Abstract: Antennas are devices for transmitting and/or receiving signals which make them a necessary component of any wireless system. In this paper, a thermal deposition technique is utilized as a method to fabricate antenna structures on substrates. Thin-film deposition is achieved by evaporating a source material (metals in our case) in a vacuum which allows vapor particles to travel directly to the target substrate which is encased with a mask that outlines the desired structure. The material then condenses back to solid state. This method is used in comparison to screen printing, chemical etching, and ink jet printing to indicate advantages and disadvantages to the method. The antenna created undergoes various testing of frequency ranges, conductivity, and a series of flexing to indicate the effectiveness of the thermal deposition technique. A single band antenna that is operated at 2.45 GHz intended for wearable and flexible applications was successfully fabricated through this method and tested. It is concluded that thermal deposition presents a feasible technique of producing such antennas.
Abstract: An electrically small meander line antenna is designed for impedance matching with RF transceiver chip CC1101. The design provides the flexibility of tuning the reactance of the antenna over a wide range of values: highly capacitive to highly inductive. The antenna was printed with silver ink on FR4 substrate using the screen printing design process. The antenna impedance was perfectly matched to CC1101 at 433 MHz. The measured radiation efficiency of the antenna was 81.3% at resonance. The 3 dB and 10 dB fractional bandwidth of the antenna was 14.5% and 4.78%, respectively. The read range of the antenna was compared with a copper wire monopole antenna over a distance of five meters. The antenna, with a perfect impedance match with RF transceiver chip CC1101, shows improvement in the read range compared to a monopole antenna over the specified distance.
Abstract: Through use of novel modern/rapid processing
techniques such as screen printing and Near-Infrared (NIR) radiative
curing, process time for the sintering of sintered nickel plaques,
applicable to alkaline nickel battery chemistries, has been drastically
reduced from in excess of 200 minutes with conventional convection
methods to below 2 minutes using NIR curing methods. Steps have
also been taken to remove the need for forming gas as a reducing
agent by implementing carbon as an in-situ reducing agent, within the
ink formulation.
Abstract: Most often the contaminants are not taken seriously into consideration, and this behavior comes out directly from the lack of monitoring and professional reporting about pollution in the printing facilities in Serbia. The goal of planned and systematic ozone measurements in ambient air of the screen printing facilities in Novi Sad is to examine of its impact on the employees health, and to track trends in concentration. In this study, ozone concentrations were determined by using discontinuous and continuous method during the automatic and manual screen printing process. Obtained results indicates that the average concentrations of ozone measured during the automatic process were almost 3 to 28 times higher for discontinuous and 10 times higher for continuous method (1.028 ppm) compared to the values prescribed by OSHA. In the manual process, average concentrations of ozone were within prescribed values for discontinuous and almost 3 times higher for continuous method (0.299 ppm).