Abstract: In this research (using induction furnace process)
nodular iron with three different percentages of copper (residual,
0.5% and 1,2%) was obtained. Chemical analysis was performed by
mass spectrometry and microstructures were characterized by Optical
Microscopy (ASTM E3) and Scanning Electron Microscopy (SEM).
The study of mechanical behavior was carried out in a mechanical
test machine (ASTM E8) and a Pin on disk tribometer (ASTM G99)
was used to assess wear resistance. It is observed that the dissolution
of copper in crystal lattice increases the pearlite structure improving
the wear and hardness behavior, but producing a contrary effect on
the energy absorption.
Abstract: In this work we report the recent progresses that have been achieved by our group in the last half decade on the field of computational proteomics. Specifically, we discuss the application of Molecular Dynamics Simulations and Electronic Structure Calculations in drug design, in the clarification of the structural and dynamic properties of proteins and enzymes and in the understanding of the catalytic and inhibition mechanism of cancer-related enzymes. A set of examples illustrate the concepts and help to introduce the reader into this important and fast moving field.
Abstract: Titanium nitride (TiN) has been synthesized using the
sheet plasma negative ion source (SPNIS). The parameters used for
its effective synthesis has been determined from previous
experiments and studies. In this study, further enhancement of the
deposition rate of TiN synthesis and advancement of the SPNIS
operation is presented. This is primarily achieved by the addition of
Sm-Co permanent magnets and a modification of the configuration in
the TiN deposition process. The magnetic enhancement is aimed at
optimizing the sputtering rate and the sputtering yield of the process.
The Sm-Co permanent magnets are placed below the Ti target for
better sputtering by argon. The Ti target is biased from –250V to –
350V and is sputtered by Ar plasma produced at discharge current of
2.5–4A and discharge potential of 60–90V. Steel substrates of
dimensions 20x20x0.5mm3 were prepared with N2:Ar volumetric
ratios of 1:3, 1:5 and 1:10. Ocular inspection of samples exhibit
bright gold color associated with TiN. XRD characterization
confirmed the effective TiN synthesis as all samples exhibit the (200)
and (311) peaks of TiN and the non-stoichiometric Ti2N (220) facet.
Cross-sectional SEM results showed increase in the TiN deposition
rate of up to 0.35μm/min. This doubles what was previously obtained
[1]. Scanning electron micrograph results give a comparative
morphological picture of the samples. Vickers hardness results gave
the largest hardness value of 21.094GPa.
Abstract: Independent component analysis (ICA) is a computational method for finding underlying signals or components from multivariate statistical data. The ICA method has been successfully applied in many fields, e.g. in vision research, brain imaging, geological signals and telecommunications. In this paper, we apply the ICA method to an analysis of mass spectra of oligomeric species emerged from aluminium sulphate. Mass spectra are typically complex, because they are linear combinations of spectra from different types of oligomeric species. The results show that ICA can decomposite the spectral components for useful information. This information is essential in developing coagulation phases of water treatment processes.