Abstract: This article presents gate-voltage controlled humidity sensing performance of vanadium dioxide nanoparticles prepared from NH4VO3 precursor using microwave irradiation technique. The X-ray diffraction, transmission electron diffraction, and Raman analyses reveal the formation of VO2 (B) with V2O5 and an amorphous phase. The BET surface area is found to be 67.67 m2/g. The humidity sensing measurements using the patented lateral-gate MOSFET configuration was carried out. The results show the optimum response at 5 V up to 8 V of gate voltages for 10 to 80% of relative humidity. The dose-response equation reveals the enhanced resilience of the gated VO2 sensor which may saturate above 272% humidity. The response and recovery times are remarkably much faster (about 60 s) than in non-gated VO2 sensors which normally show response and recovery times of the order of 5 minutes (300 s).
Abstract: As a by-product of the biodiesel industries, glycerol
has been vastly generated which surpasses the market demand. It is
imperative to develop an efficient glycerol valorization processes in
minimizing the net energy requirement and intensifying the biodiesel
production. In this study, base-catalyzed transesterification of
glycerol with dimethyl carbonate using microwave irradiation as
heating method to produce glycerol carbonate was conducted by
varying grades of glycerol, i.e. 70%, 86% and 99% purity, that is
obtained from biodiesel plant. Metal oxide catalysts were used with
varying operating parameters including reaction time, DMC/glycerol
molar ratio, catalyst weight %, temperature and stirring speed. From
the study on the effect of different operating parameters it was found
that the type of catalyst used has the most significant effect on the
transesterification reaction. Amidst the metal oxide catalysts
examined, CaO gave the best performance. This study indicates the
feasibility of producing glycerol carbonate using different grade of
glycerol in both conventional thermal activation and microwave
irradiation with CaO as catalyst. Microwave assisted
transesterification (MAT) of glycerol into glycerol carbonate has
demonstrated itself as an energy efficient route by achieving 94.2%
yield of GC at 65°C, 5 minutes reaction time, 1 wt% CaO and
DMC/glycerol molar ratio of 2. The advantages of MAT
transesterification route has made the direct utilization of bioglycerol
from biodiesel production without the need of purification. This has
marked a more economical and less-energy intensive glycerol
carbonate synthesis route.
Abstract: This study shows the effect of carbon towards
molybdenum carbide alloy when exposed to Microwave. This
technique is also known as Microwave Induced Alloying (MIA) for
the preparation of molybdenum carbide. In this study ammonium
heptamolybdate solution and carbon black powder were
heterogeneously mixed and exposed to microwave irradiation for 2
minutes. The effect on amount of carbon towards the produced alloy
on morphological and oxidation states changes during microwave is
presented. In this experiment, it is expected carbon act as a reducing
agent with the ratio 2:7 molybdenum to carbon as the optimum for
the production of molybdenum carbide alloy. All the morphological
transformations and changes in this experiment were followed and
characterized using X-Ray Diffraction and FESEM.
Abstract: This paper presents the results of the preliminary investigation of microwave (MW) irradiation pretreatments on the anaerobic digestion of food residues using biochemical methane potential (BMP) assays. Low solids systems with a total solids (TS) content ranging from 5.0-10.0% were analyzed. The inoculum to bulk mass of substrates to water ratio was 1:2:2 (mass basis). The experimental conditions for pretreatments were as follows: a control (no MW irradiation), two runs with MW irradiation for 15 and 30 minutes at 320 W, and another two runs with MW irradiation at 528 W for 30 and 60 minutes. The cumulative biogas production were 6.3 L and 8.7 L for 15min/320 W and 30min/320 W MW irradiation conditions, respectively, and 10.5 L and 11.4 L biogas for 30min/528 W and 60min/528 W, respectively, as compared to the control giving 5.8 L biogas. Both an increase in exposure time of irradiation and power of MW had increased the rate and yield of biogas. Singlefactor ANOVA tests (p
Abstract: An efficient and green protocol for the synthesis of α-
aminonitriles derivatives by one-pot reaction of different aldehydes
with amines and trimethylsilyl cyanides has been developed using
natural alumina, alumina sulfuric acid (ASA), nano-γ-alumina, nanoalumina
sulfuric acid (nano-ASA) under microwave irradiation and
solvent-free conditions. The advantages of methods are short reaction
times, high yields, milder conditions and easy work up. The catalysts
can be recovered for the subsequent reactions and reused without any
appreciable loss of efficiency.