Abstract: This paper represents the results of long term strength of mortar incorporating Rice Husk Ash (RHA). For these work mortar samples were made according to ASTM standard C 109/C. OPC cement was partially replaced by RHA at 0, 10, 15, 20, 25 and 30 percent replacement level. After casting all samples were kept in controlled environment and curing was done up to 90 days. Test of mortar was performed on 3, 7, 28, 90, 365 and 700 days. It is noticed that OPC mortar shows better strength at early age than mortar having RHA but at 90 days and onward the picture is different. At 700 days it is observed that mortar containing 20% RHA shows better result than any other samples.
Abstract: The purpose of this paper is to investigate the
durability of cement mortar in presence of Rice Husk Ash (RHA).
The strength and durability of mortar with different replacement
level (0%, 10%, 15%, 20%, 25% and 30%) of Ordinary Portland
Cement (OPC) by RHA is investigated here. RHA was
manufactured from an uncontrolled burning process. Test samples
were prepared with river sand of FM 2.73. Samples were kept in
controlled environment up to test time. The results show that
addition of RHA was shown better results for 20% replacement
level than OPC at 90 days. In durability test all samples passed for
20 cycles except 25% and 30% replacement level.
Abstract: The performance of mortar subjected to high
temperature and cooled in normal ambient temperature was examined
in the laboratory to comply with the situation of burning & cooling of
a structure. Four series of cubical (5 X 5 X 5 cm) mortar specimens
were made from OPC, and partial replacement (10, 15, 20, 25 &
30%) of OPC by Rice Husk Ash (RHA) produced in the uncontrolled
environment. These specimens were heated in electric furnace to 200,
300, 400, 500 and 7000C. The specimens were kept in normal room
temperature for cooling. They were then tested for mechanical
properties and the results shows that particular 20% RHA mixed
mortar shows better fire performance.