Abstract: In this study, the Compressive strength of concretes
made with Ground Granulated Blast furnace Slag (GGBS),
Pulverised Fuel Ash (PFA), Rice Husk Ash (RHA) and Waste Glass
Powder (WGP) after they were exposed 7800C (exposure duration of
around 60 minutes) and then allowed to cool down gradually in the
furnace for about 280 minutes at water binder ratio of 0.50 was
investigated. GGBS, PFA, RHA and WGP were used to replace up to
20% Portland cement in the control concrete. Test for the
determination of workability, compressive strength and tensile
splitting strength of the concretes were carried out and the results
were compared with control concrete. The test results showed that the
compressive strength decreased by an average of around 30% after
the concretes were exposed to the heating and cooling scenario.
Abstract: The main objective of the study is focused in
producing slag based geopolymer concrete obtained with the addition
of alkali activator. Test results indicated that the reaction of silicates
in slag is based on the reaction potential of sodium hydroxide and the
formation of alumino-silicates. The study also comprises on the
evaluation of the efficiency of polymer reaction in terms of the
strength gain properties for different geopolymer mixtures.
Geopolymer mixture proportions were designed for different binder
to total aggregate ratio (0.3 & 0.45) and fine to coarse aggregate ratio
(0.4 & 0.8). Geopolymer concrete specimens casted with normal
curing conditions reported a maximum 28 days compressive strength
of 54.75 MPa. The addition of glued steel fibres at 1.0% Vf in
geopolymer concrete showed reasonable improvements on the
compressive strength, split tensile strength and flexural properties of
different geopolymer mixtures. Further, comparative assessment was
made for different geopolymer mixtures and the reinforcing effects of
steel fibres were investigated in different concrete matrix.
Abstract: In the present study, M2 high speed steels were
fabricated by using electro-slag rapid remelting process. Carbide
structure was analysed and the fracture toughness and hardness were
also measured after austenitization treatment at 1190 and 1210oC
followed by tempering treatment at 535oC for billets with various
diameters from 16 to 60 mm. Electro-slag rapid remelting (ESRR)
process is an advanced ESR process combined by continuous casting
and successfully employed in this study to fabricate a sound M2 high
speed ingot. Three other kinds of commercial M2 high speed steels,
produced by traditional method, were also analysed for comparison.
Distribution and structure of eutectic carbides of the ESRR billet were
found to be comparable to those of commercial alloy and so was the
fracture toughness.
Abstract: High temperature is one of the most detrimental
effects that cause important changes in concrete’s mechanical,
physical, and thermo-physical properties. As a result of these
changes, especially high strength concrete (HSC), may exhibit
damages such as cracks and spallings. To overcome this problem,
incorporating polymer fibers such as polypropylene (PP) in concrete
is a very well-known method. In this study, using RRH, as a
sustainable material, instead of PP fiber in HSC to prevent spallings
and improve physical and thermo-physical properties were
investigated. Therefore, seven HSC mixtures with 0.25 water to
binder ratio were prepared incorporating silica fume and blast furnace
slag. PP and RRH were used at 0.2-0.5% and 0.5-3% by weight of
cement, respectively. All specimens were subjected to high
temperatures (20 (control), 300, 600 and 900˚C) with a heating rate
of 2.5˚C/min and after cooling, residual physical and thermo-physical
properties were determined.
Abstract: When insulation and rehabilitation of structures is important to use quality building materials with high utility value. One potentially interesting and promising groups of construction materials in this area are advanced, thermally insulating plaster silicate based. With the present trend reduction of energy consumption of building structures and reducing CO2 emissions to be developed capillary-active materials that are characterized by their low density, low thermal conductivity while maintaining good mechanical properties.
The paper describes the results of research activities aimed at the development of thermal insulating and rehabilitation material ongoing at the Technical University in Brno, Faculty of Civil Engineering. The achieved results of this development will be the basis for subsequent experimental analysis of the influence of thermal and moisture loads developed on these materials.
Abstract: This article describes to what extent the addition of energy by-products into the structures of the technical hemp filling materials influence their properties. The article focuses on the changes in physical-mechanical and thermal technical properties of materials after the addition of ash or FBC ash or slag in the binding component of material. Technical hemp filling materials are made of technical hemp shives bonded by the mixture of cement and dry hydrate lime. They are applicable as fillers of vertical or horizontal structures or roofs. The research used eight types of energy by-products of power or heating plants in the Czech Republic. Secondary energy products were dispensed in three different percentage ratios as a replacement of cement in the binding component. Density, compressive strength and determination of the coefficient of thermal conductivity after 28, 60 and 90 days of curing in a laboratory environment were determined and subsequently evaluated on the specimens produced.
Abstract: This paper presents a study on use of alkali activated bottom ash (BA) and ground granulated blast furnace slag (GGBS) blend in paver blocks. A preliminary effort on alkali-activated bottom ash, blast furnace slag based geopolymer (BA-GGBS-GP) mortar with river sand was carried out to identify the suitable mix for paver block. Several mixes were proposed based on the combination of BA-GGBS. The percentage ratio of BA: GGBS was selected as 100:0, 75:25, 50:50, 25:75 and 0:100 for the source material. Sodium based alkaline activators were used for activation. The molarity of NaOH was considered as 8M. The molar ratio of SiO2 to Na2O was varied from 1 to 4. Two curing mode such as ambient and steam curing 60°C for 24 hours were selected. The properties of paver block such as compressive strength split tensile strength, flexural strength and water absorption were evaluated as per IS15658:2006. Based on the preliminary study on BA-GGBS-GP mortar, the combinations of 25% BA with 75% GGBS mix for M30 and 75% BA with 25% GGBS mix for M35 grade were identified for paver block. Test results shows that the combination of BA-GGBS geopolymer paver blocks attained remarkable compressive strength under steam curing as well as in ambient mode at 3 days. It is noteworthy to know BA-GGBS-GP has promising future in the construction industry.
Abstract: Industries using conventional fossil fuels have an
interest in better understanding the mechanism of particulate
formation during combustion since such is responsible for emission
of undesired inorganic elements that directly impact the atmospheric
pollution level. Fine and ultrafine particulates have tendency to
escape the flue gas cleaning devices to the atmosphere. They also
preferentially collect on surfaces in power systems resulting in
ascending in corrosion inclination, descending in the heat transfer
thermal unit, and severe impact on human health. This adverseness
manifests particularly in the regions of world where coal is the
dominated source of energy for consumption.
This study highlights the behavior of calcium transformation as
mineral grains verses organically associated inorganic components
during pulverized coal combustion. The influence of existing type of
calcium on the coarse, fine and ultrafine mode formation mechanisms
is also presented. The impact of two sub-bituminous coals on particle
size and calcium composition evolution during combustion is to be
assessed. Three mixed blends named Blends 1, 2, and 3 are selected
according to the ration of coal A to coal B by weight. Calcium
percentage in original coal increases as going from Blend 1 to 3.
A mathematical model and a new approach of describing
constituent distribution are proposed. Analysis of experiments of
calcium distribution in ash is also modeled using Poisson distribution.
A novel parameter, called elemental index λ, is introduced as a
measuring factor of element distribution.
Results show that calcium in ash that originally in coal as mineral
grains has index of 17, whereas organically associated calcium
transformed to fly ash shown to be best described when elemental
index λ is 7.
As an alkaline-earth element, calcium is considered the
fundamental element responsible for boiler deficiency since it is the
major player in the mechanism of ash slagging process. The
mechanism of particle size distribution and mineral species of ash
particles are presented using CCSEM and size-segregated ash
characteristics. Conclusions are drawn from the analysis of
pulverized coal ash generated from a utility-scale boiler.
Abstract: Several review papers exist in literature related to the concrete containing mineral admixtures; however this paper reviews the durability characteristics of the concrete containing fly ash (FA), silica fume (SF), ground granulated blast furnace slag (GGBS), metakaolin (MK) and rice husk ash (RHA). Durability related properties reviewed include permeability, resistance to sulfate attack, alkali-silica reaction (ASR), carbonation, chloride ion penetration, freezing and thawing, abrasion, fire, acid and efflorescence. From review of existing literature, it is found that permeability of concrete depends upon the content of alumina in mineral admixtures, i.e. higher the alumina content, lesser the permeability which results higher resistance to sulfate and chloride ion penetration. Highly reactive mineral admixtures prevent more ASR and reduce efflorescence. The carbonation increases with the mineral admixtures because higher water binder ratio and lesser content of portlandite in concrete due to pozzolanic reaction. Mineral admixtures require air entrainment except MK and RHA for better resistance to freezing and thawing.
Abstract: Slag sample from copper smelting operation in a
water jacket furnace from DRC plant was used. The study intends to
determine the effect of cooling in the extraction of base metals. The
cooling methods investigated were water quenching, air cooling and
furnace cooling. The latter cooling ways were compared to the
original as received slag. It was observed that, the cooling rate of the
slag affected the leaching of base metals as it changed the phase
distribution in the slag and the base metals distribution within the
phases. It was also found that fast cooling of slag prevented
crystallization and produced an amorphous phase that encloses the
base metals. The amorphous slags from the slag dumps were more
leachable in acidic medium (HNO3) which leached 46%Cu, 95% Co,
85% Zn, 92% Pb and 79% Fe with no selectivity at pH0, than in
basic medium (NH4OH). The leachability was vice versa for the
modified slags by quenching in water which leached 89%Cu with a
high selectivity as metal extractions are less than 1% for Co, Zn, Pb
and Fe at ambient temperature and pH12. For the crystallized slags,
leaching of base metals increased with the increase of temperature
from ambient temperature to 60°C and decreased at the higher
temperature of 80°C due to the evaporation of the ammonia solution
used for basic leaching, the total amounts of base metals that were
leached in slow cooled slags were very low compared to the
quenched slag samples.
Abstract: Alkali Activated Slag Concrete (AASC) mixes are manufactured by activating ground granulated blast furnace slag (GGBFS) using sodium hydroxide and sodium silicate solutions. The aim of the present experimental research was to investigate the effect of increasing the dosages of sodium oxide (Na2O, in the range of 4 to 8%) and the activator modulus (Ms) (i.e. the SiO2/Na2O ratio, in the range of 0.5 to 1.5) of the alkaline solutions, on the workability and strength characteristics of self-cured (air-cured) alkali activated Indian slag concrete mixes. Further the split tensile and flexure strengths for optimal mixes were studied for each dosage of Na2O.It is observed that increase in Na2O concentration increases the compressive, split-tensile and flexural strengths, both at the early and later-ages, while increase in Ms, decreases the workability of the mixes. An optimal Ms of 1.25 is found at various Na2O dosages. No significant differences in the strength performances were observed between AASCs manufactured with alkali solutions prepared using either of potable and de-ionized water.
Abstract: In the context of large volume Big Divisor (nearly)
SLagy D3/D7 μ-Split SUSY [1], after an explicit identification
of first generation of SM leptons and quarks with fermionic superpartners
of four Wilson line moduli, we discuss the identification of
gravitino as a potential dark matter candidate by explicitly calculating
the decay life times of gravitino (LSP) to be greater than age of
universe and lifetimes of decays of the co-NLSPs (the first generation
squark/slepton and a neutralino) to the LSP (the gravitino) to be
very small to respect BBN constraints. Interested in non-thermal
production mechanism of gravitino, we evaluate the relic abundance
of gravitino LSP in terms of that of the co-NLSP-s by evaluating
their (co-)annihilation cross sections and hence show that the former
satisfies the requirement for a potential Dark Matter candidate. We
also show that it is possible to obtain a 125 GeV light Higgs in our
setup.
Abstract: The setting agent Ca(OH)2 for activation of slag
cement is used in the proportions of 0%, 2%, 4%, 6%, 8% and 10%
by various methods (substitution and addition by mass of slag
cement). The physical properties of slag cement activated by the
calcium hydroxide at anhydrous and hydrated states (fineness,
particle size distribution, consistency of the cement pastes and setting
times) were studied. The activation method by the mineral activator
of slag cement (latent hydraulicity) accelerates the hydration process
and reduces the setting times of the cement activated.
Abstract: Climate change and environmental pressures are
major international issues nowadays. It is time when governments,
businesses and consumers have to respond through more
environmentally friendly and aware practices, products and policies.
This is the prime time to develop alternative sustainable construction
materials, reduce greenhouse gas emissions, save energy, look to
renewable energy sources and recycled materials, and reduce waste.
The utilization of waste materials (slag, fly ash, glass beads, plastic
and so on) in concrete manufacturing is significant due to its
engineering, financial, environmental and ecological benefits. Thus,
utilization of waste materials in concrete production is very much
helpful to reach the goal of the sustainable construction. Therefore,
this study intends to use glass beads in concrete production.
The paper reports on the performance of 9 different concrete
mixes containing different ratios of glass crushed to 5 mm - 20 mm
maximum size and glass marble of 20 mm size as coarse aggregate.
Ordinary Portland cement type 1 and fine sand less than 0.5 mm were
used to produce standard concrete cylinders. Compressive strength
tests were carried out on concrete specimens at various ages. Test
results indicated that the mix having the balanced ratio of glass beads
and round marbles possess maximum compressive strength which is
3889 psi, as glass beads perform better in bond formation but have
lower strength, on the other hand marbles are strong in themselves
but not good in bonding. These mixes were prepared following a
specific W/C and aggregate ratio; more strength can be expected to
achieve from different W/C, aggregate ratios, adding admixtures like
strength increasing agents, ASR inhibitor agents etc.
Abstract: Reinforced Concrete (RC) structures strengthened
with fiber reinforced polymer (FRP) lack in thermal resistance under
elevated temperatures in the event of fire. This phenomenon led to
the lining of strengthened concrete with thin high performance
cementitious composites (THPCC) to protect the substrate against
elevated temperature. Elevated temperature effects on THPCC, based
on different cementitious materials have been studied in the past but
high-alumina cement (HAC)-based THPCC have not been well
characterized. This research study will focus on the THPCC based on
HAC replaced by 60%, 70%, 80% and 85% of ground granulated
blast furnace slag (GGBS). Samples were evaluated by the
measurement of their mechanical strength (28 & 56 days of curing)
after exposed to 400°C, 600°C and 28°C of room temperature for
comparison and corroborated by their microstructure study. Results
showed that among all mixtures, the mix containing only HAC
showed the highest compressive strength after exposed to 600°C as
compared to other mixtures. However, the tensile strength of THPCC
made of HAC and 60% GGBS content was comparable to the
THPCC with HAC only after exposed to 600°C. Field emission
scanning electron microscopy (FESEM) images of THPCC
accompanying Energy Dispersive X-ray (EDX) microanalysis
revealed that the microstructure deteriorated considerably after
exposure to elevated temperatures which led to the decrease in
mechanical strength.
Abstract: Reactive powder concretes (RPC) are characterized by
particle diameter not exceeding 600 μm and having very high
compressive and tensile strengths. This paper describes a new
generation of micro concrete, which has an initial, as well as a final,
high physicomechanical performance. To achieve this, we replaced
the Portland cement (15% by weight) by materials rich in Silica (Slag
and Dune Sand).
The results obtained from tests carried out on RPC show that
compressive and tensile strengths increase when adding the additions,
thus improving the compactness of mixtures via filler and pozzolanic
effect.
With a reduction of the aggregate phase in the RPC and the
abundance of dune sand (south Algeria) and slag (industrial byproduct
of blast furnace), the use of the RPC will allow Algeria to
fulfil economical as well as ecological requirements.
Abstract: As the resources for naturally occurring aggregates
diminished at an ever increasing rate, researchers are keen to utilize
recycled materials in road construction in harmony with sustainable
development. Steel slag, a waste product from the steel making
industry, is one of the recycled materials reported to exhibit great
potential to replace naturally occurring aggregates in asphalt
mixtures. This paper presents the resilient modulus properties of
steel slag asphalt mixtures subjected to short term oven ageing
(STOA). The resilient modulus test was carried out to evaluate the
stiffness of asphalt mixtures at 10ºC, 25ºC and 40ºC. Previous
studies showed that stiffness changes in asphalt mixture played an
important role in inflicting pavement distress particularly cracking
and rutting that are common at low and high temperatures
respectively. Temperature was found to significantly influence the
resilient modulus of asphalt mixes. The resilient modulus of the
asphalt specimens tested decreased by more than 90% when the test
temperature increased from 10°C to 40°C.
Abstract: In the current study, we have conducted an experimental investigation on the utilization of electronic arc furnace (EAF) reducing slag for the absorption of CO2 via wet grinding method. It was carried out by various grinding conditions. The slag was ground in the vibrating ball mill in the presence of CO2 and pure water under ambient temperature. The reaction behavior was monitored with constant pressure method, and the changes of experimental systems volume as a function of grinding time were measured. It was found that the CO2 absorption occurred as soon as the grinding started. The CO2 absorption was significantly increased in the case of wet grinding compare to the dry grinding. Generally, the amount of CO2 absorption increased as the amount of water, weight of slag and initial pressure increased. However, it was decreased when the amount of water exceeds 200ml and when smaller balls were used. The absorption of CO2 occurred simultaneously with the start of the grinding and it stopped when the grinding was stopped. According to this research, the CO2 reacted with the CaO inside the slag, forming CaCO3.
Abstract: Day by day technology increases and problems
associated with this technology also increase. Several researches
were carried out to investigate the deployment of such material safely
in geotechnical engineering in particular and civil engineering in
general. However, different types of waste material have such as
cement duct, fly ash and slag been proven to be suitable in several
applications. In this research cement dust mixed with different
percentages of sand will be used in some civil engineering
application as will be explained later in this paper throughout filed
and laboratory test. The used mixer (waste material with sand) prove
high performance, durability to environmental condition, low cost
and high benefits. At higher cement dust ratio, small cement ratio is
valuable for compressive strength and permeability. Also at small
cement dust ratio higher cement ratio is valuable for compressive
strength.
Abstract: The use of additions in cement in manufacturing,
mortar and concrete offers economic and ecological advantages. Cements with additions such as limestone, slag and natural
pouzzolana are produced in cement factories in Algeria. Several studies analyzed the effect of these additions on the physical and
mechanical properties as well as the durability of concrete. However,
few studies were conducted on the effect of local metakaolin on
mechanical properties and durability of concrete. The main purpose
of this paper is to analyze the performance of mortar and concrete with local metakaolin. The preparation of the metakaolin was carried
out by calcination of kaolin at a temperature of 850 °C for a period of 3 hours. The experimental results have shown that the rates of
substitutions of 10 and 15% metakaolin increases the compressive
strength and flexural strength at both early age and long term. The durability and the permeability were also improved by reducing the
coefficient of sorptivity.