Abstract: Magnesium borate(MB) istechnical ceramic for high heat-resisting, corrosion-resisting, super mechanical strength, superinsulation, light weight, high strength, and high coefficient of elasticity. Zinc borate (ZB) can be used as multi-functional synergistic additives with flame retardant additives in polymers. The most important properties are low solubility in water and high dehydration temperature. ZB dehydrates above 290°C and anhydrous ZB has thermal resistance about 400°C. In this study, the raw materials of ZnO, MgO and H3BO3 were used with mole ratio of 1:1:9. With the starting materials hydrothermal method was applied at a temperature of 100oC. The reaction time was determined as 30, 60, 90 and 120 minutes after some preliminary experiments. After the synthesis, the crystal structure and the morphology of the products were examined by X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). As a result, the forms of Zinc Oxide Borate Hydrate [Zn3B6O12.3.5H2O], Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.
Abstract: Dehydration behavior gives a hint about thermal properties of materials. It is important for the usage areas and transportation of minerals. Magnesium borates can be used as additive materials in areas such as in the production of superconducting materials, in the composition of detergents, due to the content of boron in the friction-reducing additives in oils and insulating coating compositions due to their good mechanic and thermal properties.
In this study, thermal dehydration behavior of admontite (MgO(B2O3)3.7(H2O)), which is a kind of magnesium borate mineral, is experimented by microwave energy at 360W. Structure of admontite is suitable for the investigation of dehydration behavior by microwave because of its seven moles of crystal water. It is seen that admontite lost its 28.7% of weight at the end of the 120 minutes heating in microwave furnace.
Abstract: Magnesium wastes are produced by many industrial activities. This waste problem is becoming a future problem for the world. Magnesium borates have many advantages such as; high corrosion resistance, heat resistance, high coefficient of elasticity and can also be used in the production of material against radiation. Addition, magnesium borates have great potential in sectors
including ceramic and detergents industry and superconducting materials.
In this study, using the starting materials of waste magnesium and H3BO3 the hydrothermal method was applied at a moderate
temperature of 70oC. Several mole ratios of waste magnesium to H3BO3 are selected as; 1:2, 1:4, 1:6, 1:8, 1:10. Reaction time was determined as 1 hour. After the synthesis, X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques are applied to products. As a result the forms of mcallisterite “Mg2(B6O7(OH)6)2.9(H2O)”, admontite “MgO(B2O3)3.7(H2O)” and magnesium boron hydrate (MgO(B2O3)3.6(H2O)” are obtained.
Abstract: The presented work is motivated by a French law
regarding nuclear waste management. A new conceptual Accelerator
Driven System (ADS) designed for the Minor Actinides (MA)
transmutation has been assessed by numerical simulation. The
MUltiple Spallation Target (MUST) ADS combines high thermal power (up to 1.4 GWth) and high specific power. A 30 mA and 1
GeV proton beam is divided into three secondary beams transmitted on three liquid lead-bismuth spallation targets. Neutron and thermalhydraulic
simulations have been performed with the code MURE, based on the Monte-Carlo transport code MCNPX. A methodology has been developed to define characteristic of the MUST ADS concept according to a specific transmutation scenario. The reference
scenario is based on a MA flux (neptunium, americium and curium)
providing from European Fast Reactor (EPR) and a plutonium multireprocessing
strategy is accounted for. The MUST ADS reference
concept is a sodium cooled fast reactor. The MA fuel at equilibrium is mixed with MgO inert matrix to limit the core reactivity and
improve the fuel thermal conductivity. The fuel is irradiated over five
years. Five years of cooling and two years for the fuel fabrication are
taken into account. The MUST ADS reference concept burns about 50% of the initial MA inventory during a complete cycle. In term of
mass, up to 570 kg/year are transmuted in one concept. The methodology to design the MUST ADS and to calculate fuel
composition at equilibrium is precisely described in the paper. A detailed fuel evolution analysis is performed and the reference scenario is compared to a scenario where only americium transmutation is performed.
Abstract: Homogeneous composites of alumina and zirconia
with a small amount of MgO (99%) were obtained for ZTA ceramic containing 0.05 wt% MgO in
1500 °C.
Abstract: In this paper, free vibration analysis of carbon nanotube (CNT) reinforced laminated composite panels is presented. Three types of panels such as flat, concave and convex are considered for study. Numerical simulation is carried out using commercially available finite element analysis software ANSYS. Numerical homogenization is employed to calculate the effective elastic properties of randomly distributed carbon nanotube reinforced composites. To verify the accuracy of the finite element method, comparisons are made with existing results available in the literature for conventional laminated composite panels and good agreements are obtained. The results of the CNT reinforced composite materials are compared with conventional composite materials under different boundary conditions.
Abstract: Waste problem is becoming a future problem all over the world. Magnesium wastes which can be used in recycling processes are produced by many industrial activities. Magnesium borates which have useful properties such as; high heat resistance, corrosion resistance, supermechanical strength, superinsulation, light weight, high coefficient of elasticity and so on. Addition, magnesium borates have great potential in the development of ceramic and detergents industry, whisker-reinforced composites, antiwear, and reducing friction additives.
In this study, using the starting materials of waste magnesium and H3BO3 the hydrothermal method was applied at a moderate temperature of 70oC with different reaction times. Several reaction times of waste magnesium to H3BO3 were selected as; 30, 60, 120, 240 minutes. After the synthesis, X-Ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR) techniques were applied to products. As a result, the forms of Admontite [MgO(B2O3)3.7(H2O)] and Mcallisterite [Mg2(B6O7(OH)6)2.9(H2O)] were synthesized.
Abstract: This paper presents a design of source encoding
calculator software which applies the two famous algorithms in the
field of information theory- the Shannon-Fano and the Huffman
schemes. This design helps to easily realize the algorithms without
going into a cumbersome, tedious and prone to error manual
mechanism of encoding the signals during the transmission. The
work describes the design of the software, how it works, comparison
with related works, its efficiency, its usefulness in the field of
information technology studies and the future prospects of the
software to engineers, students, technicians and alike. The designed
“Encodia" software has been developed, tested and found to meet the
intended requirements. It is expected that this application will help
students and teaching staff in their daily doing of information theory
related tasks. The process is ongoing to modify this tool so that it can
also be more intensely useful in research activities on source coding.
Abstract: Nano-MgO was successfully deposited on titania using deposition-precipitation method. The catalyst produced was characterised using FTIR, XRD, BET and XRF and its activity was tested on the transesterification reaction of soybean oil to biodiesel. The catalyst activity improved when the reaction temperature was increasedfrom 150 and 225 OC. It was also observed that increasing the reaction time above 1h had no significant benefit on conversion. The stability fixed MgO on TiO2 was investigated using XRF and ICP-OES. It was observed that MgO loss during the reaction was between 0.5-2.3 percent and that there was no correlation between the reaction temperature and the MgO loss.
Abstract: The effect of calcination temperature and MgO crystallite sizes on the structure and catalytic performance of TiO2 supported nano-MgO catalyst for the trans-esterification of soybean oil has been studied. The catalyst has been prepared by deposition precipitation method, characterised by XRD and FTIR and tested in an autoclave at 225oC. The soybean oil conversion after 15 minutes of the trans-esterification reaction increased when the calcination temperature was increased from 500 to 600oC and decreased with further increase in calcination temperature. Some glycerolysis activity was also detected on catalysts calcined at 600 and 700oC after 45 minutes of reaction. The trans-esterification reaction rate increased with the decrease in MgO crystallite size for the first 30 min.
Abstract: This paper presents the experimental as well as the
simulated performance studies on the transcritical CO2 heat pumps
for simultaneous water cooling and heating; effects of water mass
flow rates and water inlet temperatures of both evaporator and gas
cooler on the cooling and heating capacities, system COP and water
outlets temperatures are investigated. Study shows that both the
water mass flow rate and inlet temperature have significant effect on
system performances. Test results show that the effect of evaporator
water mass flow rate on the system performances and water outlet
temperatures is more pronounced (COP increases 0.6 for 1 kg/min)
compared to the gas cooler water mass flow rate (COP increases 0.4
for 1 kg/min) and the effect of gas cooler water inlet temperature is
more significant (COP decreases 0.48 for given ranges) compared to
the evaporator water inlet temperature (COP increases 0.43 for given
ranges). Comparisons of experimental values with simulated results
show the maximum deviation of 5% for cooling capacity, 10% for
heating capacity, 16% for system COP. This study offers useful
guidelines for selecting appropriate water mass flow rate to obtain
required system performance.
Abstract: High purity hydrogen and the valuable by-product of carbon nanotubes (CNTs) can be produced by the methane catalytic decomposition. The methane conversion and the performance of CNTs were determined by the choices of catalysts and the condition of decomposition reaction. In this paper, Ni/MgO and Ni/O-D (oxidized diamond) catalysts were prepared by wetness impregnation method. The effects of reaction temperature and space velocity of methane on the methane conversion were investigated in a fixed-bed. The surface area, structure and micrography were characterized with BET, XPS, SEM, EDS technology. The results showed that the conversion of methane was above 8% within 150 min (T=500) for 33Ni/O-D catalyst and higher than 25% within 120 min (T=650) for 41Ni/MgO catalyst. The initial conversion increased with the increasing temperature of the decomposition reaction, but their catalytic activities decreased rapidly while at too higher temperature. To decrease the space velocity of methane was propitious to promote the methane conversion, but not favor of the hydrogen yields. The appearance of carbon resulted from the methane decomposition lied on the support type and the condition of catalytic reaction. It presented as fiber shape on the surface of Ni/O-D at the relatively lower temperature such as 500 and 550, but as grain shape stacked on and overlayed on the surface of the metal nickel while at 650. The carbon fiber can form on the Ni/MgO surface at 650 and the diameter of the carbon fiber increased with the decreasing space velocity.
Abstract: Annotation of a protein sequence is pivotal for the understanding of its function. Accuracy of manual annotation provided by curators is still questionable by having lesser evidence strength and yet a hard task and time consuming. A number of computational methods including tools have been developed to tackle this challenging task. However, they require high-cost hardware, are difficult to be setup by the bioscientists, or depend on time intensive and blind sequence similarity search like Basic Local Alignment Search Tool. This paper introduces a new method of assigning highly correlated Gene Ontology terms of annotated protein sequences to partially annotated or newly discovered protein sequences. This method is fully based on Gene Ontology data and annotations. Two problems had been identified to achieve this method. The first problem relates to splitting the single monolithic Gene Ontology RDF/XML file into a set of smaller files that can be easy to assess and process. Thus, these files can be enriched with protein sequences and Inferred from Electronic Annotation evidence associations. The second problem involves searching for a set of semantically similar Gene Ontology terms to a given query. The details of macro and micro problems involved and their solutions including objective of this study are described. This paper also describes the protein sequence annotation and the Gene Ontology. The methodology of this study and Gene Ontology based protein sequence annotation tool namely extended UTMGO is presented. Furthermore, its basic version which is a Gene Ontology browser that is based on semantic similarity search is also introduced.
Abstract: Carbon nanotubes (CNTs) with their high mechanical,
electrical, thermal and chemical properties are regarded as promising
materials for many different potential applications. Having unique
properties they can be used in a wide range of fields such as
electronic devices, electrodes, drug delivery systems, hydrogen
storage, textile etc. Catalytic chemical vapor deposition (CCVD) is a
common method for CNT production especially for mass production.
Catalysts impregnated on a suitable substrate are important for
production with chemical vapor deposition (CVD) method. Iron
catalyst and MgO substrate is one of most common catalyst-substrate
combination used for CNT. In this study, CNTs were produced by
CCVD of acetylene (C2H2) on magnesium oxide (MgO) powder
substrate impregnated by iron nitrate (Fe(NO3)3•9H2O) solution. The
CNT synthesis conditions were as follows: at synthesis temperatures
of 500 and 800°C multiwall and single wall CNTs were produced
respectively. Iron (Fe) catalysts were prepared by with Fe:MgO ratio
of 1:100, 5:100 and 10:100. The duration of syntheses were 30 and
60 minutes for all temperatures and catalyst percentages. The
synthesized materials were characterized by thermal gravimetric
analysis (TGA), transmission electron microscopy (TEM) and Raman
spectroscopy.
Abstract: In this paper, we are presenting a new type of pointing interface for computers which provides mouse functionalities with near surface haptic feedback. Further, it can be configured as a haptic display where users may feel the basic geometrical shapes in the GUI by moving the finger on top of the device surface. These functionalities are achieved by tracking three dimensional positions of the neodymium magnet using Hall Effect sensors grid and generating like polarity haptic feedback using an electromagnet array. This interface brings the haptic sensations to the 3D space where previously it is felt only on top of the buttons of the haptic mouse implementations.
Abstract: Carbon nanotubes (CNTs) possess unique structural,
mechanical, thermal and electronic properties, and have been
proposed to be used for applications in many fields. However, to
reach the full potential of the CNTs, many problems still need to be
solved, including the development of an easy and effective
purification procedure, since synthesized CNTs contain impurities,
such as amorphous carbon, carbon nanoparticles and metal particles.
Different purification methods yield different CNT characteristics
and may be suitable for the production of different types of CNTs. In
this study, the effect of different purification chemicals on carbon
nanotube quality was investigated. CNTs were firstly synthesized by
chemical vapor deposition (CVD) of acetylene (C2H2) on a
magnesium oxide (MgO) powder impregnated with an iron nitrate
(Fe(NO3)3·9H2O) solution. The synthesis parameters were selected
as: the synthesis temperature of 800°C, the iron content in the
precursor of 5% and the synthesis time of 30 min. The liquid phase
oxidation method was applied for the purification of the synthesized
CNT materials. Three different acid chemicals (HNO3, H2SO4, and
HCl) were used in the removal of the metal catalysts from the
synthesized CNT material to investigate the possible effects of each
acid solution to the purification step. Purification experiments were
carried out at two different temperatures (75 and 120 °C), two
different acid concentrations (3 and 6 M) and for three different time
intervals (6, 8 and 15 h). A 30% H2O2 : 3M HCl (1:1 v%) solution
was also used in the purification step to remove both the metal
catalysts and the amorphous carbon. The purifications using this
solution were performed at the temperature of 75°C for 8 hours.
Purification efficiencies at different conditions were evaluated by
thermogravimetric analysis. Thermal and electrical properties of
CNTs were also determined. It was found that the obtained electrical
conductivity values for the carbon nanotubes were typical for organic
semiconductor materials and thermal stabilities were changed
depending on the purification chemicals.
Abstract: Nano MgO has been synthesized by hydration and
dehydration method by modifies the commercial MgO. The prepared
MgO had been investigated as a heterogeneous base catalyst for
transesterification process for biodiesel production using palm oil.
TGA, FT-IR and XRD results obtained from this study lie each other
and proved in the formation of nano MgO from decomposition of
Mg(OH)2. This study proved that the prepared nano MgO was a
better base transesterification catalyst compared to commercial MgO.
The nano MgO calcined at 600ºC had gives the highest conversion of
51.3% of palm oil to biodiesel.
Abstract: The present work consecutively on synthesis and
characterization of composites, Al/Al alloy A 384.1 as matrix in
which the main ingredient as Al/Al-5% MgO alloy based metal
matrix composite. As practical implications the low cost processing
route for the fabrication of Al alloy A 384.1 and operational
difficulties of presently available manufacturing processes based in
liquid manipulation methods. As all new developments, complete
understanding of the influence of processing variables upon the final
quality of the product. And the composite is applied comprehensively
to the acquaintance for achieving superiority of information
concerning the specific heat measurement of a material through the
aid of thermographs. Products are evaluated concerning relative
particle size and mechanical behavior under tensile strength.
Furthermore, Taguchi technique was employed to examine the
experimental optimum results are achieved, owing to effectiveness of
this approach.
Abstract: TiO2/MgO composite films were prepared by coating
the magnesium acetate solution in the pores of mesoporous TiO2
films using a dip coating method. Concentrations of magnesium
acetate solution were varied in a range of 1x10-4 – 1x10-1 M. The
TiO2/MgO composite films were characterized by scanning electron
microscopy (SEM), transmission electron microscropy (TEM),
electrochemical impedance spectroscopy(EIS) , transient voltage
decay and I-V test. The TiO2 films and TiO2/MgO composite films
were immersed in a 0.3 mM N719 dye solution. The Dye-sensitized
solar cells with the TiO2/MgO/N719 structure showed an optimal
concentration of magnesium acetate solution of 1x10-3 M resulting in
the MgO film estimated thickness of 0.0963 nm and giving the
maximum efficiency of 4.85%. The improved efficiency of dyesensitized
solar cell was due to the magnesium oxide film as the wide
band gap coating decays the electron back transfer to the triiodide
electrolyte and reduce charge recombination.
Abstract: This paper is based on a study conducted in 2006 to assess the impact of computer usage on health of National Institute for Medical Research (NIMR) staff. NIMR being a research Institute, most of its staff spend substantial part of their working time on computers. There was notion among NIMR staff on possible prolonged computer usage health hazards. Hence, a study was conducted to establish facts and possible mitigation measures. A total of 144 NIMR staff were involved in the study of whom 63.2% were males and 36.8% females aged between 20 and 59 years. All staff cadres were included in the sample. The functions performed by Institute staff using computers includes; data management, proposal development and report writing, research activities, secretarial duties, accounting and administrative duties, on-line information retrieval and online communication through e-mail services. The interviewed staff had been using computers for 1-8 hours a day and for a period ranging from 1 to 20 years. The study has indicated ergonomic hazards for a significant proportion of interviewees (63%) of various kinds ranging from backache to eyesight related problems. The authors highlighted major issues which are substantially applicable in preventing occurrences of computer related problems and they urged NIMR Management and/or the government of Tanzania opts to adapt their practicability.