Abstract: This paper deals with the performance of semi-light weight concrete, prepared by using wood ash pellets as coarse aggregates which were improved by partial replacement of cement with alccofine. Alccofine is a mineral admixture which contains high glass content obtained through the process of controlled granulation. This is finer than cement which carries its own pozzolanic property. Therefore, cement could be replaced by alccofine as 0%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, and 70% to enhance the strength and durability properties of concrete. High range water reducing admixtures (HRWA) were used in these mixes which were dosed up to 1.5% weight of the total cementitious content (alccofine & cement). It also develops the weaker transition zone into more impermeable layer. Specimens were subjected in both the accelerated curing method as well as conventional curing method. Experimental results were compared and reported, in that the maximum compressive strength of 32.6 MPa was achieved on 28th day with 30% replacement level in a density of 2200 kg/m3 to a conventional curing, while in the accelerated curing, maximum compressive strength was achieved at 40% replacement level. Rapid chloride penetration test (RCPT) output results for the conventional curing method at 0% and 70% give 3296.7 and 545.6 coulombs.
Abstract: This paper presents a maintenance policy for a system
consisting of two units. Unit 1 is gradually deteriorating and is
subject to soft failure. Unit 2 has a general lifetime distribution
and is subject to hard failure. Condition of unit 1 of the system
is monitored periodically and it is considered as failed when its
deterioration level reaches or exceeds a critical level N. At the
failure time of unit 2 system is considered as failed, and unit 2
will be correctively replaced by the next inspection epoch. Unit 1
or 2 are preventively replaced when deterioration level of unit 1
or age of unit 2 exceeds the related preventive maintenance (PM)
levels. At the time of corrective or preventive replacement of unit
2, there is an opportunity to replace unit 1 if its deterioration
level reaches the opportunistic maintenance (OM) level. If unit
2 fails in an inspection interval, system stops operating although
unit 1 has not failed. A mathematical model is derived to find
the preventive and opportunistic replacement levels for unit 1 and
preventive replacement age for unit 2, that minimize the long run
expected average cost per unit time. The problem is formulated and
solved in the semi-Markov decision process (SMDP) framework.
Numerical example is provided to illustrate the performance of the
proposed model and the comparison of the proposed model with an
optimal policy without opportunistic maintenance level for unit 1 is
carried out.
Abstract: Concrete construction in future has to be environmental friendly apart from being safe so that society at large is benefited by the huge investments made in the infrastructure projects. To achieve this, component materials of the concrete system have to be optimized with reference to sustainability. This paper presents a study on development of mix proportions of high volume fly ash concrete (HFC). A series of HFC mixtures with cement replacement levels varying between 50% and 65% were prepared with water/binder ratios of 0.3 and 0.35. Compressive strength values were obtained at different ages. From the experimental results, pozzolanic efficiency ratios and mix design curves for HFC were established.
Abstract: Fly ash-slag based Geopolymer Cement (GPC) is presenting mechanical properties and environmental advantages that make it the predominant “green” alternative to Portland Cement (PC). Although numerous life-cycle analyses praising its environmental advantages, disposal after the end of its life remains as an issue that has been barely explored. The present study is investigating the recyclability of fly ash-slag GPC as aggregate in mortars. The purpose of the study was to evaluate the effect of GPC fine Recycled Aggregates (RA), at replacement levels of 25% and 50%, on the main mechanical properties of PC and GPC mortar mixes. The results were compared with those obtained by corresponding mixes incorporating natural and PC-RA. The main physical properties of GPC-RA were examined and proven to be comparable to those of PC-RA and slightly inferior to those of natural sand. A negligible effect was observed at 28-day compressive and flexural strength of PC mortars with GPC aggregates having a milder effect than PC. As far as GPC mortars are concerned, the influence of GPC aggregates was enhancing for the investigated mechanical properties. Additionally, a screening test showed that recycled geopolymer aggregates are not prone of inducing alkali silica reaction.
Abstract: This paper reports an experimental work that aimed to investigate the effects of clay brick waste, as part of fine aggregate, on rendering mortar performance. The brick, in crushed form, was from a local brick manufacturer that was rejected due to being of-standard. It was used to replace 33.33 %, 50 %, 66.66 % and 100 % by weight of the quarry sand in mortar. Effects of the brick replacement on the mortar key properties intended for wall plastering were investigated; these are workability, compressive strength, flexural strength, linear shrinkage, water absorption by total immersion and by capillary suction. The results showed that as the brick replacement level increased, the mortar workability reduced. The linear shrinkage increases over time and decreases with the introduction of brick waste. The compressive and flexural strengths decrease with the increase of brick waste because of their great water absorption.
Abstract: In this study, the possibility of using unground oil palm ash (UOPA) for producing foamed concrete is investigated. The UOPA used in this study is produced by incinerating palm oil biomass at a temperature exceeding 1000ºC. A semi-structural density of 1300kg/m3 was used with filler to binder ratio of 1.5 and preliminary water to binder ratio of 0.45. Cement was replaced by UOPA at replacement levels of 0, 25, 35, 45, 55 and 65% by weight of binder. Properties such as density, compressive strength, drying shrinkage and water absorption were investigated to the age of 90 days. The mix with a 35% of UOPA content was chosen to be used as the base material of a newly designed interlocking, mortar-less block system.
Abstract: In the present research, whole meal barley flour
(WBF) was supplemented with gelatinized corn flour (GCF) in 0 and
30%. Whole meal wheat flour (WWF) was mixed with defatted rice
bran (DRB) to produce 0, 20, 25, and 30% replacement levels.
Rheological properties of dough were studied. Thermal properties
and starch crystallinity of flours were evaluated. Flat bread, balady
bread and pie were prepared from the different flour blends. The
different bakeries were sensory evaluated. Color of raw materials and
crust of bakery products were determined. Nutrients contents of raw
flours and food products were assessed. Results showed that addition
of GCF to WBF increased the viscosity and falling number of the
produced dough. Water absorption, dough development time and
dough stability increased with increasing the level of DRB in dough
while, weakening and mixing tolerance index decreased.
Extensibility and energy decreased, while, resistance to extension
increased as DRB level increased. Gelatinized temperature of WWF,
WBF, GCF, and DRB were 13.26, 35.09, 28.33, and 39.63,
respectively. Starch crystallinity was affected when DRB was added
to WWF. The highest protein content was present in balady bread
made from 70% WWF and 30% DRB. The highest calcium,
phosphorus, and potassium levels were present in products made
from 100% WBF. Sensory attributes of the products were slightly
affected by adding DRB and GCF. Conclusion: Addition of DRB or
GCF to WWF or WBF, respectively affect the physical, chemical,
rheological and sensory properties of balady bread, flat bread, and pie
while improved their nutritive values.
Abstract: This paper investigates the effectiveness of two
natural zeolites in reducing expansion of concrete due to alkali-silica
reaction. These natural zeolites have different reactive silica content.
Three aggregates; two natural sands and one crushed stone aggregate
were used while preparing mortar bars in accordance with accelerated
mortar bar test method, ASTM C1260. Performances of natural
zeolites are compared by examining the expansions due to alkali
silica reaction. Natural zeolites added to the mixtures at 10% and
20% replacement levels by weight of cement. Natural zeolite with
high reactive silica content had better performance on reducing
expansions due to ASR. In this research, using high reactive zeolite at
20% replacement levels was effective in mitigating expansions.
Abstract: Ceramic Waste Aggregates (CWAs) were made from
electric porcelain insulator wastes supplied from an electric power
company, which were crushed and ground to fine aggregate sizes. In
this study, to develop the CWA mortar as an eco–efficient, ground
granulated blast–furnace slag (GGBS) as a Supplementary
Cementitious Material (SCM) was incorporated. The water–to–binder
ratio (W/B) of the CWA mortars was varied at 0.4, 0.5, and 0.6. The
cement of the CWA mortar was replaced by GGBS at 20 and 40% by
volume (at about 18 and 37% by weight). Mechanical properties of
compressive and splitting tensile strengths, and elastic modulus were
evaluated at the age of 7, 28, and 91 days. Moreover, the chloride
ingress test was carried out on the CWA mortars in a 5.0% NaCl
solution for 48 weeks. The chloride diffusion was assessed by using an
electron probe microanalysis (EPMA). To consider the relation of the
apparent chloride diffusion coefficient and the pore size, the pore size
distribution test was also performed using a mercury intrusion
porosimetry at the same time with the EPMA. The compressive
strength of the CWA mortars with the GGBS was higher than that
without the GGBS at the age of 28 and 91 days. The resistance to the
chloride ingress of the CWA mortar was effective in proportion to the
GGBS replacement level.
Abstract: Fibre cement plates, often used in construction,
generally are made using quartz as an inert material, cement as a
binder and cellulose as a fibre. This paper, first of all, investigates the
mechanical properties and durability of fibre cement plates when
quartz is both partly and fully replaced with diatomite. Diatomite
does not only have lower density compared to quartz but also has
high pozzolanic activity. The main objective of this paper is the
investigation of the effects of supplementary cementing materials
(SCMs) on the short and long term mechanical properties and
durability characteristics of fibre cement plates prepared using
diatomite. Supplementary cementing materials such as ground
granulated blast furnace slug (GGBS) and fly ash (FA) are used in
this study. Volume proportions of 10, 20, 30 and 40% of GGBS and
FA are used as partial replacement materials to cement. Short and
long term mechanical properties such as compressive and flexural
strengths as well as sorptivity characteristics and mass were
investigated. Consistency and setting time at each replacement levels
of SCMs were also recorded. The effects of using supplementary
cementing materials on the carbonation and sulphate resistance of
fibre cement plates were then experimented. The results, first of all,
show that the use of diatomite as a full or partial replacement to
quartz resulted in a systematic decrease in total mass of the fibre
cement plates. The reduction of mass was largely due to the lower
density and finer particle size of diatomite compared to quartz. The
use of diatomite did not only reduce the mass of these plates but also
increased the compressive strength significantly as a result of its high
pozzolanic activity. The replacement levels of both GGBS and FA
resulted in a systematic decrease in short term compressive strength
with increasing replacement levels. This was essentially expected as
the total rate of hydration is much lower in GGBS and FA than that
of cement. Long term results however, indicated that the compressive
strength of fibre cement plates prepared using both GGBS and FA
increases with time and hence the compressive strength of plates
prepared using SCMs is either equivalent or more than the
compressive strength of plates prepared using cement alone.
Durability characteristics of fibre cement plates prepared using SCMs
were enhanced significantly. Measurements of sopritivty
characteristics were also indicated that the plates prepared using
SCMs has much lower water absorption capacities compared to
plates prepared cement alone. Much higher resistance to carbonation
and sulphate attach were observed with plates prepared using SCMs.
The results presented in this paper show that the use of SCMs does
not only support the production of more sustainable construction
materials but also enhances the mechanical properties and durability
characteristics of fibre cement plates.
Abstract: A large amount of blast furnace slag is generated in
China. Most ground granulated blast furnace slag (GGBS) however
ends up in low-grade applications. Blast furnace slag, ground to an
appropriate fineness, can be used as a partial replacement of
cementitious material in concrete. The potential for using GGBS in
structural concrete, e.g. concrete beams and columns is investigated
at Xi’an Jiaotong-Liverpool University (XJTLU). With 50% of CEM
I cement replaced with GGBS, peak hydration temperatures
determined in a suspended concrete slab reduced by 20%. This
beneficiary effect has not been further improved with 70% of CEM I
replaced with GGBS. Partial replacement of CEM I with GGBS has a
retardation effect on the early-age strength of concrete. More GGBS
concrete mixes will be conducted to identify an ‘optimum’
replacement level which will lead to a reduced thermal loading,
without significantly compromising the early-age strength of
concrete.
Abstract: This paper represents the results of long term strength of mortar incorporating Rice Husk Ash (RHA). For these work mortar samples were made according to ASTM standard C 109/C. OPC cement was partially replaced by RHA at 0, 10, 15, 20, 25 and 30 percent replacement level. After casting all samples were kept in controlled environment and curing was done up to 90 days. Test of mortar was performed on 3, 7, 28, 90, 365 and 700 days. It is noticed that OPC mortar shows better strength at early age than mortar having RHA but at 90 days and onward the picture is different. At 700 days it is observed that mortar containing 20% RHA shows better result than any other samples.
Abstract: In this paper, a parametric experimental study for producing paving blocks using fine and coarse waste glass is presented. Some of the physical and mechanical properties of paving blocks having various levels of fine glass (FG) and coarse glass (CG) replacements with fine aggregate (FA) are investigated. The test results show that the replacement of FG by FA at level of 20% by weight has a significant effect on the compressive strength, flexural strength, splitting tensile strength and abrasion resistance of the paving blocks as compared with the control sample because of puzzolanic nature of FG. The compressive strength, flexural strength, splitting tensile strength and abrasion resistance of the paving block samples in the FG replacement level of 20% are 69%, 90%, 47% and 15 % higher as compared with the control sample respectively. It is reported in the earlier works the replacement of FG by FA at level of 20% by weight suppress the alkali-silica reaction (ASR) in the concrete. The test results show that the FG at level of 20% has a potential to be used in the production of paving blocks. The beneficial effect on these properties of CG replacement with FA is little as compared with FG.
Abstract: Natural pozzolan (NP) is one of the potential
prehistoric alternative binders in the construction industry. It has
been investigated as cement replacement in ordinary concrete by
several researchers for many purposes. Various supplementary
cementitious materials (SCMs) such as fly ash, limestone dust and
silica fume are widely used in the production of SCC; however,
limited studies to address the effect of NP on the properties of SCC
are documented. The current research is composed of different SCC
paste and concrete mixtures containing different replacement levels
of local NP as an alternative SCM. The effect of volume of paste
containing different amounts of local NP related to W/B ratio and
cement content on SCC fresh properties was assessed. The variations
in the fresh properties of SCC paste and concrete represented by
slump flow (flowability) and the flow rate were determined and
discussed. The results indicated that the flow properties of SCC paste
and concrete mixtures, at their optimized superplasticizer dosages,
were affected by the binder content of local NP and the total volume
fraction of SCC paste.
Abstract: The purpose of this paper is to investigate the
durability of cement mortar in presence of Rice Husk Ash (RHA).
The strength and durability of mortar with different replacement
level (0%, 10%, 15%, 20%, 25% and 30%) of Ordinary Portland
Cement (OPC) by RHA is investigated here. RHA was
manufactured from an uncontrolled burning process. Test samples
were prepared with river sand of FM 2.73. Samples were kept in
controlled environment up to test time. The results show that
addition of RHA was shown better results for 20% replacement
level than OPC at 90 days. In durability test all samples passed for
20 cycles except 25% and 30% replacement level.
Abstract: Use of fly ash as a supplementary cementing material
in large volumes can bring both technological and economic benefits
for concrete industry. In this investigation mix proportions for high
volume fly ash concrete were determined at cement replacement
levels of 50%, 55%, 60% and 65% with low calcium fly ash. Flexural
and compressive strengths of different mixes were measured at ages
of 7, 28 and 90 days. Flexural strength of composite section prepared
from pavement quality and lean high volume fly ash concrete was
determined at the age of 28 days. High volume fly ash concrete mixes
exhibited higher rate of strength gain and age factors than
corresponding reference concrete mixes. The optimum cement
replacement level for pavement quality concrete was found to be
60%. The consideration of bond between pavement quality and lean
of high volume fly ash concrete will be beneficial in design of rigid
pavements.