Abstract: In this article, we present a layout printing way for producing Fresnel zone on 1294-1b doped liquid crystal with Methyl-Red azo dye. We made a Fresnel zone mask with 25 zones and radius of 5 mm using lithography technique. With layout printing way, we recorded mask’s pattern on cell with λ=532 nm solid-state diode pump laser. By recording Fresnel zone pattern on cell and making Fresnel pattern on the surface of cell, odd and even zones, will form. The printed pattern, because of Azo dye’s photoisomerization, was permanent. Experimentally, we saw focal length tunability from 32 cm to 43 cm.
Abstract: Lactulose is a synthetic disaccharide which has remarkable applications in food and pharmaceutical fields. Lactulose is not found in nature and it is produced by isomerization reaction of lactose in an alkaline environment. It should be noted that this reaction has a very low yield since significant amount of lactose stays un-reacted in the system. Basically, purification of lactulose is difficult and costly. Previous studies have revealed that solubility of lactose and lactulose are significantly different in ethanol. Considering the fact that solubility is also affected by temperature itself, we investigated the effect of ethanol and temperature on separation process of lactose from the syrup containing lactose and lactulose. For this purpose, a saturated solution containing lactulose and lactose was made at three different temperatures; 25⁰C (room temperature), 31⁰C, and 37⁰C first. Five samples containing 2g saturated solution was taken and then 2g, 3g, 4g, 5g, and 6g ethanol separately was added to the sampling tubes. Sampling tubes were kept at respective temperatures afterward. The concentration of lactose and lactulose after separation process measured and analyzed by High Performance Liquid Chromatography (HPLC). Results showed that ethanol has such a greater impact than operating temperature on purification process. Also, it was observed that the maximum rate of separation occurred at initial amount of added ethanol.
Abstract: WO3/SiO2 catalysts were modified by an ion exchange
method with sodium hydroxide or potassium hydroxide solution. The
performance of the modified catalysts was tested in the metathesis of
ethylene and trans-2-butene to propylene. During ion exchange,
sodium and potassium ions played different roles. Sodium modified
catalysts revealed constant trans-2-butene conversion and propylene
selectivity when the concentrations of sodium in the solution were
varied. In contrast, potassium modified catalysts showed reduction of
the conversion and increase of the selectivity. From these results,
potassium hydroxide may affect the transformation of tungsten oxide
active species, resulting in the decrease in conversion whereas
sodium hydroxide did not. Moreover, the modification of catalysts by
this method improved the catalyst stability by lowering the amount of
coke deposited on the catalyst surface.
Abstract: This work studied the isomerization of 1-butene over
hydrotalcite catalyst. The experiments were conducted at various gas
hourly space velocity (GHSV), reaction temperature and feed
concentration. No catalyst deactivation was observed over the
reaction time of 16 hours. Two major reaction products were trans-2-
butene and cis-2-butene. The reaction temperature played an
important role on the reaction selectivity. At high operating
temperatures, the selectivity of trans-2-butene was higher than the
selectivity of cis-2-butene while it was opposite at lower reaction
temperature. In the range of operating condition, the maximum
conversion of 1-butene was found at 74% when T = 673 K and GHSV
= 4 m3/h/kg-cat with trans- and cis-2-butene selectivities of 54% and
46%, respectively. Finally, the kinetic parameters of the reaction
were determined.
Abstract: The effect of additional magnesium oxide (MgO) was
investigated by using the tungsten oxide supported on silica catalyst
(WOx/SiO2) physically mixed with MgO in a weight ratio 1:1. The
both fresh and spent catalysts were characterized by FT-Raman
spectrometer, UV-Vis spectrometer, X-Ray diffraction (XRD) and
temperature programmed oxidation (TPO). The results indicated that
the additional MgO could enhance the conversion of trans-2-butene
due to isomerization reaction. However, adding MgO would increase
the amount of coke deposit on the WOx/SiO2 catalyst. The TPO
profile presented two peaks when the WOx/SiO2 catalyst was
physically mixed with MgO. The further peak was suggested that
came from coke precursor could be produced by isomerization
reaction of undesired product. Then, the occurred coke precursor
could deposit and form coke on the acid catalyst.
Abstract: Pyrolysis of waste tire is one of alternative technique
to produce petrochemicals, such as light olefins, mixed C4, and monoaromatics.
Noble metals supported on acid zeolite catalysts were
reported as potential catalysts to produce the high valuable products
from waste tire pyrolysis. Especially, Pd supported on HBeta gave a
high yield of olefins, mixed C4, and mono-aromatics. Due to the high
prices of noble metals, the objective of this work was to investigate
whether or not a non-noble Ni metal can be used as a substitute of a
noble metal, Pd, supported on HBeta as a catalyst for waste tire pyrolysis.
Ni metal was selected in this work because Ni has high activity
in cracking, isomerization, hydrogenation and the ring opening of
hydrocarbons Moreover, Ni is an element in the same group as Pd
noble metal, which is VIIIB group, aiming to produce high valuable
products similarly obtained from Pd. The amount of Ni was varied as
5, 10, and 20% by weight, for comparison with a fixed 1 wt% Pd,
using incipient wetness impregnation. The results showed that as a
petrochemical-producing catalyst, 10%Ni/HBeta performed better
than 1%Pd/HBeta because it did not only produce the highest yield of
olefins and cooking gases, but the yields were also higher than
1%Pd/HBeta. 5%Ni/HBeta can be used as a substitute of
1%Pd/HBeta for similar crude production because its crude contains
the similar amounts of naphtha and saturated HCs, although it gave
no concentration of light mono-aromatics (C6-C11) in the oil. Additionally,
10%Ni/HBeta that gave high olefins and cooking gases was
found to give a fairly high concentration of the light mono-aromatics
in the oil.