is up to 1%, whilst as the amount of tragacanth increases up to 1.5%, the compressive, tensile strength decreases slightly. The rate of water absorption of samples was more than 30%. From this result, it is concluded that these materials can not be used as external plaster or internal plaster material that faces to water. They can be used in internal plaster unless touching water and they can be used as cover plaster under roof and riprap material in sandwich panels. It is also found that, these materials can be cut with saw, drilled with screw and painted with any kind of paint.
Abstract: The present study explains the effect of aggregate
gradation on moisture damage in bituminous mixes. Three types of
aggregate gradation and two types of binder; VG-30 and Polymer
modified bitumen (PMB-40) are used. Moisture susceptibility tests
like retained stability and tensile strength ratio (TSR) and static creep
test are conducted on Marshall specimens. The creep test was also
conducted for conditioned and unconditioned specimens to observe
the effect of moisture on creep behaviour. The results indicate that
Marshall stability value is higher in PMB-40 mix than VG-30 mixes.
Moisture susceptibility of PMB-40 mixes is low when compared with
mix using VG-30. The reduction in retained stability, and indirect
tensile strength and increase in creep are evaluated for finer, coarser
and normal gradation of aggregate to observe the effect of gradation
on moisture susceptibility of mixes. The retained stability is least
affected when compared with other moisture susceptibility
parameters
Abstract: High strength concrete (HSC) provides high strength
but lower ductility than normal strength concrete. This low ductility
limits the benefit of using HSC in building safe structures. On the
other hand, when designing reinforced concrete beams, designers
have to limit the amount of tensile reinforcement to prevent the
brittle failure of concrete. Therefore the full potential of the use of
steel reinforcement can not be achieved. This paper presents the idea
of confining concrete in the compression zone so that the HSC will
be in a state of triaxial compression, which leads to improvements in
strength and ductility. Five beams made of HSC were cast and tested.
The cross section of the beams was 200×300 mm, with a length of 4
m and a clear span of 3.6 m subjected to four-point loading, with
emphasis placed on the midspan deflection. The first beam served as
a reference beam. The remaining beams had different tensile
reinforcement and the confinement shapes were changed to gauge
their effectiveness in improving the strength and ductility of the
beams. The compressive strength of the concrete was 85 MPa and the
tensile strength of the steel was 500 MPa and for the stirrups and
helixes was 250 MPa. Results of testing the five beams proved that
placing helixes with different diameters as a variable parameter in the
compression zone of reinforced concrete beams improve their
strength and ductility.
Abstract: Experimental study on the influence of fibre content
on crack behaviour and propagation in synthetic-fibre reinforced
beams has been reported in this paper. The tensile behaviour of
metallic fibre concrete is evaluated in terms of residual flexural
tensile strength values determined from the load-crack mouth
opening displacement curve or load-deflection curve obtained by
applying a centre-point load on a simply supported notched prism.
The results achieved demonstrate that an increase in fibre content has
an almost negligible effect on compressive and tensile splitting
properties, causes a marginal increment in flexural tensile strength
and increasesthe Re3 value.
Abstract: In this present study, experimental work was
conducted to study the effectiveness of newly innovated steel-CFRP
composite (CFRP laminates sandwiched between two steel strips) as
stirrups. A total numbers of eight concrete beams were tested under
four point loads. Each beam measured 1600 mm long, 160mm width
and 240 mm depth. The beams were reinforced with different shear
reinforcements; one without stirrups, one with steel stirrups and six
with different types and numbers of steel-CRFR stirrups. Test results
indicated that the steel-CFRP stirrups had enhanced the shear
strength capacity of beams. Moreover, the tests revealed that steel-
CFRP stirrups reached to their ultimate tensile strength unlike FRP
stirrups which rupture at much lower level than their ultimate
strength as werereported in various researches.
Abstract: The purpose of this research study is to investigate the manner in which various loads affect the mechanical properties of the formed mild steel plates. The investigation focuses on examining the cross-sectional area of the metal plate at the centre of the formed mild steel plate. Six mild steel plates were deformed with different loads. The loads applied on the plates had a magnitude of 5 kg, 10 kg, 15 kg, 20 kg, 25 kg and 30 kg. The radius of the punching die was 120 mm and the loads were applied at room temperature. The investigations established that the applied load causes the Vickers microhardness at the cross-sectional area of the plate to increase due to strain hardening. Hence, the percentage increase of the hardness due to the load was found to be directly proportional to the increase in the load. Furthermore, the tensile test results for the parent material showed that the average Ultimate Tensile Strength (UTS) for the three samples was 308 MPa while the average Yield Strength and Percentage Elongation were 227 MPa and 38 % respectively. Similarly, the UTS of the formed components increased after the deformation of the plate, as such it can be concluded that the forming loads alter the mechanical properties of the materials by improving and strengthening the material properties.
Abstract: At the present, auto part industries have become higher challenge in strategy market. As this consequence, manufacturers need to have better response to customers in terms of quality, cost, and delivery time. Moreover, they need to have a good management in factory to comply with international standard maximum capacity and lower cost. This would lead companies to have to order standard part from aboard and become the major cost of inventory. The development of auto part research by recycling materials experiment is to compare the auto parts from recycle materials to international auto parts (CKD). Factors studied in this research were the recycle material ratios of PU-foam, felt, and fabric. Results of recycling materials were considered in terms of qualities and properties on the parameters such as weight, sound absorption, water absorption, tensile strength, elongation, and heat resistance with the CKD. The results were showed that recycling materials would be used to replace for the CKD.
Abstract: Particle boards were prepared from Maize cob (MC) and urea-formaldehyde resin (UFR) on compression moulding machine. The amount of MC was varied from 50-120g while 30g of UFR was kept constant. Some mechanical properties of the particle boards were tested using the standard ASM methods. The results show that as the MC content increased from 50- 120g in 30g UFR, the hardness increased from about 6.89 x 102 to7.51 x 102MPa. Impact strength decreased from 3.3x 10-2 to 0.45 x 10-2J/M2, while tensile strength initially increased from 2.63 x 102 to 3.14 x 102 MPa as the MC increased from 50 to 60g in 30g UFR, thereafter, it decreased to about 1.35 x 102MPa at 120g in 30g content.
Abstract: There is a acute water problem especially in the dry
season in and around Perundurai (Erode district, Tamil Nadu, India)
where there are more number of tannery units. Hence an attempt was
made to use the waste water from tannery industry for construction
purpose. The mechanical properties such as compressive strength,
tensile strength, flexural strength etc were studied by casting various
concrete specimens in form of cube, cylinders and beams etc and
were found to be satisfactory. Hence some special properties such as
chloride attack, sulphate attack and chemical attack are considered
and comparatively studied with the conventional potable water. In
this experimental study the results of specimens prepared by using
treated and untreated tannery effluent were compared with the
concrete specimens prepared by using potable water. It was observed
that the concrete had some reduction in strength while subjected to
chloride attack, sulphate attack and chemical attack. So admixtures
were selected and optimized in suitable proportion to counter act the
adverse effects and the results were found to be satisfactory.
Abstract: The term hybrid composite refers to the composite
containing more than one type of fiber material as reinforcing fillers.
It has become attractive structural material due to the ability of
providing better combination of properties with respect to single fiber
containing composite. The eco-friendly nature as well as processing
advantage, light weight and low cost have enhanced the attraction
and interest of natural fiber reinforced composite. The objective of
present research is to study the mechanical properties of jute-coir
fiber reinforced hybrid polypropylene (PP) composite according to
filler loading variation. In the present work composites were
manufactured by using hot press machine at four levels of fiber
loading (5, 10, 15 and 20 wt %). Jute and coir fibers were utilized at a
ratio of (1:1) during composite manufacturing. Tensile, flexural,
impact and hardness tests were conducted for mechanical
characterization. Tensile test of composite showed a decreasing trend
of tensile strength and increasing trend of the Young-s modulus with
increasing fiber content. During flexural, impact and hardness tests,
the flexural strength, flexural modulus, impact strength and hardness
were found to be increased with increasing fiber loading. Based on
the fiber loading used in this study, 20% fiber reinforced composite
resulted the best set of mechanical properties.